Incinerating Volatile Organic Compounds with Ferrospinel Catalyst MnFe2O4: An Example with Isopropyl Alcohol

Abstract

This paper concerns the incineration of isopropyl alcohol (IPA) using the ferrospinel catalyst MnFe₂O₄. It covers the preparation of the ferrospinel catalyst, the screening of catalytic activity, catalytic incineration testing, and 72-hr decay testing of the catalyst. The experimental results of catalyst screening reveal that the Mn/Fe catalyst is the best of five prepared catalysts (chromium/iron [Cr/Fe], manganese/iron [Mn/Fe], zinc/iron [Zn/Fe], nickel/iron [Ni/Fe], and pure magnetite [Fe₃O₄]). In tests of the catalytic incineration system used to convert IPA, 98% conversion was obtained at a space velocity of 24,000 hr^?1, an oxygen (O₂) content of 21%, 1700 ppm of IPA, and a reaction temperature of 200 °C.     

CdSe量子点的合成及其在重金属离子检测中的应用

以3-巯基丙酸（3-MPA）为修饰剂合成了水溶性CdSe量子点,优化了合成条件,并以其为荧光探针建立了水样中Pb²⁺和Hg²⁺的检测方法。实验结果表明：在n（Se）∶n（Cd²⁺）为1∶6、n（Se）∶n（NaBH₄）为1∶3、n（Cd²⁺）∶n（3-MPA）为1∶6、反应pH为11、回流温度为100 ℃、回流时间为60 min的优化条件下合成的量子点荧光性能较优;量子点的荧光猝灭强度与Pb²⁺或Hg²⁺的质量浓度呈良好的线性关系,线性范围分别为0.005~10 mg/L和0.001~1 mg/L,检出限分别为0.003 mg/L和0.001 mg/L,相对标准偏差分别为1.23%和1.29%,可应用于实际水样中Pb²⁺和Hg²⁺的检测。     

次氯酸钠废液活化法制备柚子皮活性炭

以柚子皮为原料,采用次氯酸钠废液活化法制备了柚子皮活性炭,通过正交实验优化了制备条件,并运用SEM、FTIR和XRD技术对活性炭产品进行了表征。实验结果表明:制备柚子皮活性炭的最佳工艺条件为炭化温度350℃、次氯酸钠废液含量25%(φ)、次氯酸钠废液活化时间25 min、高温活化温度650℃、高温活化时间60 min;最佳条件下,柚子皮活性炭的产率为31.88%、碘吸附值为854 mg/g、亚甲基蓝吸附值为216.9 mg/g。表征结果显示:活化后的柚子皮炭具有更大的孔体积、更有序的孔径排布和更发达的孔隙结构;柚子皮活性炭表面存在大量的含氧基团;柚子皮活性炭的石墨化度为61.32%,具有较高的稳定性。     

Removal of arsenic from aqueous solution by two types of nano TiO2 crystals

Titanium dioxide (TiO₂) is a promising sorbent for As removal. There are two main and physico-chemically distinct polymorphs of TiO₂ in nature, namely anatase and rutile. Since the difference of arsenic removal by the two polymorphs of TiO₂ is now well known, study on the arsenic removal efficiency and the underlying mechanism is of great significance in developing new remediation strategies for As-polluted waters. Here batch experiments were carried out in combination with instrumental analysis of X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), and X-ray photoelectron spectroscopy (XPS) to investigate the effects, influential factors and mechanisms of As removal from aqueous solution by two types of nano TiO₂ crystals. The adsorption behavior of anatase and rutile for As(V) and As(III) are well described by Freundlich equations. Anatase had higher As removal efficiency and adsorption capacity than rutile. Solution pH had no influence on the As adsorption of anatase TiO₂, whereas the As removal by rutile TiO₂ was increased by 7?C18% with pH from 4 to 10. Presence of accompanying anions such as phosphate, silicate, nitrate and sulfate, decreased the As(V) and As(III) removal by both crystals, with phosphate being the most effective. However, removal of As by rutile TiO₂ was greatly enhanced in the presence of divalent cations i.e. Ca²⁺ and Mg²⁺. Shading of light decreased the removal of As(V) and As(III) of anatase by 15.5% and 17.5%, respectively, while a slight increase of As removal was observed in the case of Rutile TiO₂. FT-IR characterization of As(V) or As(III)-treated nano TiO₂ crystals indicated that both Ti-O and As-O groups participated in As adsorption. Both FT-IR and XPS analysis demonstrated that As(III) was photooxidated into As(V) when adsorbed by anatase under the light condition. Thus, the effect of crystal types and light condition on As removal should be taken into consideration when nano TiO₂ is applied for As removal from water.     

Comparative investigation of toxicity induced by UV-A and UV-C radiation using Allium test

Organisms are increasingly exposed to ultraviolet (UV) rays of sunlight, due to the thinning of the ozone layer and its widespread use in sterilization processes, especially against the SARS-CoV-2 virus. The present study was conducted with the purpose of evaluating the damages of UV-A and UV-C radiations in Allium cepa L. roots. The effects of two different types of UV on some physiological, biochemical, cytogenotoxic, and anatomical parameters were investigated in a multifaceted study. Three groups were formed from Allium bulbs, one of which was the control group. One of the other groups was exposed to 254 nm (UV-C) and the other to 365 nm (UV-A) UV. Growth retardation effect of UV was investigated with respect to germination percentage, total weight gain, and root elongation, while cytogenotoxicity arisen from UV exposure was analyzed using mitotic index (MI) and chromosomal aberration (CA) and micronucleus (MN) frequency. Oxidative stress due to UV application was investigated based on the accumulation of malondialdehyde (MDA) and the total activities of superoxide dismutase (SOD) and catalase (CAT) enzymes. Also, anatomical changes induced by UV-A and UV-C were analyzed in root meristematic cells. UV treatments caused significant reductions in growth-related parameters. Both UV treatments caused a significant increase in MDA levels and induction of SOD and CAT enzymes in root meristematic cells. A decrease in MI and an increase in the frequency of MN and CAs were observed in root tip cells, indicating the cytogenotoxic effect of UV application. Anatomical damages such as epidermis cell damage, cortex cell damage, necrotic zones, giant cell nucleus, and indistinct transmission tissue occurred in cells exposed to UV. All of the physiological, biochemical, cytogenetic, and anatomical damages observed in this study were more severe in cells treated with UV-C compared to UV-A. This study suggested that UV exposure triggered growth inhibition, cytogenotoxicity, oxidative stress, and meristematic cell damages in A. cepa roots depending on the wavelength.

     

Impact of Urban Sprawl on Water Quality in Eastern Massachusetts,USA

A study of water quality, land use, and population variations over the past three decades was conducted in eastern Massachusetts to examine the impact of urban sprawl on water quality using geographic information system and statistical analyses. Since 1970, eastern Massachusetts has experienced pronounced urban sprawl, which has a substantial impact on water quality. High spatial correlations are found between water quality indicators (especially specific conductance, dissolved ions, including Ca, Mg, Na, and Cl, and dissolved solid) and urban sprawl indicators. Urbanized watersheds with high population density, high percentage of developed land use, and low per capita developed land use tended to have high concentrations of water pollutants. The impact of urban sprawl also shows clear spatial difference between suburban areas and central cities: The central cities experienced lower increases over time in specific conductance concentration, compared to suburban and rural areas. The impact of urban sprawl on water quality is attributed to the combined effects of population and land-use change. Per capita developed land use is a very important indicator for studying the impact of urban sprawl and improving land use and watershed management, because inclusion of this indicator can better explain the temporal and spatial variations of more water quality parameters than using individual land use or/and population density.     

自制悬浮物过滤器及其在悬浮物测定中的应用

本文自制悬浮物过滤器，并提出了一种简便的悬浮物标准样品的制备方法。地表水滤液的吸光度值表明，自制悬浮物过滤器藏留悬浮物效果令人满意。该法加标回收率为95．4％～106．8％，检出限为3．2mg／L。尤其适合于强酸、强碱和强氧化性废水中悬浮物的测定。     

气田水处理药剂的筛选及应用

为了确保气田水水质处理效果,除正确选择水处理工艺和装置外,还必须选择相应的化学处理药剂。针对川东气田水水质状况,对多种絮凝剂进行了评价和筛选室内实验。综合考虑5种药剂性能和价格,无机絮凝剂选择TSY4-1效果较好;综合考虑5种处理方法的效果和药剂价格,选择TSY4-2有机絮凝剂作有机浮选剂效果较好。为验证室内实验结果,在川东气田池34井和卧20井气田水处理站分别进行了现场应用实验。结果表明筛选的组合配方药剂完全能够替代进口水处理药剂,能满足川东气田水水质处理的需要。     

Incinerating volatile organic compounds with ferrospinel catalyst MnFe2O4: an example with isopropyl alcohol

This paper concerns the incineration of isopropyl alcohol (IPA) using the ferrospinel catalyst MnFe2O4. It covers the preparation of the ferrospinel catalyst, the screening of catalytic activity, catalytic incineration testing, and 72-hr decay testing of the catalyst. The experimental results of catalyst screening reveal that the Mn/Fe catalyst is the best of five prepared catalysts (chromium/iron [Cr/Fe], manganese/iron [Mn/Fe], zinc/iron [Zn/Fe], nickel/iron [Ni/Fe], and pure magnetite [Fe3O4]). In tests of the catalytic incineration system used to convert IPA, 98% conversion was obtained at a space velocity of 24,000 hr(-1), an oxygen (O2) content of 21%, 1700 ppm of IPA, and a reaction temperature of 200 degrees C.