Toxic oxide deposits from the combustion of landfill gas and biogas

Oxide deposits found in combustion systems of landfill gas fired power stations contain relatively high concentrations of elements which form volatile species such as P, As, Sb and Sn. These deposits should be handled with care because of their potential toxicity. By contrast, deposits in biogas system engines were found to contain much lower levels of such elements. The enrichment of these elements can be attributed to a hypothetical multistage process. The elements form volatile species in the landfill body. They are selectively transported as part of the landfill gas into the gas-burning devices. Inside the burners, they are immobilized as nonvolatile oxides.     

Sinterability study of ceramic bodies made from a mixture of mineral coal bottom ash and soda-lime glass cullet.

The aim of this study was to investigate the sinterability to improve the technical properties of ceramic bodies made from coal bottom ash and soda-lime glass cullet. Different mixtures of bottom ash and glass cullet were formulated. The amount of bottom ash was 100, 70, 50 and 30 wt.%. The particle size distribution was the same for all formulations. The mixture containing 50 wt.% bottom ash also had its particle size distribution changed. Samples were formed by dry pressing and then fired at 950, 1050 and 1150 degrees C. Samples were evaluated for linear shrinkage, water absorption, flexural mechanical resistance, scanning electronic microscopy, pyroplastic deformation and thermodilatometric analysis. The higher firing temperature led to a decrease in water absorption and increased linear shrinkage, mechanical resistance and pyroplastic deformation. This effect was also observed for addition of glass up to 50 wt.%. The effect of smaller particles of bottom ash was more significant for linear shrinkage and mechanical resistance of ceramic bodies fired at 1150 degrees C. The use of a finer powder contributed to increase these properties. The influence of finer particles on water absorption and mechanical resistance of ceramic bodies fired at 950 and 1050 degrees C was not significant.