Mo-N-TiO_2光催化剂的制备、表征及其活性提高机制

以钼酸铵和氨水分别为钼源和氮源,采用溶胶-凝胶法制备了Mo-N-TiO2光催化剂,并对其进行了XRD、XPS和UV-visDRS表征。XRD结果表明,Mo、N共掺杂有效抑制了TiO2晶粒的生长,提高了TiO2由锐钛矿向金红石相的转变温度。UV-vis表明,Mo-N-TiO2光催化剂可见光吸收能力增强,吸收带边明显＂红移＂,且钼酸铵添加量（相对TiO2）为0.5%的样品＂红移＂程度最大,最大吸收带边为550 nm。XPS分析结果表明,Mo取代了TiO2晶格中的部分Ti4＋,以Mo6＋形式存在的,而N以Ti—N及N—Ti—O形式存在。以罗丹明B为模型污染物,重点考察了钼酸铵添加量与焙烧温度对Mo-N-TiO2光催剂性能的影响。结果表明,400℃焙烧下、钼酸铵添加量为0.5%的样品催化活性最好。模拟太阳光下光照120min对罗丹明B的降解率达到96.8%,是纯TiO2的2.42倍。     

溴掺杂TiO_2光催化剂的制备与性能研究

以KBr和Ti(SO4)2为原料,通过水热法制备了高催化活性的溴掺杂纳米TiO2(Br-TiO2)光催化剂,利用XRD、XPS、TEM、BET和UV-Vis DRS等测试手段对其进行了表征。通过苯酚降解实验评价了Br-TiO2的光催化活性。结果表明,700℃焙烧、溴与钛的摩尔比为0.35∶1时,Br-TiO2具有最佳光催化活性。该催化剂为晶体发育完整的锐钛矿相TiO2,粒径平均大小为50 nm,比表面积为16.81 m2/g,在紫外区的吸收得到加强,光催化能力优于Degussa P-25。确定了降解苯酚的最佳条件:催化剂投加量为0.5 g/L,苯酚初始浓度为10 mg/L,pH值为6.0。     

溴掺杂TiO2光催化剂的制备与性能研究

以KBr和Ti（SO4）2为原料,通过水热法制备了高催化活性的溴掺杂纳米TiO2（Br-TiO2）光催化剂,利用XRD、XPS、TEM、BET和UV-Vis DRS等测试手段对其进行了表征。通过苯酚降解实验评价了Br-TiO2的光催化活性。结果表明,700℃焙烧、溴与钛的摩尔比为0.35∶1时,Br-TiO2具有最佳光催化活性。该催化剂为晶体发育完整的锐钛矿相TiO2,粒径平均大小为50 nm,比表面积为16.81 m2/g,在紫外区的吸收得到加强,光催化能力优于Degussa P-25。确定了降解苯酚的最佳条件：催化剂投加量为0.5 g/L,苯酚初始浓度为10 mg/L,pH值为6.0。     

CF-TiO2的制备及其在模拟太阳光下的光催化性能

以十六烷基三甲基溴化铵(CTAB)和氟化钠分别为碳源和氟源,采用溶胶-凝胶法制备了CF-TiO2光催化剂,并对其进行了SEM、XRD、N2吸附、XPS、UV-visDRS和PL表征。研究了CF-TiO2在模拟太阳光下光催化降解亚甲基蓝溶液的活性,并讨论了氟掺杂量以及CTAB加入量对催化性能的影响。结果表明,CF-TiO2为锐钛矿型,孔结构丰富、比表面积大,氟碳共掺后使TiO2光催化剂的禁带宽度变窄为2.40 eV,在可见光区吸收增强,有效提高TiO2在模拟太阳光下的光催化活性,而且当n(F/Ti)(氟钛摩尔比)为0.1,加入碳源CTAB量为2 g时,其光催化活性最好。     

具有可见光活性的氮掺杂TiO_2光催化剂的制备及光催化性能

采用浓氨水处理Ti(SO4)2溶液,然后经过滤、干燥、煅烧制备了一种氮掺杂TiO2光催化剂TiO2-XNX,其最佳煅烧温度为400℃。对该光催化剂的XRD谱图进行分析,结果表明,TiO2-XNX的晶型为锐钛矿相。紫外—可见吸收光谱表明,该光催化剂在可见光区具有明显的吸收。甲基橙溶液的降解实验结果表明,制备的TiO2-XNX光催化剂具有可见光(波长λ400nm)活性。     

掺硫改性TiO2对活性艳红X-3B的光催化降解性能研究

以硫脲为硫的源物质,以钛酸四丁酯为TiO2的前驱体,采用溶胶-凝胶法制备了掺硫改性TiO2光催化剂.以活性艳红X-3B为目标污染物,研究了该催化剂的光催化降解性能,对硫掺杂量、催化剂焙烧温度、溶液pH值以及催化剂添加量等影响因素进行了研究,并采用XRD分析手法对光催化剂进行表征.结果表明,经掺硫改性后的TiO2的催化活性有了很大提高,且硫的掺杂有一个最佳值,即Ti:S的摩尔比为1:1.经掺硫改性的TiO2在可见光区具备一定的催化活性,180 min内对活性艳红X-3B的去除率可达35.1%,且在紫外光区的催化活性优于纯TiO2.     

B,N和Ce共掺杂TiO2催化剂光催化活性研究

采用溶胶-凝胶法制备出B,N和Ce共掺杂TiO2光催化剂,并用XRD、SEM等表征了其结构特征。以酸性大红染料溶液的光催化降解为探针反应,考察了制备条件对共掺杂TiO2催化剂活性的影响。结果表明,在400℃,当B,N和Ce的原子比为1∶2∶0.1,焙烧3 h时,光催化剂活性最大,大红染料的降解率达到98%。     

B,N和Ce共掺杂TiO_2催化剂光催化活性研究

采用溶胶-凝胶法制备出B,N和Ce共掺杂TiO2光催化剂,并用XRD、SEM等表征了其结构特征。以酸性大红染料溶液的光催化降解为探针反应,考察了制备条件对共掺杂TiO2催化剂活性的影响。结果表明,在400℃,当B,N和Ce的原子比为1∶2∶0.1,焙烧3 h时,光催化剂活性最大,大红染料的降解率达到98%。     

Pd/N共掺杂TiO_2的制备及其光催化降解苯酚的研究

将纳米管钛酸浸入含尿素和金属(Pd)硝酸盐的乙醇溶液中,乙醇超声挥发后所得样品先在空气气氛、600℃下煅烧,再在H2气氛、400℃下热还原制备得到Pd/N共掺杂TiO2光催化剂(Pd/N-TiO2)。利用光电子能谱(XPS)仪研究了催化剂表面N、Pd元素的化学态。结果表明,N元素以Ti—O—N形式存在,Pd元素以单质金属状态存在。考察了Pd/N-TiO2的紫外光光催化降解苯酚的活性,与单纯TiO2光催化剂和N掺杂TiO2光催化剂相比,Pd/N-TiO2活性明显提高。研究了催化剂用量、苯酚初始浓度和pH、O2流量以及外加双氧水等条件对紫外光光催化降解苯酚的活性的影响,得到光催化降解苯酚的最佳工艺条件:苯酚初始质量浓度为120mg/L,催化剂用量为0.10g/L,苯酚溶液初始pH为8,O2流量为80mL/min,加入适量双氧水。     

铂铈共掺杂纳米TiO2的制备、表征及光催化性能

以钛酸四丁酯为前驱体,过氧化氢为氧化剂,采用简单易行的低温氧化法制备出晶粒尺寸较小（平均尺寸25nm）的二氧化钛纳米粒子。通过贵金属Pt掺杂TiO2（Pt-TiO2）、稀土元素Ce掺杂TiO2（Ce-TiO2）和Pt、Ce共掺杂TiO2（Pt／Ce-TiO2）的掺杂的方法对二氧化钛进行改性。通过XRD,XPS,TEM,紫外漫反射等表征手段对制备的样品进行表征。通过可见光下降解罗丹明B来测试其光催化活性。实验结果表明,由ce掺杂的TiO2光催化剂对有机污染物的最大降解能力略大于Pt掺杂的TiO2,2种元素进行共同掺杂时对应的TiO2光催化剂降解能力最大。     

复合型CoO／TiO2光催化剂降解亚甲基蓝动力学研究

以钛酸四丁酯为前驱体,采用溶胶凝胶法,制备了CoO掺杂的TiO2光催化剂。利用X射线衍射（XRD）、扫描电镜（SEM）、透射电镜（TEM）、紫外可见漫反射（UV—visDRS）对催化剂进行了分析、表征。以中压汞灯为光源,研究了亚甲基蓝（MB）在CoO／TiO2微粒水悬浮液中的降解动力学。结果表明：所制备的催化剂活性组分主要是锐钛矿型的二氧化钛和CoO固溶体,粒径为25～30nm,分布均匀。亚甲基蓝的光催化降解动力学满足一级动力学,在一定的浓度范围内,反应速率常数随初始浓度增大而减少,适当的掺钴量可以有效地提高TiO2光催化活性,其最佳掺杂量重量百分比为0．25％。     

Preparation,characterization, and photocatalytic activity evaluation of Fe–N-codoped TiO2/fly ash cenospheres floating photocatalyst

Nitrogen-doped titanium dioxide (TiO₂) and Fe–N-codoped TiO₂ layers on fly ash cenospheres (FAC) as floating photocatalyst were successfully prepared through sol–gel method. Photocatalysts were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy (XPS), ultraviolet (UV)–Vis diffuse reflectance spectroscopy (DRS), and nitrogen adsorption analyses for Brunauer–Emmett–Teller (BET) specific surface area. Photocatalytic efficiency of the prepared catalyst was evaluated through using the decomposition of Rhodamine B (RhB) as a model compound under visible light irradiation. Photocatalytic activity and kinetics of catalyst under visible light were detected in details from different Fe/Ti mole ratios by detecting photodegradation of RhB. Experimental results show that when the calcination temperature was 550 °C, the dosage of FAC was 3.0 g, and the mole ratio of Fe/Ti was 0.71 %; the synthesized Fe–N-TiO₂/FAC photocatalyst presented as anatase phase and that N and Fe ions were doped into TiO₂ lattice. The material’s specific surface area was 34.027 m²/g, and UV–Vis diffuse reflectance spectroscopy shows that the edge of the photon absorption has been red shifted up to 400–500 nm. Fe–N-codoped titanium dioxide on FAC had excellent photocatalytic activity during the process of photodegradation of RhB under visible light irradiation.

     

Enhanced photocatalytic degradation of VOCs using Ln3+-TiO2 catalysts for indoor air purification

Two types of lanthanide ion-doped titanium dioxide (Ln3+-TiO2) catalysts including La3+-TiO2 and Nd3+-TiO2 were prepared by a sol-gel method. The effects of the lanthanide ion doping on the crystal structure, surface area, adsorption properties, pore size distribution, and surface chemical state of the catalysts were investigated by means of XRD, BET, and XPS. As results, the crystal size decreased significantly, while the specific surface area, t-plot total surface area, micropore volume, and the total pore volume increased owing to the lanthanide ion doping. The nitrogen adsorption-desorption isotherms of the catalysts showed that the N2 adsorption ability of the Ln3+-TiO2 catalysts was better than the TiO2 catalyst. Among them, the 0.7% Ln3+-TiO2 catalysts demonstrated the highest adsorption ability. The photocatalytic activity of the catalysts was investigated in the experiments of the photocatalytic degradation of benzene, toluene, ethylbenzene and o-xylene (BTEX) in a gaseous phase. The photocatalytic efficiency of the TiO2 catalysts with the lanthanide ion doping was remarkably enhanced by BTEX removal. The 1.2% Ln3+-TiO2 catalysts achieved the highest photocatalytic activity. The enhanced photodegradation of BTEX is possibly due to the improved adsorption ability and the enhanced electron-hole pairs separation due to the presence of Ti3+ on the surface of Ln3+-TiO2 catalysts and the electron transfer between the conduction band/defect level and lanthanide crystal field state.     

TiO2/Ti转盘液膜反应器光电催化处理罗丹明B

采用溶胶-凝胶法制备了TiO2/Ti电极,X射线衍射(XRD)分析表明,TiO2主要为锐钛矿,晶粒尺寸约为46 nm.以TiO2/Ti电极作阳极,Cu电极作阴极,组装成转盘液膜反应器,考察了其光电催化处理染料罗丹明B(RhB)的影响因素(转盘转速、偏压、溶液初始pH、RhB初始浓度和电解质浓度).得到最佳处理条件为:转盘转速90 r/min,偏压0.4V,溶液初始pH2.5,电解质(硫酸钠)质量浓度0.5 g/L.在最佳处理条件下,处理20 mg/L RhB染料废水90 min的脱色率和总有机碳(TOC)去除率分别达到97.2％和72.7％.结果表明,由于同时强化了激发光源的利用率和溶液的传质效率,TiO2/Ti转盘液膜反应器可高效光电催化处理染料废水.     

Photocatalytic degradation of isoproturon herbicide over TiO2/Al-MCM-41 composite systems using solar light

The present investigation covers immobilization of TiO2 using a simple solid state dispersion technique over mesoporous Al-MCM-41 support for the treatment of isoproturon herbicide. Catalysts are characterized by XRD, X-ray photo electron spectroscopy (XPS), surface area, UV-Vis diffused reflectance spectra (DRS), SEM and TEM. A detailed photocatalytic degradation study of isoproturon under solar light in aqueous suspensions is reported. The 10 wt% TiO2/Al-MCM-41 composite system found to be optimum with high degradation activity. The reaction follows pseudo-first order kinetics. The parameters like TiO2 loading over Al-MCM-41, amount of catalyst, concentration of substrate, pH effect, durability of the catalyst, activity comparison of TiO2 and Al-MCM-41 supported system are studied. The mineralization of isoproturon is monitored by TOC. Based on the degradation products detected through LC-MS, a plausible degradation mechanism is proposed. The data indicates that TiO2/Al-MCM-41 composite system is an effective photocatalyst for treatment of isoproturon in contaminated water.     

碘掺杂Ti02可见光光催化性能研究

在低于100℃温度条件下,采用溶胶一凝胶法以钛酸正丁酯为钛源,碘酸钾为碘源,制备了I掺杂纳米TiO2催化剂（I-TiO2）,运用x-射线衍射（XRD）、透射电镜（TEM）及x-射线光电子能谱（XPS）等对催化剂进行表征,结果表明,TiO2及I-TiO2催化剂均为锐钛矿,I吸附并包裹在TiO2表面或以间隙进入的形式存在,并未进入TiO2晶格。通过在可见光照射下（A〉420nm）以罗丹明B（RhodamineB,RhB）的光催化降解为探针反应研究了在不同条件下制备催化剂的催化性能,结果表明,掺杂比为n1：n^ti=0．05：l,焙烧温度为400℃,降解介质条件pH=7时,l-TiO2光催化活性明显优于未掺杂的TiO2。光催化降解过程通过红外光谱（IR）,总有机碳（TOC）跟踪测定,比较了TiO2掺杂前后降解RhB和对氯苯酚（4-CP）的光催化特性差异;同时采用苯甲酸荧光光度法跟踪测定体系中的氧化物种,表明在可见光下,I-TiO2光催化体系中产生·OH高活性氧化物种从而氧化降解目标化合物。     

纳米片自组装原位N掺杂(BiO)2CO3分级微球的可控合成及其优异可见光催化性能

以二氰二胺和柠檬酸铋为原料,采用一步水热法合成原位N掺杂(BiO)2CO3纳米片自组装分等级微球结构。采用XRD、SEM、XPS、FT-IR、UV-Vis DRS和PL等对合成的材料进行表征,结果表明,不同二氰二胺加入量会对(BiO)2CO3的形貌结构、禁带宽度以及电子-空穴复合率产生显著影响。二氰二胺在水热过程水解柠檬酸铋,同时N原子原位掺杂进入(BiO)2CO3晶格。N掺杂使(BiO)2CO3的光响应范围大幅拓展至可见光,通过价带XPS获得了掺杂N元素减小(BiO)2CO3禁带宽度的证据。在可见光照射下,原位N掺杂(BiO)2CO3分等级微球结构表现出对液相罗丹明B和气相NO优异的可见光催化降解活性,高于N掺杂TiO2和C掺杂TiO2。研究结果对拓展N掺杂作用向非TiO2体系的转变具有重要意义。     

V/Ce共掺杂TiO2光催化降解甲醛的实验研究

采用溶胶-凝胶法制备了不掺杂、V掺杂、Ce掺杂、V/Ce共掺杂纳米TiO2光催化剂,并将其分别负载于瓷砖上,利用X射线衍射分析（XRD）和扫描电镜分析（SEM）技术对薄膜样品的结构和形貌进行了表征。通过对甲醛的降解实验评价光催化剂的光催化活性。实验结果表明,光催化剂的负载量、共掺杂离子的掺杂量、掺杂配比、煅烧温度影响纳米TiO2的光催化活性。V/Ce共掺杂TiO2光催化剂产生了协同效应,其光催化活性优于纯TiO2和单掺杂TiO2样品。     

V/Ce共掺杂TiO2光催化降解甲醛的实验研究

采用溶胶凝胶法制备了不掺杂、V 掺杂、Ce掺杂、V/Ce共掺杂纳米TiO₂光催化剂,并将其分别负载于瓷砖上,利用X射线衍射分析（XRD）和扫描电镜分析（SEM）技术对薄膜样品的结构和形貌进行了表征。通过对甲醛的降解实验评价光催化剂的光催化活性。实验结果表明,光催化剂的负载量、共掺杂离子的掺杂量、掺杂配比、煅烧温度影响纳米TiO₂的光催化活性。V/Ce共掺杂TiO₂光催化剂产生了协同效应,其光催化活性优于纯TiO₂和单掺杂TiO₂样品。