蜂窝活性炭与沸石分子筛对涂装VOCs废气的吸脱附性能对比

选取工业涂装VOCs废气作为试验对象,以蜂窝活性炭和沸石分子筛为吸附剂,设计固定床小试装置进行VOCs吸脱附试验。结果表明：蜂窝活性炭的碘值、比表面积、总孔容及微孔孔容均大于沸石分子筛,分别是沸石分子筛的1.79,2.93,1.55,2.02倍;相同脱附温度、进气风速条件下,VOCs从蜂窝活性炭表面脱附更容易,其脱附时间远低于沸石分子筛;相同反应条件下,蜂窝活性炭对VOCs的饱和吸附量明显高于沸石分子筛,但沸石分子筛的饱和吸附量受反应温度和VOCs浓度的影响相对较小;循环吸脱附10次后,蜂窝活性炭和沸石分子筛对VOCs的吸附率分别下降为第1次时的71.35%和81.15%,沸石分子筛的吸脱附性能更为稳定;蜂窝活性炭饱和吸附量大、脱附时间快,适用于宽负荷、低风量、中高浓度VOCs废气处理;沸石分子筛空气动力学及循环吸脱附性能较好,适用于处理初始温度相对较高、中低浓度VOCs废气。     

天然沸石吸附低浓度氨氮废水的研究

采用浙江某地天然沸石吸附废水中低浓度氨氮,研究了pH、天然沸石投加量对吸附的影响,分析了吸附等温线和吸附动力学,并进行了动态吸附和脱附研究。结果表明,pH对天然沸石吸附有较大影响,吸附的最佳pH为8.0;随着天然沸石投加量的增加,氨氮的去除率逐渐增大,但吸附量随之减小。Freundlich方程比Langmuir方程更好地描述氨氮在天然沸石上的吸附行为,且此吸附是优惠吸附。假二级方程很好地拟合吸附动力学实验数据,吸附速率常数k2随着天然沸石投加量的增大而增大。装填105g天然沸石吸附柱处理含氨氮20mg/L废水的水量为15L,出水氨氮浓度小于5mg/L。用含氯化钠和氢氧化钠的溶液作为脱附剂,脱附率为95.5%。     

稻壳基A型沸石的表征及其对NH_3-N的吸/脱附动力学研究

以稻壳的煅烧灰分为原料,采用水热合成法制得稻壳沸石,运用SEM、XRD和FTIR表征了稻壳沸石的结构特性,并通过静态平衡吸附实验研究了稻壳沸石对NH3-N的吸附特性。结果表明:实验条件下可获得结晶度高、晶型较好的A型单晶沸石,降低晶化温度有利于A型沸石的生成。初始浓度为25,50,100 mg/L时稻壳沸石的最大吸附量分别为3.36,5.16,8.39 mg/g,吸附过程遵循伪二级吸附动力学模型。碱当量MNa OH/AN对NH3-N从稻壳沸石上的脱附影响较大,MNaOH/AN为0.85、8.47和42.4时伪二级模型拟合的饱和脱附值分别为7.46,16.21,19.96 mg/g,与实测值基本接近,NH3-N从稻壳沸石上的脱附主要受化学作用控制,过程遵循伪二级脱附动力学模型。     

壳聚糖对Cu~(2+)的吸附与解吸

研究了溶液pH值、Cu2+初始浓度、吸附剂投加量、吸附时间及温度对壳聚糖吸附Cu2+的影响,并对达到吸附平衡的壳聚糖进行了解吸研究。结果表明,壳聚糖对Cu2+的吸附量随pH值的升高而增大,在pH值为4.7时,基本达到吸附平衡;吸附过程同时符合Langmuir模型和Freundlich模型,最大吸附量为142.9 mg/g;与拟一级动力学模型相比,拟二级动力学模型可以更好地描述吸附过程;吸附剂最佳投加量为1 g/L。用0.03 mol/L H2SO4溶液做脱附液,搅拌10 min,脱附率为73.4%;经过4次脱附-吸附循环,壳聚糖平衡吸附量变化不大,具有良好的重复使用性。     

壳聚糖改性4A沸石分子筛颗粒去除低温水中硝酸盐的机理研究

为解决我国北方严寒地区常规工艺难以有效去除低温地下水中硝酸盐污染的问题,以4A沸石分子筛为载体,通过壳聚糖改性制备出一种具有低温去除水中硝酸盐功能的吸附颗粒,有望作为吸附剂应用于常规水处理工艺的提标改造.通过小试试验,研究壳聚糖改性4A沸石分子筛颗粒去除低温水中硝酸盐的反应机理,分析其去除硝酸盐过程的吸附动力学、吸附等温线、吸附热力学,并通过pH_PZC（零电点）测定、FT-IR（傅里叶红外光谱）和XPS（X射线光电子能谱）进一步分析其反应前、后表面物化特性.结果表明:①在温度为8~10℃下,壳聚糖改性4A沸石分子筛颗粒对硝酸盐的吸附平衡时间为8 h,平衡吸附量为1.88 mg/g.②吸附过程符合准二级动力学模型,吸附符合Langmuir和Freundlich吸附等温模型,吸附热力学参数△G0 < 0、△H0>0、△S0>0,表明吸附为熵增加的吸热过程.③壳聚糖改性4A沸石分子筛颗粒的pH_PZC为10.0,FT-IR结果表明,-NH₂和-OH官能团吸附了水中的硝酸根离子,XPS结果表明,N（1s）和O（1s）元素在吸附过程中参与反应.研究显示,壳聚糖改性4A沸石分子筛颗粒分子结构中的-NH₂和-OH基团通过静电结合和氢键作用与硝酸根离子进行吸附反应.      

改性13X沸石蜂窝转轮对甲苯的吸附性能研究

系统地考察了改性13X沸石分子筛(M-13X)蜂窝转轮对甲苯废气的吸附性能,探讨了运行参数和进气参数对转轮吸附的影响规律.结果表明,M-13X分子筛具有良好的抗湿性,转速、再生风温度过高或过低均会降低系统去除率,合适的浓缩比应兼顾效率与能耗.对于进气浓度100 mg·m-3,进气流速2 m·s-1的甲苯废气,推荐运行参数为再生风温度180℃,转速2.8~5 r·h-1,浓缩比8~12,在该运行参数下去除效率均维持在90%以上.该研究为M-13X蜂窝转轮工业应用提供设计经验及运行参数,对于高浓度废气,应控制较低的进气流速,同时加快转速、提高脱附热量以满足去除效果.     

NaCl改性沸石对水中氨氮的吸附机制

通过颗粒强度测定、扫描电镜分析（SEM）、X射线能谱分析（EDS）和零电点测定（pHPZC）考察改性前后沸石表面特性的变化,考察pH值、沸石投加量、初始氨氮浓度以及温度对吸附过程的影响,并通过吸附等温式和吸附动力学对吸附机制进行描述.经过NaCl改性后的沸石的颗粒强度明显增大,表面更加粗糙,孔径增大,钠离子通过交换作用进入到沸石内部.pH值为7,沸石投加量为8g/L,温度为35℃时吸附效果最好,平衡吸附量（qe）与氨氮初始浓度呈正相关性.Langmuir等温线比Freundlich等温线更适合描述实验数据,最大饱和吸附量为13.210mg/g.吸附动力学符合准二级动力学模型.实验表明NaCl改性沸石能够有效去除水中的氨氮.     

A型沸石对含磷废水深度处理的研究

论文探讨A型沸石对废水中磷的吸附性能,影响A型沸石对磷吸附的主要因素有吸附温度、灰水比、吸附时间和pH值。通过单因素和正交试验确定在水样体积30mL,A型沸石投加量3g,吸附时间为40~50min,吸附温度25oC,pH值4~5范围内,初始磷浓度小于20 mg/L,A型沸石对磷都有很好的吸附效果。TP去除率达99%以上,对磷的吸附容量约为0.44mg/g,适用于工业废水处理和生活污水的深度除磷。     

粉煤灰沸石吸附铜离子的试验研究

文章主要对粉煤灰沸石吸附水溶液中的铜离子进行了研究。通过试验考察了pH、温度、吸附时间、离子初始浓度等主要条件对吸附效率的影响。试验结果表明：NaA型沸石吸附铜离子的最佳pH 5;动力学研究表明,铜离子在100 min可以达到吸附平衡,而且更好地遵循二级动力学模型;热力学研究表明,45℃时吸附铜离子的效果最好,而且更好地遵循Langmuir等温式;随着离子初始浓度的增加,吸附量也相应增加。最佳条件下最大吸附量44.776 mg/g。     

13X分子筛去除水中重金属离子Cr~(3+)的研究

以13X分子筛作为吸附剂,研究废水中Cr3+的去除。考察了水的pH、Cr3+浓度和吸附时间的影响,通过对不同价态金属离子的吸附探讨了除Cr3+机理,比较了13X分子筛和732型阳离子交换树脂对Cr3+的去除效果。结果表明:水的pH等条件对Cr3+的去除有较大影响;13X分子筛对Cr3+的吸附机理以离子交换吸附为主,符合Langmuir等温吸附模型和Lagergren二级动力学方程,吸附速率控制步骤为颗粒内扩散;达到吸附平衡后,分子筛对Cr3+的去除率为92.2%;分子筛吸附Cr3+的二级反应速率常数为0.004 5 g/(mg.min),比阳离子交换树脂的相应值大。     

给水厂残泥免烧陶粒对Pb与Cd的吸附特征

针对高效低廉的吸附材料——WTR（water treatment residuals,给水厂残泥）因颗粒细小在水处理工艺中难以应用的问题,利用免烧法制备出WTR陶粒,研究其对Pb和Cd的吸附特征.批量吸附试验结果表明,准二级动力学模型和Langmuir等温吸附模型能较好地描述WTR免烧陶粒对Pb和Cd的吸附动力学（R2>0.995 8）与等温吸附过程（R2>0.994 8）.在溶液pH为5、恒温25℃、振荡24 h下,Langmuir等温吸附模型计算得到的WTR免烧陶粒对Pb和Cd的最大吸附容量分别为13.97和18.60 mg/g.单因素条件试验结果表明,WTR免烧陶粒对Pb和Cd的吸附量均随溶液初始pH的升高而增加,当pH由3升至9时,WTR免烧陶粒对Pb和Cd的吸附量分别增加了1.44和0.95倍;离子强度的增加不利于WTR免烧陶粒对Pb和Cd的吸附.批量等温解吸试验结果表明,在pH为4~8的溶液中,Pb和Cd较难从WTR免烧陶粒中解吸出来,解吸率均在3.5%以内;当溶液pH为3时,Pb和Cd的解吸率分别高达65.88%和45.01%.BCR分级提取结果表明,Pb和Cd均主要以酸提取态形式（占比在68.18%以上）存在于WTR免烧陶粒中;同时,随着初始吸附量的增加,酸提取态比例显著减少,而还原态和残渣态比例显著增加.研究显示,WTR免烧陶粒对Pb和Cd具有较强的吸附能力,可作为一种高效的重金属吸附材料应用于水处理工艺中.      

钢渣粉末吸附去除废水中磷的研究

选用平均粒径为0.060mm的钢渣粉末作为除磷吸附剂,分析了其组成和结构,研究了溶液pH和温度对钢渣粉末吸附效果的影响,结合吸附动力学过程和吸附等温模型及钢渣粉末组成成分变化探讨其吸附除磷的机理。结果表明:钢渣粉末吸附除磷的动力学过程符合准二级动力学模型。Langmuir等温吸附模型能较好地模拟钢渣对磷的等温吸附过程,理论饱和吸附量为94.61mg/g。钢渣粉末对磷的吸附量远大于钢渣颗粒,且受pH和温度影响较大。随着溶液pH的增大,钢渣粉末对磷的吸附量逐渐减小,当pH=5时,钢渣粉末对磷的吸附量最大。温度升高,有利于钢渣粉末对磷的吸附。X射线荧光光谱(XRF)和傅里叶红外分析(FITR)结果表明,钢渣粉末中CaO、Fe2O3和SiO2在吸附除磷中均发挥了重要作用。     

Evaluation of zeolites synthesized from fly ash as potential adsorbents for wastewater containing heavy metals

Both pure-form zeolites (zeolites A and X) were synthesized by applying a two-stage method during hydrothermal treatment of fly ash prepared initial gel. The difference of adsorption capacity of both fly ash-synthesized zeolits was assessed under the same adsorption conditions. Copper and zinc were chosen as target heavy metal ions. It was found that adsorption capacity of zeolite A showed much higher value than that of zeolite X. Thus, attention was focused on investigating the removal performance of heavy metal ions in aqueous solution on the synthetic pure-form zeolite A from fly ash, zeolite HS (hydroxyl-solidate) prepared from the residual fly ash (after synthesis of pure-form zeolite A from fly ash) and a commercial grade zeolite A. Batch method was employed to study the influential parameters such as initial pH value, adsorbents dosage and adsorption temperature on the adsorption process. The equilibrium data were well fitted by the Langmuir model and showed the affinity: Cu2+ > Zn2+ (adsorbent FA-ZA). The removal mechanism of metal ions followed adsorption and ion exchange processes. Attempts were also made to recover heavy metal ions and regenerate adsorbents (adsorbent FA-ZA).     

阴离子交换树脂对水杨酸的吸附与解吸性能

研究了714阴离子交换树脂对水中水杨酸的吸附与解吸性能,探讨了吸附的热力学和动力学特性.结果表明,树脂在pH=4～12时,吸附能力最好.等温吸附遵循Freundlich和Langmuir吸附平衡模型,为优惠吸附过程.在298～318K条件下,水杨酸吸附量为100～120mg/g的吸附焓变为-23.4-21.6kJ/mo...     

松树锯末对Cu~(2+)的吸附研究

文章采用松树锯末以及柠檬酸钠改性锯末为吸附材料,以Cu2+为吸附对象,研究了溶液的pH值,吸附时间,锯末投加量及模拟废水初始浓度对吸附效果的影响,研究结果表明在最佳条件下改性前后的锯末对Cu2+的最大吸附量分别为3.31 mg/g、5.75 mg/g,最大除去率分别达到84.3%和92.3%。同时对改性前后的锯末做了吸附等温线拟合及动力学研究,结果表明吸附等温线均能很好的符合Langmuir或Freundlich吸附模式,吸附过程符合拟二级动力学方程。     

Biosorption of clofibric acid and carbamazepine in aqueous solution by agricultural waste rice straw

Due to their widespread use, clofibric acid （CA） and carbamazepine （CBZ） have been frequently detected simultaneously at relatively high concentrations in aquatic environments. In this study, agricultural waste rice straw was employed as a potentially low-cost, effective and easy-to-operate biosorbent （RSB） to remove CA and CBZ. The adsorption of both pharmaceuticals followed pseudo second-order kinetics, and intraparticle diffusion was an important rate-limiting step. The adsorption isotherms of both drugs were fit well with Freundlich model. The adsorption of CA onto RSB was exothermic and was more likely to be dominated by physical processes, while the adsorption of CBZ was endothermic. Solution pH was determined to be the most important factor for CA adsorption, such that the adsorption capacity of CA onto RSB increased with the decline of solution pH. In the lower range of solution pH below 3. l, the CA removal efficiency was enhanced with the increase of biosorbent dosage. The CBZ removal efficiency was enhanced with the increase of RSB dosage without pH control. The maximum adsorption capacities were 126.3 mg/g for CA and 40.0 mg/g for CBZ.     

MnO2/TiO2改性沸石去除矿井水中Fe2+和Mn2+的试验研究

针对矿井水中Fe2+、Mn2+浓度超标及处理效果不稳定等问题,通过溶胶-凝胶法将纳米MnO₂和纳米TiO₂负载于天然斜发沸石表面制备出MnO₂/TiO₂改性沸石滤料,并分析了沸石改性前后的微观形貌和孔隙结构. 采用单因素动态吸附试验和Thomas模型拟合探究了MnO₂/TiO₂改性沸石对模拟矿井水水样中Fe2+、Mn2+的去除效果及机理,并考察水流速度、滤层厚度、溶液pH及硬度对去除效果的影响. 结果表明:较天然沸石而言,MnO₂/TiO₂改性沸石的比表面积、孔径、孔体积和阳离子交换量明显增大. 当水流速度为7 m/h、进水pH为9.5、水质硬度为350 mg/L、滤层厚度为110 cm时,改性沸石对Fe2+、Mn2+的最大吸附量分别为44.810、6.549 mg/g,且Thomas模型能较好地拟合改性沸石对Fe2+、Mn2+的吸附动力学特征. 反冲洗试验结果表明,反冲洗强度为13 L/(m2·s),反冲洗时间大于7 min时,改性沸石的再生效果良好,可重复使用. 研究显示,本文制备的MnO₂/TiO₂改性沸石吸附滤料可为同步去除矿井水中Fe2+、Mn2+污染提供一种解决办法.      

Removal of humic acid from aqueous solution by cetylpyridinium bromide modified zeolite

Natural zeolite was modified by loading cetylpyridinium bromide (CPB) to create more e cient sites for humic acid (HA) adsorption. The natural and CPB modified zeolites were characterized with X-ray di raction, field emission scanning electron microscopy, Fourier transform infrared spectroscopy and elemental analysis. The e ects of various experimental parameters such as contact time, initial HA concentration, solution pH and coexistent Ca2+, upon HA adsorption onto CPB modified zeolites were evaluated. The results showed that natural zeolite had negligible a nity for HA in aqueous solutions, but CPB modified zeolites exhibited high adsorption e ciency for HA. A higher CPB loading on natural zeolites exhibited a larger HA adsorption capacity. Acidic pH and coexistent Ca2+ were proved to be favorable for HA adsorption onto CPB modified zeolite. The kinetic process was well described by pseudo second-order model. The experimental isotherm data fitted well to Langmuir and Sips models. The maximum monolayer adsorption capacity of CPB modified zeolite with surfactant bilayer coverage was found to be 92.0 mg/g.