循环流化床锅炉水冷壁管的腐蚀失效分析

针对某高压循环流化床锅炉水冷壁管底部弯管处爆管原因进行失效分析,通过对爆管管段进行宏观检查、化学成分分析、力学性能分析、腐蚀产物分析、金相分析以及运行期间水质化验记录调查,表明锅炉水质p H偏高时在密相区弯管处向火侧内壁发生碱浓缩引起碱腐蚀,弯管处存在的残余应力在强碱性环境下引起碱应力腐蚀,两者共同作用导致了本次爆管的发生。加强水质监控和消应力处理可有效防止碱腐蚀和碱应力腐蚀。     

熔盐蒸发器管板封口焊缝泄漏原因分析

某光热电站熔盐蒸发器入口侧管板封口焊缝发生泄漏,通过表面检测和观察,发现裂纹是从封口焊缝根部发展,并从根部向外扩展的。根据裂纹扩展方向和运行数据进行综合分析认为,熔盐蒸发器在未正确操作下导致在极短时间内管板下部表面升温过快,造成封口焊缝局部热应力过大。在焊缝残余应力、工作应力和热应力共同作用下,管板下部封口焊缝根部产生裂纹并扩展至焊缝表面,形成贯穿性裂纹,造成蒸发器管板泄漏。     

余热锅炉分汽缸应力腐蚀开裂分析

某水泥余热发电锅炉分汽缸补焊缝及附近母材出现大量裂纹,部分裂纹出现穿透;宏观观察发现分汽缸表面覆盖有大量黑色粉尘状物质,裂纹沿焊缝呈环向或纵向分布;金相分析及扫描电镜形貌观察结果可见焊缝断口主要为沿晶开裂,同时在断口附近发现大量的沿晶二次裂纹;EDS能谱分析与X射线衍射物相分析结果表明分汽缸窑头侧内壁存在大量碳酸盐和碱浓缩;通过对补焊的未开裂焊缝和附近筒体母材分别进行残余应力测试,结果表明焊缝位置最大应力达251MPa,超出材料屈服强度。综合分析表明:分汽缸内壁存在碳酸盐积聚和碱浓缩,在焊接残余应力和工作应力等因素的共同作用下,分汽缸焊缝及附近区域出现了应力腐蚀开裂。     

乙二醇不锈钢蒸发器贴补焊残余应力数值模拟

某厂乙二醇不锈钢蒸发器在检修过程中发现封头与筒体环焊缝处存在大量裂纹,失效原因为晶间应力腐蚀开裂。采用加内贴板补焊的措施来进行修复,焊接残余应力是影响贴补焊接头完整性的主要因素之一。本文采用有限元法对贴补焊产生的残余应力进行分析,比较手工电弧焊（MAW）和钨极氩弧焊（TIG）两种方法对残余应力分布的优劣,得到贴补焊接头的残余应力分布状态。结果表明：钨极氩弧焊所产生的残余应力较小,有利于降低应力腐蚀开裂的敏感性,提高贴补焊结构的完整性。     

L245A级钢管在湿H_2S环境下的氢致开裂(HIC)与硫化物应力腐蚀开裂(SSCC)试验研究

管线钢在湿H2S环境下运行必须考虑其抗氢致开裂(HIC)和硫化物应力腐蚀开裂(SSCC)性能,因此,在确保L245A级钢管力学性能合格的前提下,根据NACETM0284—2003和NACETM0177—2005标准,按照L245A级钢管及焊缝所处的不同介质浓度和运行压力设计了8组试验。通过降低介质浓度和运行压力对L245A级钢管在湿硫化氢环境下的抗氢致开裂性能和硫化物应力腐蚀开裂性能(SSCC)进行了试验评定;通过4组试验得出:L245A级钢管在标准湿H2S环境下不会产生氢致开裂,发生硫化物应力腐蚀开裂,在设计条件和工作条件下不发生应力腐蚀开裂的结论。同时笔者对管道在湿H2S环境下的安全运行提出了建议。     

氧化铝厂蒸发器发生应力腐蚀的原因分析与防治

对氧化铝厂蒸发器发生应力腐蚀的危害性作了介绍 ,描述了应力腐蚀裂纹的特征 ;对应力腐蚀产生的原因进行了分析 ,并提出了防治措施     

丁二烯装置基于风险的检验技术应用

采用RBI技术对丁二烯装置进行风险评估,经分析装置存在的主要损伤机理有碱应力腐蚀开裂、有机酸腐蚀、冷却水腐蚀、冲刷腐蚀和丁二烯自聚等,装置的风险由失效后果主导,失效可能性较高的评估.单元集中在脱重冷凝系统和薄壁小直径管道。根据基于风险的检验策略对装置实施检验,检验过程中发现装置存在脱重冷凝系统设备应力腐蚀开裂、一萃塔系统换热器点蚀、接管角焊缝开裂和压力管道腐蚀減薄等主要问题,检验检测结果与风险评估过程中识别的损伤机理和薄弱环节保持一致。     

分子筛装置交换反应罐焊接部位腐蚀原因分析及防腐建议

某催化剂分子筛装置的奥氏体不锈钢焊缝腐蚀主要集中在交换罐,其材质为1Cr18Ni9Ti或0Cr18Ni9Ti,罐体焊缝腐蚀的部位主要集中在罐底部。在环纵焊缝邻近处液面以下,交换罐在运行期间多处发生微裂纹渗漏现象,渗漏多发生在焊接热影响区,母材中也有发生。本文通过交换罐内腐蚀介质的分析、焊接件的耐蚀性评价、失效分析等实验,分析出腐蚀原因主要是由酸性条件下Cl-引起的晶间腐蚀、应力腐蚀开裂,并从焊缝焊接技术的改进、焊缝的防腐表面处理及新罐的选材等几方面提出相关防腐建议。     

甲醇精馏塔再沸器管板泄漏失效分析

精馏塔再沸器运行工况并不苛刻,腐蚀程度轻微,工艺介质中亦没有引起环境开裂的典型介质,管板与管束连接角焊缝却频繁开裂泄漏,严重影响到装置的连续生产。本文从管板应力强度方面分析,表明造成角焊缝开裂的原因是由于管板角焊缝厚度偏薄导致的强度不足,在使用过程中,操作压力和温差引起的轴向应力使角焊缝开裂。     

碳四装置气相平衡线开裂分析

某工厂碳四装置醇精制单元ZM1601气相平衡碳钢管线在运行过程中发生开裂泄露,通过宏观检查,表面PT检测、金相观察、能谱分析对开裂原因进行了分析。结果表明开裂原因为碱液进入管道,在工作温度下发生碱应力腐蚀开裂,引发泄露。     

换热器不锈钢换热管束开裂原因分析

一台换热器换热管束发生了开裂泄漏.采取全面检验的方式,通过宏观检查、化学成分分析、断口微观形貌和能谱分析、金相分析等方法,对换热管开裂原因进行了分析.结果表明:该换热管开裂为氯化物应力腐蚀开裂.壳程介质循环冷却水中CI元素含量是应力腐蚀开裂的主要因素,结构缺陷、敏感的工作温度区间、水中溶解氧和含S杂质导致了应力腐蚀的快速发展.     

混凝土中钢筋锈蚀的研究

钢筋腐蚀对混凝土耐久性和安全性有很大影响。笔者阐述了研究钢筋锈蚀的原因、目的和意义;研究了钢筋在未开裂和裂缝状态下的锈蚀机理,钢筋的腐蚀过程实质上是一个电化学反应过程;影响钢筋锈蚀的主要因素有混凝土的密实度、混凝土碳化、环境湿度、氯离子侵入等;对钢筋腐蚀过程中的4个阶段进行了研究;从锈后钢筋截面面积损失率对结构受力的影响进行讨论;从正常使用寿命和承载能力使用寿命两方面对在役混凝土结构剩余寿命进行预测;并提出了钢筋锈蚀应采取的预防措施,以提高结构的耐久性和安全性,减少耐久性破坏造成的损失。研究的成果在工程上具有一定的理论意义和实用价值。     

流化床锅炉的特点和检验重点

通过对流化床锅炉特点的论述,阐明该型锅炉的检验重点.介绍了不同流化床锅炉的检测方法、对重点部位的检验要求和应该达到的标准,以及重点检验的程序和方法,保证流化床锅炉安全可靠的运行,确实保证流化床锅炉的脱硫效果,保证流化床锅炉高效经济运行.     

A failure analysis of fillet joint cracking in an oil storage tank

This paper has studied failure of an oil storage tank. During operation, several cracks were observed at the fillet weldment between reactor shell and annular plates in the bottom of oil storage tank. Extreme stresses in the structure during its operation were determined taking into account shape and geometry imperfections as well as corrosion influence. Both reactor shell and annular plates are made of carbon steel (SM53C). In this study, in order to identify the causes for the fillet weldment cracking, failure analysis such as fractography, tensile test, hardness test, corrosion test(SSRT), chemical analysis was performed. The failure of oil storage tank is the result of the combined and synergistic interaction of mechanical stress and corrosion reactions. Although cracks were initiated by corrosion, failure was generated by propagation of crack caused by stresses concentration. It was recommended that (1) the local stresses be reduced by improved weld toe geometry, and (2) the reinforcement be used in order to avoid failure by stresses concentration.     

304L不锈钢废水管线腐蚀泄漏失效分析

某304L不锈钢废水管线使用30天左右即发生腐蚀泄漏。采用宏观检验、化学成分分析、金相检验、电镜观察、三氯化铁试验等分析方法,对该废水管道的腐蚀泄漏进行失效分析。分析结果表明,该不锈钢管线所通的废水中含有高浓度的Cl^-,且试运行后一直未使用,最终在管内残留废水的作用下发生了点蚀穿孔。     

DG1025-18.2 Ⅱ 4型锅炉再热器集箱三通环焊缝开裂原因分析及处理措施

通过宏观形貌检查、化学成分分析及金相组织分析等方法对某电厂中温再热器集箱三通开裂原因进行了系统分析。分析结果表明:2002年连接管改造时未能将原有裂纹完全打磨消除,加上削薄斜面斜率过大,运行中残余微裂纹扩展,最终导致三通近焊缝处开裂。最后针对具体失效原因,提出了按标准要求削薄、打磨后表面检测、磨平焊口进行超声波检测及相关排查等改进措施和建议。     

造纸蒸球开裂原因分析

本文对碱法造纸蒸球贯穿性裂纹进行了分析,并结合工作实际指出裂纹产生的原因,主要是焊接工艺控制不严、焊工责任心不强、热处理方式处理不当且在使用过程中随着碱浓度的增加,蒸球存在较大的腐蚀及较大的复合应力。针对缺陷,笔者在设计、制造、检验、使用方面给出合理建议。     

Design of single vertical tube falling-film evaporation basing on experiment

An experimental study for fluid hydrodynamic characteristics in thin water films falling down the outside of a vertical tube was performed with the analysis of several factors about the uniformity and stability of the film. Liquid evaporation is of major interest for many fields in process engineering. One of these is chemical process engineering, where evaporation of liquids and generation of super heated steam is mandatory for numerous processes. Generally, this is performed by the use of classical pool boiling and evaporation process equipment, providing relatively limited performance. The performance of the film distributor will affect the production capacity and service life of the evaporator. In this publication a novel falling-film distributor which is used annular gap and inlet tube rotated tangentially 270° to guarantee the film uniformity is presented. Experimental data suggested that there is optimum annular gap distance is between 1.5 and 2.0 mm and the spray density should be controlled between 250 and 700 kg m⁻¹ h⁻¹. Several suggestions for evaporator design are proposed.