有机磷酸HEDP稳定垃圾焚烧飞灰重金属的研究

研究了有机磷酸羟基亚乙基二膦酸（HEDP）对生活垃圾焚烧飞灰中重金属的稳定方法.通过对不同HEDP投加量处理后的飞灰试样作危险废物浸出毒性鉴别试验,分析HEDP最佳使用剂量,并评价了稳定化飞灰的长期稳定性.结果表明,HEDP最适使用剂量为0.03 Ml/g（以商品级HEDP与飞灰的体积质量比计）,处理后飞灰与原状飞灰相比,Pb、Zn和Hg的浸出浓度分别降低了98.3%、99.5%和85.0%.HEDP对飞灰中重金属稳定效果排序为：Pb＞Zn＞Hg＞Ni＞Cu＞Cd＞CrHAs.重金属pH相关浸出测试（pH-dependent leaching tests）表明：经0.03mL/g HEDP稳定处理的飞灰,在0.3 mol/L HNO3和0.3 mol/L NaOH的浸取条件下,其重金属浸出浓度均低于国家危险废物鉴别标准,显示具有良好的长期稳定性.     

垃圾焚烧飞灰有毒重金属固化稳定技术研究综述

采用焚烧法处理生活垃圾正呈快速增长的趋势,焚烧过程产生的飞灰中所含有的大量有毒重金属对自然环境和人类生存都造成极大影响。阐述了目前常用的几种固化稳定垃圾焚烧飞灰有毒重金属的方法,综合分析了其固化特点和优缺点,并初步探索了一种低能耗环境下实现高温熔融处置技术的有效途径,从而为垃圾焚烧飞灰高温固化稳定有毒重金属的实施提供一定的理论基础和技术支持。     

生活垃圾焚烧飞灰重金属的受热特性

研究了飞灰重金属在不同煅烧温度下的挥发情况及其存在形态.结果表明:重金属挥发能力由强到弱依次为Hg＞Pb＞As、Cd＞Zn＞Cr、Ni、Cu;其中Hg、Pb、As和Cd属易挥发重金属,在1 150 ℃时几乎全部挥发;Zn属较易挥发重金属,1 150 ℃时的挥发率在40%～50%;Cr、Ni和Cu属难挥发重金属,在1 150 ℃的挥发率不超过10%;在400～1 150 ℃,随温度的升高,部分Zn、Hg、Cu、Pb、Cd、Ni和As由可溶态向残渣态、铁锰氧化态转化;在400～900 ℃,随温度的升高Cr可溶态比例减少,而在900～1 150 ℃,随温度的升高其可溶态比例增加.     

酸洗-电沉积联用技术回收垃圾焚烧飞灰中的重金属

垃圾焚烧飞灰中的重金属浸出能力强、毒性大,属于危险废物,若处置不当将会对环境造成严重污染。采用酸洗-电沉积联用技术,考察硝酸浓度、液固比和酸洗时间对重金属去除率的影响,研究电沉积电压和时间对酸洗废液中重金属回收率的影响,同时评估处理后飞灰的浸出毒性。结果表明,在浓度为2 mol·L⁻¹、液固比为25的硝酸中浸渍洗涤60 min条件下,酸洗能成功去除飞灰中95.26%的Zn、83.06%的Pb、72.62%的Cu和97.85%的Cd;在电压为14 V,电沉积4 h的条件下可回收酸洗废液中95.80%的Zn、99.04%的Pb、79.95%的Cu和90.37%的Cd。对Zn、Pb、Cu、Cd的连续提取和浸出毒性测试表明,处理后飞灰易浸出组分占比降低,残余态物质占比提高,重金属浸出质量浓度符合《生活垃圾填埋场污染控制标准》(GB 16889-2008)要求,可直接进行填埋或作为非危废固体进行资源化利用。本研究结果可为飞灰中重金属脱除和回收利用提供参考。     

有机磷酸HEDP稳定垃圾焚烧飞灰重金属的研究

研究了有机磷酸羟基亚乙基二膦酸(HEDP)对生活垃圾焚烧飞灰中重金属的稳定方法.通过对不同HEDP投加量处理后的飞灰试样作危险废物浸出毒性鉴别试验,分析HEDP最佳使用剂量,并评价了稳定化飞灰的长期稳定性.结果表明,HEDP最适使用剂量为0.03 Ml/g(以商品级HEDP与飞灰的体积质量比计),处理后飞灰与原状飞灰相比,Pb、Zn和Hg的浸出浓度分别降低了98.3%、99.5%和85.0%.HEDP对飞灰中重金属稳定效果排序为:Pb＞Zn＞Hg＞Ni＞Cu＞Cd＞CrHAs.重金属pH相关浸出测试(pH-dependent leaching tests)表明:经0.03mL/g HEDP稳定处理的飞灰,在0.3 mol/L HNO3和0.3 mol/L NaOH的浸取条件下,其重金属浸出浓度均低于国家危险废物鉴别标准,显示具有良好的长期稳定性.     

掺加矿粉胶凝固化垃圾焚烧飞灰中重金属的研究

通过单因素实验探究了矿粉质量分数、激发剂(NaOH)投加量和加水量对掺加矿粉胶凝固化垃圾焚烧飞灰中重金属的影响,并初步探究了固化机理。结果表明,矿粉质量分数和激发剂投加量对重金属的固化影响较大,而加水量影响不大。综合考虑增容比、重金属浸出浓度和抗压强度,矿粉质量分数15%、激发剂投加量3%(质量分数)、加水量37.5%(质量分数)为有效稳定固化重金属的最佳条件,此时重金属浸出质量浓度分别是Ba 19.091mg/L、Cd 0.041mg/L、Ni 0.216mg/L、Pb 0.196mg/L,含水率为27.04%,满足《生活垃圾填埋场污染控制标准》(GB 16889—2008),抗压强度为9.61 MPa,可进入垃圾填埋场填埋。所制备胶凝材料的最终水化产物主要为水化硅酸钙、水化铝硅酸钙和钙矾石,它们可以通过包裹和吸附对重金属进行固化。     

重庆市垃圾焚烧飞灰特性及重金属浸出行为的研究

通过激光粒度仪分析了重庆市垃圾焚烧飞灰颗粒粒径的分布特征,并研究了在GB5085.3-2007和USEPA-TCLP浸出条件下及不同pH、浸出液固比和浸出时间等因素下重庆市垃圾焚烧飞灰中重金属的浸出行为.结果表明,重庆市垃圾焚烧飞灰颗粒平均粒径为36.4μm,飞灰中主要重金属总量约1.04%,Zn、Pb含量较高,具有较...     

水泥对垃圾焚烧飞灰的固化处理试验研究

对垃圾焚烧飞灰的化学成分、重金属物质的含量及浸出浓度进行测试分析.结果表明,飞灰中Pb和Cr等重金属物质浸出量超过浸出毒性标准,因而被认为是危险废物,必须进行固化处理.还考察了水泥对焚烧飞灰中重金属物质固化的效果,研究表明当飞灰掺量适当时,重金属物质的固化效果良好.重金属物质通过物理固封、替代,沉淀反应和吸附等形式可固化进水泥水化产物结构中.     

矿渣高温固化垃圾焚烧飞灰中的重金属

垃圾焚烧飞灰由于含有大量重金属属于危险固体废物,重金属的浸出含量影响其资源化利用。模拟高炉矿渣在熔融状态下固熔部分飞灰,研究固熔体急冷后其重金属的浸出规律,采用SEM-EDS、XRD、FTIR研究固熔体固化重金属的机理。结果表明：重金属浸出量随着熔融温度的升高而减少,随着飞灰掺量的增加而增加,但浸出浓度远低于国家标准;SEM-EDS表明,主要重金属均出现在固熔体中;XRD证实有部分Zn以生成Ca2ZnSi2O7的形式被固化;FTIR的结果也表明固化的重金属影响了Si—O—Si键的周围环境。     

垃圾焚烧飞灰磷酸洗涤对重金属的固定效应研究

重金属的固定是垃圾焚烧飞灰资源化技术的核心问题.通过系统试验,研究了垃圾焚烧飞灰磷酸洗涤对重金属溶出、后续烧结过程中重金属挥发,以及重金属化学形态变迁的影响.试验结果表明,磷酸洗涤在有效洗脱飞灰中氯盐的情况下,能够显著减少洗涤过程中重金属的溶出,抑制烧结过程中重金属的挥发,从而避免了飞灰处理过程的二次污染;同时,磷酸洗涤使飞灰中的重金属在烧结前后均向更为稳定的化学形态转化,烧结产物中重金属主要以残留态存在,从而提高了烧结产物资源化利用的长期环境安全性.     

Dehalogenation Potential of Municipal Waste Incineration Fly Ash

BACKGROUND, AIMS AND SCOPE: In the first part of this paper the main principles which control the dehalogenation of polychlorinated aromatic compounds on municipal waste incineration fly ash (MWI-FA) have been discussed and the model fly ash of similar dehalogenation activity has been proposed. Even if both systems show comparable dehalogenation properties, the main question concerning the postulated identical reaction mechanism in both cases is left unanswered. The other very important point is to what extent is this dechlorination mechanism thermodynamically controlled. The same problem is often discussed in the literature also for the de novo synthetic reactions. From the data it is clear that metallic copper plays a decisive role in the mechanism of the dehalogenation reaction. Although the results reported in the first part strongly support the idea that copper acts in this dechlorination as the reaction component, in contrast to its generally accepted catalytic behaviour, we believed that additional support for this conclusion can be obtained with the help of a thermodynamic interpretation of the mechanism of the reaction. RESULTS AND DISCUSSION: The pathways of hexachlorobenzene dechlorination on MWI-FA and model fly ash were studied in a closed system at 260-300 degrees C under nitrogen atmosphere. These pathways were the same for both systems, with the following prevailing sequences: hexachlorobenzene --> pentachlorobenzene --> 1,2,3,5-tetrachlorobenzene --> 1,3,5-trichlorobenzene --> 1,3-dichlorobenzene. Thermodynamic calculations were carried out by using the method of minimization total Gibbs energy of the whole system. In the calculations, the following reaction components were taken into account: all gaseous chlorinated benzenes, benzene, hydrogen chloride, a gaseous trimer Cu3Cl3, and also Cu2O and CuCl2 as solid components. The effect of the reaction temperature and the amount of copper and water vapour were considered as well. The effect of reaction temperature was determined from the data calculated for the 500 to 750 K temperature region. The effect of the initial composition was determined for the molar amounts of copper = 0.01-3 moles and water vapour = 0.2 to 3 moles per mole of chlorobenzene isomer CONCLUSIONS: The results of hexachlorobenzene dechlorination by MWI-FA and model fly ash under comparable reaction conditions allow us to conclude that both dechlorinations proceed via the same dechlorination pathways, which can be taken as an evidence of the identical dehalogenation mechanism for both systems. The relative percentual distribution of the dehalogenated products depends on the temperature, but not on the initial amount of water vapour or copper metal. On the other hand, the initial amount of copper substantially affects the conversion of the dehalogenation as well as the molar ratio of Cu3Cl3 to HCl in the equilibrium mixture. Comparison of the experimental with thermodynamic results supports the idea that dehalogenation reactions are thermodynamically controlled. RECOMMENDATIONS AND OUTLOOK: Thermodynamic analysis of the dehalogenation reactions may prove useful for a wide range of pollutants. The calculations concerning polychlorinated biphenyls and phenols are under study.     

常熟垃圾焚烧飞灰安全填埋场工程设计

介绍了常熟垃圾焚烧飞灰安全填埋工程的设计，包括飞灰预处理系统、填埋库结构、防渗和封场设计以及渗沥液处理等。结合工程设计实践，探讨了飞灰安全填埋场的设计技术和设计原则。     

垃圾焚烧飞灰的稳定化处置与资源化利用研究进展

随着垃圾焚烧处理日益广泛的应用，垃圾焚烧飞灰的稳定化处置和资源化利用成为一个亟待解决的问题。文中对垃圾焚烧飞灰的稳定化处置和资源化利用技术分别进行了综合论述，为飞灰的无害化和资源化处理提供参考。     

医疗垃圾焚烧飞灰重金属形态分析

利用原子吸收光谱仪分别对医疗垃圾焚烧飞灰重金属含量和重金属形态及其随颗粒度分布特性进行了分析,结果表明,飞灰中Cd、Zn、Pb等的浸出浓度远超标与这些重金属的可交换态和碳酸盐态含量较高有关;飞灰颗粒度主要在96 μm以下,96～150 μm的颗粒中Cd、Pb含量最高,且Zn、Cd的形态以可交换态为主.     

熔盐法处置高熔点垃圾焚烧飞灰重金属的浸出特性

对熔盐法处置高熔点垃圾焚烧飞灰重金属离子浸出特性进行了实验研究。结果表明,熔盐物料组成、熔盐温度和热处理气氛对重金属离子的热挥发特性具有重要影响。在还原性气氛条件下,热处理温度为900～1 000 ℃,添加质量分数为10%～50%的CaCl2的氯化钠熔盐中处理2 h后,垃圾焚烧飞灰渣中Pb、Cd、Cu和Zn等重金属浸出浓度降低90%以上,可以完全达到生活垃圾填埋场填埋标准。在此过程中,灰渣较原灰可减轻50%,同时转化成具有良好胶凝性能的水泥活性混合材料,XRD测试表明其晶体矿物组成为硅酸二钙、硅酸三钙和阿里尼特以及硫酸钙等。     

危险废物焚烧飞灰中重金属的稳定化处理

以上海市某危险废物焚烧厂飞灰为研究对象,采用Na2S、FeSO4、Na3PO4、和Na3C3N3S34种不同类型化学稳定药剂对飞灰进行了稳定化处理,并应用XRD、IR、SEM和连续化学提取法等仪器和手段对Na3C3N3S3处理焚烧飞灰的产物进行分析研究。研究结果表明,Na3C3N3S3对飞灰中的重金属Cr、Pb、Zn的稳定效果最好,Na3PO4对Cr无明显稳定效果。稳定后产物表面变得致密化,Na3C3N3S3与重金属离子生成的沉淀物干燥后无明显晶型存在。经稳定处理后飞灰中的重金属形态由弱酸提取态转化为可氧化态,减少了飞灰中重金属的浸出毒性。     

城市生活垃圾焚烧处理过程中重金属迁移规律研究

通过采集厦门2个垃圾焚烧发电厂进厂垃圾、渗滤液、飞灰、炉渣和烟气样品,分析垃圾组成成分及各组分的重金属含量,结果表明,垃圾中以厨余、橡塑类和纸类为主,共占到垃圾干基的78．08％,重金属含量大小次序为Zn〉Cu〉Pb〉Cr〉Ni〉Cd〉Hg;垃圾渗滤液中除Zn外,其他金属的含量都较低,一厂渗滤液中重金属Ni、Zn迁移量较大,分别达到24．46％和8．52％。二厂渗滤液中重金属的迁移有相同的趋势,但含量相对较高。垃圾焚烧后其重金属主要分布在飞灰和废渣中,烟气中的含量非常少,不同金属的含量均有差别,这与金属的性质有很大关系;通过浸出毒性分析,飞灰中重金属酸溶态含量多,容易浸出,属于危险废物。同时,不同烟气处理工艺产生的飞灰的重金属浸出量有很大差别。     

不同粒径垃圾焚烧底渣的特性和PAHs含量及毒性浸出

研究了不同粒径垃圾焚烧底渣的质量分布、物质成分(XRF)、晶体结构(XRD)、PAHs含量、酸反应特性、PAHs含量以及在2种浸出液中的毒性浸出情况。在比较国内外相关研究的基础上,实验得出垃圾焚烧底渣主要分布在粒径大于0.28 mm范围内,相比一些地区的研究结果要偏细;主要的物质成分为SiO2、CaO、Al2O3、Fe2O3、MgO、Na2O和K2O,而主要的晶体结构则分别为CaCO3、SiO2、Ca(OH)2和Mg0.3Ca0.97CO3,都与其他地区的研究结果基本相同;PAHs含量为0.043 4~0.247 mg/kg,与一些研究欧洲地区底渣中PAHs的含量的结果基本相近,且PAHs同类物的含量也随着底渣粒径的减小而增大;同时,实验还得出底渣中8种重金属在2种浸出液中的浸出浓度都未超出危险废物浸出毒性鉴别标准值(GB 5085.3-2007),但当底渣粒径大于0.6 mm时,其对环境中酸性物质的缓冲能力变弱。通过比较国外的一些研究结果,得出如将底渣作为建材利用时,需采用相应防范措施以防止其所含的重金属对周围土壤和水体的影响。希望能为进一步认识、处理和利用垃圾焚烧底渣提供一定的理论参考。     

垃圾焚烧过程中影响重金属分布因素的研究

在转式垃圾焚烧炉和固定床加热炉中,研究了有机垃圾焚烧过程中温度、水分、无机氯及有机氯对几种重金属分布的影响。研究结果表明,焚烧垃圾过程中焚烧温度对重金属分布特性的影响特性不一,重金属锌和铅容易转移到气相中去,而重金属镍和铬大部分是以固态形式残留在底渣中;水能与重金属及其化合物发生反应,引起物质转变,影响重金属的分布;氯的存在也影响重金属的分布特性,氯的参与使重金属更易向飞灰或烟气中迁移。     

污水厂出水回用于污泥焚烧烟气的净化

开展了污水处理厂出水回用于污泥焚烧烟气净化的实验研究。生化出水净化吸收污泥焚烧烟气的效果与气水比、进气浓度、进水pH、进水碱度和水温等因素有关。研究结果表明,气水比10∶1,进水pH为7条件下,生化出水能够有效吸收污泥焚烧烟气中的各种污染物质,出气中气体污染物低于《生活垃圾焚烧污染控制标准》（GB18485-2001）的排放限值要求,吸收后出水各指标均低于《污水综合排放标准》（GB8978-1996）中污染物排放限值的要求。该工艺脱硫效率可达90%,具有系统简单可靠、以废治废、不产生二次污染等优点。