配方型吸附剂脱硫脱硝的实验研究

通过溶胶-凝胶法制得(V_2O_5-WO_3/TiO_2)SCR催化剂,以质量配比为3 1的活性焦和载银沸石为载体制备负载V_2O_5-WO_3/TiO_2得到活性焦-载银沸石配方型吸附剂,利用X射线光电子能谱仪和X射线多晶衍射仪对SCR催化剂进行表征。在固定床实验系统上进行该配方型吸附剂的脱硫脱硝的实验研究。实验结果表明,SO_2质量浓度为3 428 mg/m3、温度为120℃、O_2体积分数为6%、H_2O体积分数为8%的条件下,脱硫效率达到66.67%;当温度升高时,脱硫效率降低;SO_2质量浓度升高时,SO_2脱除效率呈现先增加后降低的趋势;氧气体积分数对SO_2的脱除有较大影响。NO质量浓度为821 mg/m3、温度为180℃、O_2体积分数为6%、NH_3/NO为1的条件下,NO脱除效率达到53.8%;温度升高,脱硝效率增加;NO的质量浓度对NO脱除效率影响不大;NH_3/NO是影响脱硝的一个重要因素,脱硝效率与其比值呈正相关。     

烧结烟气中氨-络合法同步脱硫脱硝络合剂再生的实验研究

对氨-络合法同步脱硫脱硝废液中络合剂再生进行了实验研究。结果表明,在50℃、p H值为5.65、Fe(Ⅱ)-EDTA浓度为0.04 mol/L、再生剂/Fe(Ⅱ)EDTA为2∶1的条件下,经铁粉再生后吸收液最高脱硫脱硝效率分别达到99%和75%;焦粉再生最高脱硫脱硝效率达到97%和46%;而乙二醛再生最高脱硫脱硝效率仅为80%和20%。同时铁粉再生中试结果也还表明脱硫效果可以稳定在100%,脱硝效果可维持在60%。     

氨法-Fe(Ⅱ)EDTA法同步脱硫脱硝的研究

在氨法脱硫的基础上提出了氨法-Fe(Ⅱ)EDTA法同步脱硫脱硝的新工艺,重点研究了Fe(Ⅱ)EDTA浓度、反应温度、进气流量、初始pH值等参数对脱硫脱硝效率的影响。研究结果表明,氨法-Fe(Ⅱ)EDTA法同步脱硫脱硝工艺可行,在温度40℃,初始pH值为8,进气量50 L/h,Fe(Ⅱ)EDTA浓度为0.075 mol/L的条件下可以保持99%以上的脱硫率和70%以上的脱硝率。     

湿法串联氧化脱硝机理研究

采用鼓泡法测试一定质量分数的H_2O_2和NaClO_2溶液在不同的温度和质量分数条件下氧化吸收剂对脱硝效率的影响,得出各自最优脱硝条件,最后与一定质量分数的KMnO_4溶液两两串联得出最优脱硝条件。结果表明:(1)NaClO_2的脱硝效率高于H_2O_2的脱硝效率。(2)在一定质量分数范围内,H_2O_2和NaClO_2的脱硝效率随质量分数的增加而增加,但超过临界质量分数后,脱硝效率降低。(3)NaClO_2与KMnO_4溶液串联,得到的脱硝效率最高。     

脱硫、脱硝用脉冲电源的设计及工业应用

使用常规半导体开关和脉冲磁压缩技术开发了平均功率15 kW、脉冲上升时间500 ns、重复频率300 Hz的脱硫、脱硝用脉冲电源。配备了9台电源的脉冲电晕等离子体脱硫、脱硝装置,在1台130 t/h蒸发量的燃煤锅炉上配套使用,取得了59%的脱硫效率、53%的脱硝效率和77%的除尘效率。     

Fe再生氨/Fe~(Ⅱ)EDTA法同步脱硫脱硝废液研究

采用氨/Fe~(Ⅱ)EDTA法同步脱除烧结烟气中SO_2和NO_x,并通过铁屑再生废液中Fe~(Ⅱ)维持脱硝效率。实验结果显示,氨/Fe~(Ⅱ)EDTA法脱硫效率可达100%,脱硝效率可达68.3%。但是,随着实验时间的延长,脱硝效率逐步下降。通过铁屑再生Fe~(Ⅱ)-除铁后,脱硝效率从48.8%增加至57.1%。     

甲醇对等离子体脱硫脱硝影响的实验研究

应用等离子体耦合催化剂进行烟气同时脱硫脱硝实验,重点分析了甲醇对脱硫脱硝效率的影响,同时研究了反应温度、甲醇浓度等因素的影响。实验结果表明,在V2O5/TiO2催化剂耦合等离子体反应器中,200℃时添加0.4%的甲醇能将NO的氧化效率从38%提高到99%。     

影响炭化型煤成型性能的工艺参数研究

对无烟粉煤生产炭化型煤的成型工艺进行了研究,得出了粉煤成型的最优工艺参数。同时用扫描电镜(SEM)对炭化型煤高温时的粘结机理进行了研究,结果表明,粘结剂用量为16%,成型水的质量分数为13%~15%,成型压力为50 MPa,炭化温度为800℃时,制得的高性能型煤的抗压强度和跌落强度分别为13.2 MPa和98.2%。型煤炭化时,煤改性粘结剂产生液相胶质体在无烟煤表面形成胶质薄膜层,薄膜层逐渐缩聚、固化,填充于颗粒间,提高了型煤强度。     

燃煤工业锅炉烟气湿法脱硫脱硝技术探讨

依据燃煤工业锅炉烟气的特点,结合目前主流的脱硫脱硝工艺,提出了一种新型的用于燃煤工业锅炉烟气脱硫脱硝的工艺一塔式液相氧化吸收联合脱硫脱硝技术。介绍了工艺流程、技术优势和主要系统组成,以北京市某供热厂2×70 MW燃煤锅炉烟气脱硫脱硝工程为例,分析了工艺的脱硫脱硝技术、经济指标。结果表明,一塔式液相氧化吸收联合脱硫脱硝技术具有脱硫脱硝效率高、工艺投资省、运行费用低等优点,是一种符合我国国情、值得推广应用的新型脱硫脱硝技术。     

同时脱硫脱硝固态反应剂研究进展

针对于干法同时控制热力发电厂NO_x和SO_2的排放,综述了近年来研究较广泛的钙基吸收剂、改性活性炭吸收剂、γ-Al_2O_3吸收-催化剂、天然锰矿石反应剂等几种同时脱硫脱硝固态反应剂的结构特性,以及脱硫脱硝效率。根据这几种固态反应剂的研究现状指出了应更进一步对氮氧化物和硫氧化物在同时脱除时的相互影响进行研究,从而提高同时脱硫脱硝效率。     

油浸变压器排油注氮装置在500kV变电站的设计与应用

在分析500kV变电站主变压器消防系统的现状,比较3类消防系统优缺点的基础上,详细论述了主变排油注氮装置的结构组成、工作原理、参数计算、控制系统设计以及需要注意的事项等,为下一步排油注氮装置的推广应用打下基础.     

公路隧道火灾逃生疏散研究

以苍岭隧道为背景,首先采用经验计算理论和计算软件building EXODUS相结合的方式,从被困人员的安全疏散时间、高温烟气的影响、隧道横通道的利用率以及人员的疏散行为特性进行了研究。结果表明:中小规模火灾情况下的安全疏散时间控制在8 min之内,高温烟气影响不大,但横通道的利用率不平均,且人员疏散路线相对集中。然后对存在的逃生疏散问题提出针对性建议以及其他相关建议,旨在为更大程度降低事故的严重性和经济财产损失。     

建筑安全管理的系统定义与评价

在系统论与控制论的背景下，定义建筑安全管理作为社会时效系统的控制模型、应用评价方程式，既可以定量地评价各种条件下建筑安全管理的绩效，又可以指导社会与企业建筑安全管理工作，实现建筑安全管理工作科学化与规范化。     

Potentially preventable prehospital deaths from motor vehicle collisions

Background: In 2011, about 30,000 people died in motor vehicle collisions (MVCs) in the United States. We sought to evaluate the causes of prehospital deaths related to MVCs and to assess whether these deaths were potentially preventable.

Methods: Miami–Dade Medical Examiner records for 2011 were reviewed for all prehospital deaths of occupants of 4-wheeled motor vehicle collisions. Injuries were categorized by affected organ and anatomic location of the body. Cases were reviewed by a panel of 2 trauma surgeons to determine cause of death and whether the death was potentially preventable. Time to death and hospital arrival times were determined using the Fatality Analysis Reporting System (FARS) data from 2002 to 2012, which allowed comparison of our local data to national prevalence estimates.

Results: Local data revealed that 39% of the 98 deaths reviewed were potentially preventable (PPD). Significantly more patients with PPD had neurotrauma as a cause of death compared to those with a nonpreventable death (NPD) (44.7% vs. 25.0%, P =.049). NPDs were significantly more likely to have combined neurotrauma and hemorrhage as cause of death compared to PPDs (45.0% vs. 10.5%, P <.001). NPDs were significantly more likely to have injuries to the chest, pelvis, or spine. NPDs also had significantly more injuries to the following organ systems: lung, cardiac, and vascular chest (all P <.05). In the nationally representative FARS data from 2002 to 2012, 30% of deaths occurred on scene and another 32% occurred within 1 h of injury. When comparing the 2011 FARS data for Miami–Dade to the remainder of the United States in that year, percentage of deaths when reported on scene (25 vs. 23%, respectively) and within 1 h of injury (35 vs. 32%, respectively) were similar.

Conclusions: Nationally, FARS data demonstrated that two thirds of all MVC deaths occurred within 1 h of injury. Over a third of prehospital MVC deaths were potentially preventable in our local sample. By examining injury patterns in PPDs, targeted intervention may be initiated.     

空气气氛下木材表观热解动力学

研究了空气气氛下马尾松和楠木的树叶、树皮和树干试样的热解过程,发现每种试样的热解均包含两步主要的失重过程,在600℃时总失重均达90%以上.利用积分方法建立了适用于所有试样的两阶段一级动力学模型,实验失重曲线较好地符合模型计算出的失重曲线.     

胶粘剂对芳纶无纬布防弹性能的影响

通过物理共混的方法,将固化剂及消泡剂加入到丙烯酸酯胶粘剂中,从而改善丙烯酸酯胶粘剂织造的无纬布表面粘手及不平整的问题,并利用电子拉力实验机对无纬布进行力学性能测试。研究表明：固化剂的添加可明显提高布样的粘结强度,并且布样的表面不粘手;消泡剂的添加能够明显改善布样的表观质量,布样表面平整、无气泡;添加固化剂可提高布样的力学性能,同时还可提高了材料的防弹性能,子弹穿透层数减少,布样的平均凹陷明显降低,减少了对人体的二次钝伤。     

地铁事故应急疏散模拟及优化研究

为探究如何提高地铁车站应急疏散的效率,以我国近十年来地铁常见事故类型统计为基础,在事故风险分析的前提下,利用风险矩阵和元胞自动机设定应急疏散等级,分析不同事故水平下相应疏散措施。以北京地铁西直门站为实例,使用疏散仿真软件Pathfinder构建模拟环境,对高峰时期下站内最短逃生路径进行疏散模拟;按照事故与疏散的响应过程,从预防次生事故角度出发,针对西直门站疏散过程中可能发生的踩踏事故的诱发因素进行优化;研究拥堵对疏散进度的具体影响,选取使用率较低的M通道设施,进行不同使用率下的多次模拟,得到最优的疏散方案,研究结果可为进一步提高疏散设施利用率、改善应急疏散效果提供技术支持。     

不同通风条件下密闭空间CO2泄漏及排散过程模拟研究

为了探究密闭空间内通风对气体泄漏扩散过程的影响,基于FLACS模拟软件,对密闭空间内CO2泄漏及排散过程进行模拟,探讨入风口、出风口相对位置对泄漏及排散过程的影响。研究结果表明:入风口高度与出风口高度越高,越有利于CO2气体排散,应急排散时间更短;入风口位于屋顶时,CO2排散效果最好。     

基于DEMATEL/ISM的深水井喷风险影响因素研究*

为提高深水井喷事故风险管理水平,提出研究深水井喷风险影响因素的分析方法。从技术、人员、环境和管理4个方面,识别深水井喷事故风险致因因素,建立深水井喷事故风险评价指标体系;运用矩阵决策实验室分析法（DEMATEL）,研究风险因素之间的相互影响关系,计算不同风险因素的中心度和原因度,确定关键风险因素;进一步基于解释结构模型（ISM）划分不同影响因素的层次结构,分析风险因素之间的综合影响关系,建立深水井喷事故风险影响因素模型。结果表明:层级1为近邻致因,可直接导致井喷事故的发生;层级2~7为过渡致因,在风险传递过程中起到桥梁作用,对井喷事故的直接影响较小;而层级8则为本质致因,重视本质致因的改善有利于从根源上降低井喷事故的风险。研究结果可为深水井喷事故风险的预防和控制提供理论依据。     

化工企业DVR风险分析模型的构建及应用——基于公共安全三角形模型*

为对化工企业风险进行评价,根据公共安全三角形理论,从危险源破坏性、目标脆弱性和应急处置可恢复性3个方面建立风险分析模型。在危险源破坏性上,从事故发生可能性和事故后果危险性2个方面进行讨论并得出可能性和危险性系数。在目标脆弱性上,建立人和物的脆弱性计算模型得出目标脆弱性的系数。设立应急管理指标,结合专家评分得出应急处置可恢复性系数。将各系数归一化相乘得到化工安全风险分析整合系数,建立基于危险源破坏性（Destructiveness）、目标脆弱性（Vulnerability）、应急处置可恢复性（Recoverability）的DVR风险分析模型,并进行应用实例分析。结果表明:该模型在化工企业的风险评价中具有一定的实用性。