负载型TiO2膜太阳光光催化降解活性深蓝K-R的研究

采用抛物线槽型反应装置,研究了玻璃弹簧和微珠负载型TiO2膜太阳光催化降解活性深蓝K-R,结果表明,由于玻璃弹簧具有良好的光透距离,脱色性能显著优于玻璃微珠,玻璃弹簧为载体,水溶液浓度为15mg/L,pH为3,流速为20mL/s,太阳光强度在1200 μW/cm2以上,光降解6h时,脱色率达到96%; 该降解反应可用一级反应动力学方程进行描述,反应速率常数（K）与光强I的关系为：K∝I1.92。     

Removal of methylene blue by coupling black carbon adsorption with TiO2 photodegradation

In this study, the removal of methylene blue (MB) by the coupling of black carbon (BC) and TiO₂ was investigated. The effects of different parameters such as catalyst dose, sorbent, initial concentrations of dye, pH of the solutions, recycles on discoloration, and chemical oxidation demand (COD) reduction of MB were monitored to optimize the reaction conditions. The discoloration and COD conversation rate of MB obtained by the coupling process were 100% after 90?min irradiation. The synergistic effect of MB-adsorption on BC followed by degradation through TiO₂ photocatalysis was proved by FT–IR spectrophotometer. The BC as by-product of natural materials is a promising adsorbent for waste water treatment.     

粉煤灰吸附去除弱酸性艳蓝印染废水

利用粉煤灰对弱酸性艳蓝印染废水进行了处理。研究表明：粉煤灰的粒径、灰水比、废水pH值以及振荡吸附时间对粉煤灰的吸附能力均有较大影响。在以下工艺条件下：20℃,粉煤灰的粒径200目,灰水比为1：30,pH为2．0,振荡吸附2．5h,弱酸性艳蓝印染废水经粉煤灰处理后,COD值由576mg／L降至71mg／L,COD去除率可达87．7％：废水色度可从10000倍降为50倍,色度的去除率达99．5％,出水pH为6．5。出水水质达到了国家印染废水一级排放标准(GB4287—92)。     

La/Ce掺杂钛基二氧化铅电极的制备及电催化性能研究

采用电沉积法制备了稀土La、Ce改性的钛基二氧化铅(Ti/PbO2)电极.利用SEM和XRD分析了电极的表面形貌和晶体结构,结果表明,稀土La、Ce掺杂后改变了电极表面的微观结构和晶面取向,使电极表面变得更加致密、均匀;用LS和CV测试了电极的电化学性能,分析表明,稀土La、Ce的掺杂提高了电极的析氧过电位和峰电流密度,改善了电极的催化性能.用所制备的不同掺杂量下的改性电极降解亚甲基蓝模拟染料废水(methylene blue,MB),结果表明,当La、Ce掺杂量分别为8.0g.L-1和5.0 g.L-1时,电极对MB及其COD的去除率达到最佳,分别为83.85%、79.95%和79.18%、76.21%,显示了良好的去除效果和催化性能,并在此基础上进一步分析了MB可能的降解路径和机制.     

兼氧混合菌对亚甲基蓝废水生物降解实验研究

采用厦门某生物科技有限公司提供的兼氧混合菌为研究对象,利用相关设备进行中试实验,验证了该项技术的可行性。同时探究了重金属对该混合菌种生物降解能力的影响,通过中试实验研究后发现5mg/L的重铬酸钾和硫酸铜均对该混合菌种的生物降解能力有一定的影响,并且硫酸铜的影响大于重铬酸钾。此外该技术对甲基橙、刚果红废水也有一定的生物降解能力,这为兼氧混合菌用于印染废水处理提供了实验依据。     

反应气氛对绿色合成纳米铁的组分及其活性的影响

成本低廉和无二次污染的"绿色"合成纳米材料是发展原位纳米环境修复技术的前沿研究课题之一.本文以绿茶提取液为还原剂和稳定剂进行"绿色"合成纳米铁,探讨在不同的气氛下"绿色"合成的纳米铁颗粒的主要成分,以期为调控合成纳米铁系材料提供基础研究.首先,利用扫描电子显微镜(SEM)、X射线能谱(EDS)、X射线光电子能谱分析(XPS)和傅里叶变换红外光谱(FTIR)等表征手段对不同反应气氛下合成的纳米铁颗粒的表面微观形貌、尺寸和价态结构进行分析.结果发现,在通入N2情况下,合成的纳米铁颗粒粒径为(84.7±11.5)nm,其主要成分以纳米零价铁为主;在通入空气情况下,合成的纳米铁粒径为(117.8±26.2)nm,其主要成分是纳米零价铁、氧化铁和四氧化三铁的混合物;通入O2时,合成的纳米铁粒径为(141.2±26.3)nm,其主要成分以四氧化三铁为主.其次,评价在不同气氛条件下合成纳米铁颗粒对去除亚甲基蓝(MB)的反应活性.结果表明,在反应温度313 K下降解初始浓度为50 mg·L-1的MB溶液,反应5 min时已达到平衡,通入N2合成的纳米铁降解MB,去除率高达98.7%,而通入O2合成的纳米铁反应效率低,对MB的去除率仅为65.3%.最后,从以上发现提出不同气氛下可以调控"绿色"合成的铁系纳米材料成分,从而导致不同的纳米修复环境中污染物的能力.     

Activated carbon coated palygorskite as adsorbent by activation and its adsorption for methylene blue

An activation process for developing the surface and porous structure of palygorskite/carbon(PG/C) nanocomposite using ZnC l2 as activating agent was investigated. The obtained activated PG/C was characterized by X-ray diffraction(XRD), Fourier transform infrared spectroscopy(FTIR), field-emission scanning electron microscopy(SEM), and Brunauer–Emmett–Teller analysis(BET) techniques. The effects of activation conditions were examined,including activation temperature and impregnation ratio. With increased temperature and impregnation ratio, the collapse of the palygorskite crystal structure was found to accelerate and the carbon coated on the surface underwent further carbonization. XRD and SEM data confirmed that the palygorskite structure was destroyed and the carbon structure was developed during activation. The presence of the characteristic absorption peaks of C_C and C–H vibrations in the FTIR spectra suggested the occurrence of aromatization. The BET surface area improved by more than 11-fold(1201 m2/g for activated PG/C vs. 106 m2/g for PG/C) after activation, and the material appeared to be mainly microporous. The maximum adsorption capacity of methylene blue onto the activated PG/C reached 351 mg/g. The activated PG/C demonstrated better compressive strength than activated carbon without palygorskite clay.     

环境规制的蓝色红利效应研究

利用中国工业企业数据库2004~2009年制造业企业数据,以清洁生产目录标准的政策实施为外生冲击事件,基于倍差估计法（DID）实证检验了环境规制对企业盈利能力、盈利质量、波特效应和管理创新成本等蓝色红利的影响.结果发现：环境规制显著提升了制造企业的利润率和企业的现金流充裕性,改善了企业的盈利能力和盈利质量;环境规制显著降低了企业管理创新成本,但波特效应不显著.环境规制的蓝色红利效应存在地方策略互动、企业规模和所有制的异质性：地方政府之间的策略性不合作抑制了环境规制蓝色红利效应.企业规模的扩大提高了管理创新成本,但强化其他相关的蓝色红利效应.环境规制对国有企业的利润率、现金流以及全要素生产率的改善作用强于非国有企业,但更有助于降低非国有企业的管理创新成本.     

Pickering乳液模板多孔WG-g-PNaA水凝胶去除水体中的亚甲基蓝

为拓展小麦加工副产物麦麸蛋白(WG)在印染废水处理工业中的应用,以其中的醇溶蛋白稳定的O/W型Pickering乳液为孔模板,WG与AA原位自由基接枝聚合,制备了多孔小麦麸质蛋白-g-聚丙烯酸钠(WG-g-PNaA)水凝胶。通过FT-IR、FESEM表征手段对合成的水凝胶进行结构和表面形貌表征,考察了其对水体中亚甲基蓝(MB)的去除性能。结果表明：WG与PAA链成功接枝聚合,Pickering乳液滴被洗除后在WG-g-PNaA水凝胶网络中留下规整的连续孔隙,BET比表面积为18.04 m²·g⁻¹;在溶液pH=9.0,初始浓度C₀≤300 mg·L⁻¹时,多孔WG-g-PNaA水凝胶对MB的去除率可达98.5%以上,其等温吸附过程符合Langmuir单层吸附模型,饱和吸附量为2 144.2 mg·g⁻¹;吸附热力学研究结果表明：温度对吸附影响较小,吸附动力学数据符合准二级动力学模型,物理化学静电吸附为速率控制步骤;但吸附初期Pickering乳液致孔凝胶的粒子内扩散模型的K_1d(28.59)远大于无Pickering乳液致孔凝胶的K_1d(12.89),这说明凝胶网络中的孔隙在吸附初期有利于MB分子扩散传质,提高吸附速率。研究结果可为WG在印染废水处理中的应用提供参考。     

KOH活化花生壳生物质炭对亚甲基蓝吸附性能研究

以花生壳生物质炭(P-BC)为原料,KOH为活化剂,采用化学活化法制得活化生物质炭(K-BC),通过考察对亚甲基蓝的吸附性能,研究了花生壳生物质炭的最佳活化条件,并利用N2吸附-脱附实验、SEM等对最佳活化条件下的生物质炭进行表征.结果表明,K-BC活化的最佳条件为碱炭比为1.5:1,活化温度为800℃,活化时间为90 min,此时K-BC的比表面积达到597.93 m2/g,总孔容达到0.76 cm3/g.并考察了亚甲基蓝初始浓度、pH等对K-BC吸附亚甲基蓝的影响,随着初始浓度的增加,吸附平衡时间显著延长,亚甲基蓝去除率显著降低;当pH=6时,K-BC对亚甲基蓝的吸附量最大;K-BC对亚甲基蓝的吸附动力学曲线符合伪二阶动力学模型,吸附平衡时K-BC对亚甲基蓝的吸附能力为80~149.95 mg/g.