The effects of manganese precursors on Mn-based/TiO2 catalysts for catalytic reduction of NO with NH3

Manganese acetate (MnAc) and manganese nitrate (MnN) were employed as precursors for the preparation of MnAc)/TiO2, Mn (N)/TiO2, Mn(Ac)-Ce/TiO2, and Mn(N)-Ce/TiO2 by impregnation. These complexes were used as catalysts in the low-temperature selective catalytic reduction of NO with NH3. The influence of manganese precursors on catalyst characteristics, the reduction activity, and the stability of the catalysts to poisoning by H2O and SO2 were studied. Experiments showed that Mn(N) produced MnO2 with large grain sizes in Mn(N)/TiO2 catalyst. On the contrary, Mn(Ac) led to highly dispersed and amorphous Mn2O3 in Mn (Ac)/TiO2 catalyst, which had better catalytic activity and stability to SO2 at low temperatures. The doping of cerium reduced the differences in catalytic performance between the catalysts derived from different Mn precursors.     

H2O和SO2对V2O5-WO3/TiO2催化剂催化氧化NO的影响

研究了在120℃的反应温度下,H2O和SO2对V2O5-WO3/TiO2催化剂选择性催化氧化（SCO）NO的影响。结果表明,在H2O和SO2存在的情况下催化剂失活很快,停止通入H2O和SO2后活性不能恢复,但在加热到250℃后催化活性基本恢复。FT-IR分析表明,催化剂表面形成了金属硝酸盐和Ti的硫酸盐,对催化活性有一定影响,但不影响催化剂在250℃下催化活性的恢复。SO2、H2O和NO的竞争吸附与SO2和NO2的铅室反应是影响催化剂活性的主要原因。     

负载型Mn-Ce／TiO2催化剂的制备及其低温脱硝活性

以成型TiO2作为载体,通过浸渍法制备了Mn-Ce／TiO2低温SCR催化剂,并系统研究了制备方法、煅烧条件、活性组分担载量、Mn含量等参数对催化剂催化还原NO性能的影响。结果表明,煅烧温度的升高会促使活性组分结晶度的提高,从而引起催化活性的降低,在500℃和600℃下所得Mn-Ce／TiO2催化剂活性组分为无定型态,表现出较高的脱硝活性。活性组分担载量的增加有利于催化活性的提高。Mn含量对Mn-Ce／TiO2催化剂的活性有较大影响,当Mn／（Mn＋Ce）摩尔比为40％和85％时,催化剂活性最高。     

Catalytic reduction of NO on copper/MCM-41 studied by in situ EXAFS and XANES

Speciation of copper in the channels of MCM-41 during reduction of NO with CO at 473-773 K was studied by in situ extended X-ray absorption fine structural (EXAFS) and X-ray absorption near edge structural (XANES) spectroscopies in the present work. The component fitted (in situ) XANES spectra of the catalyst showed that about 72% of metallic copper (Cu(0)) in MCM-41 was oxidized to higher oxidation state coppers (Cu(II) (46%) and Cu(I) (26%)) during the NO reduction process (at 473 K). By EXAFS, we also found that in the NO reduction process, oxygen was inserted into the metallic copper matrix and led to a formation of the copper oxide species with a Cu-O bond distance of 1.93 A which was greater than that of the model compound Cu(2)O (typically 1.86 A). At 573-673 K, mainly Cu(II) was found in the channels of MCM-41. Nevertheless, at a higher temperature (e.g., 773 K), about 61% Cu(I), 31% Cu(II), and 8% Cu(O) with averaged Cu-Cu and Cu-O bond distances of 3.04 and 1.88 A, respectively were observed, that might account for the high selectivity-to-decomposition (S/D) ratios for yields of N(2) and CO(2) in the catalytic reduction of NO with CO.     

Effects of NO2 and SO2 on selective catalytic reduction of nitrogen oxides by ammonia

The selective catalytic reduction (SCR) characteristics of NO and NO(2) over V(2)O(5)-WO(3)-MnO(2)/TiO(2) catalyst using ammonia as a reducing agent have been determined in a fixed-bed reactor at 200-400 degrees C. The presence of NO(2) enhances the SCR activity at lower temperatures and the optimum ratio of NO(2)/NO(x) is found to be 0.5. During the SCR reactions, there are some side reactions occurred such as ammonia oxidation and N(2)O formation. At higher temperatures, the selective catalytic oxidation of ammonia and the nitrous oxide formation compete with the SCR reactions. The denitrification (DeNO(x)) conversion decreases at lower temperatures but it increases at higher temperatures with increasing SO(2) concentration. The presence of SO(2) in the feeds inhibits N(2)O formation.     

Fe2O3-Cr2O3/TiO2系列催化剂的结构和脱硝性能

研究以纳米TiO2为载体,浸渍负载过渡金属氧化物,以CO为还原剂的脱硝催化剂的脱硝性能。实验中以计算量的Ni（NO3）2和Fe（NO3）3混合溶液浸渍纳米TiO2粉末,室温下搅拌30 min至混合均匀,放入旋转蒸发器中,70℃下至水分蒸干为止;所得粉末在550℃下、空气气氛中焙烧4 h即得所需催化剂。用以上方法分别制备2%Fe2O3-10%Cr2O3/TiO2、4%Fe2O3-8%Cr2O3/TiO2、6%Fe2O3-6%Cr2O3/TiO2、8%Fe2O3-4%Cr2O3/TiO2与10%Fe2O3-2%Cr2O3/TiO2等5种催化剂样品。实验结果表明,制备的催化剂具有较好的结构,分散较为均匀。对于CO＋NO反应,Fe2O3-Cr2O3/TiO2系列催化剂具有较好的催化活性,NO的转化率都达到了100%。其中,10%Fe2O3-2%Cr2O3/TiO2样品具有最好的低温活性,H2-TPR结果表明,这是由于10%Fe2O3-2%Cr2O3/TiO2催化剂更易于被CO预还原。     

TiO2纳米管催化活性再生处理技术

采用H2O2、Fe2（SO4）3和Fenton溶液对失活的TiO2纳米管进行再生处理,重点考察了3种溶液的浓度和处理时间等对再生效果的影响,初步分析了经处理后TiO2纳米管催化活性得到再生或增强的机理。结果表明,经H2O2溶液处理后TiO2催化活性能得到有效再生,经Fe2（SO4）3,和Fenton溶液处理后其催化活性不仅得到再生,还能显著增强,这与H2O2和Fenton的强氧化作用,及进入TiO2纳米管的Fe3＋的阻止电子．空穴对再复合作用有关。     

CuCoOx／TiO2催化氧化NO性能研究

采用浸渍法制备了CuCoOx／TiO2催化剂,考察了焙烧温度、反应温度、氧含量、NO浓度和空间速度对催化剂催化氧化NO性能的影响,并考察了催化剂的抗硫抗水性能。XRD、TPR和BET分析表明,350℃焙烧的催化剂具有CuCo2O4尖晶石结构,比表面积大,对NO的氧化效果好。在空速为5000h^-1,NO进口浓度500mg／m^3,含氧量10％的条件下,反应温度300℃时NO转化率可达79．5％,250℃时NO转化率接近50％。该催化剂具有良好的单独抗SO2、抗H2O毒化性能,H2O和SO2同时存在时很快失活。该催化剂可用于不同时含H2O和SO2的含NO气体催化氧化后再吸收处理。     

Superior pillared clay catalysts for selective catalytic reduction of nitrogen oxides for power plant emission control

Fe(3+)-, Cr(3+)-, Cu(2+)-, Mn(2+)-, Co(2+)-, and Ni(2+)-exchanged Al2O3-pillared interlayer clay (PILC) or TiO2-PILC catalysts are investigated for the selective catalytic reduction (SCR) of nitric oxide by ammonia in the presence of excess oxygen. Fe(3+)-exchanged pillared clay is found to be the most active. The catalytic activity of Fe-TiO2-PILC could be further improved by the addition of a small amount of cerium ions or cerium oxide. H2O and SO2 increase both the activity and the product selectivity to N2. The maximum activity on the Ce-Fe-TiO2-PILC is more than 3 times as active as that on a vanadium catalyst. Moreover, compared to the V2O5-WO3/TiO2 catalyst, the Fe-TiO2-PILC catalysts show higher N2/N2O product selectivities and substantially lower activities (by approximately 85%) for SO2 oxidation to SO3 under the same reaction conditions. A 100-hr run in the presence of H2O and SO2 for the CeO2/Fe-TiO2-PILC catalyst showed no decrease in activity.     

SO2-4/TiO2光催化降解苯酚

以工业硫酸氧钛为原料水解制得SO42-/TiO2光催化剂,并以苯酚为目标降解物,考察了SO24-/TiO2的光催化性能。结果表明:随着SO42-/TiO2制备过程中焙烧温度的升高,其光催化活性逐渐增加,650℃焙烧获得的SO24-/TiO2的光催化活性最好,此后再升高温度会因催化剂中硫的挥发而下降;在确定苯酚原液初始浓度为50 mg/L条件下,SO42-/TiO2的光催化降解苯酚的最佳工艺条件为反应时间2 h、苯酚pH为7、催化剂用量1 g/L。XRD、SEM和FTIR的分析结果显示实验温度下制得的SO42-/TiO2均为锐钛型TiO2;其间掺杂的SO24-在TiO2表面分散性较好,没有聚集成大的颗粒;红外分析的结果初步判定低温(<550℃)焙烧制得的催化剂SO42-在TiO2表面是螯合双配位吸附,高温焙烧时(>550℃)SO42-在TiO2表面是桥式配位吸附。     

SCR脱硝蜂窝陶瓷催化剂载体的制备

以二氧化钛、氧化铝作为主要原料,通过柱塞式挤压成型法制备了0.15 m×0.15 m×1 m规格的蜂窝陶瓷催化剂载体。通过对不同原料组成的载体性能对比,研究了各配方组分对载体性能的影响。为了提高载体活性,在21号配方的基础上加入A、B 2种商用造孔剂,考察了不同造孔剂的造孔性能。考察了蜂窝陶瓷载体负载催化剂后选择性催化还原(SCR)NO的活性,结果负载催化剂后的载体21a的在300℃时NO转化率达到最大96.5%。     

Comparison of titania nanotubes and titanium dioxide as supports of low-temperature selective catalytic reduction catalysts under sulfur dioxide poisoning

A series of iron–manganese oxide catalysts supported on TiO₂ and titanium nanotubes (TNTs) were studied for low temperature selective catalytic reduction (SCR) of NO with NH₃ in the presence of SO_2. The results showed that the specific surface area and the amount of Brønsted acid sites were highly correlated. The results also demonstrated that higher Mn⁴⁺/Mn³⁺ ratios and larger specific surface areas might be the main reasons for the excellent performance of MnFe-TNTs catalyst after SO₂ poisoning. The SO₂ poisoning effect could be minimized by reducing the GHSV, increasing the reaction temperature, or increasing the [NH₃]/[NO] molar ratio. The results also indicated that the formation of ammonium sulfate had a stronger effect on the NO conversion efficiency as compared to the formation of metal sulfate. Thus operating the low temperature SCR at above 230 ^oC to avoid the formation of ammonium sulfate would be the priority choice when SO₂ poisoning is a concerned issue.?Implications: Low-temperature selective catalytic reduction (SCR) has attracted increasing attention due to that it can reduce the energy consumption for the SCR process employed in industries such as steel plants and glass manufacturing plants. However, it also suffers from the sulfur dioxide (SO₂) poisoning problem. This study investigates the possibility of using titania nanotubes (TNTs) as the support of Mn/Fe bimetal oxide catalysts for low-temperature SCR to reduce the SO₂ poisoning. The results indicated that the MnFe-TNT catalyst can tolerate SO₂ for a longer time as compared with the MnFe-TiO₂ catalyst.     

Improving the activity of Mn/TiO2 catalysts through control of the pH and valence state of Mn during their preparation

In this study, the authors investigated the influence of the valence state of Mn on the efficacy of selective catalytic reduction using a Mn-based catalyst. The nitrogen oxides (NOx) conversion rate of the catalyst was found to be dependent on the type of TiO2 support employed and on the temperature, as the catalyst showed an excellent conversion of > 80% at a space velocity of 60,000 hr(-1) when the temperature was above 200 degrees C. Brunauer-Emmett-Teller, X-ray diffraction, and X-ray photoelectron spectroscopy analyses confirmed that catalyst displaying the highest activity contained the Mn4+ species and that its valence state was highly dependent on the pH during the catalyst preparation.     

Performance of the supported copper oxide catalysts for the catalytic incineration of aromatic hydrocarbons

A fixed bed reactor was used to assess the catalytic incineration of toluene by various transition-metal oxide species supported on gamma-Al(2)O(3). CuO/gamma-Al(2)O(3) was found to be the most active of seven catalysts investigated. The CuO species, with a Cu content of 5% (wt), was hence used with four different supports (CeO(2), gamma-Al(2)O(3), TiO(2) and V(2)O(5)) in order to define the optimal combination. Results of the catalytic incineration of toluene, X-ray diffraction (XRD) analysis, oxygen-temperature programmed desorption (O(2)-TPD), toluene-temperature programmed desorption (toluene-TPD) and hydrogen-temperature programmed reduction (H(2)-TPR) showed that CuO/CeO(2) was the most active catalyst, followed by CuO/gamma-Al(2)O(3). The activity of CuO/CeO(2) with respect to the VOC molecule was observed to follow this sequence: toluen>p-xylene>benzene. The addition of water vapor or CO(2) significantly inhibited the activity of the CuO/CeO(2) and CuO/gamma-Al(2)O(3) catalysts. The inhibiting effect of both was reversible for CuO/gamma-Al(2)O(3). For CuO/CeO(2), the inhibiting effect of CO(2) was reversible and even insignificant at a higher temperature (220 degrees C), but the effect of H(2)O vapor was somewhat irreversible at lower incineration temperatures (220 degrees C). For complete oxidation of toluene, the required reaction temperature increased with gas hourly space velocity (GHSV) and toluene inlet concentration.     

铜铈掺杂六铝酸盐的脱硝性能

用共沉淀法制备用于脱除NO的六铝酸盐催化剂LaMxAl12-xO19(M =Cu,Ce,CuCe).用XRD、H2-TPR和BET对催化剂进行了结构和物性表征.用微型催化反应装置考察了催化剂在CO选择性催化还原NO中的活性.结果表明,Cu离子易于进入六铝酸盐晶格内,形成完整的六铝酸盐结构.Ce离子不易于进入六铝酸盐晶格内,主要以CeO2的形式存在.在CO+ NO条件下,3种催化剂都表现出较好的脱硝活性,LaCuCeAl10O19中由于Cu离子与Ce离子间产生协同作用,该催化剂的脱硝活性有所增加.加入SO2后,3种催化剂都有不同程度的失活现象发生,其中LaCuAl11O19催化剂受SO2中毒影响最严重,LaCuCeAl10O19催化剂的脱硝活性在三者中最好.     

活性炭纤维负载TiO_2光催化降解甲醛的影响因素

利用自制光催化气体反应器体系,以活性炭纤维负载TiO2作催化剂,在紫外光照射下模拟降解室内污染气体甲醛,测试了活性炭纤维负载TiO2催化剂的催化活性,探讨了紫外光光强、催化剂的酸度、反应器内湿度及反应时间等控制反应的主要因素对甲醛降解率的影响.结果表明,活性炭纤维与TiO2的协同作用大大提高了对甲醛的降解效果;紫外光强增倍对甲醛降解率有一定提高,但提高幅度仅为11.71%;活性炭纤维用pH=5的TiO2溶胶浸泡做催化剂对甲醛的降解效果最好,60 min内降解率达到68.37%;反应器内的湿度为81%甲醛降解率最高,反应60 min后达82.2%;随着反应时间的延长,甲醛降解率的上升幅度不断减小,最高只能达到94.59%.     

Effects of acid treatments of activated carbon on its physiochemical structure as a support for copper oxide in DeSO(2) reaction catalysts

To enhance the dispersion of active sites, modification of the AC supports with different acid solution might result in various surface oxygen groups which act as anchoring sites for metallic precursor to stay and improve the reactivity between AC supports and copper precursor. In the present work, the AC support is tailored with HCl and HNO(3), respectively. The pore structure, surface oxygen groups of the AC support and catalysts as well as catalyst dispersion before and after acid treatments are systematically studied by BET, pH(slurry), TPD, and XRPD analyses. It is found that the order of activity in DeSO(2) reaction is as follows: Cu/AC-HCl>Cu/AC>Cu/AC-HNO(3). The same sequence is also observed for the pore structure of AC supports, the catalyst dispersion, but not for the amounts of CO(2) evolving during TPD experiments of supports. The key role of acid treatment on carbon surface chemistry and pore structure, which are closely related to catalyst dispersion and adsorption capacity, is examined to rationalize these findings. Furthermore, under the NO/NH(3)=1 the NO could be selective catalytic reduction with NH(3) in the presence of O(2), which catalyzed by fresh and spent AC-supported catalyst.     

Catalytic reduction of N2O over Ag-Pd/Al2O3 bimetallic catalysts

A study of the catalytic conversion of N2O to N2 over a bimetallic Ag-Pd catalyst is described in this article. Several Ag-Pd catalytic systems were prepared supported on Al2O3 with different ratios and their catalytic activity for the direct decomposition of N2O and their reduction with CO was measured. Based on the experimental results, it was observed that Ag-Pd bimetallic catalyst (5-0.5%) was the most active for both nitrous oxide reduction and direct decomposition. This high activity seems to be connected with a synergistic effect between Ag and Pd.     

GeO_2改性TiO_2催化超声降解活性红（M-3BE）染料废水的应用研究

制备了经GeO2改性的纳米TiO2,并用之作为超声降解活性红M-3BE反应的催化剂,研究了各种因素对制备的GeO2改性的纳米TiO2催化超声降解活性红染料废水的影响,并用XRD,SEM等手段对催化剂进行了表征。结果表明：GeO2改性的纳米TiO2作为催化剂,其对超声降解活性红染料废水的催化剂作用明显优于单纯以锐钛矿型T...     

Catalytic wet oxidation of ammonia: why is N2 formed preferentially against NO3 -?

The role of catalyst and the reason for the preferential formation of N(2) in the catalytic oxidation reaction of ammonia in water over a Ru (3wt.%)/TiO(2) catalyst were elucidated. It was verified that the catalyst in the reaction had no direct relevance to the selective formation of N(2), but was responsible only for the oxidation of aqueous ammonia, NH(3)(aq), finally giving a molecule of nitrous acid. The preferential production of N(2) was experimentally demonstrated due to the homogeneous aqueous phase reaction of the nitrous acid-dissociated NO(2)(-) with NH(4)(+) ions. Even under the highly oxidizing condition, NO(2)(-) was much more likely to react with NH(4)(+) to form N(2) than being oxidized over the catalyst to NO(3)(-) as long as NH(4)(+) was available in solution.