Effect of transition metal doping under reducing calcination atmosphere on photocatalytic property of TiO2 immobilized on SiO2 beads

TiO₂ immobilized on SiO₂ (TiO₂/SiO₂) have been prepared by sol-gel method and various ions of transition metals (Cr³⁺, Co²⁺, Ni²⁺, Cu²⁺, and Zn²⁺) were doped on the photocatalyst using wet impregnation method under reducing calcination atmosphere. The photocatalytic activity of metal doped TiO₂/SiO₂ towards phenol degradation under black light irradiation were investigated and compared with undoped TiO₂/SiO₂. The results showed that the photoresponse of Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂ were larger than undoped TiO₂/SiO₂, indicating that the photogenerated carriers were separated more efficiently in Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂. The reactivity was in the order of Cu²⁺ > Zn²⁺ > Ni²⁺ > Cr³⁺ > Co²⁺. The different photoreactivity was ascribed to combine effect of the different ionic radii and photocorrison tendency of the dopants. The sample was also characterized by surface analytical methods such as X-ray diffraction, scanning electron micrograph/electron dispersive X-ray analyzer and UV-Vis absorption spectrum.     

Enhanced photocatalytic activity of quantum-dot-sensitized one-dimensionally-ordered ZnO nanorod photocatalyst

An efficient photocatalyst was fabricated by assembling quantum dots （QDs） onto one-dimensionally-ordered ZnO nanorods, and the photocatalytic properties for Methyl Orange degradation were investigated by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, UV-Vis-NIR absorption spectroscopy and photoluminescence. The results indicate that the catalyst with assembled QDs is more favorable for the degradation than the pristine ZnO nanorods. The QDs with core-shell structure lower the photocatalytic ability due to the higher carder transport barrier of the ZnS shell layer. Besides its degradation efficiency, the photocatalyst has several advantages given that the one-dimensionally-ordered ZnO nanorods have been grown directly on indium tin oxide substrates. The article provides a new method to design an effective and easily recyclable photocatalyst.     

Waste oyster shell as a kind of active filler to treat the combined wastewater at an estuary

Estuaries have been described as one of the most difficult environments on Earth. It is difficult to know how to treat the combined wastewater in tidal rivers at the estuary, where the situation is very different from ordinary fresh water rivers. Waste oyster shell was used as the active filler in this study in a bio-contact oxidation tank to treat the combined wastewater at the Fengtang Tidal River. With a middle-experimental scale of 360 ma/day, the average removal efficiency of COD, BOD, NH3-N, TP and TSS was 80.05%, 85.02%, 86.59%, 50.58% and 85.32%, respectively, in this bio-contact oxidation process. The living microbes in the biofilms on the waste oyster shell in this bio-contact oxidation tank, which were mainly composed of zoogloea, protozoa and micro-metazoa species, revealed that waste oyster shell as the filler was suitable material for combined wastewater degradation. This treatment method using waste oyster shell as active filler was then applied in a mangrove demonstration area for water quality improvement near the experiment area, with a treatment volume of 5 × 10^3 m^3/day. Another project was also successfully applied in a constructed wetland, with a wastewater treatment volume of 1 ×10^3 m^3/day. This technology is therefore feasible and can easily be applied on a larger scale,     

磁性多孔陶粒生物膜反应器处理焦化废水的试验研究

以磁性材料为原料,经过特定的工艺处理,对多孔陶瓷进行磁化改性获得磁性多孔载体,并将该载体应用于生物膜反应器中进行焦化废水处理试验。对不同类型的多孔陶粒载体进行对比试验,结果表明:磁性载体生物膜反应器对COD、NH3-N的去除率比普通活性污泥法高出25%³0%,比非载体生物膜反应器高出15%30%,比非载体生物膜反应器高出15%²0%左右。反应器的曝气量为1.5 L/h,曝气时间为10 h/d,温度为2520%左右。反应器的曝气量为1.5 L/h,曝气时间为10 h/d,温度为25³0℃。焦化废水经磁性载体生物膜反应器处理后,上清液中COD,NH3-N的去除率均在90%左右。出水浓度达到国家工业废水排放二级标准(GB18918-2002)。     

纳米Fe_3O_4/膨润土的制备、表征及光催化降解焦化废水

以铝柱撑膨润土负载纳米Fe_3O_4制备出性能良好的复合型催化剂。结合X射线粉末衍射(XRD)、扫描电镜(SEM)和比表面孔隙分析(BET)对催化剂的晶相、比表面积和粒度进行表征。负载的纳米Fe_3O_4粒径约为20～30nm,均匀分散到膨润土表面,未发生明显的团聚。在紫外光作用下用该催化剂对焦化厂二沉池出水进行深度处理。结果表明,在催化剂投加量为0.7 g/L,pH为2.5,温度40℃,H_2O_2初始浓度为17.6mmol/L的反应条件下,二沉池出水(化学需氧量COD=140mg/L,色度=400度)经催化氧化降解后,COD和色度可分别降低到54.44 mg/L和10度,达到国家工业再生用水水质标准GB/T 19923-2005(COD≤60 mg/L,色度≤30度)。催化剂重复使用4次时,废水COD和色度去除率保持稳定。     

磁性纳米Fe_3O_4对毒死蜱的增效和催化降解研究

应用溶剂热法制备了磁性纳米Fe3O4(NMFO),并用聚乙二醇-6000对其进行改性,使纳米Fe3O4表面由亲水性转变为亲脂性,从而实现与亲脂性毒死蜱的复合。纳米Fe3O4的加入使毒死蜱的生物活性明显提高。室内毒力试验结果表明:含0.2%纳米Fe3O4的Fe3O4/毒死蜱制剂的毒力在室内和紫外光照下分别是同浓度纯毒死蜱的3.84倍和4.17倍;其降解率也显著提高,纳米Fe3O4/毒死蜱制剂在太阳光照下放置10 d,其降解率可达93.2%,相同条件下纯毒死蜱的降解率是10.14%,而将添加或未添加纳米Fe3O4的毒死蜱于暗处放置相同的时间,其降解率分别为1.21%和0.23%。     

活性焦烟气脱硫技术在大型燃煤电站的应用

本文通过分析活性焦烟气脱硫技术的主要原理、工艺流程、主要原料消耗、脱硫副产品综合利用、SO2污染物达标情况,探讨该技术在内蒙古地区大型燃煤电站脱硫工程应用的可行性.     

UV-Fenton体系处理活性黑KNB染料废水的实验研究

采用UV-Fenton体系处理活性黑KNB染料废水.研究了pH值、H2O2和FeSO4用量、反应温度和反应时间等对染料废水脱色率的影响.实验结果表明,当KNB的初始浓度为50mg/L时,在t=25℃、pH =5.4、[H2O2]=0.2ml/L,[FeSO4]=0.7mmol/L,使用30W的紫外灯光照射条件,反应1小时后,KNB染料废水脱色率几乎可达100％.通过比较反应前后染料废水的UV-Vis吸收光谱,初步探讨了KNB的降解机理.研究表明,UV-Fenton体系可以有效地处理活性黑KNB染料废水,为该工艺处理实际染料废水提供基础数据.     

酞菁-二氧化钛光催化剂的制备及其光催化降解效果

采用溶胶-凝胶法制备酞菁-TiO2光催化剂,并分别掺杂铁、铜、钴、镍元素。酞菁作为光敏化剂,提高TiO2在可见光下对有机染料的降解效果。采用SEM对催化剂进行表征,研究在可见光下酞菁-TiO2光催化剂对5种有机染料(甲基橙、甲基红、甲酚紫、亚甲基蓝和孔雀石绿)的降解效果,结果表明,酞菁铁-TiO2,酞菁钴-TiO2,酞菁铜-TiO2,酞菁镍-TiO2均能有效降解这几种有机染料,光催化反应300 min后降解率达92%。比较4种催化剂对甲基橙的降解率,酞菁钴-TiO2催化剂降解效果最明显,以下是酞菁铁、酞菁镍和酞菁铜-TiO2催化剂。     

土地利用变化对土壤硝化及氨氧化细菌区系的影响

以西藏高原相邻的原始森林、天然草原和农田土壤为研究对象,分别采用室内培养法和nested PCR-DGGE技术,对比研究了这3个生态系统的土壤硝化势、硝态氮浓度以及土壤氨氧化细菌（AOB）菌群区系.结果表明,农田土壤的硝化势和硝态氮（NO 3--N）浓度显著高于相邻的草原和森林土壤,硝化势分别是森林和草原土壤的9倍和11倍,NO 3--N是农田土壤无机氮（Nmin）的主要成分,占无机氮的70%～90%.铵态氮（NH 4＋-N）则是森林和草原土壤中主要的无机氮形态.原始森林和天然草原间的硝化势和硝态氮浓度没有显著差异.原始森林的土壤AOB菌群数量、多样性及均匀度最低.天然草原生态系统转换为农田后,土壤AOB菌群的多样性和均匀度显著降低,但是农田土壤的AOB菌群结构仍与其前身草原生态系统有较高的相似性.原始森林的AOB菌群数量、多样性及均匀度最低直接导致了其硝化势最低;农田土壤的硝化势和硝态氮浓度最高意味着农田生态系统中优势AOB的活性最高.以上结果表明,土地利用变化导致土壤氮素内循环及其关键微生物AOB的多样性与活性均发生显著变化,这些变化会影响土壤环境质量以及生态系统的持续与稳定.