储罐用钢在3.5%NaCl溶液中的腐蚀行为研究

目的对比研究三种油气储罐在水压试验时的腐蚀行为特征。方法选用9Ni钢、Q235碳钢、304L不锈钢储罐用材料以及3.5%NaCl模拟海水溶液,采用开路电位、电化学阻抗谱、动电位极化曲线测试方法研究三种储罐用钢在模拟海水中的电化学腐蚀特征,同时结合浸泡质量损失试验和微观腐蚀形貌进行分析。结果 9Ni钢、Q235碳钢、304L不锈钢稳定后的开路电位(vs.SCE)分别为-0.55、-0.64、-0.10m V,Rt值分别为2 792、1 765、125 100,平均腐蚀深度分别为0.070 6、0.160 3、0.002 5 mm/a。微观腐蚀形貌显示,9Ni钢和Q235碳钢表面发生明显的腐蚀,而304L不锈钢只发生轻微的点蚀。结论在3.5%NaCl模拟海水溶液中,304L不锈钢最耐腐蚀,Q235碳钢最易腐蚀,9Ni钢居于两者之间。因此在9Ni钢和Q235碳钢储罐海水试压过程中需要采取临时保护。     

喷丸强化技术在某型作动筒延寿修理中的应用

目的将某型作动筒的寿命由6000±150起落延长至12 000±150起落。方法采用喷丸强化技术对作动筒的主要承力零件进行喷丸强化处理,提高零件的抗疲劳和抗应力腐蚀性能。通过疲劳寿命试验验证对比喷丸强化处理前后典型零件和作动筒的寿命指标是否达到了预期目标。结果喷丸强化处理前的3件前耳环螺栓试验循环次数均未超过1.8×10~6即断裂,喷丸强化后达到3.6×10~6时仍未断裂。喷丸强化处理后的4件主耳环螺栓与喷丸强化处理前对比,断裂时的试验循环次数均有不同程度的提高,均值寿命比值大于2.36。喷丸强化处理前后的主前作动筒疲劳寿命试验达到预期的循环次数时,均没有出现断裂或者损坏。结论喷丸强化处理能有明显提高作动筒的抗疲劳和抗应力腐蚀性,强化处理后的零件疲劳寿命能够超过处理前的2倍,可以采用喷丸强化技术延长作动筒的使用寿命。     

印制电路板海洋环境试验与实验室环境试验相关性研究

目的研究机载电子设备印制电路板西沙海洋大气环境与实验室环境试验的相关性。方法在西沙海域环境下开展两种印制电路板的棚下暴露试验,暴晒试验时间为3年,同时在实验室开展盐雾试验,分别通过测试绝缘电阻、品质因数研究两种试验环境的相关性。结果将以绝缘电阻、品质因数为基准相关性评价结果进行平均,得出印制电路板实验室加速试验和自然暴露试验存在着强相关。两种样品的加速系数分别是3.5,5.15。结论建立了印制电路板在西沙海洋环境试验和实验室盐雾环境试验的相关性,可为后续西沙环境试验的加速处理提供依据。     

用EXCEL进行精密度-偏性分析质控数据处理

利用EXCEL强大的数据处理功能，可以方便地对精密度—偏性分析质控数据进行处理，具有较高的推广价值。     

Investigation of the Influence of Seagrass on Fisheries Catch Level Using Isotonic Regression

The relationship between seagrass area and the commercial catch of some economically important South Australian fish species is not known in any quantitative sense. However, there is evidence in the literature to suggest that seagrass decline will detrimentally impact on species abundance and composition, and consequently that the presence or absence of seagrass will compromise the commercial and recreational fishery. In this paper we describe the construction of models based on order restricted (isotonic) regression and discuss the role of seagrass area, in terms of its influence on the level of commercial catch through modifying the effect of fishing 'effort'.     

Large-scale mercury variations in Lake Vänern (Sweden) 1974-98

Lake V?nern, the largest lake in Sweden, has been seriously contaminated with mercury during the 20th century. In the 1970's and 80's the direct load, mainly from a chlor-alkali industry in the area, of mercury was drastically reduced as a response to new legislation, from three to five tons down to between five and ten kg yr(-1). Large amounts of the disposed pollutant have accumulated in the sediments. The question posed in this work is now, is the effect of the drastic load reduction after more than two decades visible in the sediments? The question is relevant as large areas still are blacklisted for fishing, but also as a follow-up of a major remedy action. The lake also serves as a freshwater reservoir for even Sweden's second largest city. This work synthesises and compares data of mercury in the sediments from three major field programs, in 1974, 1984 and 1998. The interest is focused on both spatial heterogeneity and temporal trends. In 1974, the surface concentrations are significantly higher than in subsequent surveys. Significant differences are also found between 1984 and 1998. Significant spatial differences within the lake are found for respective year. The most contaminated area is located in the north, close to the major point source (a former chlor-alkali industry). This is also the area with the largest improvement, as a direct response to the reduction in load. Further from the outlet, the recovery is more affected by burial and transport processes out into the deeper basins.     

车载巡测在区域射频电磁环境质量监测与表征中的应用分析

对北京中央电视塔周围25 km²区域电磁环境质量分别进行了射频的网格法手工监测和车载巡测自动监测，通过SPSS软件等对两种监测方法获取的数据进行了统计对比分析，发现两组数据在总体水平及数值分布特征上较为接近，因此车载巡测监测可以替代网格法监测。以车载巡测数据为基础，绘制了实测数据的道路电磁地图，利用插值法绘制了区域电磁地图，对区域电磁环境质量进行了直观表征。从回应公众关注和城市电磁规划出发，建议今后可利用车载巡测监测加强时域和频域的监测。     

DOAS大气环境质量监测系统与传统点式采样监测法可比性研究

系统比较了DOAS大气监测系统与传统点式采样设备在测定环境空气中二氧化硫的性能。     

消油剂乳化率检验中标准曲线的选择

本文经过比实验，详细研究了添加双象１号消油剂对原油标线的影响，并对乳化率检验中的两种标准曲线进行了统计检验。结果表明：不添加消油剂制作的原油标线可使乳化率结果降低１￣３％左右，甚至个别消油剂的乳化率结果可相差２０％左右，两条标线的统计差异非常显著。所以制作标准曲线时必须按比例添加消测剂才能确保执法数据的可靠性。     

GJB 150A淋雨试验强化试验程序数值模拟和试验装置设计研究

目的 研究GJB 150.8A—2009《军用装备实验室环境试验方法第8部分:淋雨试验》中强化试验程序的工程实现方法.方法 在标准解读的基础上,以强化试验程序用喷嘴为对象,建立数值模型,分析喷嘴在强化试验程序过程中的流场分布,并基于分析结果给出强化试验程序试验装置设计的思路和方法.结果 在喷嘴内,压力变化剧烈,极短距离内由276 kPa迅速降至101 kPa.水流经过喷嘴经历了激烈的加速过程,从距离喷嘴出口0.01～0.4 m,水流速度从251 m/s迅速降至17.8 m/s,到远场趋于稳定.结论 分析结果对指导强化试验程序的试验装置的设计和试验实施具有重要参考意义.