Tuning the fill percentage in the hydrothermal synthesis process to increase catalyst performance for ozone decomposition

The performance of Ce-OMS-2 catalysts was improved by tuning the fill percentage in the hydrothermal synthesis process to increase the oxygen vacancy density. The Ce-OMS-2 samples were prepared with different fill percentages by means of a hydrothermal approach (i.e. 80%, 70%, 50% and 30%). Ce-OMS-2 with 80% fill percentage (Ce-OMS-2-80%) showed ozone conversion of 97%, and a lifetime experiment carried out for more than 20?days showed that the activity of the catalyst still remained satisfactorily high (91%). For Ce-OMS-2-80%, Mn ions in the framework as well as K ions in the tunnel sites were replaced by Ce⁴⁺, while for the others only Mn ions were replaced. O₂-TPD and H₂-TPR measurements proved that the Ce-OMS-2-80% catalyst possessed the greatest number of mobile surface oxygen species. XPS and XAFS showed that increasing the fill percentage can reduce the AOS of Mn and augment the amount of oxygen vacancies. The active sites, which accelerate the elimination of O₃, can be enriched by increasing the oxygen vacancies. These findings indicate that increasing ozone removal can be achieved by tuning the fill percentage in the hydrothermal synthesis process.     

Hygroscopicity measurement of sodium carbonate, β-alanine and internally mixed β-alanine/Na2CO3 particles by ATR-FTIR

Water-uptakes of pure sodium carbonate(Na_2CO_3),pure β-alanine and internally mixedβ-alanine/Na_2CO_3 aerosol particles with different mole ratios are first monitored using attenuated total reflectance Fourier transform infrared spectroscopy(ATR-FTIR) technique.For pure Na_2CO_3 aerosol particles,combining the absorptions at 877 and 1422 cm-1 with abrupt water loss shows the efflorescence relative humidity(ERH) of 62.9%–51.9%.Upon humidifying,solid Na_2CO_3 firstly absorbs water to from Na_2CO_3·H2 O crystal at 72.0% RH and then deliquesces at 84.5% RH(DRH).As for pure β-alanine particles,the crystallization takes place in the range of 42.4%–33.2% RH and becomes droplets at ～ 88.2% RH.When β-alanine is mixed with Na_2CO_3 at various mole ratios,it shows no efflorescence of Na_2CO_3 whenβ-alanine to Na_2CO_3 mole ratio(OIR) is 2:1.For 1:1 and 1:2 β-alanine/Na_2CO_3 aerosols,the ERHs of Na_2CO_3 are 51.8%–42.3% and 57.1%–42.3%,respectively.While β-alanine crystal appears from 62.7% RH for 2:1 and 59.4% RH for both 1:1 and 1:2 particles and lasts to driest state.On hydration,the DRH is 44.7%–75.2% for Na_2CO_3 with the OIR of 1:1 and 44.7%–69.0%for 1:2 mixture,and those of β-alanine are 74.8% for 2:1 mixture and 68.9% for two others.After the first dehumidification–humidification,all the water contents decrease despite of constituent fraction.And at ～ 92% RH,the remaining water contents are 92%,89% and 82%at ～ 92% RH,corresponding to OIR of 2:1,1:1 and 1:2 mixed system,respectively.     

Performance of different macrophytes in the decontamination of and electricity generation from swine wastewater via an integrated constructed wetland-microbial fuel cell process

Plants constitute a major element of constructed wetlands(CWs).In this study,a coupled system comprising an integrated vertical flow CW(IVCW) and a microbial fuel cell(MFC) for swine wastewater tre atment was developed to research the effects of macrophytes commonly employed in CWs,Canna indica,Acorus calamus,and Ipomoea aquatica,on decontamination and electricity production in the system.Because of the different root types and amounts of oxygen released by the roots,the rates of chemical oxygen demand(COD) and ammonium nitrogen(NH_4~+-N) removal from the swine wastewater differed as well.In the unplanted,Canna indica,Acorus calamus,and Ipomoea aquatica systems,the COD removal rates were 80.20%,88.07%,84.70%,and 82.20%,respectively,and the NH_4~+-N removal rates were 49.96%,75.02%,70.25%,and 68.47%,respectively.The decontamination capability of the Canna indica system was better than those of the other systems.The average output voltages were 520±42,715±20,660±27,and 752±26 mV for the unplanted,Canna indica,Acorus calamus,and Ipomoea aquatica systems,respectively,and the maximum power densities were 0.2230,0.4136,0.3614,and0.4964 W/m~3,respectively.Ipomoea aquatica had the largest effect on bioelectricity generation promotion.In addition,electrochemically active bacteria,Geobacter and Desulfuromonas,were detected in the anodic biofilm by high-throughput sequencing analysis,and Comamonas(Proteobacteria),which is widely found in MFCs,was also detected in the anodic biofilm.These results confirmed the important role of plants in IVCW-MFCs.     

Dynamic nano-Ag colloids cytotoxicity to and accumulation by Escherichia coli: Effects of Fe3+, ionic strength and humic acid

Released Ag ions or/and Ag particles are believed to contribute to the cytotoxicity of Ag nanomaterials, and thus, the cytotoxicity and mechanism of Ag nanomaterials should be dynamic in water due to unfixed Ag particle:Ag⁺ ratios. Our recent research found that the cytotoxicity of PVP-Ag nanoparticles is attributable to Ag particles alone in 3 hr bioassays, and shifts to both Ag particles and released Ag⁺ in 48 hr bioassays. Herein, as a continued study, the cytotoxicity and accumulation of 50 and 100 nm Ag colloids in Escherichia coli were determined dynamically. The cytotoxicity and mechanisms of nano-Ag colloids are dynamic throughout exposure and are derived from both Ag ions and particles. Ag accumulation by E. coli is derived mainly from extracellular Ag particles during the initial 12 hr of exposure, and thereafter mainly from intracellular Ag ions. Fe³⁺ accelerates the oxidative dissolution of nano-Ag colloids, which results in decreasing amounts of Ag particles and particle-related toxicity. Na⁺ stabilizes nano-Ag colloids, thereby decreasing the bioavailability of Ag particles and particle-related toxicity. Humic acid (HA) binds Ag⁺ to form Ag⁺-HA, decreasing ion-related toxicity and binding to the E. coli surface, decreasing particle-related toxicity. HA in complex conditions showed a stronger relative contribution to toxicity and accumulation than Na⁺ or Fe³⁺. The results highlighted the cytotoxicity and mechanism of nano-Ag colloids are dynamic and affected by environmental factors, and therefore exposure duration and water chemistry should be seriously considered in environmental and health risk assessments.     

Development of a static test apparatus for evaluating the performance of three PM2.5 separators commonly used in China

PM_(2.5) separator directly affects the accuracy of PM_(2.5) sampling.The specification testing and evaluation for PM_(2.5) separator is particularly important,especially under China's wide variation of terrain and climate.In this study,first a static test apparatus based on polydisperse aerosol was established and calibrated to evaluate the performance of the PM_(2.5) separators.A uniform mixing chamber was developed to make particles mix completely.The aerosol concentration relative standard deviations of three test points at the same horizontal chamber position were less than 0.57%,and the particle size distribution obeyed logarithmic normal distribution with an R~2 of 0.996.The flow rate deviation between the measurement and the set point flow rate agreed to within ± 1.0% in the range of -40 to 50℃.Secondly,the separation,flow and loading characteristics of three cyclone separators(VSCC-A,SCC-A and SCC112) were evaluated using this system.The results showed that the 50% cutoff sizes(D_(50)) of the three cyclones were 2.48,2.47 and 2.44 μm when worked at the manufacturer's recommended flow rates,respectively.The geometric standard deviation(GSD) of the capture efficiency of VSCCA was 1.23,showed a slightly sharper than SCC-A(GSD = 1.27),while the SCC112 did not meet the relevant indicator(GSD = 1.2 ± 0.1) with a GSD = 1.44.The flow rate and loading test had a great effect on D_(50),while the GSD remained almost the same as before.In addition,the maintenance frequency under different air pollution conditions of the cyclones was summarized according to the loading test.     

Cytotoxicity of the soluble and insoluble fractions of atmospheric fine particulate matter

Inhaled atmospheric fine particulate matter(PM_(2.5)) includes soluble and insoluble fractions,and each fraction can interact with cells and cause adverse effects.PM_(2.5) samples were collected in Jinan,China,and the soluble and insoluble fractions were separated.According to physiochemical characterization,the soluble fraction mainly contains watersoluble ions and organic acids,and the insoluble fraction mainly contains kaolinite,calcium carbonate and some organic carbon.The interaction between PM_(2.5) and model cell membranes was examined with a quartz crystal microbalance with dissipation(QCM-D) to quantify PM_(2.5) attachment on membranes and membrane disruption.The cytotoxicity of the total PM_(2.5) and the soluble and insoluble fractions,was investigated.Negatively charged PM_(2.5) can adhere to the positively charged membranes and disrupt them.PM_(2.5)also adheres to negatively charged membranes but does not cause membrane rupture.Therefore,electrostatic repulsion does not prevent PM_(2.5) attachment,but electrostatic attraction induces remarkable membrane rupture.The human lung epithelial cell line A549 was used for cytotoxicity assessment.The detected membrane leakage,cellular swelling and blebbing indicated a cell necrosis process.Moreover,the insoluble PM_(2.5) fraction caused a higher cell mortality and more serious cell membrane damage than the soluble fraction.The levels of reactive oxygen species(ROS) enhanced by the two fractions were not significantly different.The findings provide more information to better understand the mechanism of PM_(2.5) cytotoxicity and the effect of PM_(2.5) solubility on cytotoxicity.     

Density functional theory (DFT) studies of vanadium-titanium based selective catalytic reduction (SCR) catalysts

Based on density functional theory (DFT) and basic structure models, the chemical reactions on the surface of vanadium-titanium based selective catalytic reduction (SCR) denitrification catalysts were summarized. Reasonable structural models (non-periodic and periodic structural models) are the basis of density functional calculations. A periodic structure model was more appropriate to represent the catalyst surface, and its theoretical calculation results were more comparable with the experimental results than a non-periodic model. It is generally believed that the SCR mechanism where NH₃ and NO react to produce N₂ and H₂O follows an Eley-Rideal type mechanism. NH₂NO was found to be an important intermediate in the SCR reaction, with multiple production routes. Simultaneously, the effects of H₂O, SO₂ and metal on SCR catalysts were also summarized.     

Effects of calcination temperature on physicochemical property and activity of CuSO4/TiO2 ammonia-selective catalytic reduction catalysts

CuSO_4/TiO_2 catalysts with high catalytic activity and excellent resistant to SO_2 and H_2 O,were thought to be promising catalysts used in Selective catalytic reduction of nitrogen oxides by NH_3.The performance of catalysts is largely affected by calcination temperature.Here,effects of calcination temperature on physicochemical property and catalytic activity of CuSO_4/TiO_2 catalysts were investigated in depth.Catalyst samples calcined at different temperatures were prepared first and then physicochemical properties of the catalyst were characterized by N2 adsorption-desorption,X-ray diffraction,thermogravimetric analysis,Raman spectra,Fourier-transform infrared spectroscopy,X-ray photoelectron spectroscopy,temperature-pro grammed desorption of NH_3,temperature-programmed reduction of H_2 and in situ diffuse reflectance infrared Fourier transform spectroscopy.Results revealed that high calcination temperature had three main effects on the catalyst.First,sintering and anatase transform into rutile with increase of calcination temperature,causing a decrement of specific surface area.Second,decomposition of CuSO_4 under higher calcination temperature,resulting in disappears of Br(?)nsted acid sites(S-OH),which had an adverse effect on surface acidity.Third,CuO from the decomposition of CuSO_4 changed surface reducibility of the catalyst and favored the process of NH_3 oxidation to nitrogen oxides(NO_x).Thus,catalytic activity of the catalyst calcined under high temperatures(≥600℃) decreased largely.     

Synergistic effects of Cu species and acidity of Cu-ZSM-5 on catalytic performance for selective catalytic oxidation of n-butylamine

In this work, a series of Cu-ZSM-5 catalysts with different SiO₂/Al₂O₃ ratios (25, 50, 100 and 200) were synthesized and investigated in n-butylamine catalytic degradation. The n-butylamine can be completely catalytic degradation at 350°C over all Cu-ZSM-5 catalysts. Moreover, Cu-ZSM-5 (25) exhibited the highest selectivity to N₂, exceeding 90% at 350°C. These samples were investigated in detail by several characterizations to illuminate the dependence of the catalytic performance on redox properties, Cu species, and acidity. The characterization results proved that the redox properties and chemisorption oxygen primarily affect n-butylamine conversion. N₂ selectivity was impacted by the Brønsted acidity and the isolated Cu²⁺ species. Meanwhile, the surface acid sites over Cu-ZSM-5 catalysts could influence the formation of Cu species. Furthermore, in situ diffuse reflectance infrared Fourier transform spectra was adopted to explore the reaction mechanism. The Cu-ZSM-5 catalysts are the most prospective catalysts for nitrogen-containing volatile organic compounds removal, and the results in this study could provide new insights into catalysts design for VOC catalytic oxidation.