生物基聚合物PHBV和PLA复合材料在不同介质中的生物降解及其影响因素

传统工艺的塑料生产不仅依赖石油资源的持续开发利用,同时给环境造成了前所未有的压力,近年来生物基聚合物（聚（3-羟基-3-戊酸酯）-PHBV,聚乳酸-PLA）日渐成为传统石油基塑料的替代产品.本文采用呼吸测试手段,旨在揭示均质复合材料在不同环境介质（土壤、熟化堆肥、水体）条件下及有机添加剂（木质素）,无机添加剂（蒙脱石）和天然有机物链增长剂（Joncryl）作用下的生物降解特征.结果表明：当链增长剂Joncryl添加量为5%时,对所有介质PHBV和PLA复合材料产生显著抑制作用.Joncryl添加量为0.2%时,未对所测样品的生物降解行为产生干扰作用.在熟化堆肥介质中,PLA复合材料比PHBV基质混合物的生物降解速率明显降低.有机木质纤维添加剂（榛子壳粉末）单独在聚合物中添加或者和链增长剂Joncryl以及非有机添加剂（Dellite72T）共同作用下都可促进PLA聚合物中各组分的相容连接性.实验结果表明,新型添加剂在不同介质中以二元或三元添加的方式对生物降解过程产生重要影响,该研究将为新型材料使用后的生物降解效应提供理论依据.     

Effects of Na+ on Cu/SAPO-34 for ammonia selective catalytic reduction

Copper-exchanged chabazite (Cu/CHA) catalysts have been found to be affected by alkali metal and alkaline earth ions. However, the effects of Na⁺ ions on Cu/SAPO-34 for ammonia selective catalytic reduction (NH₃-SCR) are still unclear. In order to investigate the mechanism, five samples with various Na contents were synthesized and characterized. It was observed that the introduced Na⁺ ion-exchanges with H⁺ and Cu^2 + of Cu/SAPO-34. The exchange of H⁺ is easier than that of isolated Cu^2 +. The exchanged Cu^2 + ions aggregate and form “CuAl₂O₄-like” species. The NH₃-SCR activity of Cu/SAPO-34 decreases with increasing Na content, and the loss of isolated Cu^2 + and acid sites is responsible for the activity loss.     

Seasonal variation and size distribution of biogenic secondary organic aerosols at urban and continental background sites of China

Size-resolved biogenic secondary organic aerosols(BSOA) derived from isoprene and monoterpene photooxidation in Qinghai Lake, Tibetan Plateau(a continental background site) and five cities of China were measured using gas chromatography/mass spectrometry(GC/MS). Concentrations of the determined BSOA are higher in the cities than in the background and are also higher in summer than in winter. Moreover, strong positive correlations(R2= 0.44–0.90) between BSOA and sulfate were found at the six sites,suggesting that anthropogenic pollution(i.e., sulfate) could enhance SOA formation,because sulfate provides a surface favorable for acid-catalyzed formation of BSOA. Size distribution measurements showed that most of the determined SOA tracers are enriched in the fine mode( 3.3 μm) except for cis-pinic and cis-pinonic acids, both presented a comparable mass in the fine and coarse( 3.3 μm) modes, respectively. Mass ratio of oxidation products derived from isoprene to those from monoterpene in the five urban regions during summer are much less than those in Qinghai Lake region. In addition, in the five urban regions relative abundances of monoterpene oxidation products to SOA are much higher than those of isoprene. Such phenomena suggest that BSOA derived from monoterpenes are more abundant than those from isoprene in Chinese urban areas.     

Regionalization based on spatial and seasonal variation in ground-level ozone concentrations across China

Owing to the vast territory of China and strong regional characteristic of ozone pollution,it's desirable for policy makers to have a targeted and prioritized regulation and ozone pollution control strategy in China based on scientific evidences. It's important to assess its current pollution status as well as spatial and temporal variation patterns across China.Recent advances of national monitoring networks provide an opportunity to insight the actions of ozone pollution. Here, we present rotated empirical orthogonal function(REOF)analysis that was used on studying the spatiotemporal characteristics of daily ozone concentrations. Based on results of REOF analysis in pollution seasons for 3 years' observations, twelve regions with clear patterns were identified in China. The patterns of temporal variation of ozone in each region were separated well and different from each other, reflecting local meteorological, photochemical or pollution features. A rising trend in annual averaged Eight-hour Average Ozone Concentrations(O_3-8 hr) from 2014 to 2016 was observed for all regions, except for the Tibetan Plateau. The mean values of annual and 90 percentile concentrations for all 338 cities were 82.6 ± 14.6 and 133.9 ± 25.8 μg/m~3,respectively, in 2015. The regionalization results of ozone were found to be influenced greatly by terrain features, indicating significant terrain and landform effects on ozone spatial correlations. Among 12 regions, North China Plain, Huanghuai Plain, Central Yangtze River Plain, Pearl River Delta and Sichuan Basin were realized as priority regions for mitigation strategies, due to their higher ozone concentrations and dense population.     

房屋建筑工程施工现场环境保护以及节能降耗控制措施研究

房屋建筑施工阶段是建筑工程中最为重要的阶段,也是资源消耗和环境污染的集中阶段。房屋建筑施工造成的环境污染主要来源于:施工中的固体垃圾、液体垃圾和气体垃圾,且在施工现场,相关人员节能降耗意识薄弱,对于施工中存在的资源浪费现象经常会忽视。基于此,给出了如下措施:加强施工过程的监控,合理排放施工现场的污水和固体废弃物;提高水的利用率,并在施工过程中,通过节水工艺对路面进行喷洒;合理排放施工过程产生的污水,对含有化学品、油漆的建筑材料要实施防渗漏措施;设置封闭式垃圾容器,利用袋装化形式将施工垃圾带出施工现场;倡导绿色施工。     

海水中阴极极化对X80钢应力腐蚀及氢脆敏感性的影响

目的研究不同p H值海水中阴极极化对X80管线钢应力腐蚀及氢脆的抑制作用。方法采用慢应变速率拉伸试验、电化学测试、微观组织观察等分析方法。结果 X80钢在天然海水中的析氢电位约为-940m V(vs.SCE,下同),海水p H为3.5时析氢电位发生正移。其应力腐蚀敏感性与极化电位有很大关系,随着极化电位负移,X80钢的氢脆敏感性增加。天然海水中当极化电位负于-950 m V时,断口出现准解理断裂特征形貌。在-1050 m V极化电位下,钢材进入氢脆断裂区发生脆性断裂。海水p H为3.5时,-900 m V钢材有发生氢脆的危险。结论与天然海水相比,X80钢在p H为3.5的酸性海水中具有较高的应力腐蚀敏感性,两种海水介质中X80钢的应力腐蚀敏感性均随极化电位负移而增加。     

7B04铝合金和30CrMnSiA钢短期腐蚀的电化学行为研究

目的研究7B04铝合金和30CrMnSiA合金钢试样的电化学性能。方法采用电化学实验、扫描电子显微镜(SEM)、腐蚀坑深度测试分别对7B04铝合金和30CrMnSiA合金钢试样在是否经过天然海水浸泡的情况下进行测试分析,得到微观腐蚀形貌和腐蚀坑深度以及试样表面不带锈和带锈时的电化学性能。结果随着Na Cl浓度增大,7B04铝合金和30CrMnSiA钢的自腐蚀电流变大,两者之间存在明显的电位差,接触后会发生电偶腐蚀。电偶电流与阴阳极面积比和Na Cl浓度有关,阴阳极面积比增大或Na Cl浓度升高均会导致电偶效应增强。经过海水短期浸泡后,7B04铝合金表面的锈层不仅没有起到抑制腐蚀的作用,反而使自腐蚀加重,但电偶效应确实有所减弱。结论沿海设备在使用过程中应竭力避免铝合金在锈层下工作。     

舰空导弹杀伤概率随机化检验方法

目的充分有效利用生产方风险,在既定的生产方风险和有限的试验样本条件下,合理分配舰空导弹杀伤概率假设检验中的双方风险。方法通过似然函数推导检验问题的最优势检验,设计一种随机化检验方法,在检验完成后且必要时进行一次Bernoulli试验,以确定是否接受原假设。结果计算结果显示,相对经典假设检验方法,随机化检验方法可以保证实际生产方风险不超过既定的生产方风险上限,同时可使军方风险更小。结论该方法能够合理利用生产方风险,在不增加试验样本的条件下,降低军方风险,具有很好的工程实践意义。     

铜合金实验室试验与实海挂片结果的比较与分析

目的比较实验室试验结果与实海挂片结果对B10和H62两种铜合金腐蚀性能评价的异同之处。方法采用线性极化、电化学阻抗、显微形貌观察等,比较两种铜合金在实验室模拟海水中的的腐蚀速率、点蚀倾向,结合反应机理、腐蚀形貌、环境等外部因素,分析导致实验室与实海环境下出现差异的原因。结果除榆林海域外,实海挂片与实验室结果都表明,B10试样的平均腐蚀速率小于H62。B10和H62两种铜合金随温度升高腐蚀速率增大,在实验室和实海情况下表现出一致性,且平均腐蚀速率都随浸泡时间的延长而降低。结论在实海环境中,温度不是影响点蚀的主要因素,微生物等其他环境因素会对点蚀产生较大影响。     

飞机用铝合金腐蚀行为和腐蚀预测研究现状及问题分析

针对不同的航空铝合金结构及部位,从腐蚀机理、腐蚀行为和腐蚀预测技术三方面较为系统地分析了研究现状及进展。在此基础上,明确了航空铝合金腐蚀预测技术需要进一步研究的问题,分别为飞机结构表面腐蚀环境的确定问题,材料在海洋大气环境下腐蚀电化学性能的准确测量问题,腐蚀预测模型的选取问题。