内凸筋口琴管连续挤压模具

内凸筋口琴管,是汽车空调的一种新型散热管.具有散热效果好、单位面积小、重.量轻等优点.此文介绍了连续挤压内凸筋口琴管模具的设计方法及其模具芯头的冷挤压加工.     

基于surfer8.0的高密度电阻率法在水利水电工程灾害性评价中的应用

surfer8.0是一款画三维图的软件,结合高密度电阻率法在水利水电工程灾害性评价中的应用实例,验证了高密度电阻率法在水利水电工程中具有的可行性、有效性和实用性.     

Monitoring of atrazine in milk using a rapid tube-based ELISA and validation with HPLC

Although atrazine has been banned in the European Union since 2007 it still persists in soil from where it can enter the food chain. Milk-producing animals accumulate atrazine from contaminated feed and water and since large quantities of milk and milk products are consumed its quality should be constantly monitored. The objective of this investigation was to develop a simple tube ELISA procedure suitable for use in non-specialised laboratories and in the field. A polyclonal antibody raised in sheep and the hapten-gelatine conjugate was immobilised onto polystyrene tubes. This enables the colour produced to be read on a basic spectrophotometer. Milk samples were collected from three farms in different regions of Poland and diluted before immunoassay was performed. Samples were extracted with hexane-acetone for HPLC analysis. The amount of fat in the milk samples interferes with the dose response so it essential that the standards are prepared in the same samples matrix. A good correlation between 1% and 2% was found between the two methods in the analysis of real samples. However the ELISA procedure was more sensitive that the HPLC method since atrazine was detected in some samples by the ELISA but was not confirmed by the HPLC method. The study demonstrated that the simple antigen-coated tube assay provides a cost effective and valuable screening test that can be easily modified for direct use as a screening tool in the field.     

Importance of accounting for the piping system and boundary conditions in determining the maximum surge pressure following heat-exchanger tube-rupture

Shell-tube type heat exchangers are often used to exchange heat between a high-pressure fluid and a low-pressure fluid, and the pressure difference between the two fluids could be significantly high. If the difference in the design pressure between the low-pressure (LP) and high-pressure sides is greater than that covered by American Petroleum Institute (API 520 and 521) 10/13^th rule, dynamic analysis is required to ascertain that the maximum surge pressure that could be reached does not compromise the integrity of the LP side of the exchanger. API guidelines also notes that attention should also be given not only to the shell-side of the heat exchanger under evaluation, but also to the “upstream and downstream systems” This paper offers further insight into the importance of including the surrounding piping systems around the subject heat-exchanger where a tube-rupture scenario is considered, and also directs attention to the importance of correctly specifying the appropriate boundary conditions (B.C.) at the far ends of both the upstream and downstream piping systems. It demonstrates the effects of specifying different B.C. on the maximum pressure surge via a case study of a hot separator vapour condenser in a bitumen hydrotreating unit, where the process fluid on the tube-side is a vapour–liquid mixture at 9660 kPa(g). The vapour mass fraction of the process fluid is approximately 0.5, and is mostly hydrogen. The fluid on the LP side is cooling water connected to the plant supply and return cooling systems as well as another adjacent low pressure condenser. The design pressure for the cooling water piping system and the adjacent condenser is 1380 kPa(g).     

从原油储罐破裂事故谈原油储罐完整性的控制

在介绍储罐泄漏类型与泄漏危害的基础上,以原油储罐破裂事故为例,分析了储罐破裂的原因,进而阐述了原油储罐生命周期内完整性的控制。     

长时间服役的进口锅炉T91炉管失效行为研究

针对某进口亚临界锅炉三级过热器T91炉管失效事件,通过对其进行硬度、金相组织和SEM扫描电镜分析找出导致爆管的原因,并根据高温氧化皮厚度对其进行蠕变剩余寿命评估,结果表明该段T91管材爆管类型为典型长期过热爆管,炉管长期处于较高温度运行导致组织老化严重,力学性能下降,引起材料蠕变损伤,导致长期过热爆管,经计算其蠕变剩余寿命已达到寿命极限。本文对该锅炉防止类似事故具有重要作用,并对国内其他同在二十世纪90年代开始服役的T9彳炉管具有重大的参考价值和借鉴意义。     

熔盐蒸发器管板封口焊缝泄漏原因分析

某光热电站熔盐蒸发器入口侧管板封口焊缝发生泄漏,通过表面检测和观察,发现裂纹是从封口焊缝根部发展,并从根部向外扩展的。根据裂纹扩展方向和运行数据进行综合分析认为,熔盐蒸发器在未正确操作下导致在极短时间内管板下部表面升温过快,造成封口焊缝局部热应力过大。在焊缝残余应力、工作应力和热应力共同作用下,管板下部封口焊缝根部产生裂纹并扩展至焊缝表面,形成贯穿性裂纹,造成蒸发器管板泄漏。     

Insight into vented explosion mechanism and premixed flame dynamics in linked vessels: Influence of membrane thickness and blocking rate

To effectively prevent and mitigate explosion hazards and casualties, relief venting of flammable gas explosions has been applied in production processes in a broad variety of industries. This work conducted fully vented experiments to investigate the influence of venting membrane thickness, and partially vented experiments to investigate the influence of baffle blocking rate on the explosion characteristics of 9.5 vol% methane-air mixtures in linked vessels with a 0.5 m long vented duct. Results indicate that the membrane thickness and blocking rate for the two types of vented explosions significantly affected the explosion overpressure. The smaller the membrane thickness and blocking rate, the lower the explosion overpressure. Secondary explosions were observed in the vented duct through experiments and a weaker explosion flame appeared at a small blocking rate of 20%. With the further increase in the blocking rate, the flame became extremely weak, and no secondary explosions occurred. The overpressure evolution process at different positions in the explosion duct and secondary explosion phenomenon in the vented duct were investigated. This work could probably serve as an important reference for the selection of technical parameters of explosion venting in the practical industrial processes.     

长管拖车气瓶火烧损伤分析及安全评定

结合长管拖车的结构和火灾事故特点，对瓶体常见损伤模式进行分析，并根据损伤程度的不同制定安全评定流程和相应指标。若漆层完好仅发生熏黄、熏黑，可进行正常定期检验；若漆层发生烧黑、碳化或脱落，抛丸后瓶体未发生颜色异常，则对着火部位硬度测定，合格则正常定检，不合格进行金相分析；若抛丸后瓶体颜色发生变化或微量凸起，则进行硬度测定、金相分析和水压试验；若瓶体发现明显变形，则直接判废。硬度评定合格指标为183〈HB〈269，在269〈HB〈286范围内的需结合化学成分和金相组织综合评定；金相组织以索氏体为主，不允许出现铁素体和珠光体；水压试验要求容积残余变形率小于10％。