Effect of barium sulfate modification on the SO2 tolerance of V2O5 /TiO2 catalyst for NH3-SCR reaction

Sulfur poisoning of V_2O_5/BaSO_4–TiO_2(VBT),V_2O_5/WO_3–TiO_2(VWT) and V_2O_5/BaSO_4–WO_3–TiO_2(VBWT) catalysts was performed in wet air at 350℃ for 3 hr,and activities for the selective catalytic reduction of NO_x with NH_3 were evaluated for 200–500℃.The VBT catalyst showed higher NO_x conversions after sulfur poisoning than the other two catalysts.The introduction of barium sulfate contributed to strong acid sites for the as-received catalyst,and eliminated the redox cycle of active vanadium oxide to some extent,which resulted in a certain loss of activity.Readily decomposable sulfate species formed on VBT-S instead of inactive sulfates on VWT-S.These decomposable sulfates increased the number of strong acid sites significantly.Some sulfate species escaped during catalyst preparation and barium sulfate was reproduced during sulfur poisoning,which protects vanadia from sulfur oxide attachment to a great extent.Consequently,the VBT catalyst exhibited the best resistance to sulfur poisoning.     

石墨烯复合材料在水处理中的应用研究

新型碳材料石墨烯,因其比表面积大,物理、化学特性优异,通常作为吸附剂或复合材料载体,用于难降解有机废水处理.载体石墨烯改性后,可优化复合材料性能,包括溶解性和可控性.基于复合材料制备,选取典型污染物废水,如染料废水、苯酚废水、农药废水,从吸附处理和催化降解两方面展开,简要介绍石墨烯复合材料的应用研究及作用效果,显示出复合材料可有效提高污染物降解效率,回用效果好.此外,石墨烯复合材料在回用及实际应用方面仍有待进一步研究.     

Fe-MnOx-CeO2/ZrO2低温催化还原NO性能研究

以纳米ZrO2为载体,用浸渍法制备出Fe-MnOx-CeO2/ZrO2催化剂,考察了活性组分配比和助剂负载量对催化剂低温NH3选择性催化还原NO活性的影响,并对催化剂进行了XRD、SEM、EDS和BET表征;探讨了温度、H2O和SO2对Fe-MnOx-CeO2/ZrO2催化剂低温下NH3选择性催化还原NO的影响,结果表明,无SO2和H2O条件下,8%Fe-10%MnOx-CeO2/ZrO2催化剂具有良好的催化活性和稳定性.120℃时,催化剂的脱硝效率为85.23%,当温度升至180℃时,脱硝效率可达到92.0%.SO2和H2O共存条件下,催化剂易失活,采用傅立叶变换红外光谱对各反应阶段的催化剂进行了表征,对其失活机制进行深入研究,结果表明,催化剂失活的主要原因是催化剂表面硫酸铵盐的沉积和催化剂本身活性成分的硫酸盐化.     

H2S匀圆杂选择性催化氧化工艺及催化剂研究现状

论述了石油流化催化裂化烟气中H2S气体的选择性催化氧化处理工艺和工艺中所使用的各种类型选择性氧化催化剂.目前已发展并投入使用的选择性氧化工艺主要有:Superclaus工艺、Euroclaus工艺、Clinsulf-Do工艺、BSR/Hi-Activity工艺、Selectox工艺和Modop工艺等,各工艺具有不同的特点和应用范围.H2S选择氧化催化剂主要包括以下几种体系:碳体系、SiC载体体系、分子筛体系、氧化物体系和柱撑黏土体系等.其中碳体系和氧化物体系的研究开展的较早较多,关于分子筛体系的研究近期有所减少,SiC是研究人员认为非常有潜力的一个载体体系,其相关体系研究也一直在进行之中,柱撑黏土体系还处于初步研究阶段,离实际应用尚有距离.     

Formic acid as an alternative reducing agent for the catalytic nitrate reduction in aqueous media

Formic acid was used for the nitrate reduction as a reductant in the presence of Pd:Cu/γ-alumina catalysts. The surface characteristics of the bimetallic catalyst synthesized by wet impregnation were investigated by SEM, TEM-EDS. The metals were not distributed homogeneously on the surface of catalyst, although the total contents of both metals in particles agreed well with the theoretical values. Formic acid decomposition on the catalyst surface, its influence on solution pH and nitrate removal efficacy was investigated. The best removal of nitrate (50 ppm) was obtained under the condition of 0.75 g/L catalyst with Pd:Cu ratio (4:1) and two fold excess of formic acid. Formic acid decay patterns resembled those of nitrate removal, showing a linear relationship between kf (formic acid decay) and k (nitrate removal). Negligible amount of ammonia was detected, and no nitrite was detected, possibly due to buffering effect of bicarbonate that is in situ produced by the decomposition of formic acid, and due to the sustained release of H2 gas.     

半干法烟气脱硫灰改性及应用

文章主要对半干法脱硫灰中亚硫酸钙的氧化转化进行研究。半干法脱硫灰中亚硫酸钙对建材质量具有一定影响,通过筛选合适的催化-氧化剂体系对其进行了氧化改性。试验得到了一种复合催化剂,成功用于半干法脱硫灰改性。结合蒸压砖的生产工艺,使亚硫酸钙在生产过程中实现了部分转化,生产的蒸压砖能达到JC239-2001《粉煤灰砖》MU10强度等级。     

燃煤电厂PM2.5微细颗粒物控制新技术——旋转电极式电除尘性能特点及安装技术

本文介绍了燃煤电厂PM2.5微细颗粒物控制新技术——旋转电极式电除尘器的工作原理、性能特点.同时介绍了某电厂330MW机组旋转电极式电除尘改造工程应用实例.在积累多个旋转电极式电除尘器安装调试经验的基础上,介绍了旋转电极式电除尘器安装工艺流程及安装调试技术.     

催化剂Ru/ZrO2-CeO2催化湿式氧化苯酚

催化剂Ru/ZrO₂-CeO₂催化湿式氧化苯酚的过程表明,Ru/ZrO₂-CeO₂可以显著提高COD和苯酚去除效果,当反应温度为170℃,压力为3 MPa,反应120 min后,COD和苯酚的去除率分别达到了99％和100％.试验还考察了不同反应条件对苯酚溶液COD去除的影响,并获得了最优的反应条件：温度为170℃,压力为3 MPa,催化剂的投加量为5　g/Ｌ,搅拌速度为500 r/min.通过对中间产物的分析,本研究提出了催化湿式氧化苯酚的简单路径图,认为苯酚首先被氧化成小分子有机酸,接着小分子有机酸被氧化成二氧化碳和水.前一个过程是快速反应,后一个过程中的乙酸氧化是慢速过程,需要在高温下才能完成.乙酸的氧化主要是自由基攻击α碳上的C—H键,先生成甲酸,并最终生成二氧化碳和水.     

Kinetics of selective catalytic reduction of NO by NH3 on Fe-Mo/ZSM-5 catalyst

The catalyst of Fe-Mo/ZSM-5 has been found to be more active than Fe-ZSM-5 and Mo/ZSM-5 separately for selective catalytic reduction (SCR) of nitric oxide (NO) with NH3. The kinetics of the SCR reaction in the presence of O2 was studied in this work. The results show that the observed reaction orders were 0.74-0.99, 0.01-0.13, and 0 for NO, O2 and NH3, respectively, at 350-450℃. And the apparent activation energy of the SCR was 65 kJ/mol on the Fe-Mo/ZSM-5 catalyst. The SCR mechanism was also deduced. Adsorbed NO species can react directly with adsorbed ammonia species on the active sites to form N2 and H2O. Gaseous O2 might serve as a reoxidizing agent for the active sites that have undergone reduction in the SCR process. It is also important to note that a certain amount of NO was decomposed directly over the Fe-Mo/ZSM-5 catalyst in the absence of NH3.