Selective sorption of perfluorooctane sulfonate on molecularly imprinted polymer adsorbents

Perfluorooctane sulfonate (PFOS), as a potential persistent organic pollutant, has been widely detected in water environments, and has become a great concern in recent years. PFOS is very stable and difficult to decompose using conventional techniques. Sorption may be an attractive method to remove it from water. In this study, the molecularly imprinted polymer (MIP) adsorbents were prepared through the polymerization of 4-vinylpyridine under different preparation conditions in order to remove perfluorooctane sulfonate (PFOS) from water. The MIP adsorbents using perfluorooctanoic acid (PFOA) as the template had good imprinting effects and could selectively remove PFOS from aqueous solution. The sorption behaviors including sorption kinetics, isotherms, and effect of pH, salt, and competitive anions were investigated. Experimental results showed that the sorption of PFOS on the MIP adsorbents was very fast, pH-dependent, and highly selective. The achieved fast sorption equilibrium within 1 h was attributed to the surface sorption on the fine adsorbents. The sorption isotherms showed that the sorption selectivity of PFOS on the MIP adsorbents decreased at high PFOS concentrations, which may be due to the double-layer sorption and the formation of PFOS micelles on the sorbent surface. The sorption of PFOS on the MIP adsorbents was mainly dominated by the electrostatic interaction between the protonated vinylpyridine on the adsorbent surface and the anionic PFOS. The prepared MIP adsorbents can potentially be applied in water and wastewater treatment for selective removal of PFOS.     

聚丙烯酰胺对聚合物驱含油污水中油珠沉降分离的影响

研究发现阴离子聚丙烯酰胺(HPAM)对聚合物驱含油污水处理有正反2方面影响.聚合物能增加污水粘度,降低油珠上浮速度,而且聚合物能增加油水界面水膜强度,延缓油珠聚并时间,这是聚合物对油珠沉降分离的不利影响;同时,聚丙烯酰胺具有絮凝性,能将水中油珠连接到一起,有利于油珠聚并.当聚丙烯酰胺相对分子质量为2.72×10⁶,浓度小于800mg/L时,絮凝作用大于粘度作用,有利于油珠的沉降分离.初始油珠粒径小是聚合物驱含油污水难处理的主要原因.横向流除油器可以加速油珠聚并,缩短沉降时间,适合处理聚合物驱含油污水.     

振打机构摆臂疲劳寿命仿真及可靠性分析

目的 针对振打机构关键部件摆臂,开展疲劳寿命及关键参数影响程度仿真分析,获得寿命分布及可靠性数据,校核摆臂设计是否满足使用要求。方法 基于S-N曲线进行振打机构摆臂的寿命仿真,开展动力学仿真与应力仿真,获得不同温度下摆臂最低寿命与管壁壁厚的关系。通过对关键寿命影响参数进行影响程度仿真分析,获得寿命分布及可靠性数据。结果 当摆臂壁厚大于1.77mm时,摆臂的平均寿命大于144万次,满足产品设计要求。疲劳寿命与弹性模量E负相关,与抗拉强度和表面加工系数正相关。可靠度R取0.8时,摆臂的可靠寿命约为29 005次;可靠度R取0.9时,摆臂的可靠寿命约为11 891次。结论 振打机构摆臂壁厚需大于1.77 mm,摆臂表面质量系数大于0.827 3,材质抗拉强度大于907.76 MPa,弹性模量E小于2.041×10^(5)MPa。     

膨胀污泥中丝状菌的分离鉴定与特性分析

为了阐明膨胀污泥中的丝状菌种类和特性,利用培养法、显微镜检和分子生物学分析技术从城市污水处理厂的膨胀污泥中分离鉴定丝状菌,并对典型丝状菌进行特性分析.利用高氏一号培养基和淀粉培养基分离出的丝状菌可归入18个属,其中链霉菌属(Streptomyce)、细杆菌属(Microbacterium)属于放线菌门,其余均属于真菌.青霉菌属(Penicillium)、枝孢菌属(Cladosporium)、链格孢属(Alternaria)、曲霉菌属(Aspergillus)、毛孢子菌属(Trichosporon)在培养基上的出现频次较高.毛孢子菌、链霉菌、青霉菌和链格孢菌都能在pH中性或偏酸性条件下良好生长.高浓度的Na Cl能够抑制毛孢子菌和链霉菌,但对青霉菌和链格孢菌的抑制作用不明显.除毛孢子菌外,链霉菌、青霉菌和链格孢菌都可有效地利用蔗糖、淀粉和纤维素,碳源浓度增加会促进它们的生长.r DNA-ITS区高通量测序结果表明膨胀污泥中存在大量未知真菌.     

合成有机物结构-生物降解性关系的研究

本文综述了合成有机物生物降解性的研究方法.以及定性结构-生物降解性关系(SBR).重点综述了芳香类化合物的结构与生物降解性的关系.研究这一关系有助于有毒化学品生物降解性的预测.     

钻井液化学剂可生物降解性研究

实验测定了16种钻井液化学剂的BOD_5和COD_cr，并计算其BOD_5／COD_cr比值。提出了以BOD_5／COD_cr的比值划分钻井液化学剂可生物降解性的分级标准，并对16种钻井液化学剂的可生物降解性进行分级，为其应用提供依据。     

循环式超声强化光催化降解双酚A

设计了一种循环式超声强化光催化反应器,以TiO2作为光催化剂,研究了超声功率、TiO2加入量、循环液流速和空气流量对双酚A(BPA)降解效果的影响。实验结果表明:超声与光催化过程在循环式超声强化光催化反应器中实现了较好的协同效应;在初始BPA质量浓度为20.0mg/L、超声功率为600W、TiO2加入量为7g/L、循环液流速为4.05×10-2m/s、空气流量为200mL/min的条件下,反应150min后,BPA降解率可达90.5%,溶液中剩余BPA质量浓度仅为1.8mg/L,反应240min后TOC去除率可达84.5%。     

热电池失效分析及等效加速贮存试验技术

目的 建立基于实测环境载荷的热电池等效加速贮存试验技术,掌握其在环境载荷作用下的性能退化规律。方法 在分析热电池组成和所受环境载荷情况的基础上,分析热电池的主要失效模式,设计基于实测环境数据的等效加速贮存试验,开展热电池等效加速贮存试验,分析热电池性能和热图像的变化情况,利用粒子滤波算法对电池剩余电容量进行预测。结果 随加速循环次数（时间）的增加,热电池的电容量下降。热图像表明,热电池经过等效加速贮存试验后,其放电过程表面温度要高于初始放电表面温度。粒子滤波算法能够有效模拟电容量的退化过程,电池剩余电容量预测结果与试验结果误差在10%以内。结论 等效加速贮存试验得到了热电池的性能退化规律,从而为热电池的贮存试验提供一种解决方案。     

橡胶助剂析出的原因及防治探析——以武警现行列装鞋靴产品为例

橡胶助剂析出是橡胶制品的常发问题,本文从原料、配方设计、炼胶工艺、硫化工艺、存储条件等方面分析了武警现行鞋靴橡胶助剂析出的原因、形式及危害,提出了防治对策。     

铝合金-丁腈橡胶航空带垫卡箍典型环境损伤研究

目的研究典型环境对丁腈橡胶-铝合金带垫卡箍的损伤效应。方法通过模拟铝合金-丁腈橡胶航空带垫卡箍使用时的装配结构和应力状态,应用GJB 150A—2009中的湿热和太阳辐射两种典型老化环境,采用宏观形貌观察、卡箍保持力测试和橡胶衬垫拉伸性能测试方法,结合扫描电子显微镜和傅里叶红外光谱技术,分析带垫卡箍的性能劣化过程。结果带垫卡箍在湿热和太阳辐射环境中老化50 d后,卡箍橡胶衬垫表面出现大量微孔缺陷,拉伸性能大幅降低,导致卡箍保持力分别下降了35%和51%。结论带垫卡箍在模拟装配状态下进行湿热和太阳辐射环境暴露实验,卡箍橡胶衬垫内部结构由致密逐渐变得疏松,部分碳碳双键发生氧化交联反应,并在一定程度上提高了聚合物的交联密度,材料硬度提高,回弹性能减弱,橡胶衬垫对芯轴的包裹能力降低,导致卡箍保持力性能降低。