2024铝合金连接结构两种防护涂层耐蚀性研究

目的研究铝合金两种防护涂层在5%NaCl盐雾环境下的腐蚀疲劳性能。方法针对在两种涂层防护作用下的2024铝合金连接结构,开展实验室加速试验,采用"腐蚀环境-疲劳加载"交替循环的试验模式,得到铝合金两种防护涂层在5%NaCl盐雾环境下的腐蚀疲劳寿命值,对比分析涂层体系对铝合金连接结构的腐蚀疲劳寿命影响。结果 5%NaCl盐雾环境对于铝合金连接结构疲劳寿命有较大影响,相较于传统涂层,纳米涂层在5%NaCl盐雾环境下的防护效果更好。结论纳米涂层表面破坏后快速生成的致密氧化膜能有效提高涂层的耐蚀性能。     

两种新型涂铁改性砂的过滤性能及反冲洗条件研究

以两种新型涂铁改性石英砂(纳米氧化铁改性砂,Nano-OCS;氧化铁改性砂,IOCS)及普通石英砂(RQS)为研究对象,考察了两种新型改性砂对沉后水腐殖酸及浊度的直接过滤效果,对其反冲洗条件进行优化研究,并对3种滤料的过滤效果进行了比较.结果表明,1滤层厚度为45 cm时,最佳滤速为6 m·h-1;3种滤料对腐殖酸和浊度的直接过滤效果依次为:Nano-OCSIOCSRQS,其中两种涂铁砂对腐殖酸的去除率分别为71.70%和61.61%;2Nano-OCS和IOCS滤柱的反冲洗流程分4步,对应的流程及最佳操作条件为:首先,用0.5 mol·L-1NaOH的溶液浸泡,气冲强度13 L·s-1·m-2,气冲时间6 min;然后,用0.075 mol·L-1的NaOH溶液与空气同时反冲洗,NaOH溶液冲洗强度为8 L·s-1·m-2,气冲强度13 L·s-1·m-2,冲洗时间3 min;接着用0.015 mol·L-1的FeCl3溶液与空气同时反冲洗,FeCl3溶液冲洗强度为8 L·s-1·m-2,气冲强度13L·s-1·m-2,冲洗时间2 min;最后,用清水冲洗,冲洗强度8 L·s-1·m-2,冲洗时间4 min.两种涂铁砂反冲洗前后表面形态结构更加复杂、粗糙度增加,对腐殖酸去除率进一步提高.3当滤层厚度由45 cm增加到80 cm时,Nano-OCS对腐殖酸直接过滤的最高去除率由74.6%提高至80.3%,平均去除率由57.9%提高至68.5%.     

新型聚乙烯包装材料的可环境消纳性能研究

借助人工加速老化实验箱、户外暴晒架、自然土壤填埋坑等实验方法，采用力学性能测试、扫描电镜、热－红联用仪和乌氏粘度计等测试方法对所研制的新型聚乙烯（PE）塑料包装材料的可环境消纳性能进行探讨。实验结果表明，该材料自然暴露35d，羰基指数（CI）为45，光照10d后自然土壤掩埋，一年后CI为70，粘均分子质量Mη降到3678；生物降解性能达到3级；进行焚烧处理，尤其是在受光照后进行焚烧，可完全燃烧，不产生有害气体或粉尘。     

浸没式双轴旋转厌氧膜生物反应器处理啤酒废水试验

研究了新型浸没式双轴旋转厌氧膜生物反应器(SDRAnMBR)处理模拟啤酒废水的运行性能.研究结果表明,SDRAnMBR对啤酒废水有较好的处理效果,处理过程负荷提高快,有机物去除率高,系统耐冲击负荷的能力强,而且运行非常稳定.正常运行期间,进水COD在2900～5200mg·L-1,容积负荷为4.97～12.48kg·m-·3d-1(以COD计)时,COD的平均去除率为95.15%.膜截留和三相旋转流的共同作用,加强了在高污泥浓度(MLSS)和高负荷条件下运行时的混合和传质,从而强化了SDRAnMBR在高MLSS和高容积负荷下运行的稳定性和出水水质.     

烟台市环境受体PM2.5四季污染特征与来源解析

于2016～2017年四季在烟台市3个点位采集了PM_(2.5)样品,分析了其质量浓度和化学组分特征.利用CMB模型对受体进行解析,并利用后向轨迹和PSCF对传输气流和潜在源区进行了分析.结果表明,烟台市监测点位冬季、春季、夏季和秋季的PM_(2.5)平均质量浓度分别为(89. 45±56. 80)、(76. 78±28. 44)、(32. 65±17. 92)和(57. 32±24. 60)μg·m~(-3). PM_(2.5)浓度表现出明显的季节变化特征(P 0. 01).全年PM_(2.5)各源类分担率大小依次为:二次硝酸盐源(20. 3%)城市扬尘源(15. 7%)机动车排放源(14. 9%)燃煤源(13. 8%)二次硫酸盐源(12. 8%) SOC(6. 1%)建筑水泥尘源(5. 5%)海盐源(2. 9%),可以看到烟台市以二次源、扬尘、机动车排放源和燃煤源为主要污染源.春季硝酸盐源和城市扬尘源是重要贡献源类,夏季硫酸盐源贡献突出,燃煤源在秋冬季占比突出.烟台市气流输送和潜在源区也呈现出明显的季节变化:冬季主要受烟台市短距离输送的影响;夏季主要受烟台东部沿海和本地的影响;春秋季主要受山东东北部和东部沿海地区的区域传输和烟台市本地源的影响.     

A restoration-promoting integrated floating bed and its experimental performance in eutrophication remediation

Numerous studies on eutrophication remediation have mainly focused on purifying water first, then restoring submerged macrophytes. A restoration-promoting integrated floating bed （RPIFB） was designed to combine the processes of water purification and macrophyte restoration simultaneously. Two outdoor experiments were conducted to evaluate the ecological functions of the RP1FB. Trial 1 was conducted to compare the eutrophication purification among floating bed, gradual-submerging bed （GSB） and RPIFB technologies. The results illustrated that RPIFB has the best purification capacity. Removal efficiencies of RPIFB for TN, TP,NH4＋-N, NO3-N, CODcr, Chlorophyll-a and turbidity were 74.45%, 98.31%, 74.71%, 88.81%, 71.42%, 90.17% and 85%, respectively. In trial 2, influences of depth of GSB and photic area in RPIFB on biota were investigated. When the depth of GSB decreased and the photic area of RPIFB grew, the height of Potamogeton crispus Linn. increased, but the biomass of Canna indica Linn. was reduced. The mortalities of Misgurnus anguillicaudatus and Bellamya aeruginosa in each group were all less than 7%. All results indicated that when the RPIFB was embedded into the eutrophic water, the regime shift from phytoplankton-dominated to macrophyte-dominated state could be promoted. Thus, the RPIFB is a promising remediation technology for eutrophication and submerged macrophyte restoration.     

高温好氧反硝化菌的分离鉴定及其反硝化性能研究

通过高温筛选,从燃煤电厂生物滴滤系统填料的生物膜上分离出1株高效好氧反硝化细菌TAD1.该菌株革兰氏染色呈阴性,短杆状,大小为(0.67～0.89)μm×(1.03～1.41)μm;经生理生化特性和基于16S rDNA序列分析,初步鉴定该菌为螯台球菌属(Chelatococcus 8p.).对菌株TAD1的反硝化性能进...     

市政污泥脱水性能实验研究与形态学分析

本研究将运用微波技术与离心脱水相结合的方法来达到促进污泥中结合水释放及改善脱水特性的目的.通过测定毛细吸水时间、黏度、含水率,采集污泥图像、提取形态学特征进行污泥脱水改性的效果分析及分形维数的分析.离心脱水实验结果表明,适当增加离心转速和温度时,污泥的含水率降低;正交实验结果表明微波功率1000W、微波温度50℃、离心转速2000r/min、离心时间15min的条件下含水率最低达到83.75%,且适当的微波预处理条件有利于污泥的脱水;微波预处理后污泥分形维数在2.4~2.8之间,污泥结构改变.对污泥脱水性能的表征参数与污泥含水率进行拟合,建立污泥脱水性能的模型,为预测和改善污泥脱水性能提供基础性研究.     

固定源可凝结颗粒物稀释采样器的设计

固定污染源烟气排放进入大气环境后稀释降温,气相中部分饱和蒸气压较低的组分转化为可凝结颗粒物,这部分颗粒物在固定源烟气颗粒物监测中通常被忽略.为评价固定源可凝结颗粒物的排放情况,本文设计开发并评测了一套稀释采样器.稀释采样器稀释比在10：1~40：1范围内,混合停留时间为5~10 s.实验室评测结果表明,稀释气颗粒物背景值低（（~0.1±0.08） 个·cm^-3）,稀释采样器气密性良好,烟气和稀释气能够均匀混合,颗粒物损失较少,细颗粒物 （PM_2.5）损失在5%以下.本稀释采样器能模拟烟气与环境空气混合降温过程,可用于固定源可凝结颗粒物的测量.     

双循环多级水幕脱硫塔的设计和性能测试

双循环多级水幕脱硫塔是在常规两段式湿法脱硫塔基础上加以改进而成的新型脱硫塔,其双循环浆液采用不同pH控制,低pH促进CaCO2溶解,高pH提高SO2吸收效果;同时,多级水幕强化气液流态,增加气液接触面积和传质动力,促进对SO2的吸收.实验利用SPSSV13.0软件进行正交实验设计,通过数据分析得出两个不同的优化运行方案,再利用多指标分析法中的综合平衡法进行单因素实验,得出最优运行方案.在最优运行方案条件下,即烟气流量为100 m3/h,上循环浆液pH为6.0,下循环浆液pH为4.8,上、下循环液气比均为20 L/m3,人口 SO2质量浓度为1 000mg/m3时,脱硫效率达97.8%,CaCO3利用率为95.2%,钙硫质量比约为1.03.双循环多级水幕脱硫塔具有良好的应用前景,实验结果对现场脱硫系统的调试和运行有很好的参考价值.