嗜水气单胞菌强化老化纳米零价铁去除水中Cr(VI)

基于老化对纳米零价铁（NZVI）去除水中Cr（VI）的不利影响,本研究考察了接种嗜水气单胞菌（Aeromonas hydrophila）强化老化NZVI对水中Cr（VI）的去除,并分析了溶解氧、温度、pH、Cr（VI）初始浓度对其去除Cr（VI）的影响,同时利用扫描电镜（SEM）、X射线光电子能谱（XPS）等分析了反应前后材料的形貌特征及Cr的价态变化.结果表明,接种嗜水气单胞菌能显著提高无氧条件下老化NZVI对Cr（VI）的去除效果,且在酸性条件和30~40 ℃条件下去除效果较好,可能是因为该条件下更有利于老化NZVI的腐蚀和微生物的生长,此外,Cr（VI）去除效率随Cr（VI）初始浓度升高而降低.在pH=6,温度为30 ℃,老化nZVI投加量为0.1 g·L^-1,Cr（VI）初始浓度为50 mg·L^-1的条件下反应24 h后,Cr（VI）的去除率可达到100%.XPS分析表明,反应后NZVI表面沉积的Cr主要以Cr（III）的形式存在,可能为Cr（OH）₃沉淀或Fe_xCr_1-x（OH）₃共沉淀物.动力学研究发现,Cr（VI）去除过程符合准二级动力学,去除机制为Cr（VI）的吸附、还原与共沉淀,其中以还原作用为主.     

有机凹凸棒石负载纳米零价铁去除水中六价铬

以黏土为载体负载纳米零价铁（nZVI,nanoscale zero-valent iron）可改善零价铁颗粒的团聚行为,增强其反应性.在负载过程中铁和黏土用量比例不同,对nZVI颗粒团聚和反应性的影响也不同.以有机凹凸棒石（CTMAB/A）为载体,采用液相还原法在1：3和1：5两种铁土质量比条件下制备负载型纳米零价铁复合材料CTMAB/A-nZVI-3和CTMAB/A-nZVI-5.利用X射线衍射仪（XRD）和扫描电子显微镜（SEM）表征了两种负载样品和不添加黏土载体时nZVI的分散差异,并通过X射线光电子能谱仪（XPS）分析样品与Cr（VI）反应后的产物分布.结果表明：降低负载反应时的铁土比能明显改善nZVI粒子的团聚现象、减小nZVI平均粒径、提高小粒径颗粒占比、增强其反应活性.小于10nm的nZVI颗粒在CTMAB/A-nZVI-3和CTMAB/A-nZVI-5负载nZVI总数中占比分别为3.60%和7.60%,在不负载的nZVI样品中占比为0.铁的投加量同为0.75g/L时,CTMAB/A-nZVI-5中铁对Cr（VI）去除率为86.20%,CTMAB/A-nZVI-3中为78.00%.     

纳米零价铁对水中芴的去除研究

研究了实验室自制的纳米零价铁在不同投加量、初始浓度、pH及温度条件下,对芴溶液的吸附效果、吸附等温线及吸附动力学.结果表明,随着纳米铁投加量的增加,芴的去除率升高;增加芴的初始浓度,去除率则相应下降,同时平衡吸附量增加.另一方面,纳米铁对芴的吸附能力随pH的升高而下降;温度为15~35℃时,芴的平衡吸附量随温度的升高而增加,但变化不大.纳米铁对芴的吸附等温线符合Langmuir和Freundlich方程;纳米铁对芴的吸附过程很好地符合准二级速率方程,吸附速率随芴初始浓度的增大而减小,平衡吸附量随芴初始浓度的增大而增大.除上述结果以外,本文还对此反应体系的吸附机理进行了初步探讨.     

零价纳米铁吸附去除水中六价铬的研究

利用液相还原法制备的零价纳米铁(nZVI)进行了去除水中Cr(Ⅵ)的实验研究.结果表明,nZVI对Cr的去除效果明显优于还原铁粉和粉末活性碳;pH值越小、初始Cr浓度越低、nZVI放置时间越短及投加量越大均有利于水中Cr(Ⅵ)的去除,最佳去除率近100%;反应动力学拟合结果表明,nZVI去除六价铬符合准二级动力学模型;反应后nZVI颗粒的扫描电镜及电子能谱结果显示Cr占12.02%(wt),结合对反应溶液中Cr(Ⅵ)和Cr(Ⅲ)分析,说明吸附、还原与共沉淀可能是nZVI去除水中六价铬的主要机理.     

硫化纳米零价铁(S-nZVI)对水体中镉的去除研究

由于矿山开采、工业废水排放及农业施肥等人类活动,使得我国镉污染日益突出.本研究采用液相还原法制备硫化纳米零价铁(S-nZVI),研究其对Cd的去除行为.考察了不同硫化剂、合成方法、S/Fe比(物质的量比)及pH对Cd去除的影响,并采用扫描电子显微镜(SEM)、拉曼光谱(Raman)、X-射线衍射(XRD)等技术对反应前后的材料进行表征,结合批实验结果探讨Cd的去除机理.结果表明,采用一步法以硫化钠(Na_2S)为硫化剂合成的S-nZVI对Cd的去除效率远高于其它方法,去除容量可达385.6 mg·g~(-1).反应120 min后,S-nZVI对Cd的去除率随S/Fe比的增加而升高,S-nZVI反应体系受pH影响较小.材料表征结果显示,S-nZVI颗粒由Fe~0、Fe_3O_4、FeS组成,其中,FeS的含量随S/Fe比的升高而增加.S-nZVI对Cd的去除机理主要是Cd将FeS中的Fe置换,与S结合形成稳定的CdS.     

氨基改性生物炭负载纳米零价铁去除水中Cr(VI)

以聚乙烯亚胺（PEI）为功能单体,玉米秸秆生物炭为载体,制备了氨基改性生物炭负载型纳米零价铁（nZVI@PEI-HBC）,并利用扫描电镜（SEM）、红外光谱（FTIR）和X射线光电子能谱（XPS）等手段对材料进行了表征,分析了溶液pH、温度、材料投加量等因素对其去除Cr（VI）的影响及其去除机理.结果表明：在投加量为0.5 g·L^-1,温度为20℃,pH值为5,Cr（VI）初始浓度为20 mg·L^-1条件下,各材料对Cr（VI）的去除率大小为nZVI@PEI-HBC > nZVI > PEI-HBC > HBC.SEM显示nZVI颗粒较均匀地分散在生物炭表面,FTIR分析表明PEI改性后材料表面增加了氨基等重金属配位基团,这可能是nZVI@PEI-HBC去除Cr（VI）效果更好的原因.影响因素研究表明,材料具有较好稳定性,老化28 d后其Cr（VI）去除性能变化不大;酸性环境、升温、增大材料投加量均有利于nZVI@PEI-HBC对Cr（VI）的去除.机理研究发现,水中溶解氧加速了nZVI的腐蚀和Fe（II）的释放,促进Cr（VI）还原为Cr（III）,然后通过共沉淀作用和氨基等基团的吸附作用被去除.     

沸石负载纳米零价铁去除水中Sb(Ⅲ)和Sb(Ⅴ)的研究

锑矿开采和含锑化合物的应用在一定程度上会造成环境锑污染的加重,对人体健康和生态系统带来风险,为缓解这一现象,采用液相还原负载的方式制备沸石负载纳米零价铁(Z-ZVI)复合材料,探究其对Sb(Ⅲ)和Sb(Ⅴ)的去除效果;采用扫描电子显微镜(SEM)、X射线衍射(XRD)和X射线光电子能谱(XPS)对反应前后复合材料进行表征,并探究不同材料配比、溶液初始pH及无机阴离子对Sb(Ⅲ)和Sb(Ⅴ)吸附效率的影响.结果表明：(1)沸石负载后的纳米零价铁(Z-ZVI)具有较高的比表面积(54.54 m²/g)和反应活性,能够有效吸附、还原高价锑.(2)在pH=7、1.0 g/L Z-ZVI的条件下,反应4 h对20 mg/L Sb(Ⅲ)和Sb(Ⅴ)的吸附率分别达到88%和62%,吸附过程符合准二级动力学方程和Freundlich等温吸附模型.(3)Sb(Ⅲ)的去除率受pH变化的影响不大,但Sb(Ⅴ)的去除率随初始pH的升高而下降,溶液反应终点pH相比初始pH均有所上升.(4)XRD和XPS表征发现,Sb的去除过程中同时存在吸附和还原作用,Fe⁰氧化过程中...     

甘蔗渣负载纳米零价铁吸附剂去除水中Cr(Ⅵ)的研究

以改性甘蔗渣做载体,采用液相还原法制备负载型纳米零价铁吸附剂,研究了原甘蔗渣、改性甘蔗渣、纳米零价铁及纳米零价铁/改性甘蔗渣4种物质对于水中Cr(Ⅵ)的吸附特性,探讨了反应时间、溶液pH值、固液比、Cr(Ⅵ)初始浓度等因素对于Cr(Ⅵ)吸附效果的影响。实验结果表明:4种吸收剂中,纳米零价铁/甘蔗渣的吸附能力最好,在pH=4,固液比=0.5 g/L,Cr(Ⅵ)初始浓度小于25 mg/L时,可全部去除Cr(Ⅵ)。并对甘蔗渣基纳米零价铁和Cr(Ⅵ)的反应机理进行了初探。     

零价纳米铁处理水中Cr(Ⅵ)的实验研究

采用NaBH4还原Fe3+制备纳米级零价铁(NZVI).运用X射线衍射(XRD)、扫描电镜(SEM)对样品进行表征.以Cr(Ⅵ)为研究对象,批实验考察了初始浓度、纳米铁投加量、温度对去除效果的影响,研究NZVI对Cr(Ⅵ)离子的吸附动力学.结果表明,NZVI加入量0.15 gL,水体中20 mg/L的Cr(Ⅵ)的去除率...     

生物炭负载硫化改性纳米零价铁去除水中的Cr(Ⅵ)

为研发治理地下水Cr(Ⅵ)污染的可行除铬材料,以碳热法制得生物炭负载纳米零价铁（BC-nZVI）,并通过对BC-nZVI硫化改性制备得到改性材料（M-BC-nZVI）,采用除铬容量、铬铁比（Cr/Fe）、反应活性分析M-BC-nZVI的除铬优势,通过模拟柱试验建立失效速率模型,从而推算M-BC-nZVI完全失效的除铬容量,最后与相关文献数据进行对比,分析M-BC-nZVI除Cr(Ⅵ)的应用可行性。结果表明：M-BC-nZVI材料的除铬容量、Cr/Fe、拟一级反应速率常数（k_obs）分别是BC-nZVI的1.86倍、1.95倍和3.00倍,因此相对于BC-nZVI来说M-BC-nZVI更具除铬优势;各模拟柱在运行过程中无明显堵塞情况,且随着进水浓度的升高,M-BC-nZVI的失效速率常数变大。当失效除铬速率为初始除铬速率的1.0%、进水Cr(Ⅵ)浓度为5 mg/L时,除铬容量最高,可以达到12.70 mg/g;对比M-BC-nZVI与其他文献报道的铁基材料及铁基改性材料的Cr/Fe可知,M-BC-nZVI的Cr/Fe为其他文献的1.06~42.06倍,故从材料的除铬性能来看,M-BC-nZVI应用于可渗透反应墙处理地下水Cr(Ⅵ)污染可行。

     

纳米零价铁降解水中四氯化碳的试验研究

以四氯化碳为目标污染物,研究了不同因素对自制纳米零价铁降解水中四氯化碳的影响,并对反应产物及可能的反应路径进行了探讨.结果表明,自制纳米零价铁对四氯化碳有很好的降解效果.在pH=3和30℃的条件下,当初始四氯化碳浓度为2.0 mg·L~(-1),纳米零价铁浓度为1.0 g·L~(-1)时,去除率高达96.7%.纳米零价铁降解四氯化碳的酸碱适应范围较大(pH值3~9).随着温度升高和纳米零价铁投加量的增大,四氯化碳降解率显著提高.该反应符合一级动力学,且反应活化能较低,反应易于进行.     

双表面活性剂修饰下纳米零价铁对水中Cr(Ⅵ)污染去除研究

为解决纳米级零价铁（nZVI）在环境中易团聚、易氧化的问题,强化其去除水中Cr（VI）的能力,选择非离子型表面活性剂聚乙烯吡咯烷酮（PVP）和阴离子表面活性剂油酸钠（NaOA）同时对nZVI进行修饰.同时,通过对比不同pH值、材料干湿状态、初始浓度及共存离子条件下的反应效果,结合材料的XRD和XPS表征、动力学实验和25℃等温线的拟合进行机理分析.结果表明：酸性条件有利于Cr（VI）的去除;材料的干湿状态对去除效率影响较大;材料去除水中Cr（VI）可在3 h内达到反应平衡,去除效率在90%以上,实验条件下最大去除量为183.1 mg·g^-1,反应过程符合准二级动力学模型及Langmuir模型;反应过程中Cr（VI）大部分转化为Cr（Ⅲ）.     

Degradation of chlorinated phenols by nanoscale zero-valent iron

Chlorophenols (CPs), as important contaminants in groundwater, are toxic and difficult to biodegrade. Recently nanoscale zero-valent iron received a great deal of attention because of its excellent performance in treating recalcitrant compounds. In this study, nanoscale zero-valent iron particles were prepared using chemical reduction, and the reductive transformations of three kinds of chlorinated phenols (2-CP, 3-CP, and 4-CP) by nanoscale zero-valent iron under different conditions were investigated. The transformation process of the CPs was shown to be dechlorination first, then cleavage of the benzene ring. The removal efficiency of the CPs varied as follows: 2-CP > 3-CP > 4-CP. The reactivity of CPs was associated with their energy of lowest unoccupied molecular orbit (E _LUMO). With the increase in initial concentrations of CPs, removal efficiency decreased a little. But the quantities of CPs reduced increased evidently. Temperature had influence on not only the removal efficiency, but also the transformation pathway. At higher temperatures, dechlorination occurred prior to benzene ring cleavage. At lower temperatures, however, the oxidation product was formed more easily. __________ Translated from China Environmental Science, 2006, 26(6): 698–702 [译自: 中国环境科学]     

Performance of bimetallic nanoscale zero-valent iron particles for removal of oxytetracycline

In this study, bimetallic nanoscale zero-valent iron particles(nZVI), including copper/nanoscale zero-valent iron particles(Cu/nZVI) and nickel/nanoscale zero-valent iron particles(Ni/nZVI), were synthesized by one-step liquid-phase reduction and applied for oxytetracycline(OTC) removal. The effects of contact time and initial p H on the removal efficiency were studied. The as-prepared nanoscale particles were characterized by scanning electron microscopy(SEM), energy dispersive spectroscopy(EDS) and X-ray diffraction(XRD). Finally, the degradation mechanisms of OTC utilizing the as-prepared nanoparticles were investigated by using X-ray photoelectron spectroscopy(XPS) and mass spectrometry(MS). Cu/n ZVI presented remarkable ability for OTC degradation and removed71.44% of OTC(100 mg/L) in 4 hr, while only 62.34% and 31.05% of OTC was degraded by Ni/nZVI and nZVI respectively. XPS and MS analysis suggested that OTC was broken down to form small molecules by ·OH radicals generated from the corrosion of Fe0. Cu/nZVI and Ni/n ZVI have been proved to have potential as materials for application in OTC removal because of their significant degradation ability toward OTC.     

海藻酸钠/蒙脱石联合负载型纳米Fe0对Cu(II)的去除研究

由于蒙脱石负载型纳米Fe~0(Mt-n ZVI)在使用中易随水迁移,造成出水水质混浊和Fe~0流失.因此,本研究制备了海藻酸钠(SA)和蒙脱石(Mt)联合负载型纳米零价铁(SA/Mt-n ZVI),探究其对水中Cu(Ⅱ)的去除效果,并考察了Cu(Ⅱ)初始浓度、pH值对去除率的影响.结果表明:以2%(质量分数)SA和6%(质量分数)Mt-n ZVI条件制备的SA/Mt-n ZVI小球对Cu(Ⅱ)处理效果好,反应24 h后,SA/Mt-n ZVI小球对初始浓度为40 mg·L-1Cu(Ⅱ)的去除率达到92.11%,与游离的Mt-n ZVI颗粒相比,其活性并未降低;Cu(Ⅱ)的去除率随其初始浓度升高而降低;在pH为2~6之间,Cu(Ⅱ)去除率随pH升高而升高.SA/Mt-n ZVI小球可有效净化污水中的Cu(Ⅱ),将其重复使用3次后,对Cu(Ⅱ)的去除率仍维持在59.52%.     

改性生物炭负载nZVI对土壤Cr(VI)的修复差异研究

考察了生物炭(BC)、酸洗生物炭(HCl-BC)和纳米零价铁负载生物炭(n ZVI-HCl-BC)对土壤中Cr(VI)还原和总Cr形态转化的影响.结果表明,生物炭对Cr(VI)还原率随土壤含水率的升高而显著提高.在较高土壤含水率(70%)条件下,各生物炭对Cr(VI)的最高还原率排序为:HCl-BC(97.26%)n ZVI-HCl-BC(88.36%)BC(87.61%).在不同Cr(VI)污染水平下(150、300、600和900 mg·kg~(-1)),HCl-BC对土壤中Cr(VI)的还原率最高.随Cr(VI)含量升高,BC和HCl-BC对Cr(VI)的还原率呈降低趋势,而n ZVI-HCl-BC对Cr(VI)的还原率为先降低后升高.形态分析表明,生物炭在不同程度上增加了土壤中Cr残渣态的比例:n ZVI-HCl-BC(11.58%)HCl-BC(9.53%)BC(1.42%),表明生物炭对土壤Cr起到稳定作用.综上,改性生物炭显著促进Cr(VI)还原及总Cr向残渣态转化,表明其具有修复Cr污染土壤的潜力.     

Superior trichloroethylene removal from water by sulfide-modified nanoscale zero-valent iron/graphene aerogel composite

Sulfide-modified nanoscale zero-valent iron (S-nZVI) is a promising material for removal of organic pollutants from water, but S-nZVI nanoparticles (NPs) easily agglomerate and have poor contact with organic contaminants. Herein, we propose a new S-nZVI/graphene aerogel (S-nZVI/GA) composite which exhibits superior removal capability for trichloroethylene (TCE) from water. Three-dimensional porous graphene aerogel (GA) can improve the efficiency of electron transport, enhance the adsorption of organic pollutants and restrain the agglomeration of the core-shell S-nZVI NPs. The TCE removal rates of FeS, nZVI, GA and S-nZVI were 27.8%, 42%, 63% and 75% in 2?hr, respectively. Furthermore, TCE was completely removed within 50?min by S-nZVI/GA. The TCE removal rate increased with increasing pH and temperature, and TCE removal followed the pseudo-first-order kinetic model. The results demonstrate the great potential of S-nZVI/GA composite as a low-cost, easily separated and superior monolithic adsorbent for removal of organic pollutants.     

有机膨润土负载纳米铁去除废水中硝基苯

用具有良好吸附能力的有机膨润土作载体,通过FeSO4与NaBH4反应制得负载型的纳米铁(NZVL/CTMAB-Bent),用XRD、BET对其性能进行了表征.以硝基苯为目标污染物,试验了 -NZVI/CTMAB-Bent对不同起始浓度硝基苯的去除作用,考察了介质PH对其去除效率的影响,并与相同铁含量的纳米铁(NZVI)进行了比较.此外.还对NZVI/CTMAB-Bent还原硝基苯的机理进行了探讨.结果表明,NZVI/CTMAB-Bent对硝基苯的去除能力远高于相同铁含量的NZVI.也明显优于相同含量的有机膨润土和相同铁含量的NZVI对硝基苯去除率的加和.