树脂基纳米钛锆氧化物复合吸附剂同步去除水中磷和氟

以大孔强碱性阴离子交换树脂D201为基体,负载纳米钛、锆氧化物,制备新型树脂基纳米钛锆氧化物复合吸附剂TiZr-D201.通过吸附等温线实验、pH影响实验、竞争吸附实验、动力学实验及柱吸附实验,并结合对吸附剂的表征,探讨了复合吸附剂对水中磷和氟的吸附性能和相应的吸附机制.结果表明,当pH值为5.8,温度为308K时,Ti-Zr-D201对磷和氟的Langmuir拟合最大吸附容量分别是34.9 mg·g~(-1)和35.1 mg·g~(-1),且吸附行为是自发进行的,温度越高,吸附效果越好;与磷相比,pH值对Ti-Zr-D201吸附氟的影响更为显著;选取SO_4~(2-)、NO_3~-和Cl~-作为竞争离子,Ti-Zr-D201较基体D201表现出很好的抗干扰能力;内扩散模型拟合结果表明Ti-Zr-D201在吸附平衡前存在两个不同的吸附阶段;柱吸附实验表明Ti-Zr-D201具有稳定的结构和良好的动态吸附性能,并且可再生循环使用,具备实际应用的潜力.     

磁性氮掺石墨烯活化过硫酸钾降解水中亚甲基蓝

活化过硫酸盐产生硫酸根自由基的高级氧化技术在水环境污染物治理中引起了广泛的关注和研究.本研究采用水热法制备磁性氮掺石墨烯(M-N-G)作为催化剂.利用SEM、BET、XRD和VSM等手段表征材料,系统研究了该材料活化过硫酸盐降解亚甲基蓝的效能.结果表明:M-N-G的比表面积为94.35 m2·g-1,磁性Fe3O4分布在材料表面,能有效的活化过硫酸钾降解亚甲基蓝.当催化剂的用量为200 mg·L~(-1),过硫酸钾浓度为0.4~0.5 mmol·L~(-1)时,在p H=3~6时对10 mg·L~(-1)亚甲基蓝的降解率达90%以上.体系温度在15~32℃时,降解速率常数在0.0227~0.0488 min-1,反应活化能为33.7 k J·mol-1.EPR分析及自由基漼灭实验证明了体系中有羟基自由基和硫酸根自由基产生.TOC分析结果表明:TOC去除率可达50%.M-N-G经过简单的稀硫酸和水洗后,可高效重复利用4次.该技术方法简单、高效、无二次污染,能为有机污染物废水处理提供一种新的方法选择.     

不同构造措施的钢管混凝土边框钢板剪力墙抗震性能试验研究

钢管混凝土边框钢板剪力墙是一种新型抗震剪力墙,为了比较不同构造措施对该新型剪力墙抗震性能的影响,进行了3个剪跨比为1.5的钢管混凝土边框钢板剪力墙低周反复荷载试验.其中,试验模型1为墙体钢板与边框柱钢管焊接,试验模型2为墙体钢板与边框柱钢管螺栓连接,试验模型3为墙体钢板开孔并与边框柱钢管焊接.通过试验研究,比较了各剪力...     

纳米TiO2/CNTs复合材料的制备及其光学性质

TiO2在碳纳米管上的复合材料可以增加材料的光催化性能,已成为新的研究热点.本文采用低温液相法成功地合成了TiO2/CNTs复合材料,并用TEM、XRD和UV-vis对材料进行了表征,结果表明,TiO2很好地分散在CNTs上,具有显著的催化效果,有很好的应用前景.     

漂浮负载型光催化剂制备及降解草甘膦研究

以漂珠(FP)为载体,采用溶胶-凝胶-浸渍法制备了漂浮负载型CdS/TiO2/FP复合膜光催化剂,通过SEM、XRD对其结构进行了表征.以甘草膦农药的光催化降解为模型反应,使用不同光源研究了CdS/TiO2/FP的光催化性能,探讨了影响催化剂活性的因素及采用太阳光做光源处理草甘膦的可行性.结果表明,经4层镀膜500℃热处理的20%(w/w)CdS/TiO2/FP光催化剂具有良好的光催化性能,最佳降解条件为:催化剂加入量3 g/L,初始pH 7～9,Fe2 浓度为2.0×10-3 mol/L.通气量200 mL/min.在最佳条件下,对135 mg/L草甘膦溶液降解率可以分别达到96.3%(125 W高压汞灯,60 min)和82.4%(太阳光,180 min).     

火灾高温下CFRP加固钢筋混凝土梁温度场分析

综合国外CFRP加固混凝土结构抗火试验相关研究,总结了CFRP的高温热工性能参数。用ANSYS软件对火灾高温下不同情况(无防火保护层和有防火保护层)和不同工况(防火涂料涂抹形式)下CFRP加固后的钢筋混凝土梁进行了温度场数值模拟研究。结果表明,防火涂料厚40 mm时,梁耐火极限可达2.5小时以上,且底面和两侧面全面涂抹防火涂料的防火效果最好。本文研究有助于进一步深入认识CFRP加固钢筋混凝土结构在高温下的力学性能和耐火极限,且对CFRP加固后的结构防火设计具有一定的指导意义。     

An analysis of end-of-life terminology in the carbon fiber reinforced plastic industry

While many studies and reviews into the practices conducted by industry and academia to recycle and remanufacture carbon fibre-reinforced plastic (CFRP) exist, to date no investigation exists which regards the correctness of the use of the terms recycling and remanufacturing. As such, this paper seeks to analyse the CFRP reuse industry’s attempt to recycle and remanufacture manufacturing waste CFRP and end-of-life (EOL) CFRP with an emphasis on the terminology used to describe these practices. Firstly, this paper presents a justification of the importance of using EOL terminology correctly; outlining the benefits and problems associated with using the correct and incorrect terminology. This paper finds that in the case of CFRP remanufacturing, terminology is being applied incorrectly and in the case of CFRP recycling, particular care should be taken when applying the term recycled to CFRP or stating that CFRP has been recycled. Further, this paper proposes new terminology (in keeping with EU directives) which could be adopted by industry and academia working in this area. This paper also finds that in the case of remanufacture, CFRP is incapable of being remanufactured.     

g-C_3N_4/C@Bi_2MoO_6复合光催化剂的制备及其光催化活性

通过水热合成法和液相沉积法制备g-C_3N_4/C@Bi_2MoO_6复合光催化剂,并采用X射线衍射、扫描电子显微镜、氮气吸脱附、紫外-可见漫反射等技术对其进行表征。研究了可见光下g-C_3N_4/C@Bi_2MoO_6催化降解罗丹明B(Rh B)的影响因素,并对其光催化反应机理进行初步探讨。实验结果表明:g-C_3N_4掺杂量为60%(w)时g-C_3N_4/C@Bi_2MoO_6的光催化活性最高;在60%g-C_3N_4/C@Bi_2MoO_6的投加量为1.00 g/L、初始Rh B质量浓度为2.50 mg/L、可见光照射150 min的条件下,Rh B的降解率达到97.90%;在g-C_3N_4/C@Bi_2MoO_6光催化降解体系中,h~+和·O_2~-是主要活性物种。     

钙钛矿型催化剂催化湿式氧化处理煤气化废水纳滤浓缩液

采用溶胶-凝胶法制备了Mn掺杂钙钛矿型催化剂LaFexMn1-xO3,并以其为催化剂催化湿式双氧水氧化处理煤气化废水纳滤浓缩液。采用XRD,SEM,FTIR技术对催化剂进行了表征。表征结果显示：制备的催化剂均具有标准的钙钛矿型结构,其中,LaFe0.9Mn0.1O3的结构稳定,比表面积大。实验结果表明：制备的催化剂中LaFe0.9Mn0.1O3的催化活性最高,且稳定性好,连续使用5次后催化活性未见明显减弱;在H2O2投加量3.0 g/L、n（H2O2）∶n（LaFe0.9Mn0.1O3）=12∶1、反应温度160 ℃、反应压力1 MPa、浓缩液pH 3、反应时间60 min的最优条件下,COD、UV254和TOC的去除率分别达到80.9%、95.2%和68.0%,BOD5/COD由0.02提升至0.40,可生化性大幅提高。     

微生物絮凝剂M-C11处理高岭土悬浊液的响应曲面优化

采用响应曲面法对微生物絮凝剂M-C11处理高岭土悬浊液的过程参数进行优化,选取中心复合实验设计(CCD),以p H、M-C11投加量和Ca Cl2投加量等因素为自变量,以处理后的高岭土悬浊液絮凝率(Fr)为响应值,并借助扫描电镜对絮凝剂的作用机理进行初步探讨。结果表明,微生物絮凝剂M-C11可显著改善高岭土悬浊液的絮凝性能,且选取的3种单因素水平均可影响絮凝剂活性。经多元回归拟合分析,在M-C11投加量为2.56 m L,Ca Cl2投加量为0.37 g/L的最优条件下,微生物絮凝活性实验值可达92.37%,接近模型预测值(92.30%)。Ca Cl2投加量对絮凝效果的影响高于M-C11投加量(PCa Cl2相似文献