负载型燃烧催化剂La_(0.8)Ce_(0.2)CoO_3/Ce_(0.8)Zr_(0.2)O_2制备及性能研究

以复合氧化物La0.8Ce0.2CoO3为活性组分,Ce0.8Zr0.2O2固溶体为载体,采用柠檬酸络合法制备出负载型燃烧催化剂La0.8Ce0.2CoO3/Ce0.8Zr0.2O2。用XRD、BET和SEM对其进行表征,考察了焙烧温度、反应时间、反应温度及H2S存在对催化剂活性的影响。结果表明,载体表面形成了均一的钙钛矿相;该负载型催化剂对二甲苯完全氧化反应具有较高的催化活性,有良好的热稳定性、操作稳定性和强的抗H2S毒化能力。这可能是载体与负载组分之间密切的协同作用所导致。     

Catalytic performance of copper and cerium oxides-based γ-Al_2O_3 on combustion of toluene

以γ-Al2O3为载体,以复合氧化物CuxCe1-xO2为活性组分,其中,x=0.1,0.2,0.4,0.6,0.8,通过浸渍法制备了一系列CuxCe1-xO2/γ-Al2O3催化剂.在固定床反应器中评价了催化剂对甲苯的催化活性,通过XRD、SEM对催化剂进行表征,并运用ICP-MS分析并计算Cu、Ce的摩尔比以及活性组分的负载量.结果表明,在CuxCe1-xO2/γ-Al2O3催化剂中Cu、Ce摩尔比的实际值与理论值相近,活性组分的负载量在19%以上,而且对甲苯都有较好的低温催化活性,其中当x=0.2时,即Cu0.2Ce0.8O2/γ-Al2O3催化剂对甲苯的催化活性最高,其中T10=160℃,T90=265℃;当甲苯的进口浓度在700～3000mg·m-3时,进口浓度对Cu0.2Ce0.8O2/γ-Al2O3催化剂的催化活性影响较小,且经过连续80h的稳定性操作后转化率仍然保持在90%以上.     

La0.8Ce0.2CoO3/Al2O3对油烟的催化净化

将稀土金属La、Ce和过渡金属Co按照一定的比例采用浸渍法负载在γ-Al2O3载体上制备成La0.8Ce0.2CoO3/Al2O3催化剂,用X-射线衍射仪和扫描电镜对催化剂负载层的表面形态、晶相结构和粒径大小进行了表征,并用正交实验法考察了其对油烟的催化净化效果。结果表明,当负载量30%、焙烧温度800℃、催化温度300℃、烟气流量10L/min时催化剂对油烟的净化效果最佳,净化效果可达88%,催化剂对油烟的催化具有较好的低温高活性。     

LaMnO_3掺杂Sr/Ce催化剂的制备及研究

采用柠檬酸络合法,在LaMnO_3催化剂基础上掺杂Sr和Ce制得了钙钛矿型催化剂La_(0.9)Sr_(0.1)MnO_3和La_(0.8)Ce_(0.2)MnO_3,用于净化柴油车尾气污染物NO_x、碳烟颗粒、CO与烃类化合物。通过活性评价实验和XRD、SEM等表征手段,选出了四效催化活性较高的催化剂并测试了其在含硫条件下的耐久性。研究结果表明制得的几种催化剂都具有钙钛矿结构;其中La_(0.9)Sr_(0.1)MnO_3可使碳烟起燃温度达到239.9℃,使C_3H_6和CO在300℃以后大部分被去除,使NO_x有较高转化率,其四效催化性能优于掺杂Ce与不掺杂的LaMnO_3催化剂,并能在硫环境下仍然保持一定的催化活性。     

钙钛矿La_(1-x)B_xCoO_3光催化降解SDBS的研究

文章采用了溶胶-凝胶法制备了钙钛矿催化剂La1-x Bx CoO3(B=Mg、Ca、Sr;x=0,0.1,0.3,0.5,0.7,0.9,1)并以X衍射线对其结构进行表征,以甲基橙光催化降解率来评价所制备的催化剂的活性。结果表明SrCoO3对甲基橙的降解有较高的活性。在紫外光下,催化剂的量为2.5 g/L、pH=8.0、30%H2O2的量为2 mL/L,SrCoO3对SDBS溶液有较好的降解效果,降解率达到96%。     

负载型钌催化剂的制备对甲苯催化燃烧的影响

采用浸渍法,将贵金属钌负载到分子筛制备了钌基催化剂,探讨了分子筛类型、钌负载量、焙烧温度和催化剂粒径等制备条件对催化剂催化氧化甲苯性能的影响。结果表明,以ZSM-5为载体制备的钌基催化剂催化甲苯的效果优于β分子筛为载体的催化剂;随着钌负载量的增加,在1%～1.2%的范围内催化剂活性明显上升,之后有所下降;焙烧温度在250～350℃的范围内,催化剂对甲苯的催化活性随焙烧温度的升高显著上升,但350℃之后活性变化不大;在一定范围内适当降低催化剂粒径可增加催化剂的活性,但降到40目以下时催化剂活性变化不大。实验条件下制备的催化剂可在180℃时催化转化98%的甲苯,表现出了低温催化去除甲苯的优异性能。     

焙烧温度对CeO_2(ZrO_2)/TiO_2选择性催化脱硝性能的影响

采用溶胶-凝胶法并以不同温度焙烧制备一系列CeO_2(ZrO_2)/TiO_2(CZT)催化剂,考察了CZT催化剂固相结构、酸量、比表面积等性能与催化活性的关系。采用XRD、BET、NH3-TPD、H2-TPR以及XPS等表征技术对催化剂进行表征。结果表明:焙烧温度为450℃时CZT催化剂具有最高的催化活性,其在240~400℃的温度窗口内活性均高于90%,且具有较好的抗水和抗硫中毒能力。随着焙烧温度的提高,催化剂表面的Ce和Zr原子进入体相晶格且Ce0.5Zr0.5O2向Ce0.75Zr0.25O2转变,导致催化剂的储释氧能力和氧化还原性能降低。另外,锐钛矿和金红石型TiO_2晶粒尺寸的增加,催化剂的有效比表面积和总酸量降低,因此CZT催化活性随着焙烧温度的提高而有所降低。换言之,大的比表面积、良好的氧化还原性能、表面Ce4+的富集以及酸性位的增多均有利于NH3-SCR活性的提高。     

二氧化钛复合型催化剂制备及其微波辅助催化氧化甲苯性能

实验采用溶胶凝胶法和传统浸渍法制备了TiO2-分子筛复合载体及复合载体负载过渡金属与稀土元素催化剂,通过微波辅助催化氧化甲苯的性能实验考察其催化活性.结果表明,复合TiO2明显提高了载体结构的稳定性与耐温性,并使过渡金属铜(Cu)、锰(Mn)和稀土元素铈(Ce)等活性组分在催化剂表面的分散更均匀;在复合载体吸附、吸波性能与多相活性组分催化的共同作用下,Cu-Mn-Ce/TiO2-分子筛催化剂微波辅助催化氧化甲苯的完全燃烧温度仅为175℃,此时甲苯去除率可达99％;15 h的连续性实验表明,TiO2复合型催化剂具有良好的催化活性与稳定性.由催化剂表征分析结果可知,活性组分颗粒的均匀分布与铜、锰氧化物及铜锰尖晶石固溶物等活性相的存在促进了甲苯的催化氧化,锐钛矿型TiO2较高的电子迁移速率与催化剂孔径的增大均有助于甲苯的氧化降解.     

MnCeOx/沸石催化剂对工业典型VOCs的催化性能

以沸石为载体制备了锰铈复合氧化物催化剂（记为:MnCeO_x/沸石催化剂）,探究了催化剂对工业典型VOCs的二元催化性能,并对催化剂进行BET、XRD及SEM表征。结果表明:Ce的加入,促进了Mn的分散,提高了MnCeO_x/沸石催化剂的活性;当n（Mn）∶n（Ce）为1∶1,负载率为20%,焙烧温度为500℃时,催化剂的活性最高,其对甲苯的起燃温度（T₅₀）和完全燃烧温度（T₉₀）分别为155,255℃;单组分实验中,催化剂对3种有机物均表现出较高活性,转化率达到90%时的反应温度均在275℃以下,其活性顺序为乙酸乙酯>甲苯>丙酮,主要受反应活化能大小及分子极性的影响;二元催化实验中,由于竞争吸附的影响,3种物质的T₅₀和T₉₀较单组分均分别提高了8~13,14~38℃。     

新型CuMn/TiO2苯类催化燃烧催化剂的研制及活性实验

采用浸溃法制备了CuMn/TiO2新型甲苯燃烧催化剂,其活性明显优于传统CuMn/γ-Al2O3和Cu-Mn复合氧化物催化剂.研究发现,载体TiO2自身有一定催化活性,而γ-Al2O3则几乎没有活性;TiO2与Cu-Mn之间的协同作用更提高了新型催化剂的活性.XRD、LRS结果显示,CuMn/TiO2催化剂的主要活性相为铜锰尖晶石(CuMn2O4),它的存在是CuMn/TiO2催化活性优良的另一个主要原因.考察了Cu-Mn负载量、铜锰比和焙烧温度对催化剂活性的影响,CuMn/TiO2下对甲苯的去除率达95%以上时催化床层温度为215℃,比CuMn/γ-Al2O3和Cu-Mn复合氧化物对甲苯去除率达95%时分别下降了30℃、50℃左右.     

CuxCe1-xO2/γ-Al2O3催化剂催化燃烧甲苯性能的研究

以γ-Al₂O₃ 为载体,以复合氧化物Cu_xCe_1-xO₂为活性组分,其中,x=0.1,0.2,0.4,0.6,0.8,通过浸渍法制备了一系列Cu_xCe_1-xO₂/γ-Al₂O₃催化剂.在固定床反应器中评价了催化剂对甲苯的催化活性,通过XRD、SEM对催化剂进行表征,并运用ICP-MS分析并计算Cu、Ce的摩尔比以及活性组分的负载量.结果表明,在Cu_xCe_1-xO₂/γ-Al₂O₃催化剂中Cu、Ce摩尔比的实际值与理论值相近,活性组分的负载量在19%以上,而且对甲苯都有较好的低温催化活性,其中当x=0.2时,即Cu_0.2Ce_0.8O₂/γ-Al₂O₃催化剂对甲苯的催化活性最高,其中T₁₀=160 ℃,T₉₀=265 ℃;当甲苯的进口浓度在700~3000 mg·m^-3时,进口浓度对Cu_0.2Ce_0.8O₂/γ-Al₂O₃催化剂的催化活性影响较小,且经过连续80 h的稳定性操作后转化率仍然保持在90%以上.     

Catalytic removal of phenol from gas streams by perovskite-type catalysts

Three perovskite-type catalysts prepared by citric acid method are applied to remove phenol from gas streams with the total flow rate of 300 mL/min, corresponding to a GHSV of10,000/hr. LaMnO_3 catalyst is first prepared and further partially substituted with Sr and Cu to prepare La_(0.8)Sr_(0.2)MnO_3 and La_(0.8)Sr_(0.2)Mn_(0.8)Cu_(0.2)O_3, and catalytic activities and fundamental characteristics of these three catalysts are compared. The results show that phenol removal efficiency achieved with La_(0.8)Sr_(0.2)Mn_(0.8)Cu_(0.2)O_3 reaches 100% with the operating temperature of 200°C and the rate of mineralization at 300°C is up to 100%, while the phenol removal efficiencies achieved with La_(0.8)Sr_(0.2)MnO_3 and LaMnO_3 are up to 100% with the operating temperature of 300°C and 400°C, respectively. X-ray photoelectron spectroscopy(XPS) analysis shows that the addition of Sr and Cu increases the lattice oxygen of La_(0.8)Sr_(0.2)Mn_(0.8)Cu_(0.2)O_3, and further increases mobility or availability of lattice oxygen. The results indicate that La_(0.8)Sr_(0.2)Mn_(0.8)Cu_(0.2)O_3 has the best activity for phenol removal among three catalysts prepared and the catalytic activity of phenol oxidation is enhanced by the introduction of Sr and Cu into LaMnO_3. Apparent activation energy of 48 k J/mol is calculated by Mars–Van Krevelen Model for phenol oxidation with La_(0.8)Sr_(0.2)Mn_(0.8)Cu_(0.2)O_3 as catalyst.     

纳米TiO_2-Al_2O_3负载CuMnO_x对甲苯的催化燃烧

研究采用改进的溶胶-凝胶法制备了TiO2-Al2O3复合载体,并用浸渍法制备CuMnOX/TiO2-Al2O3催化剂,通过对甲苯废气催化燃烧的实验,分别考察了Cu-Mn负载量、Cu/Mn摩尔比、焙烧温度及载体对催化剂制备过程及催化剂活性的影响。实验结果表明:活性组分负载量25%,铜锰活性组分的配比Cu:Mn=1:2,焙烧温度500℃是浸渍法制备CuMnOX/TiO2-Al2O3催化剂较佳的工艺条件;XRD衍射图谱表明,500℃下铜锰尖晶石的存在是催化剂催化活性优良的主要原因;由复合载体制备的CuMnOX/TiO2-Al2O3催化剂比单一载体制备的CuMnOX/Al2O3催化剂具有更高的甲苯转化率,其T99比单一载体要低20℃以上。     

LaBO3钙钛矿催化剂的VOCs催化燃烧特性

采用共沉淀法制备了LaBO3(B=Cr、Fe、Mn、Co、Ni)钙钛矿催化剂,并用XRD、BET、H2-TPR、O2-TPD等手段对其进行了表征,考察了催化剂对苯、甲苯、乙酸乙酯和丙酮的催化燃烧性能.结果表明,Cr、Fe钙钛矿晶相中存在少量的La2CrO6和La2O3杂晶相,破坏了其活性结构.Mn、Co、Ni则能与La形成完善的钙钛矿晶相,且表现出优良的催化性能,其中LaMnO3为阳离子缺陷结构,存在较丰富的晶格氧,更适合催化燃烧C—H键键能较高和难以活化的有机分子(如苯);LaCoO3、LaNiO3属于阴离子缺陷钙钛矿结构,存在更丰富的表面氧,更适合催化燃烧易在低温下活化的含氧类有机分子(如乙酸乙酯、丙酮).     

Unraveling SO2-tolerant mechanism over Fe2（SO4）3/TiO2 catalysts for NOx reduction

Developing low-temperature SO₂-tolerant catalysts for the selective catalytic reduction of NO_x is still a challenging task. The sulfation of active metal oxides and deposition of ammonium bisulfate deactivate catalysts, due to the difficult decomposition of the as-formed sulfate species at low temperatures（<300 °C）. In recent years, metal sulfate catalysts have attracted increasing attention owing to their good catalytic activity and strong SO₂ tolerance at hi...     

老化对钴铈基催化剂催化氧化丙烷的影响

采用柠檬酸络合法合成Co-CeO_x多活性中心催化剂,在不同温度进行加速老化处理,测试新鲜和老化后催化剂对丙烷的催化氧化性能,同时对其结构和性质进行表征.结果表明,当加速老化温度低于650℃时,丙烷转化率达50%的温度变化幅度小于10℃;加速老化温度高于750℃时,催化剂氧化丙烷的性能快速下降.表征结果显示,Co-CeO_x催化剂主要表现为尖晶石结构,老化后晶粒尺寸显著增大,Co³⁺的含量减少,氢还原峰温度升高.加速老化处理对Co-CeO_x催化剂物理结构的影响进而抑制了其化学特性及催化活性.测试Co-CeO_x催化剂对丙酮和甲苯的催化氧化性能,分别在179和244℃达到90%的脱除效率.因此,Co-CeO_x多活性中心催化剂具有良好的氧化性能,且表现出一定的稳定性.     

CuxMn1-xCe0.75Zr0.25Oy催化降解甲苯的性能

采用溶胶凝胶法制备了双主金属、双助剂的Cu_xMn_1-xCe_0.75Zr_0.25O_y催化剂,在固定床反应器中评价了催化剂降解甲苯的性能,并采用XRD、H₂-TPR、O₂-TPD和Raman对催化剂进行表征。试验结果表明:催化剂中Cu含量的增加有助于增强Cu-Ce金属之间的相互作用,增加催化剂中的氧空位浓度和晶格氧含量,提高催化剂低温还原性,从而促进催化活性的提高。Cu₁CeZr催化剂降解甲苯活性最好,其完全降解甲苯的温度（T₁₀₀）为220℃,比Mn₁CeZr催化剂低60℃。