A Comparison of Skin Temperatures and Clothing Microclimate During Moderate Intermittent Exercise in the Cold Between One and Two Layers of Cotton and Polypropylene Underwear

The purpose of this study was to compare the effects of 2 kinds of underwear made from hydrophobic and hydrophilic fabrics on the mean skin temperatures and clothing microclimate (temperature, humidity) in participants performing intermittent exercise in cold environmental conditions.

One or 2 layers of cotton underwear (C1, C2) with a 2-piece long-sleeved shirt and long-legged trousers, and 1 or 2 layers of polypropylene underwear (P1, P2) with a 2-piece long-sleeved shirt and long-legged trousers were used as experimental underwear. In addition, the participants wore a 2-piece ski suit as 100% polyester clothing including 100% polyester padding. Ten young adult females volunteered as participants. The experiments were performed in a climatic chamber at an ambient temperature (T_a) of 0°C and an air velocity of 0.26 m s^?1.

The major findings are summarized as follows: (a) Although the clothing microclimate humidity was not different within the ski suit of outer clothing between C1 and P1, it was significantly higher in P2 than in C2; (b) Clothing microclimate temperature inside the ski suit did not differ between C1 and P1, whereas it was significantly higher in P2 than in C2; (c) The thermal gradient between innermost and outermost of clothing microclimate at back level did not show any difference between C1 and P1, but it was significantly higher in C2 than in P2. These results are discussed in terms of thermal physiology and clothing sciences.     

聚丙烯微塑料对污泥厌氧消化效能作用影响

以聚丙烯（PP）微塑料为研究对象,考察不同浓度PP微塑料对污泥厌氧消化产CH₄和产酸效能的作用影响,同时采用荧光定量PCR方法定量检测了乙酸激酶（AK）和mcrA基因在不同PP微塑料作用下的丰度变化.结果表明,PP微塑料对污泥厌氧消化产CH₄和产酸效能具有促进影响,CH₄和乙酸累计产量随PP微塑料投加量的增大而升高,当PP微塑料投加量为0.2g/g VSS时,CH₄和乙酸累计产量与空白对照相比分别提高148.2%和15.2%,达227.1mL/g VSS和1291.2mg/L.相应地,mcrA基因丰度随之提高98.2%,表明PP微塑料对产甲烷菌的生长和繁殖具有促进作用,进而强化污泥厌氧消化产CH₄效能.     

活性炭生物转盘法处理化工废水

使用固定剂将颗粒状活性炭固定在盘片上，制成了一种新型生物转盘盘片——活性炭生物转盘盘片。采用一级微型生物转盘法处理模拟化工废水，对比了活性炭、石英砂、聚丙烯3种生物转盘的处理效果。实验结果表明，活性炭生物转盘对COD的去除效果好于其他两种转盘。在进水COD为600mg／L、水力停留时间为6h、盘片转速为4r／min的条件下，活性炭生物转盘对COD的去除率可达71．3％。此外，活性炭生物转盘还有较强的耐有机负荷冲击能力。在废水处理过程中，活性炭仅在挂膜的前7天起吸附作用，挂膜成功后生物降解起主导作用。     

粉煤灰和电石渣对聚丙烯塑举裂解的影响研究

研究了粉煤灰和电石渣对聚丙烯塑料裂解的影响，讨论了加入量对裂解速度和裂解产物的影响。结果表明：粉煤灰和电石渣都使裂解产物中的轻质部分（汽油和裂解气）增加、重油降低；粉煤灰比电石渣更能加快反应的进行，而且加入量越多，反应越快，需时越短；粉煤灰比电石渣对聚丙烯塑料的裂解具有明显的催化促进效果。     

滑石粉对阻燃聚丙烯土工格栅性能的影响

将滑石粉加入聚丙烯阻燃格栅料中制成聚丙烯阻燃土工格栅材料,并探讨滑石粉对阻燃格栅的力学性能、熔融指数、燃烧性能、热稳定性和结晶性能的影响。结果表明:滑石粉的加入能提高阻燃格栅的熔融指数和结晶度,但对力学性能和阻燃性能有负面影响。与未添加滑石粉的阻燃格栅相比,添加5%wt的滑石粉后,阻燃格栅的断裂伸长率下降了9633%,峰值热释放速率和总释放热分别增加了4736%和2164%;当滑石粉添加量进一步增加到10%wt时,阻燃格栅的阻燃性能略有提高,但断裂伸长率却下降了975%。热重和差热分析表明,阻燃格栅阻燃性能的下降与热稳定性下降有关,而熔融指数提高则与α晶型熔点下降有关     

改性聚丙烯纤维的制备及其对苯系物的吸附

分别采用熔融接枝法和共混法制备聚丙烯(PP)/苯乙烯(St)改性纤维(PP-g-St)和聚丙烯/聚苯乙烯(PS)改性纤维(PP/PS),研究了熔融接枝条件对St接枝率的影响,考察了PP纤维、PP/PS纤维和PP-g-St纤维对纯苯系物和水中乳化、溶解态苯系物的吸附性能,并探讨了再生后的重复吸附性能。实验结果表明:PP熔融接枝St的最优配比为w(St)=9%,w(过氧化二异丙苯)=0.5%,此时St接枝率为4.7%,且能顺利纺丝;相比于PP纤维,PP-g-St纤维和PP/PS纤维对纯苯系物和水中乳化、溶解态苯系物的吸附量显著提高;吸油饱和的PP-g-St纤维和PP/PS纤维通过离心法再生5次后吸附性能再生率仍能够分别达到82.0%和87.6%。     

聚丙烯基改性纤维固相萃取水中的苯酚

通过高能电子束辐照的方法,在聚丙烯（PP）纤维基体上分别接枝长链丙烯酸十八酯（SA）和亲水性丙烯酸-β-羟乙酯（HEA）2种单体,并将该纤维作为固相萃取填料,用于固相萃取（SPE）水中的痕量苯酚。研究了SPE过程中上样速度、洗脱溶剂、洗脱体积以及洗脱速度等因素对纤维萃取效果的影响。结果表明,改性纤维对痕量苯酚的富集倍数达95~145倍,回收率达到90%~98%,甲醇对纤维有良好的再生效果,纤维重复使用6次以内时,吸附性能无明显变化。     

聚丙烯超滤膜的低温等离子体改性方法比较

为了研究低温等离子体对中空纤维膜的改性效果,对聚丙烯(PP)中空纤维膜进行了4种等离子体改性处理,以接枝率、力学性能、膜面官能团变化以及膜面形态为评价指标,比较了不同改性方法的改性效果。FT-IR特征分析发现,以同时照射法改性后的膜面官能团变化最大,且接枝率高,力学性能好。元素能谱分析表明,处理后的膜表面的N、O含量均有不同程度的变化,且与接枝率成正相关。SEM照片及力学性能反映出:改性后膜面存在损失,柔韧性变差。综合各指标的比较发现,同时照射法是一种最佳的改性方法。因此,特别考察了同时照射改性膜的清水通量的变化,结果表明,该方法能够大幅度提高膜的清水通量。     