纳米Fe3 O4-H2 O2 非均相Fenton反应催化氧化邻苯二酚

由四氧化三铁(Fe3O4)-过氧化氢(H2O2)构成的非均相Fenton体系主要利用H2O2分解产生的羟基自由基氧化去除难降解有机污染物.研究了邻苯二酚在纳米Fe3O4-H2O2构成的非均相Fenton体系中的催化氧化特征,同时对实验室制备的纳米级Fe3O4和商品微米级Fe3O4两种催化剂的催化活性进行比较,并考察了H2O2初始浓度对邻苯二酚的催化氧化的影响.结果表明,自制纳米Fe3O4-H2O2体系较商品Fe3O4-H2O2体系,能更快速地去除溶液中的邻苯二酚和总有机碳(TOC),邻苯二酚的去除率接近100%,同时能迅速催化H2O2分解.邻苯二酚的催化氧化反应遵循准一级反应动力学方程,H2O2的分解反应能用三级反应动力学方程较好拟合.此外,反应过程中铁释放低于0.3 mg.L-1,不足以启动均相Fenton反应,反应机制为由界面反应控制的非均相反应机制.     

磁场协同Ca2O2/Fe2+处理活性红染料废水的实验研究

利用磁场协同Ca2O2/Fe2 催化氧化体系处理活性红染料废水,研究不同磁化时间、磁场强度和催化氧化各种影响因素下对活性红染料模拟废水的去除率.结果表明:在pH值为3,C(FeSO4·7H2O)=50 mg,C(Ca2O2)=1.45g条件下,反应20min,去除率达62.5%.外加磁场磁场强度为427.8 mT的作用下,磁化反应20 min,CODCr的去除率提高了8.3%.     

天然矿物负载Fe/Co催化H2O2氧化降解阳离子红3R

类Fenton反应关键是催化剂的活性,利用浸渍法负载铁、钴双金属对天然矿物材料进行改性,提高其催化活性,并运用扫描式电子显微镜(SEM)、X射线能谱仪(EDS)、X射线衍射(XRD)等表征手段对负载前后的材料进行表征分析.结果表明负载后材料中生成Fe2O3和Co Fe2O4两种新物质.将合成的催化剂用于催化H2O2氧化阳离子红3R染料废水,在催化剂投加量3 g·L-1,H2O2投加量0.3 m L·L-1,反应时间1 h条件下,100 mg·L-1阳离子红3R废水脱色率可达99.8%,TOC去除率可达58.4%,催化剂中活性组分主要为表面负载的Fe2O3和Co Fe2O4,电子自旋共振(ESR)分析表明催化氧化过程中产生羟基自由基,阳离子红3R发色基团在1 min已被完全破坏,光谱分析表明反应过程中有小分子物质生成.催化氧化效果受染料废水初始p H值影响小,适应p H范围广,解决了传统Fenton反应p H条件苛刻的问题.研究结果为印染废水处理提供了具有工程应用潜力的技术方法.     

非均相催化氧化处理活性艳红染料废水

以粉煤灰作为载体,制备了非均相催化剂。研究了非均相催化氧化处理98mg·L^-1活性艳红模拟染料废水的实验效果。实验结果表明,在催化剂投加量40g·L^-1、30％的H2O2投加量3mL·L^-1、pH值4、处理时间10min的最佳处理条件下,非均相催化体系对活性艳红染料的脱色率达到98．21％。对比均相催化氧化法,非均相催化氧化技术提高了对活性艳红染料的脱色率,缩短了反应时间,提高了H2O2利用效率,扩大了pH值范围,改进了Fe^2＋流失的不足。     

Cu~(2+)/吡啶/H_2O_2对直接大红4BE的快速脱色研究

为了明确影响Cu2+/吡啶/H2O2对模拟染料(DR4BE)废水脱色的主要因素,采用动力学分析、正交和Box-Behnken实验设计研究了不同溶液pH、Cu2+、吡啶、H2O2浓度及Cu2+、吡啶和H2O2组合对初始脱色速率常数和最终脱色率的影响.同时,采用自由基抑制、H2O2催化分解实验探索了Cu2+/吡啶/H2O2对染料的脱色机理.结果发现,Cu2+/吡啶/H2O2能有效使DR4BE快速脱色,脱色效率远高于Cu2+/H2O2;pH是影响初始脱色速率最重要的因素,吡啶、Cu2+及pH是影响最终脱色率最重要的因素;溶液pH在7.0左右时有利于该脱色过程的快速进行.Cu2+与吡啶的交互作用相对较强,吡啶、Cu2+与H2O2的交互作用相对较弱.羟基自由基氧化是Cu2+/吡啶/H2O2对染料DR4BE初始快速脱色的主要机理.研究结果还表明,Cu2+/吡啶/H2O2体系可用于中性条件下染料废水的快速脱色处理.     

纳米Fe3O4/CeO2-H2O2非均相类Fenton体系对3,4-二氯三氟甲苯的降解

以浸渍法制备的新型纳米Fe3O4/Ce O2为催化剂,3,4-二氯三氟甲苯(3,4-DCBTE)为目标污染物,在Fe3O4/Ce O2-H2O2非均相类Fenton体系中对目标污染物的降解进行研究,考察催化剂的催化效果和温度、p H、H2O2投加量等因素对催化剂催化效果的影响.结果表明,以纳米Fe3O4/Ce O2作为催化剂的非均相类Fenton体系对3,4-二氯三氟甲苯的处理效果极佳;随着温度的升高,纳米Fe3O4/Ce O2的催化效果不断提高;在偏酸性环境中,p H越低催化效果越好,p H=2时反应去除效率可达96.67%;随着H2O2投加量的增加,3,4-二氯三氟甲苯的降解效率先提高后降低,投加量为15 mg·L-1时去除效果最好可达99.47%;随着催化剂投加量的增加,同样出现了处理效果先升高后降低的现象,投加量为0.5 g·L-1时催化效果最好可达99.64%.在以纳米Fe3O4/Ce O2为催化剂的非均相类Fenton体系中,3,4-二氯三氟甲苯的降解符合一级反应动力学,反应所需活化能较低只需30.26 k J·mol-1.     

O3、O3/H2O2、O3/H2O2/UV工艺降解炸药工业废水中RDX的试验研究

为了研究高级氧化技术对含黑索今(RDX)的炸药工业废水的处理效果,本文采用O3、O3/H2O2、O3/H2O2/UV 3种氧化工艺分别对废水中的RDX进行了降解试验,并对比分析了3种工艺的处理效果和机制。结果表明:O3/H2O2、O3/H2O2/UV工艺对RDX的去除率明显优于O3工艺;提高体系的pH值将有利于RDX的降解;随着RDX初始浓度的增加,RDX的去除率呈现下降趋势;投加H2O2和UV照射可提高臭氧的利用率,且O3/H2O2/UV工艺催化臭氧分解的能力比O3/H2O2工艺强。     

二茂铁催化光助非均相类Fenton氧化法处理含罗丹明B废水

采用二茂铁(Fc)替代UV/Fenton体系中的催化剂Fe2+,构建了一个新的UV/H2O2/Fc非均相Fenton反应体系,研究了该反应体系对含罗丹明B模拟废水的脱色性能.结果表明,Fc对水中UV/Fenton反应具有良好的催化活性,对罗丹明B起氧化作用的主要物质是·OH和其他活性物质.对水中罗丹明B的氧化脱色反应的催化性稳定,对Fc重复回收利用3次后对模拟废水仍有99%以上的脱色率;UV/H2O2/Fc体系处理罗丹明B的最佳工艺条件是H2O2的浓度为1.5′10-2mol/L,Fc的投加量为0.13g/L,初始pH值在2~6之间.证实了Fc作为光助非均相Fenton体系催化剂的可能性.     

GAC/H2O2/UV降解二级出水中溶解性有机物

颗粒活性炭(GAC)既可以作为吸附剂,又能作为催化剂。研究利用GAC、过氧化氢(H2O)2、紫外(UV)三者联合深度处理二级出水。采用连续流反应器,对比了GAC/H2O2/UV联合体系与GAC、UV、H2O2、GAC/UV、GAC/H2O2、UV/H2O2条件下溶解性有机物的降解效果,并重点探讨GAC对H2O2的催化作用、UV对H2O2的分解作用在联合体系中的贡献。结果表明,GAC/H2O2/UV联合连续降解效果明显高于其它条件下的降解效果;停留时间越长,降解率越高;虽GAC可催化H2O2,但UV/H2O2在联合体系中起关键作用;GAC/H2O2/UV联合体系能减少出水中H2O2的剩余量。     

UV/Fenton体系中Fe2+/Fe3+的相互转化规律

为了控制UV/Fentan方法中铁元素的用量,合理利用溶解态铁的催化反应过程并提高其降解效率,研究以难生物降解性染料罗丹明B为目标物,通过正交实验和单因素实验确定了UV/Fenton体系的最佳反应条件,并利用一元线性方程模拟了罗丹明B退色反应的的动力学方程.结果显示,当体系的最初pH为3.00,溶液中[Fe2+]=0.180 mmol·L-1、[H2O2]=124.022 mmol·L-1时,UV/Fenton氧化罗丹明B退色符合一级反应动力学方程.研究了总铁含量维持在0.180mmol·L-1、保持紫外光照射、4次向同一UV/Fenton体系中添加1.7mLH2O2,每次反应后Fe2+/Fe3+的循环转化规律和溶液的脱色效果.研究结果表明,每次反应结束阶段(30 min),Fe2+浓度均高于Fe3+浓度,残余液仍具有较强的催化能力,溶液的脱色率达到99.9%;退色反应速率常数始终维持在较高水平,最后一次循环反应结束后,反应速率常数达到0.2547,相对于初始反应速率常数只下降了17%左右.     

Ti/RuO2-TiO2-IrO2-SnO2电极电解氧化含氨氮废水

研究了含氨氮(NH^＋₄-N)废水在循环流动式电解槽中的电化学氧化,其中阳极为Ti/RuO₂-TiO₂-IrO₂-SnO₂网状电极,阴极为网状钛电极.考察了出水放置时间、进水流量和电流密度对氨氮去除的影响,并对能耗、阳极效率和瞬时电流效率（ICE）进行分析.结果表明,在氯离子浓度为400　mg/L,初始氨氮浓度为40 　mg/L时,进水流量对氨氮去除的影响不大,电流密度的影响比较大.在进水流量为600 mL/min,电流密度为20 mA/cm² ,电解时间为90 min时,氨氮去除率为99.37％,去除1 kg氨氮的能耗和阳极效率为500 kW·h和 2.68 h·m²·A,瞬时电流效率（ICE）为0.28.表明电解氧化含氨氮废水具有较好的应用前景.     

Effect of Ce doping of TiO2 support on NH3-SCR activity over V2O5-WO3/CeO2-TiO2 catalyst

CeO2–TiO2composite supports with different Ce/Ti molar ratios were prepared by a homogeneous precipitation method, and V2O5–WO3/CeO2–TiO2catalysts for the selective catalytic reduction（SCR） of NOx with NH3 were prepared by an incipient-wetness impregnation method. These catalysts were characterized by means of BET, XRD, UV–Vis,Raman and XPS techniques. The results showed that the catalytic activity of V2O5–WO3/TiO2 was greatly enhanced by Ce doping（molar ratio of Ce/Ti = 1/10） in the TiO2 support.The catalysts that were predominantly anatase TiO2 showed better catalytic performance than the catalysts that were predominantly fluorite CeO2. The Ce additive could enhance the surface adsorbed oxygen and accelerate the SCR reaction. The effects of O2 concentration, ratio of NH3/NO, space velocity and SO2 on the catalytic activity were also investigated. The presence of oxygen played an important role in NO reduction. The optimal ratio of NH3/NO was 1/1 and the catalyst had good resistance to SO2 poisoning.     

Fe3O4/CeO2-H2O2非均相类Fenton体系下降解TCE的研究

采用浸渍法成功合成了新型催化剂纳米Fe3O4/CeO_2,并且用Fe3O4/CeO_2-H_2O_2非均相Fenton体系对TCE进行降解研究,考察了初始pH、H_2O_2浓度、温度及催化剂投加量等因素对于TCE降解效率的影响.实验结果表明,Fe3O4/CeO_2-H_2O_2非均相Fenton体系对TCE具有较好的去除效果:在初始pH=3,温度50℃,H_2O_2浓度30 mmol·L-1和Fe3O4/CeO_2投加量0.5 mg·L-1时,TCE去除率高达97.29%.同时实验结果表明pH在2~7范围内对TCE均有降解效果,所以相对于传统Fenton体系,该体系拥有更宽pH应用范围.目标污染物的降解符合一级动力学,反应活化能为30.77 k J·mol-1,表明反应易于进行.     

磁性Mn0.6Zn0.4Fe2O4@SiO2催化H2O2降解亚甲基蓝效能及机制

为制备易固液分离和稳定性好的高效非均相类Fenton催化剂,利用正硅酸乙酯水解对Mn_0.6Zn_0.4Fe₂O₄磁性纳米颗粒（SF-MNPs）进行功能化修饰,制备得到Mn_0.6Zn_0.4Fe₂O₄@SiO₂（MZF@SiO₂）磁性纳米复合物催化剂,采用透射电镜、 X射线光电子能谱和振动样品磁强计等对MZF@SiO₂进行了表征,以难生物降解偶氮染料亚甲基蓝（MB）为目标污染物,考察了不同初始pH对MZF@SiO₂催化效能的影响,在近中性条件下（pH=6.5）研究了H₂O₂用量、 MZF@SiO₂投加量和温度等对MB去除率的影响,及MZF@SiO₂的稳定性和循环使用性能,推测了催化反应机制.结果表明,无定形SiO₂将SF-M...     

基于ZrO2/TiO2催化H2O2氧化低温脱硝的实验研究

以纳米TiO_2为载体,采用等体积浸渍法掺杂过渡金属氧化物ZrO_2进行改性,制备了一系列ZrO_2/TiO_2催化剂,以催化H_2O_2低温氧化NO脱硝,并采用X射线衍射(XRD)、H_2程序升温还原(H_2-TPR)、O_2程序升温氧化(O_2-TPO)、X射线光电子能谱(XPS)及电子顺磁共振(EPR)等表征分析探究了影响H_2O_2脱硝活性的因素.表征结果表明ZrO_2的负载量会影响催化剂中晶格氧的含量,晶格氧相对含量的增加有利于氧化还原反应中的电子传递,这是促进H_2O_2活化分解的关键.在微观表征的基础上,通过实验研究筛选获得了催化剂的最佳ZrO_2负载量,同时对比考察了非催化和纳米TiO_2催化作用下的H_2O_2氧化低温脱硝性能;针对获取的最优催化剂,进一步考察了不同烟气工况对催化剂活性的影响.实验结果表明,ZrO_2/TiO_2催化剂能有效促进H_2O_2的活化分解实现低温脱硝,且ZrO_2负载量为4%(质量分数)时,催化活性最高;在烟温为160℃、[H_2O_2]/[NO]物质的量比为2及空速为30000 h~(-1)时,NO转化率最高可达81%.     

Fe3O4/TiO2-H2O2非均相类Fenton体系对3，4-二氯三氟甲苯的降解

用Fe_3O_4/Ti O_2-H_2O_2体系对3,4-二氯三氟甲苯(3,4-DCBTE)进行降解反应研究,同时考察了pH值、催化剂投加量、H_2O_2投加量、温度等因素对3,4-DCBTE降解效率的影响.实验结果表明,Fe_3O_4/Ti O_2-H_2O_2非均相类Fenton体系对3,4-二氯三氟甲苯的处理效果极佳;并且在H_2O_2投加量为45.0 mg·L~(-1)、Fe_3O_4/TiO_2的物质的量比为1∶1、pH=3.0、温度为40.0℃的条件下反应效果最佳,去除率高达99.1%.同时从实验结果可以看出,pH在2.0~7.0范围内该体系对3,4-二氯三氟甲苯均有降解效果,说明该体系相比于传统的Fenton体系有较宽的pH适用范围.目标污染物的降解符合一级反应动力学,其发生反应所需的活化能为36.9 k J·mol~(-1).     

Fe3O4/FeS2活化H2O2降解典型苯胂酸类污染物

利用水热法成功制备了Fe₃O₄/FeS₂催化剂,并将其用于构建非均相芬顿体系降解典型的苯胂酸类污染物（洛克沙胂,ROX）.XRD、SEM、XPS和磁学测量系统（VSM）等表征结果表明,Fe₃O₄/FeS₂呈明显的颗粒状且具有良好的磁性.降解实验结果显示,在最优条件下（初始pH值为4.5、ROX起始浓度为20mg/L、Fe₃O₄/FeS₂投加量为0.15g/L和H₂O₂浓度为0.034g/L,Fe₃O₄/FeS₂介导的非均相芬顿体系可以超快速降解ROX,1min后的降解效率达到96.74%,明显优于单独的Fe₃O₄或FeS₂体系.此外,Fe₃O₄/FeS₂可以通过磁铁进行快速回收利用,同时也具有良好的重复利用性能,使用3次后,ROX的降解效率仍超过80%.机理分析表明,Fe₃O₄/FeS₂能够快速地催化H₂O₂产生具有强氧化性的羟基自由基（·OH）.在·OH的作-用下,ROX分子结构中C-As、C-N和C-C等化学键发生断裂,发生脱砷、脱硝和开环等反应,进而生成一系列的有机产物（如酚类、醌类、小分子有机酸等）和无机产物（As （V）和NO₃^-）.之后,无机砷能够被吸附在催化剂表面,而有机产物则进一步被矿化.     

纳米Fe3O4/H2O2降解诺氟沙星

采用纳米Fe3O4催化H2O2氧化降解水环境中的诺氟沙星.考察了溶液酸度、温度、催化剂和H2O2浓度对诺氟沙星降解的影响,对比不同底物在Fe3O4/H2O2体系中的降解情况,并进一步探讨了其反应机制.结果表明,溶液酸度显著影响诺氟沙星的降解率,在酸性条件下（pH=3.5）诺氟沙星的降解效率最高.诺氟沙星的降解率随纳米F...     

SO2-NO2-NH3-H2O四元反应体系中气溶胶的生成特性

通过烟雾箱实验,研究了SO₂-NO₂-NH₃-H₂O四元反应体系在气-粒转化过程中新形成颗粒物数浓度与粒径分布的变化.研究发现,SO₂-NO₂-NH₃-H₂O四元反应体系具有显著的成核能力,且其成核强度大,持续时间短.当SO₂、NO₂浓度为200mg/m³,NH₃浓度为12x10^-6时,反应体系的气溶胶总个数浓度在2min时达到峰值2.5x10⁶cm^-3.缺少任一种气体均会使气溶胶成核强度下降.SO₂、NO₂及NH₃浓度分别为0的工况下气溶胶总个数浓度峰值分别下降了41.0%、83.6%及98.5%.在电厂污染气体排放浓度区间内,NO₂对气溶胶生成影响大于SO₂.燃煤电厂控制NO_x排放浓度对改善烟囱出口气溶胶数浓度更有效.在实验基础上,对颗粒物成核特性进行拟合,反应体系在气-粒转化过程中产生的新颗粒物总个数浓度及中值粒径与气态前体物浓度线性相关;采用布朗团聚模型对气溶胶成核后的团聚过程总个数浓度及粒径变化进行模拟计算,根据给定的燃煤电厂SO₂、NO₂、NH₃排放浓度,给出预测气溶胶颗粒成核速率、粒径分布及总个数浓度变化的方法.