Solid phase high explosive (HE) residues from munitions detonation may be a persistent source of soil and groundwater contamination at military training ranges. Saturated soil column tests were conducted to observe the dissolution behavior of individual components (RDX, HMX, and TNT) from two HE formulations (Comp B and C4). HE particles dissolved readily, with higher velocities yielding higher dissolution rates, higher mass transfer coefficients, and lower effluent concentrations. Effluent concentrations were below solubility limits for all components at superficial velocities of 10-50 cm day(-1). Under continuous flow at 50 cm day(-1), RDX dissolution rates from Comp B and C4 were 34.6 and 97.6 microg h(-1) cm(-2) (based on initial RDX surface area), respectively, significantly lower than previously reported dissolution rates. Cycling between flow and no-flow conditions had a small effect on the dissolution rates and effluent concentrations; however, TNT dissolution from Comp B was enhanced under intermittent-flow conditions. A model that includes advection, dispersion, and film transfer resistance was developed to estimate the steady-state effluent concentrations.     

Evaluating the strength development of mortar using clinker fine aggregate with a combination of fly ash and its inhibitory effects on alkali–silica reaction and delayed ettringite formation

The aggregate composed of cement clinker, an intermediate cement product, improves strength development and mass transfer resistance of concrete. Fly ash (FA) is a supplementary cementitious material that can be substituted by cement. This study investigated the strength development of highly FA-substituted mortar mixed with cement clinker fine aggregate (CL) and tested its inhibitory effect against the alkali–silica reaction (ASR). In addition to these, this study provides the testing results of evaluating the effects of using cement clinker fine aggregate on delayed ettringite formation (DEF), which can be problematic for precast concrete products. The study results revealed that at 91 days of age, in the case of 80% replacement ratio of fly ash to cement, using CL exhibited similar strength development as mortar with limestone fine aggregate and no FA substitution. Furthermore, mortars with 70% and 80% FA substitution did not exhibit clear ASR-induced expansion even at 182 days of age. Lastly, mortar using clinker fine aggregate could suppress DEF-induced expansion at 182 days of age, which was similar to the effect obtained using FA. These results can promote the utilization of CL resources for concrete and using clinker as fine aggregate in precast concrete products.

     

Verification of the mutually complementary effect of fly ash and clinker aggregate on the strength,heat of hydration,and alkali-silica reaction

Journal of Material Cycles and Waste Management - Although fly ash, as used for supplementary cementitious material in Portland cement concrete, can reduce the heat of hydration and suppress the...