锌冶炼废渣浸出液硫化法除砷的研究

以硫化钠为沉淀剂,将锌冶炼废渣浸出液中的砷以硫化砷的形式沉淀析出,实验考察了浸出液酸度、硫化钠加入量、反应时间等因素对除砷效率的影响.实验结果表明,当浸出液中游离H2SO4浓度为3 mol/L,Na2S·9H2O投加量为16.1 g/L(浸出液),反应时间为30 min时,浸出液中的砷去除率达到99.3%,较好地解决了...     

Dissolution behavior of representative elements from red mud (RM) by leaching with titanium white waste acid (TWWA)

Titanium white waste acid (TWWA) was used to dissolve the representative elements from red mud (RM) to achieve the goal of “treating waste with waste.” The leaching parameters on the leaching efficiency of Na, Sc, and Al were investigated, in which the analysis of XRD and SEM–EDS on RM and leaching residue was performed. The leaching kinetics of Na, Sc, and Al was studied with unreacted shrinking core model (USCM). The results show that the dealkalization efficiency was close to 100%, and the leaching efficiency of Sc and Al was 82% and 75%, respectively. Cancrinite was dissolved from RM, and then the elements such as Na, Al, and Ca reacted with H₂SO₄ of TWWA. Na existed in the leaching liquor in the form of ions. Ca reacted with sulfuric acid to form anhydrite, which existed in the leaching residue. The particles of RM became smaller and dispersed with each other by acid leaching. The leaching apparent activation energy of Na, Sc, and Al was 4.947 kJ/mol, 6.361 kJ/mol, and 31.666 kJ/mol, respectively. The leaching kinetic equation of Na, Sc, and Al was 1???(1???a)^2/3?=?0.084·exp[??595.05/T]·t by external diffusion, 1???2a/3???(1???a)^2/3?=?0.021·exp[??765.16/T]·t by internal diffusion, and ln(1???a)/3?+?(1???a)^?2/3 – 1?=?67.12·exp[??3808.8/T]·t by joint action, respectively.

     

Utilization of nSiO2, fly ash, and nSiO2/fly ash composite for the remediation of triphenyltin (TPT) from contaminated seawater

The removal of triphenyltin chloride from contaminated simulated seawater with adsorption method was discussed. The adsorbents used are fly ash, nSiO₂, and nSiO₂/fly ash composite. The results showed that the adsorption of the adsorbents increases with increase in the adsorbent dose, contact time, pH, stirring speed, initial TPT concentration, and decreased with increase in temperature. The adsorption fitted well with the Freundlich isotherm, showing that the adsorbent and TPT combined with function groups and the adsorption kinetics followed the pseudo-second-order kinetic model. The thermodynamic parameters were also evaluated. Optimal conditions for the adsorption of TPT from simulated seawater were applied to TPT removal from natural seawater. A higher removal efficiency of TPT (>99 %) was obtained for the nSiO₂/fly ash composite but not for fly ash and nSiO₂.     

热镀锌厂酸洗废水及锌灰中锌回收

分别采用蒸酸法、氨络合法和硫化沉淀法分离回收热镀锌厂酸洗废水及锌灰中锌铁。分别考察了酸洗废水中盐酸的逸出特性和氨浸法回收蒸馏渣中锌的效果;利用酸洗废水的酸度浸取锌灰中的锌并用氨络合法分离酸浸出液中锌铁;利用硫化物不同溶度积选择性沉淀酸浸出液中的锌,考察了Na2S加入量、曝气时间、反应溶液pH和反应时间的影响。研究结果表明硫酸的加入能提高盐酸的蒸发率但效果不明显,氨络合法难于有效分离锌铁,但硫化物沉淀法可较好地分离锌铁,铁回收率可达97．12％,锌沉淀率达到99．99％,所得沉淀物中ZnS纯度为68．51％。     

Immobilization of antimony waste slag by applying geopolymerization and stabilization/solidification technologies

During the processing of antimony ore by pyrometallurgical methods, a considerable amount of slag is formed. This antimony waste slag is listed by the European Union as absolutely hazardous waste with a European Waste Catalogue code of 10 08 08. Since the levels of antimony and arsenic in the leachate of the antimony waste slag are generally higher than the landfilling limits, it is necessary to treat the slag before landfilling. In this study, stabilization/solidification and geopolymerization technologies were both applied in order to limit the leaching potential of antimony and arsenic. Different combinations of pastes by using Portland cement, fly ash, clay, gypsum, and blast furnace slag were prepared as stabilization/solidification or geopolymer matrixes. Sodium silicate–sodium hydroxide solution and sodium hydroxide solution at 8 M were used as activators for geopolymer samples. Efficiencies of the combinations were evaluated in terms of leaching and unconfined compressive strength. None of the geopolymer samples prepared with the activators yielded arsenic and antimony leaching below the regulatory limit at the same time, although they yielded high unconfined compressive strength levels. On the other hand, the stabilization/solidification samples prepared by using water showed low leaching results meeting the landfilling criteria. Use of gypsum as an additive was found to be successful in immobilizing the arsenic and antimony.

ImplicationsDespite the wide use of antimony for industrial purposes, disposal options for an antimony waste such as slag from thermal processing of antimony ore were not reported in the existing literature. This study aimed to develop a disposal strategy for the hazardous antimony waste slag. The findings of this study would contribute to understand the immobilization mechanisms of antimony and arsenic and will also be of interest to the owners of the antimony ore processing plants and to researchers investigating the efficiency of stabilization/solidification and geopolymerization technologies.     

氢氧化钠-钢渣双碱法烧结烟气脱硫工艺

在鼓泡反应器中考察了氢氧化钠-钢渣双碱法烧结烟气脱硫的主要影响因素。结果表明,在温度为常温,钢渣反应时间为2 h,钢渣加入量为40 g,SO2进口浓度为2 400 mg/m3,钢渣粒径为200目以上,烟气流量为0.05 m3/h,循环液pH保持在7～8,Na+浓度为0.5 mol/L,循环液为500 mL的条件下,脱硫率可长时间保持在80%以上。同时,对钢渣-氢氧化钠双碱法烧结烟气脱硫机理进行了探讨。     

Deodorization of pig manure using lignin peroxidase with different electron acceptors

Odor pollution is a big environmental problem caused by large-scale livestock production in China, and developing a practical way to reduce these odors is pressing. In this study, a combination of 0.2–1.0 U/mL lignin peroxidase (LiP) and one of three peroxides (H₂O₂, CaO₂, 2Na₃CO₃·3H₂O₂) was examined for its efficiency in reducing the release of eight chemicals (propionic acid, isobutyric acid, isocaproic acid, isovaleric acid, phenol, p-cresol, indole, and skatole), NH₃, H₂S, and odor intensity from pig manure. The results showed an approximately 90% reduction in p-cresol, 40–60% reduction in odor intensity, 16.5–40% reduction in indolic compounds, and 25–40% reduction in volatile fatty acids. Being the electron acceptors of LiP, 2Na₃CO₃·3H₂O₂ and CaO₂ performed better than H₂O₂ in reducing the concentration of eight chemicals, NH_3, H₂S, and odor intensity from pig manure. The effect of deodorization can last for up to 72 hr.

Implications: In China, one of the major environmental problems caused by confined feeding is odor pollution, which brings a major threat to the sustainability, profitability, and growth of the livestock industry. To couple the LiP with the electron acceptors, a low–cost, simple, and feasible method for odor removal was established in this study. Based on the study results, a practical treatment method was provided for odor pollution and supply the farm operators a more flexible time to dispose treated manure.     

Pozzolanic reactivity of the synthetic slag from municipal solid waste incinerator cyclone ash and scrubber ash

This study investigates the pozzolanic reactions and compressive strength of the blended cement manufactured using synthetic slag obtained from municipal solid waste incinerator (MSWI) cyclone ash and scrubber ash as partial replacement of portland cement. The synthetic slag was made by co-melting the MSWI scrubber ash and cyclone ash mixtures at 1400 degrees C for 30 min. Following pulverization, the different types of slag were blended with cement as cement replacement at ratios ranging from 10 to 40 wt %. The synthetic slag thus obtained was quantified, and the characteristics of the slag-blended cement pastes were examined. These characteristics included the pozzolanic activity, compressive strength, hydration activity, crystal phases, species, and microstructure at various ages. The 90-day compressive strength developed by slag-blended cement pastes with 10 and 20 wt % of the cement replaced by the synthetic slag outperformed ordinary portland cement by 1-7 MPa. X-ray diffraction species analyses indicated that the hydrates in the slag-blended cement pastes were mainly portlandite, the calcium silicate hydrate gels, and calcium aluminate hydrate salts, similar to those found in ordinary portland cement paste. Differential thermal and thermogravimetric analysis also indicated that the slag reacted with portlandite to form calcium silicate hydrate gels.     

Preparation of Calcium Silicate Absorbent from Iron Blast Furnace Slag

ABSTRACT

Calcium silicate hydrate (CSH) solids were prepared from hydrated lime and iron blast furnace slag in an aqueous agitated slurry at 92 °C. While it was hoped a minimal lime/slag ratio could be used to create near-amorphous CSH, the surface area of the product improved by increasing the lime/slag weight ratio to 2. The addition of gypsum to the lime/slag system dramatically improved the formation of surface area, creating solids with 139 m²/g after 30 hr of reaction when only a minimal amount of lime was present. The SO₂ reactivity of solids prepared with gypsum greatly exceeded that of hydrated lime, achieving greater than 70-80% conversion of the alkalinity after 1 hr of reaction with SO₂. The use of CaCl₂ as an additive to the lime/slag system, in lieu of gypsum, also produced high-surface-area solids, 115 m²/g after 21 hr of reaction. However, the SO₂ reactivity of these sorbents was relatively low given the high surface area. This emphasized that the correlation between surface area and SO₂ reactivity was highly dependent on the solid phase, which was subsequently dependent on slurry composition.     

危险废物焚烧飞灰中重金属的稳定化处理

以上海市某危险废物焚烧厂飞灰为研究对象,采用Na2S、FeSO4、Na3PO4、和Na3C3N3S34种不同类型化学稳定药剂对飞灰进行了稳定化处理,并应用XRD、IR、SEM和连续化学提取法等仪器和手段对Na3C3N3S3处理焚烧飞灰的产物进行分析研究。研究结果表明,Na3C3N3S3对飞灰中的重金属Cr、Pb、Zn的稳定效果最好,Na3PO4对Cr无明显稳定效果。稳定后产物表面变得致密化,Na3C3N3S3与重金属离子生成的沉淀物干燥后无明显晶型存在。经稳定处理后飞灰中的重金属形态由弱酸提取态转化为可氧化态,减少了飞灰中重金属的浸出毒性。     

Impacts of simulated acid rain on recalcitrance of two different soils

Laboratory experiments were conducted to estimate the impacts of simulated acid rain (SAR) on recalcitrance in a Plinthudult and a Paleudalfs soil in south China, which were a variable and a permanent charge soil, respectively. Simulated acid rains were prepared at pH 2.0, 3.5, 5.0, and 6.0, by additions of different volumes of H₂SO₄ plus HNO₃ at a ratio of 6 to 1. The leaching period was designed to represent 5 years of local annual rainfall (1,200 mm) with a 33 % surface runoff loss. Both soils underwent both acidification stages of (1) cation exchange and (2) mineral weathering at SAR pH?2.0, whereas only cation exchange occurred above SAR pH?3.5, i.e., weathering did not commence. The cation exchange stage was more easily changed into that of mineral weathering in the Plinthudult than in the Paleudalfs soil, and there were some K⁺ and Mg²⁺ ions released on the stages of mineral weathering in the Paleudalfs soil. During the leaching, the release of exchangeable base cations followed the order Ca²⁺?>?K⁺?>?Mg²⁺?>?Na⁺ for the Plinthudult and Ca²⁺?>?Mg²⁺?>?Na⁺?>?K⁺ for the Paleudalfs soil. The SARs above pH?3.5 did not decrease soil pH or pH buffering capacity, while the SAR at pH?2.0 decreased soil pH and the buffering capacity significantly. We conclude that acid rain, which always has a pH from 3.5 to 5.6, only makes a small contribution to the acidification of agricultural soils of south China in the short term of 5 years. Also, Paleudalfs soils are more resistant to acid rain than Plinthudult soils. The different abilities to prevent leaching by acid rain depend upon the parent materials, types of clay minerals, and soil development degrees.     

应用神经网络方法优化垃圾焚烧模拟灰渣熔点的预测

采用SiO₂、Al₂O₃、CaO、Na₂CO₃、NaCl和Fe₂O₃等物质来模拟垃圾焚烧的真实灰渣组成,通过实验测定模拟灰渣熔点,建立神经网络模型进行熔点预测,由预测结果来指导进一步实验,得到修正的模型,最终预测出的半球温度（HT）平均误差低于5%。     

玻璃减薄蚀刻液中氟硅酸的选择性脱除方法

光电玻璃减薄蚀刻液中氟硅酸(H2SiF6)的累积,是导致蚀刻液无法连续使用而转化为废液的主要原因。尝试对蚀刻废液中氟硅酸进行选择性脱除工艺,探索刻蚀液循环利用的有效处理方法。鉴于氟硅酸的碱金属盐具有溶解度较低的特点,研究考察了利用钠盐或钾盐为沉淀剂,将废液中的H2SiF6以氟硅酸盐的形式沉淀去除,为实现蚀刻液的循环利用提供可能。结果表明,KCl相比NaCl对H2SiF6处理效果更好,但生成的K2SiF6的结晶颗粒过细,难以自然沉降,过滤效果较差;而Na2SiF6结晶沉降特性较好,且使用NaCl为沉淀剂具有价廉易得等特点,可作为氟硅酸的理想沉淀剂。H2SiF6去除率与碱金属盐H2SiF6摩尔计量比正相关,当摩尔计量比NaCl/H2SiF6=2,H2SiF6含量10%的模拟废液,其H2SiF6去除率可达到90%以上。     

非均相Fenton体系中无机助剂对亚甲基蓝脱色的影响

直接使用有机过渡金属化合物二茂铁作为催化剂,研究了非均相Fenton反应中亚甲基蓝的降解,并考虑了实际排放的印染废水中存在的无机助剂,进一步分析了典型无机助剂CuSO4、NaCl、Na2CO3、Na2SO4、Na2S的存在对该非均相Fenton体系的影响,结果表明：直接使用二茂铁做催化剂反应120min后,亚甲基蓝的剩余率为0．6％,羟基自由基的表观生成率为83．4％。NaCl、Na2CO3、Na2SO4、Na2S的加入会阻碍反应的进行,而CuSO4的加入会促进反应的进行。     

Performance of the Annular Denuder System with Different Arrangements for HNO3 and HNO2 Measurements in Taiwan

ABSTRACT

Experiments on different annular denuder system (ADS)arrangements for sampling nitrous acid (HNO₂) and ni-tric acid (HNO₃) gases were conducted in this study toevaluate their sampling artifacts. The evaluation basis isthe one that employed one sodium chloride denuder forsampling HNO₃ gas and two sodium carbonate (Na₂CO₃)denuders for sampling HNO₂ gas, which is a commonlyemployed ADS arrangement in many field applicationsin the United States. A field study was conducted inHsinchu, Taiwan, and the results indicated that this ADSarrangement may yield over 80% relative errors for HNO₃gas. It also showed that the relative errors for HNO₂ gascan be less than 10% as sampled with only one Na₂CO₃denuder. This is attributed to the fact that the ambientHNO₃ concentration measured in this study was relativelylow while the HNO₂ concentration was high, as comparedto typical concentrations of these two gases measured inthe United States.

The sampling error of HNO₃ gas may be due to highconcentrations of N-containing interfering speciespresent in Taiwan’s atmosphere. Because the relative sam-pling errors of HNO₃ and HNO₂ gases depend mainly ontheir concentrations in the atmosphere as well as con-centrations caused by interfering species, the risk for higherror while measuring low HNO₂ concentrations by onlyone Na₂CO₃ denuder is also possible. As a result, it is sug-gested that pretests are necessary to evaluate possiblesources and degrees of sampling errors before fieldsampling of HNO₂ and HNO₃ gases. The sampling errorsof these two gases can, therefore, be minimized with abetter arrangement of the ADS.     

Synthesis of a novel slow-release potassium fertilizer from modified Pidgeon magnesium slag by potassium carbonate

A novel slow-release potassium fertilizer (SPF) was synthesized using Pidgeon magnesium slag (PMS) and potassium carbonate, which could minimize fertilizer nutrient loss and PMS disposal problems. Orthogonal experiments were conducted to determine the optimum conditions for synthesis. The potassium (K)-bearing compounds of SPF existed mainly in the form of crystalline phases Ca_1.197K_0.166SiO₄, K₂MgSiO₄, and K₄CaSi₃O₉, and in the noncrystalline phase. The active silicon content of SPF was 2.09 times as much as that of magnesium slag, and the slow-release character of SPF met the requirement for partly slow-release fertilizer in the national standard (GB/T23348-2009). The best models for describing the K release kinetics in water and 2% citric acid were the Elovich model and the first-order model, respectively. The heavy metal contents of SPF conformed to the national standard for organic–inorganic compound fertilizers, and the leaching mass concentrations of heavy metals and Fluorine were far lower than the limit values of the identification standard for hazardous waste identification for extraction toxicity (GB5085.3-2007), and also met the class II quality standard for ground water. The environmental risk of SPF is therefore very low, but because SPF is alkaline, its effect on soil pH should be taken into account.

Implications: PMS is the solid waste resulting from the production of magnesium metal by Pidgeon’s reduction process. Utilization of PMS in the high-technology and high-value areas may promote the high-efficiency development of worldwide collection metallic magnesium industry and contribute to the reduction of emissions of fine dust to air. This paper presents one of the new techniques in the use of PMS as a slow-release fertilizer by adding K₂CO₃. The product can serve as a very cost-effective and reliable artificial fertilizer.     

Advantages and risks of using steel slag in preparing composts from raw organic waste

It had been reported that iron and manganese oxides in steel slag enhanced the production of humic acid (HA) from low-molecular-weight compounds, such as phenolic acids, amino acids, and saccharides. In the present study, this function of steel slag was applied to the composting of raw organic wastes (ROWs). The degree of humification of HAs is an important factor in evaluating compost quality. Thus, HAs were extracted from the prepared composts and the humification parameters were determined, in terms of elemental compositions, acidic functional group contents, molecular weights, spectroscopic parameters from UV–vis absorption and ¹³C NMR spectra. The timing for adding steel slag affected the degree of humification of HAs in the composts. The weight average molecular weight of a HA when slag was added initially (29 kDa) was significantly higher than when slag was added after elevating the temperature of the compost pile (17–18 kDa). These results show that ROWs are decomposed to low-molecular-weight compounds after the pile temperature is elevated and the presence of slag enhances the polycondensation of these compounds to produce HAs with a higher degree of humification. Because the slag used in the present study contained several-tens ng g^?1 to several μg g^?1 of toxic elements (B, Cu, Cr, and Zn), leaching tests for these elements from the prepared composts were carried out. Levels for leaching boron from composts prepared by adding slag (0.2–0.4 mg L^?1) were obviously higher than the corresponding levels without slag (0.05 mg L^?1).     

Heavy metal availability,bioaccessibility, and leachability in contaminated soil: effects of pig manure and earthworms

A pot experiment and a leaching experiment were conducted to investigate the effects of earthworms and pig manure on heavy metals (Cd, Pb, and Zn) immobility, in vitro bioaccessibility and leachability under simulated acid rain (SAR). Results showed manure significantly increased soil organic carbon (SOC), dissolved organic carbon (DOC), available phosphorus (AP), total N, total P and pH, and decreased CaCl₂-extractable metals and total heavy metals in water and SAR leachate. The addition of earthworms significantly increased AP (from 0.38 to 1.7 mg kg^?1), and a downward trend in CaCl₂-extractable and total leaching loss of heavy metals were observed. The combined earthworm and manure treatment decreased CaCl₂-extractable Zn, Cd, and Pb. For Na₄P₂O₇-extractable metals, Cd and Pb were decreased with increasing manure application rate. Application of earthworm alone did not contribute to the remediation of heavy metal polluted soils. Considering the effects on heavy metal immobilization and cost, the application of 6% manure was an alternative approach for treating contaminated soils. These findings provide valuable information for risk management during immobilization of heavy metals in contaminated soils.

     

SGA对垃圾焚烧飞灰中重金属的固化性能研究简

根据EPA 1311、HJ/T 299-2007、HJ/T 300-2007和HJ 557-2009等国内外不同标准,研究了深圳某垃圾焚烧发电厂垃圾焚烧飞灰的浸出毒性,探讨了六硫代胍基甲酸（sixthio guanidine acid,SGA）、二甲基二硫代氨基甲酸盐（sodium dimethyl dithio carbamate,SDD）和Ca（OH）₂浓度对垃圾焚烧飞灰中重金属的固定性能的影响。研究结果表明,随着浸提液pH的降低,该厂焚烧飞灰中大部分金属元素的浸出量增大,焚烧飞灰浸出液中的Cd、Ni、Pb和Zn浓度分别超过国家危险废物鉴别标准（GB5085.3-2007）规定值的4.75倍、1.47倍、6.72倍和2.20倍,属于危险废弃物,必须进行稳定化处理。当固化剂SGA加入量为0.1 mol/kg时,稳定化后的重金属浸出浓度已经低于危险废物鉴别标准,且对Cd、Cr、Cu和Pb的固化性能优于SDD和Ca（OH）₂;当固化剂SGA、SDD和Ca（OH）₂加入量为0.5 mol/kg时,稳定化后的焚烧飞灰重金属浸出浓度均低于国家危险废物鉴别标准（GB 5085.3-2007）中的规定值。与SDD和Ca（OH）₂相比,SGA对垃圾焚烧飞灰中重金属的固化处理更具有优势。     

Fe2+活化过硫酸钠降解1,2-二氯苯

以Na2S2O8为氧化剂,柠檬酸螯合Fe2+为活化剂,对水中1,2-二氯苯进行处理。首先研究了Na2S2O8浓度、FeSO4浓度、柠檬酸浓度及初始pH值等因素对1,2-二氯苯降解的影响;然后通过正交实验,发现在Na2S2O8浓度14.28 mmol/L、FeSO4浓度7.14 mmol/L、柠檬酸浓度3.57 mmol/L、初始pH值3.0的条件,1,2-二氯苯降解率达到最大(99.28%)。进一步研究表明,柠檬酸螯合FeSO4活化Na2S2O8降解1,2-二氯苯的过程可分为2个阶段,其中第1阶段为快速反应,第2阶段反应速度较慢并且符合一级反应动力学规律。