以载银TiO2为催化剂,以紫外光为激发光源,考察了溶液的pH值和溶液中Fe3+﹑Fe2+﹑Mn2+等金属离子浓度对Aroclor1260降解速率的影响.结果表明,酸性条件更有利于Aroclor1260的光解作用,而且多数PCB单体在pH值为4时有最大的光解速率.所考察的3种金属离子对于Aroclor1260的光解作用都有较大的影响.其中Aroclor1260的光催化降解速率随Fe3+离子浓度的变化符合表观一级反应动力学规律;Fe2+和Mn2+的影响作用十分相似,并呈U型影响趋势,即低浓度的促进作用和高浓度的抑制作用.     

空心玻璃微球附载TiO2清除水面漂浮的油层

以空心玻璃微球为载体，采用浸涂法制备出ＴｉＯ２／ｂｅａｄｓ光催化剂．研究了利用ＴｉＯ２／ｂｅａｄｓ光催化剂降解水面漂浮的正十二烷及甲苯的可行性．结果表明，３７５Ｗ中压汞灯照射１２０ｍｉｎ，正十二烷的光催化去除率达９３．５％，光照８０ｍｉｎ时甲苯被完全光催化去除；通入空气有利于正二十烷及甲苯的光催化去除，外加微量的Ｈ２Ｏ２（５．０ｍｍｏｌ／Ｌ）可大大提高光催化去除率，向反应液中加入少量Ｎａ＋对正十二烷及甲苯的光催化去除率无明显的影响．     

Microwave photocatalytic degradation of Rhodamine B using TiO2 supported on activated carbon： Mechanism implication

The photocatalytic degradation of Rhodamine B (RhB) was carried out using TiO2 supported on activated carbon (TiO2-AC) under microwave irradiation. Composite catalyst TiO2-AC was prepared and characterized using X-ray di raction (XRD), transmission electron microscopy (TEM) and Brunauer-Emmett-Teller (BET). In the process of microwave-enhanced photocatalysis (MPC), RhB (30 mg/L) was almost completely decoloured in 10 min, and the mineralization e ciency was 96.0% in 20 min. The reaction rate constant of RhB in MPC using TiO2-AC by pseudo first-order reaction kinetics was 4.16 times of that using Degussa P25. Additionally, according to gas chromatography/mass spectrometry (GC/MS) and liquid chromatography/mass spectrometry (LC/MS) identification, the major intermediates of RhB in MPC included two kinds of N-de-ethylation intermediates (N,N-diethyl-N’-ethyl-rhodamine (DER)), oxalic acid, malonic acid, succinic acid, and phthalic acid, maleic acid, 3-nitrobenzoic acid, and so on. The degradation of RhB in MPC was mainly attributed to the destruction of the conjugated structure, and then the intermediates transformed to acid molecules which were mineralized to water and carbon dioxide.     

Photocatalytic degradation of organochlorine compounds using TiO2 supported on fiberglass cloth

The feasibility of photocatalytic degradation of organochlorine compounds using TiO₂ supported on fiberglass cloth as a photocatalyst was studied. The results showed that 2.0×10^-4 mol/dm³ of dichloroethylene, trichloroethylene and tetrachloroethylene can be completely photocatalytically degraded within a short time under illumination with a 375W medium pressure mercury lamp. The effects of parameters such as illumination time, initial concentration of organochlorine compounds, amount of air flow and concentration of H₂O₂ on the photocatalytic degradation were investigated. The TiO₂ supported on the fiberglass was not easily detached and after 500h illumination there was no significant loss of photocatalytic activity of TiO₂. The passible mechanisms of photocatalytic degradation were discussed.     

邻-氯酚在TiO_2膜上光催化降解及反应动力学特征

以钛酸四丁酯为原料采用Sol Gel法制备了玻璃负载TiO2 膜光催化剂 ,应用XRD表征了不同实验条件下薄膜中TiO2 的晶相结构和粒度。分析了不同层数TiO2 膜的光催化活性和溶液 pH值对邻 氯酚 (2 CP)的影响。结果表明 :处理温度为 50 0℃时不同厚度薄膜中TiO2 均为锐钛矿晶型 ,粒径 8～ 33nm ,5层涂膜光催化活性最高。在高 pH值和低pH值区域 2 CP ,在TiO2 膜上的光催化降解速率较大。 2 CP初始浓度 (C0 )与反应速率 (r0 )的关系符合Langmuir Hinshelwood方程 ,当C0 ≤ 0 .6mmol·L- 1 时 ,降解反应可用一级动力学模式来描述。     

TiO_2薄膜光催化降解邻苯二甲酸乙酯的研究

采用solgel法制备TiO2薄膜。以该薄膜为催化剂,研究了在H2O2存在的条件下,对内分泌干扰物质邻苯二甲酸乙酯(DEP)的光催化降解反应。分别讨论了pH值、H2O2的加入量、DEP的初始浓度以及光照时间对降解反应的影响。结果表明在pH=2、50mg/L的H2O2中对初始浓度为50mg/L的DEP溶液光照150min有较好的降解效果。     

玻璃膜载Fe3+/TiO2的制备及其光催化活性研究

采用溶胶-凝胶法制备了稳定的涂膜Fe3+/TiO2溶胶,通过浸渍-提拉法分别制备了Fe3+/TiO2玻璃负载薄膜,讨论了分散剂加入量、提拉速度对成膜质量的影响,并对所制薄膜进行了结构分析,通过降解4-氟苯甲酸溶液初步研究了其光催化活性。     

Fe3+掺杂TiO2薄膜的制备及光催化降解甲醛的研究

采用溶胶-凝胶法制备Fe3+掺杂的TiO2薄膜光催化剂,进行甲醛的光催化实验,考察Fe3+掺杂量、薄膜焙烧温度及溶胶体系pH值对光催化性能的影响。结果表明,Fe3+掺杂量为1.0%,焙烧温度500℃1h,加硝酸溶胶体系pH=4时,Fe3+掺杂TiO2薄膜光催化活性最高。     

金属离子修饰纳米TiO2薄膜光催化降解苯酚

通过溶胶-凝胶法制备纳米TiO2薄膜，在制备过程中分别掺杂一定量的Fe^3 、Zn^2 、Pd^2 等金属离子。以高压汞灯做光源，用制得的纳米TiO2薄膜对苯酚作光催化降解实验，结果表明：掺杂Fe^3 、Zn^2 、Pd^2 的纳米TiO2催化剂光催化性能明显提高。并探讨了金属离子掺杂浓度和氧化剂对光催化的影响。     

Photocatalytic degradation of dye effluent by titanium dioxide pillar pellets in aqueous solution

Photocatalytic oxidation (PCO) process is an effective way to deal with organic pollutants in wastewater which could be difficult to be degraded by conventional biological treatment methods. Normally the TiO2 powder in nanometre size range was directly used as photocatalyst for dye degradation in wastewater. However the titanium dioxide powder was arduous to be recovered from the solution after treatment. In this application, a new form of TiO2(i. e. pillar pellets ranging from 2.5 to 5.3 mm long and with a diameter of 3.7 mm) was used and investigated for photocatalytic degradation of textile dye effluent. A test system was built with a flat plate reactor(FPR) and UV light source(blacklight and solar simulator as light source respectively) for investigating the effectiveness of the new form of TiO2. It was found that the photocatalytic process under this configuration could efficiently remove colours from textile dyeing effluent. Comparing with the TiO2 powder, the pellet was very easy to recovered from the treated solution and can be reused in multiple times without the significant change on the photocatalytic property. The results also showed that to achieve the same photocatalytic performance, the FPR area by pellets was about 91% smaller than required by TiO2 powder. At least TiO2 pellet could be used as an alternative form of photocatalyst in applications for textile effluent treatment process, also other wastewater treatment processes.     

CTMAB/TiO2表面修饰膨胀珍珠岩制备及降解苯酚研究

用溴化十六烷基三甲铵(CTMAB)和/或TiO2对膨胀珍珠岩(EP)进行表面修饰,获得不同表面修饰膨胀珍珠岩(EP、TiO2-EP、CTMAB-EP和TiO2/CTMAB-EP)。并研究了其对水中苯酚的吸附降解动力学方程以及去除效果和影响因素。结果表明,膨胀珍珠岩对苯酚的吸附去除能力很小,CTMAB对其进行表面修饰后可小幅提高对苯酚的去除率,同时负载CTMAB和TiO2的膨胀珍珠岩对水中苯酚的去除率有很大提高;修复材料投加量、振荡时间、苯酚初始浓度和pH值等对苯酚的去除效果有较大影响;在溶液初始pH小于8时,TiO2对苯酚的光催化降解能力随pH增加而提高,强酸或强碱环境均不适合苯酚的光催化降解。在膨胀珍珠岩上同时负载CTMAB和TiO2可望成为一种高效去除环境中有机污染物的新型环境修复材料。     

非晶态TiO2-W薄膜的光催化性能研究

采用磁控溅射技术在玻璃基片上制备了W掺杂的非晶态TiO2薄膜,用XRD、XPS和椭圆偏光测厚仪等对薄膜进行了微观分析.结果表明,TiO2-W薄膜为非晶态结构.Ti以 4价存在;W以0价和 6价形式存在,并且6价和0价W的原子浓度比为6.4:1;薄膜中Ti和W的原子浓度比为2.6:1.对5 mg·L-1的亚甲基蓝溶液光催化脱色试验表明,随着膜厚的增加,光催化降解率递增,当膜厚达到141 nm时,所制备的TiO2-W薄膜对亚甲基蓝的脱色率在2 h达到90%;当膜厚大于141 nm时,光催化降解率不再增加.     

纳米TiO2对气相中甲醛光催化降解的研究

采用溶胶-凝胶法制备了掺杂金属离子的纳米TiO₂光催化剂,运用透射电镜和X射线衍射手段对催化剂的结构进行了表征,并将制备的光催化剂负载于不锈钢丝网、玻璃弹簧和泡沫镍板3种不同载体上,以室内空气典型污染物甲醛气体为模型反应物,研究了3种不同改性纳米TiO₂光催化剂对甲醛气体的光催化作用,3种光催化反应器的催化效率以及环境因素对光催化效率的影响,同时考察了催化剂的失活特征.结果表明:该负载型纳米TiO₂光催化剂具有较高的光催化活性,其中掺镧1.5%(质量分数)的TiO₂对甲醛的降解率最高,60 min达到91.5%,大于掺铁和掺银;泡沫镍板作为负载载体的光催化效率大于玻璃弹簧和不锈钢丝网;循环风量和不同波长紫外光对该光催化反应影响不大,反应中催化剂存在失活现象,但在清洁后能够恢复.      

TiO2纳米膜光催化深度处理城市污水的实验研究

采用溶胶-凝胶方法制备光催化性能优良的TiO2纳米膜,应用X射线衍射仪分析了TiO2纳米膜的结构,探讨了铁离子和贵金属Ag、Pt掺杂对TiO2纳米膜光催化降解性能的影响,研究了TiO2纳米膜及掺杂改性TiO2纳米膜对生物二级处理系统出水中有机物光催化去除的性能。贵金属Ag、Pt掺杂提高了TiO2纳米膜光催化性能,而铁离子掺杂则降低了其催化性能。未掺杂的TiO2纳米膜使二级出水的COD下降8.9%,而贵金属Ag、Pt掺杂的TiO2纳米膜则使COD分别下降19.4%和22.3%。实验结果表明TiO2纳米膜有优良的光催化降解性能,TiO2纳米膜有广阔的应用前景。     

掺入金属离子的TiO2纳米粒子光催化降解吖啶橙

利用酸催化溶胶－凝胶法（ｓｏｌ－ｇｅｌ）制备了 Ｆｅ３＋和 Ｃｒ３＋不同掺入量的 ＴｉＯ２半导体纳米粒子研究了这些纳米粒子对吖啶橙光催化氧化降解的影响．结果表明，微量 Ｆｅ３＋和 Ｃｒ３＋的掺入可明显提高 ＴｉＯ２的光催化活性．进一步研究表明，在 Ｆｅ３＋－ＴｉＯ２体系中，最佳掺入量为 ０．１％，而且中性介质和自然光有利于光催化氧化反应的进行，反应３ｈ后降解率可达９７．７５％．在Ｃｒ３＋－ＴｉＯ２体系中，弱碱性介质和自然光有利于光催化氧化反应，最佳掺入量为０．０５％，降解率可达８７．５４％．     

负载型纳米TiO2/AC对偶氮染料的光催化降解研究

以钛酸四丁酯和粒状活性炭(AC)为主要原料,采用溶胶-凝胶-浸渍法制备出负载型纳米TiO2/AC催化剂.在流化床反应器中分别对2种典型的偶氮类染料橙黄G、活性艳红X-3B模拟废水进行了光催化降解研究,探讨了pH值、外加氧化剂对光催化降解率的影响,并对催化剂进行了回收再生利用试验.结果表明,TiO2/AC催化剂具有良好的光催化活性、吸附特性及可再生性,60 min后对2种染料反应的光催化降解率分别可达到99.71%和97 12%,反应180 min后的TOC去除率分别达到81.54%和81.99%;反应后TiO2/AC催化剂回收率大于95%,经焙烧再生后对橙黄G反应60 min的光催化降解率仍高达95.93%.     

泡沫镍负载纳米ZnO-SnO2光催化降解三氯乙烯

采用比较简单的共沉淀法技术制备了纳米ZnO-SnO2复合氧化物光催化剂,并将其负载在泡沫镍上制成了负载型纳米光催化剂,以三氯乙烯为挥发性有机物的模型反应物,研究了反应气流速、湿度等因素对反应的影响,同时考察了催化剂的失活特征,结果表明该负载型纳米光催化剂具有较高的光催化活性,同时具有较强的抗失活性能,在205h反应中没有出现失活现象．     

光催化降解有机磷农药的研究

研究以ＴｉＯ２粉末作为光催化剂,光降解３种不同结构的有机磷农药的可行性。结果表明,有机磷农药结构不同其光降解率不同;浓度１．０×１０－４ｍｏｌ／Ｌ的４种有机磷农药,３７５Ｗ中压汞灯照射４０ｍｉｎ有机磷将完全转变为无机磷,并检测出人效磷农药催化降解的部分中间产物。研究光催化剂ＴｉＯ２的用量、空气流量、外加Ｆｅ３＋浓度对光催化降解的影响,并初步探讨了机理。     

TiO2纳米管对水源水中MC-LR的光催化降解

采用“草酸+氟化铵”水相电解液体系通过阳极氧化法制备出了TiO₂纳米管材料,可有效光催化深度降解水源水中的微囊藻毒素（MC-LR）.结果表明,阳极氧化电压为20V、组分配比为1/12mol/L H₂C₂O₄·2H₂O+0.5wt% NH₄F、电解液pH值为4、阳极氧化时间1~2h的条件下制得的纳米管形貌最清晰,孔径为50nm左右,管长为250~600nm;催化剂经过500~600℃的温度煅烧后对MC-LR的光催化降解效率相对较高;pH值在3.5或8左右时,有利于MC-LR的光催化降解,且光化学反应符合准一级反应动力学模型;MC-LR的光催化降解机理主要包括产生的强氧化性·OH自由基对Adda支链共轭双键、Mdha氨基酸单双键以及Adda支链中甲氧基等部位的攻击氧化和肽键的水解.     

金属掺杂纳米TiO2薄膜的制备和抗菌性能研究

采用sol—gel法在载玻片表面制备了Ce,Cu,i．a,Ag掺杂的锐铁矿相TiO2薄膜,并通过SEM,XRD．FT—IR及UVVIS进行了表征,比较了薄膜的抗菌性能．UV—VIS研究表明,金属掺杂纳米TiO2薄膜在近紫外区吸光度有明显提高。抗菌实验表明掺Ag的TiO2薄膜抗菌效果最佳。