Removal of 2-chlorophenol from water using rice-straw derived ash (RSDA) was evaluated in this study to compare with commercial activated carbon. RSDA was obtained by burning rice-straw at 400 °C and 700 °C for 1 h. This ash can provide a better adsorbent for 2-chlorophenol. The adsorption capacities of RSDA at 400 °C and 700 °C are 37 and 52 mg g?1 at pH 4, respectively, and decrease to 9.0 and 40 mg g?1 at pH 10. Adsorption of either neutral or anionic 2-cholorphenol by the RSDA are shown as L-shaped nonlinear isotherms, suggesting surface adsorption rather than partitioning is occurring. At higher-burning temperatures, the surface area, porosity, point of zero charge and aromaticity of the resultant RSDA increase, but the oxygen content and surface acidity decrease. The combined effects result in a higher 2-chlorophenol adsorption of RSDA at 700 °C, which shows a slight pH effect on the adsorption of 2-chlorophenol, due to the lower content of oxygen-containing functional groups. Oxygen-containing functional groups contribute to surface acidity and H-bonding sites for adsorbed water, which compromises the interaction between 2-chlorophenol and the adsorbents. Thus, it suggests that rice-straw derived carbon (RSDC) can be used as an effective low-cost substitute material for activated carbon for removal of chlorophenols from wastewater. 相似文献
A pilot program focusing on municipal solid waste (MSW) source-separated collection was launched in eight major cities throughout China in 2000. Detailed investigations were carried out and a comprehensive system was constructed to evaluate the effects of the eight-year implementation in those cities. This paper provides an overview of different methods of collection, transportation, and treatment of MSW in the eight cities; as well as making a comparative analysis of MSW source-separated collection in China. Information about the quantity and composition of MSW shows that the characteristics of MSW are similar, which are low calorific value, high moisture content and high proportion of organisms. Differences which exist among the eight cities in municipal solid waste management (MSWM) are presented in this paper. Only Beijing and Shanghai demonstrated a relatively effective result in the implementation of MSW source-separated collection. While the six remaining cities result in poor performance. Considering the current status of MSWM, source-separated collection should be a key priority. Thus, a wider range of cities should participate in this program instead of merely the eight pilot cities. It is evident that an integrated MSWM system is urgently needed. Kitchen waste and recyclables are encouraged to be separated at the source. Stakeholders involved play an important role in MSWM, thus their responsibilities should be clearly identified. Improvement in legislation, coordination mechanisms and public education are problematic issues that need to be addressed. 相似文献
Currently, activated coke is widely used in the removal of multiple pollutants from industrial flue gas. In this paper, a series of novel FexLayOz/AC catalysts was prepared by the incipient wetness impregnation for NH3-SCR denitrification reaction. The introduction of Fe-La bimetal oxides significantly improved the denitrification performance of activated coke at mid-high temperature, and 4% Fe0.3La0.7O1.5/AC exhibited a superior NOx conversion efficiency of 90.1% at 400 °C. The catalysts were further characterized by BET, SEM, XRD, Raman, EPR, XPS, FTIR, NH3-TPD, H2-TPR, et al., whose results showed that the perovskite-type oxide of LaFeO3 and oxygen vacancies were produced on the catalysts’ surfaces during roasting. Fe-La doping enhanced the amount of acid sites (mainly Lewis and other stronger acid sites) and the content of multifarious oxygen species, which were beneficial for NOx removal at mid-high temperature. Moreover, it was investigated that the effect of released CO from activated coke at mid-high temperature on the NOx removal through the lifetime test, in which it was found that a large amount of CO produced by pyrolysis of activated coke could promote the NOx removal, and long-term escaping of CO on the activated coke carrier did not have a significant negative impact on catalytic performance. The results of the TG-IR test showed that volatile matter is released from the activated coke while TG results showed that the weight loss rate of 4% Fe0.3La0.7O1.5/AC only was 0.0015~0.007%/min at 300–400 °C. Hence, 4% Fe0.3La0.7O1.5/AC had excellent thermal stability and denitrification performance to be continuously used at mid-high temperature. Finally, the mechanisms were proposed on the basis of experiments and characterization results.