电催化氧化法处理生活污水研究

研究制作了3种金属氧化物修饰电极:Ti/SnO2-Sb2O3、Ti/RuO2-IrO2、Ti/SnO2-Sb2O3-MnO2/PbO2,用这3种电极电解葡萄糖溶液,筛选出了处理效果最好的电极——Ti/SnO2-Sb2O3-MnO2/PbO2电极。通过Ti/SnO2-Sb2O3-MnO2/PbO2电极电解葡萄糖溶液实验,研究了电解时间、电流密度、电解质浓度等因素对电解效果的影响。     

改性Ti/SnO2-Sb电极催化降解1,4-二氯苯废水试验研究

采用聚合物前驱体法制备了未掺杂、掺杂Cu、掺杂Bi、掺杂Ni的4种Ti/Sn O2-Sb电极,运用SEM和XRD分析电极表面形貌及结构,通过线性极化扫描、循环伏安等测试考察其电化学性能,同时进行1,4二氯苯(p-DCB)降解实验进一步探究电极的电催化氧化特性.SEM和XRD结果表明,掺杂金属可改善电极表面形貌,增大其比表面积;电化学测试表明,Ti/Sn O2-Sb电极的析氧电位并未因金属掺杂而有明显改变,掺杂金属后,Ti/Sn O2-Sb电极具有更优的电催化活性和稳定性.p-DCB降解实验表明,改性Ti/Sn O2-Sb电极对p-DCB的降解效率明显提高,其中Ti/Sn O2-Sb-Cu电极的电催化处理效果最优,电解2 h后p-DCB的去除率即达到87.6%,且p-DCB的降解反应遵循一级反应动力学规律.     

电化学氧化PFOA阳极材料筛选及其机制研究

全氟辛酸(PFOA)具有环境持久性及内分泌干扰性,传统的生物降解及高级氧化法对PFOA的去除效果微弱.本研究采用电化学氧化法降解PFOA,选取BDD(掺硼金刚石电极)、Pt、Ti、Ti/RuO2、Ti/RuO2-IrO2、Ti/In2O3、Ti/SnO2-Sb2O5-IrO2、Ti/SnO2-Sb2O5-RhO2、Ti/SnO2-Sb2O5、Ti/SnO2-Sb2O5-CeO2和Ti/SnO2-Sb2O5-Bi2O3这11种阳极材料为备选电极.采用线性扫描伏安法测试析氧电位(OEP),评价11种电极对PFOA的降解效果和脱氟效果,并采用超声-电化学协同方法间接证明PFOA分子在电极表面的直接电子转移是降解反应的第一步.Ti/SnO2-Sb2O5-Bi2O3、Ti/SnO2-Sb2O5-CeO2、Ti/SnO2-Sb2O5和BDD对PFOA有较好的电氧化效果,降解率分别是89.8%、89.8%、93.3%和98.0%.Pt、Ti/SnO2-Sb2O5-RhO2、Ti/SnO2-Sb2O5-IrO2和Ti/In2O3对PFOA的电氧化效果微弱,降解率分别是2.1%、2.3%、12.5%和3.1%.而Ti、Ti/RuO2和Ti/RuO2-IrO2对PFOA没有电氧化能力.PFOA分子经过电极表面的直接电化学氧化发生脱羧反应,后经过逐步脱掉CF2单元的循环生成短链的全氟羧酸类化合物C6F13COO-、C5F11COO-、C4F9COO-和C3F7COO-.     

双极电化学氧化降解水中苯胺

采用钛基氧化物涂层材料（Ti/SnO2-Sb2O5）为阳极,石墨为阴极,在含Fe2＋和不含Fe2＋2种电解质条件下研究了苯胺的电化学氧化降解效率和机制.结果表明,Ti/SnO2-Sb2O5阳极氧化降解有机物的电位约2.0 V±0.1 V,而石墨阴极还原O2生成H2 O2的优化电位为-0.65 V.H2 O2单独作用不能...     

La-PTFE共掺杂二氧化铅电极的制备及其性能研究

以Ti为基体,掺杂La2O3和聚四氟乙烯(PTFE),通过电沉积法制备了Ti/SnO2+Sb2O3/PTFE+La2O3+β-PbO2电极,并将所制备的电极应用于亚甲基蓝模拟染料废水的降解.结果发现,与常规的Ti/SnO2+Sb2O3/PTFE+β-PbO2电极相比,Ti/SnO2+Sb2O3/PTFE+La2O3+β-PbO2电极对亚甲基蓝及COD有较好的去除效果.含有La2O3活性层的Ti/SnO2+Sb2O3/PTFE+La2O3+β-PbO2电极在电解质浓度为0.15mol.L-1,电极极距为6.0cm的酸性条件下降解亚甲基蓝的效果最佳.降解3.0h后,对100mg.L-1亚甲基蓝的去除率可达到97.92%,对COD去除率为93.39%.SEM结果显示,Ti/SnO2+Sb2O3/PTFE+La2O3+β-PbO2电极表面颗粒鲜明,比表面积增大,改善了电极的微观结构和催化效果.电化学测试表明,La2O3的掺杂显著提高了二氧化铅电极的析氧过电位,显示出较好的应用前景.     

AEO-7改性PbO2电极电催化降解结晶紫

通过在镀液中添加表面活性剂AEO-7,以不锈钢为基体,利用阳极氧化法制备了改性PbO2电极.同时,在结晶紫模拟废水中对比了改性前后PbO2电极的阳极极化曲线和塔菲尔曲线,并对质量浓度为10 mg·L-1的结晶紫模拟废水进行了电催化降解实验.实验结果表明,制备的改性PbO2电极对结晶紫废水的降解显示出了较好的电催化活性,最佳电解实验条件为:电解电流密度30 mA·cm-2,支持电解质Na2SO4浓度5g·L-1,处理温度35℃,在此条件下电解40 min后,结晶紫的去除率可达到90％以上.     

电化学催化氧化法降解水中甲基橙的研究

采用电沉积-热解氧化法制备了含有中间层SnO2+Sb2O3的钛基体二氧化铅电极(Ti/SnO2+Sb2O3/PbO2),以甲基橙水溶液为模拟废水,研究了所制备的电极对其所具有的电催化氧化脱色性能。考察了电极制备条件对电极催化性能的影响,同时对甲基橙脱色降解实验条件进行了优化。用该电极对含60mg/L甲基橙的模拟废水处理2h,脱色率可达到82.21%,COD去除率为76.75%。     

电-Fenton法降解废水中苯乙酮

以活性炭纤维为阴极,Ti/SnO2-Sb2O3为阳极,采用电-Fenton法处理苯乙酮废水,考察了Fe2+浓度、电流密度等对污染物降解过程的影响.结果表明,电-Fenton法可以破坏苯乙酮分子中的苯环结构,并使废水CODCr明显下降,同不投加Fe2+的传统二维电极处理技术相比,污染物的去除效率和电流效率均明显提高.电流...     

Ti/SnO2-Sb2O5/PbO2阳极电化学氧化降解苯甲酸研究

文章研究了TI/SnO2-Sb2O5/Pbo2在两室电解池中氧化降解苯甲酸的性能,主要考察了电流密度、初始pH值、初始苯甲酸浓度和支持电解质这四个参数对TOC去除效率的影响。实验表明在电流密度为30 mA/cm2,初始苯甲酸浓度为0.5 mmol/L,支持电解质(Na2SO4)为0.1mol/L的条件下,经过6 h反应...     

不锈钢基PbO_2电极的制备及其降解活性艳兰的研究

采用电沉积法制备不锈钢基PbO2电极。采用SEM、XRD、XPS等方法对电极的表面形貌、元素组成及元素化学态进行表征和分析。对不锈钢基PbO2电极电催化氧化活性艳兰模拟废水的脱色效果进行研究,结果表明:当电流密度为40 mA/cm2、无水硫酸钠浓度为0.04 mol/L,电解25 mg/L的活性艳兰模拟废水15 min,脱色率可以达到95%以上。     

钛基氧化物电极的制备及其在水处理中的应用

介绍了钛基氧化物电极制备的理论基础 ,并综述了 Ti/Sn O2 和 Ti/Pb O2 系列电极在水处理中的应用     

Ce修饰Ti/PbO2阳极电催化氧化降解苯酚的研究

采用电沉积法制备Ce修饰Ti/PbO2电极,通过动态极化法、循环伏安法、快速电极寿命法对电极性能进行了研究,表明该电极具有较高的析氧电位(2.11 V)和良好的电催化活性,预测电极使用寿命为2.3年.以苯酚为目标降解物,探讨了电极电催化性能,并考察苯酚初始浓度、电流密度、阳极材料、溶液温度、搅拌速度对苯酚降解效果的影响.结果表明最佳工艺参数为:电流密度为0.06 A·cm-2,pH=6.7,电极间距为2 cm,温度20℃,搅拌速度180 r·min-1,采用0.5 mol·L-1的Na2SO4溶液作为支持电解质,5 h后苯酚去除率达到95.5%.     

适用于废水处理的DSA电极的研究进展

电化学氧化技术因其具有氧化能力强、可控性高、运行费用低及对环境友好的特点,引起了人们极大的关注.处于核心地位的DSA（Dimensionally Stable Anodes）电极是电化学工作者研究的重点.Ti基氧化铅、氧化铱、锡锑氧化物等电极是目前最有研究价值的DSA电极,文章介绍了这些电极的一些最新的研究成果.     

适用于废水处理的DSA电极的研究进展

电化学氧化技术因其具有氧化能力强、可控性高、运行费用低及对环境友好的特点,引起了人们极大的关注。处于核心地位的DSA（Dimensionally Stable Anodes）电极是电化学工作者研究的重点。Ti基氧化铅、氧化铱、锡锑氧化物等电极是目前最有研究价值的DSA电极,文章介绍了这些电极的一些最新的研究成果。     

Photoelectrochemical degradation of Methylene Blue with -PbO2 electrodes driven by visible light irradiation

-PbO2 electrodes were prepared by electro-deposition and characterized by scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and linear sweep voltammetry. We confirmed pure -PbO2 crystals were on the electrode and it had a high oxygen evolution potential. The photoactivity and photoelectrochemical (PEC) properties of the -PbO2 electrode were investigated under visible light irradiation ( > 420 nm) for the decolorization of Methylene Blue. Pseudo first-order kinetics parameter (Kapp) for dye decolorization using the -PbO2 electrode achieved 6.71×10?4 min?1 under visible light irradiation, which indicated its excellent visible light-induced photoactivity. The Kapp of the PEC process was as much as 1.41×10?3 min?1 and was 1.71 times that of visible light irradiation or electrolysis even in the presence of the -PbO2 electrode. A significant synergetic effect was observed in the PEC system. We also employed TiO2 modified -PbO2 electrodes in this test, which revealed that the TiO2 immobilized on the -PbO2 electrode inhibited the visible light-induced PEC efficiency despite the amount of TiO2 used for electrode preparation. The -PbO2 electrode was also superior to the dimensionally stable anode (Ti/Ru0:3Ti0:7O2) in visible light-induced photoactivity and PEC efficiency.     

声电氧化处理亚甲基蓝废水的研究

采用电沉积法制备了稀土和氟树脂等共掺杂的新型二氧化铅电极,并用于声电氧化体系中作为阳极处理典型模拟染料废水.考察了声电耦合氧化条件下的协同因子变化,发现PbO2/Ti电极和La-PbO2/Ti电极作阳极时,协同因子分别为1.29、1.36.考察并优化了该氧化镧掺杂电极用于声电氧化体系的作用因素,结果表明,在功率为49.58W/cm2、频率为50Hz、阳极电极为La-PbO2/Ti电极、电流密度为71.43mA/cm2、硫酸钠为14.2g/L的条件下,200mg/L的亚甲基蓝模拟废水经过2h后去除率达到89.51%.通过GC-MS、IC等分析手段检测了中间产物,提出了亚甲基蓝可能的降解途径.     

Effect of Sb dopant amount on the structure and electrocatalytic capability of Ti/Sb-SnO2 electrodes in the oxidation of 4-chlorophenol

Ti/Sb-SnO_2 anodes were prepared by thermal decomposition to examine the influence',of the amount of Sb dopant on the structure and electrocatalytic capability of the electrodes in the oxidation of 4-chlorophenol.The physicochemical properties of the Sb-SnO_2 coating were markedly influenced by different amounts of Sb dopant.The electrodes,which contained 5% Sb dopant in the coating, presented a much more homogenous surface and much smaller mud-cracks,compared with Ti/Sb-SnO_2 electrodes containing 10% or 15% Sb dopant,which exibited larger mud cracks and pores on the surface.However,the main microstructure remained unchanged with the addition of the Sb dopant.No new crystal phase was observed by X-ray diffraction(XRD).The electrochemical oxidation of 4-chlorophenol on the Ti/SnO_2 electrode with 5% Sb dopant was inclined to electrochemical combustion;while for those containing more Sb dopant,intermediate species were accumulated.The electrodes with 5% Sb dopant showed the highest efficiency in the bulk electrolysis of 4-chlorophenol at a current density of 20 mA/cm~2 for 180 min;and the removal rates of 4-chlorophenol and COD were 51.0% and 48.9%,respectively.     

不同涂层电极和抑制剂对电化学氧化降解苯酚的影响

采用热分解法和电沉积法2种工艺制得4个二氧化铅电极,用扫描电镜（SEM）观察了电极表面形貌.以水杨酸(2-HBA)为捕获剂,用高效液相色谱仪测定羟基自由基与水杨酸的羟基化产物2,5-二羟基苯甲酸(2,5-DHBA)的量作为产生的羟基自由基的浓度.通过羟基自由基的浓度的测定和苯酚的降解,研究了不同涂层电极和抑制剂对电化学氧化对苯酚降解的影响.热分解电极、无掺杂电极、掺铋电极和掺镧电极产生羟基自由基的最大浓度分别为0.781、1.048、1.838、2.044 μmol/L,以这4个电极为阳极对苯酚进行电解, 1.5　h苯酚去除率分别为87.30%、93.55%、97.95%、98.70%,5　h　TOC去除率分别为86.75%、94.26%、98.53%、99.60%;以掺镧电极为阳极,加入抑制剂CO^2-₃、PO^3-₄、CH₃ＣＯＯ^-产生的羟基自由基的最大浓度分别为无检出、0.170 μmol/L、0.270 μmol/L,对苯酚进行电解,5 h苯酚去除率分别为99.06%、99.98%、99.79%.电沉积法制得电极对苯酚的降解效果优于热分解法制得的电极,而掺杂的电极优于无掺杂的电极,掺镧电极对苯酚降解效果最好,抑制剂CO^2-₃、PO^3-₄、CH₃ＣＯＯ^-存在时会对苯酚的降解起到阻碍作用,CO^2-₃阻碍作用最强.不同制备方法和掺杂不同添加剂制得的电极的催化性能不同,对苯酚的降解效果也不同;羟基自由基的浓度越大,苯酚的降解效果越好,抑制剂捕获了产生的羟基自由基,不利于苯酚的降解.