Sulfur poisoning of V_2O_5/BaSO_4–TiO_2(VBT),V_2O_5/WO_3–TiO_2(VWT) and V_2O_5/BaSO_4–WO_3–TiO_2(VBWT) catalysts was performed in wet air at 350℃ for 3 hr,and activities for the selective catalytic reduction of NO_x with NH_3 were evaluated for 200–500℃.The VBT catalyst showed higher NO_x conversions after sulfur poisoning than the other two catalysts.The introduction of barium sulfate contributed to strong acid sites for the as-received catalyst,and eliminated the redox cycle of active vanadium oxide to some extent,which resulted in a certain loss of activity.Readily decomposable sulfate species formed on VBT-S instead of inactive sulfates on VWT-S.These decomposable sulfates increased the number of strong acid sites significantly.Some sulfate species escaped during catalyst preparation and barium sulfate was reproduced during sulfur poisoning,which protects vanadia from sulfur oxide attachment to a great extent.Consequently,the VBT catalyst exhibited the best resistance to sulfur poisoning.     

一种低功耗高性能数据采集数字处理平台的设计

目的构建一套基于中频信号基带数字信号处理的软件无线电平台。方法通过选择芯片设计硬件电路设计出合适的PCB板。结果主要依据软件无线电平台,提出了一种基于A/D+FPGA+D/A的硬件设计方案,该系统包括了前端的A/D数据采集和后端的D/A模拟数据恢复的详细收发电路原理设计。结论构建了一个从前端数据接收到后端模拟发送的高速基带数字信号处理平台。     

某城市污水处理厂二期污水处理工程设计研究

详细介绍了某城市第一污水处理厂在现有工程的基础上二期工程的工艺设计以及构筑物、设备参数;二期工程充分利用原有工程场地,本着现有、新建运行管理便捷统一原则,采用改良型A/A/O生化池作为二级处理主体工艺;二期工程投入运营后,某城市污水处理厂达到20×104 m3/d的污水设计规模.最终污水厂出水水质达到了《城镇污水处理厂污染物排放标准》(GB 18918-2002)一级 A排放标准.污水处理厂运营后,经济效益显著,可保本经营,并具有企业自我发展的能力.     

石墨烯复合材料在水处理中的应用研究

新型碳材料石墨烯,因其比表面积大,物理、化学特性优异,通常作为吸附剂或复合材料载体,用于难降解有机废水处理.载体石墨烯改性后,可优化复合材料性能,包括溶解性和可控性.基于复合材料制备,选取典型污染物废水,如染料废水、苯酚废水、农药废水,从吸附处理和催化降解两方面展开,简要介绍石墨烯复合材料的应用研究及作用效果,显示出复合材料可有效提高污染物降解效率,回用效果好.此外,石墨烯复合材料在回用及实际应用方面仍有待进一步研究.     

间歇曝气SBR与传统SBR处理养猪沼液的比较研究

采用间歇曝气序批式反应器(intermittently aerated sequencing batch reactor,IASBR)和传统序批式反应器(SBR)处理养猪沼液,研究进水中化学需氧量(COD)与总氮(TN)比值(COD/TN)和运行负荷对污染物去除效果的影响.结果表明,在进水COD/TN约为2.2、氨氮负荷为(0.12±0.04)kg·(m3·d)-1时,IASBR中的氨氮、TN和有机物去除率分别为97.2%±4.4%、81.5%±7.5%、88.5%±2.4%,优于SBR的78.3%±19.6%、79.8%±4.9%、86.6%±3.2%;当氨氮负荷提高至(0.18±0.02)kg·(m3·d)-1时,IASBR中的氨氮、TN和有机物去除率略有降低,分别为92.4%±7.3%、77.5%±5.3%、86.4%±2.2%,但仍然优于SBR中的相应去除率78.1%±15.4%、61.8%±11.2%、81.8%±5.6%.在氨氮负荷为(0.20±0.01)kg·(m3·d)-1下,提高进水COD/TN至约3.0,则IASBR和SBR的污染物去除能力较进水COD/TN为2.2时有显著提升,IASBR中氨氮、TN和有机物去除率分别达到99.6%±0.2%、91.5%±2.9%和92.0%±0.9%,仍然高于SBR的90.2%±1.4%、83.0%±1.9%、90.2%±0.5%.总体而言,相较SBR,IASBR对TN和氨氮的去除更高效、耐冲击负荷能力更强,因此对养猪沼液等低碳氮比的废水更为适用.     

凤眼莲对富营养化水体中氨氧化和反硝化微生物的影响

凤眼莲近年来广泛应用于富营养化淡水湖泊的生态修复中,但其对微生物的相互作用和对水体中氮素的去除鲜有报道.本研究在氮素去除过程中对比凤眼莲和细菌的相对重要性,并且检测浮游植物对硝化细菌和反硝化细菌相对丰度及多样性的影响.水体中氮素的去除率以及硝化和反硝化作用的潜在能力使用定量聚合酶链式反应(qPCRs)对硝化作用基因amoA和反硝化作用基因nirS/K进行检测,从微观角度研究富营养化水体中是否会受到凤眼莲存在的影响.结果表明,TN的减少在70d的实验周期中所有处理组表现较为一致,但凤眼莲存在的实验组在24h内TN和NH_4~+-N的去除上有显著的降低,并且amoA的丰度有所增加,nirS/K的丰度有所降低.T-RFLP结果表明亚硝化单胞菌在氨氧化微生物中占优势.凤眼莲的种植可以实现富营养化水体中NH_4~+-N的快速有效减少,且微生物的相互作用可以充分利用到淡水生态系统的修复中.     

Ag-AgI/CN/MA复合物的制备及其可见光催化性能

采用沉淀法和热聚合法分别将AgI、氮化碳(CN)负载在介孔γ-Al_2O_3(MA)上,并通过光还原银离子成功制备了等离子体诱导可见光催化剂Ag-AgI/CN/MA.利用X射线衍射(XRD)、X射线光电子能谱(XPS)、场发射扫描电子显微镜(FESEM)、紫外可见漫反射光谱(UV-vis DRS)和透射电子显微镜(TEM)对Ag-AgI/CN/MA复合材料进行表征,并对其在可见光照射下(λ420 nm)的光催化性能进行了研究,考察了初始溶液pH值及催化剂投加量等条件对光催化反应的影响.结果表明,表面银以Ag+和Ag0形式共存,并且Ag和AgI均匀地分散在CN的表面.与CN和Ag-AgI/MA相比,Ag-AgI/CN/MA复合物对甲基橙(MO)具有更高的可见光催化降解效率,且反应过程中Ag+的释放量显著减少,显示出良好的稳定性.当溶液pH值为7、催化剂投加量为1 g·L~(-1)时,Ag-AgI/CN/MA-2显示出最优的催化性能.同时,其对罗丹明B(Rh B)、甲基红(MR)和刚果红(CR)等不同电性的染料均体现出良好的催化性能.     

Fe-MnOx-CeO2/ZrO2低温催化还原NO性能研究

以纳米ZrO2为载体,用浸渍法制备出Fe-MnOx-CeO2/ZrO2催化剂,考察了活性组分配比和助剂负载量对催化剂低温NH3选择性催化还原NO活性的影响,并对催化剂进行了XRD、SEM、EDS和BET表征;探讨了温度、H2O和SO2对Fe-MnOx-CeO2/ZrO2催化剂低温下NH3选择性催化还原NO的影响,结果表明,无SO2和H2O条件下,8%Fe-10%MnOx-CeO2/ZrO2催化剂具有良好的催化活性和稳定性.120℃时,催化剂的脱硝效率为85.23%,当温度升至180℃时,脱硝效率可达到92.0%.SO2和H2O共存条件下,催化剂易失活,采用傅立叶变换红外光谱对各反应阶段的催化剂进行了表征,对其失活机制进行深入研究,结果表明,催化剂失活的主要原因是催化剂表面硫酸铵盐的沉积和催化剂本身活性成分的硫酸盐化.     

H2S匀圆杂选择性催化氧化工艺及催化剂研究现状

论述了石油流化催化裂化烟气中H2S气体的选择性催化氧化处理工艺和工艺中所使用的各种类型选择性氧化催化剂.目前已发展并投入使用的选择性氧化工艺主要有:Superclaus工艺、Euroclaus工艺、Clinsulf-Do工艺、BSR/Hi-Activity工艺、Selectox工艺和Modop工艺等,各工艺具有不同的特点和应用范围.H2S选择氧化催化剂主要包括以下几种体系:碳体系、SiC载体体系、分子筛体系、氧化物体系和柱撑黏土体系等.其中碳体系和氧化物体系的研究开展的较早较多,关于分子筛体系的研究近期有所减少,SiC是研究人员认为非常有潜力的一个载体体系,其相关体系研究也一直在进行之中,柱撑黏土体系还处于初步研究阶段,离实际应用尚有距离.     

不同pH下纳米铁镍颗粒对生物降解苯酚的影响

研究不同pH(8.0、6.0和3.0)下金属纳米颗粒(Fe和Fe/Ni)对纺锤芽孢杆菌(BFN)降解苯酚的影响.实验结果发现pH在8.0和6.0时投加2种金属纳米颗粒(Fe和Fe/Ni)对BFN降解苯酚有促进作用,其原因主要是纳米颗粒在水中持续腐蚀产生H2,为BFN降解苯酚提供电子,促进BFN的生长.但在pH=3.0时,只有BFN-纳米Fe耦合体系才使苯酚得到部分降解,主要是因为纳米Fe颗粒与水反应产生OH-,使pH值有所升高,更适宜BFN的生长,同时提供电子供体H2促进BFN对苯酚的利用.扫描电镜(SEM)和能谱分析(EDS)数据证实金属纳米颗粒(Fe和Fe/Ni)在反应后附着在微生物表面,但微生物的表面形态并未发生显著改变.因此,纳米金属颗粒虽然通过附着影响微生物的活性,但其在腐蚀过程中产生的H2将作为电子供体而被BFN所利用,综合作用的结果是有利于BFN的生长进而提高苯酚的降解速率.