Fe2O3 particles as superior catalysts for low temperature selective catalytic reduction of NO with NH3

Fe203 particle catalysts were experimentally studied in the low temperature selective catalytic reduction （SCR） of NO with NH3. The effects of reaction temperature, oxygen concentration, [NH3]/[NO] molar ratio and residence time on SCR activity were studied. It was found that Fe203 catalysts had high activity for the SCR of NO with NH3 in a broad temperature range of 150-270℃, and more than 95% NO conversion was obtained at 180℃ when the molar ratio [NH3]/[NO] = 1, the residence time was 0.48 seconds and 02 volume fraction was 3%. In addition, the effect of SO2 on SCR catalytic activity was also investigated at the temperature of 180℃. The results showed that deactivation of the Fe2O3 particles occurred due to the presence of SO2 and the NO conversion decreased from 99.2% to 58% in 240 min, since SO2 gradually decreased the catalytic activity of the catalysts. In addition, X-ray diffraction, Thermogravimetric analysis and Fourier transform infrared spectroscopy were used to characterize the fresh and deactivated Fe2O3 catalysts. The results showed that the deactivation caused by SO2 was due to the formation of metal sulfates and ammonium sulfates on the catalyst surface during the de-NO reaction, which could cause pore plugging and result in suppression of the catalytic activity.     

零价铁PRB技术在地下水原位修复中的研究进展

PRB(可渗透反应墙)是地下水治理中新型的原位修复技术,具有成本低、处理效果好、对环境干扰小等优点,已逐渐应用到实际. 原位修复技术中PRB根据结构的不同可分为单处理系统PRB和多单元处理系统PRB,单处理系统PRB适用于单一污染物、污染浓度较低、污染羽规模较小的场地,多单元系统用于污染场地较复杂、污染种类较多的场地. 零价铁PRB去除地下水中无机污染物及有机组分的反应机理主要是氧化还原反应和还原性脱卤反应. 实际场地PRB的运行中存在的主要问题是零价铁钝化及PRB堵塞,现阶段的解决方法主要包括超声、电化学等,但为了提高PRB技术的实用性,铁材料的解钝化技术、实际场地PRB的设计与安装、PRB体系的长期运行及服务期满后的处置均需进一步的研究探索.      

城市突发环境事件的三维矩阵管理模式研究

针对我国环境事件频繁发生和应急管理法制建设缺位、体制不健全之间的矛盾,结合矩阵管理与应急管理理念,创建了基于事件分级、事件生命周期和事件运行管理为三维的矩阵管理模式,并以此模式分析结果为基础,提出城市应急管理能力建设的阶段性建议。     

中国大气NH3和NOx排放的时空分布特征

根据我国不同氨源的数量、燃料消费量和相应的氨与氮氧化物排放因子,计算了我国大陆地区1995~2004年历年的氨(NH3)排放量与1985~2005年历年的氮氧化物(NOx)排放量,在此基础上模拟了2006~2010年的NOx排放量,并分析了NH3和NOx排放强度的空间分布.结果表明:2004年,我国NH3排放量为12.0Tg,比1995年的10.6Tg增加了大约13.2%;2004年的NOx排放量为20.6Tg,比1995年的12.2Tg增加了大约68.9%,比1985年的6.2Tg增加了大约2.3倍.在1996年以前,我国NH3和NOx的排放量基本相当,但是此后NH3的年排放量在经历了1997~1999年的下降之后,变化比较平稳,而NOx的排放量自2000年之后呈逐年迅速增加的趋势.2004年全国NH3的排放总量中,畜禽排泄、氮肥施用、人类粪便、氮肥与合成氨生产的贡献率分别为69.2%、15.2%、13.9%和1.9%;2004年全国NOx的排放总量中,由于受到我国能源消费结构的制约,煤炭来源的NOx占到了排放总量的77.4%.NH3和NOx的排放强度都具有明显的空间差异,表现在中东部地区的排放强度明显高于西部地区,这与中东部地区人口多、能源消费量大以及畜禽养殖数量大有关.     

离子液体1-丁基-3-甲基咪唑氯盐对斜生栅藻的毒性效应

按照毒性试验标准方法研究了不同浓度离子液体1-丁基-3-甲基咪唑氯盐([BMIM]Cl)对斜生栅藻的影响,测定了半数抑制浓度(IC50)、叶绿素含量、超氧化物歧化酶(SOD)活性、过氧化氢酶(CAT)活性以及藻细胞通透性的变化,观察了80mg/L[BMIM]Cl处理96h对藻细胞的影响.结果表明:[BMIM]Cl对斜生栅藻生长具有抑制作用,随着浓度的增大抑制率增加,叶绿素含量下降, 48h IC50、72h IC50和96h IC50分别为103.77、76.44和68.49mg/L.藻细胞对[BMIM]Cl有一定的氧化应激反应,CAT和SOD活性随[BMIM]Cl浓度升高而降低.[BMIM]Cl对藻细胞的细胞膜有一定程度的破坏作用,藻细胞通透性随浓度升高而增大,同时藻细胞的超微结构受到了[BMIM]Cl的影响,造成质壁分离,叶绿体片层断裂,线粒体嵴数量减少.     

羟基磷灰石-四氧化三铁-沸石复合材料制备及去除水中刚果红研究

采用可溶性磷酸盐、钙离子、二价铁离子、三价铁离子和天然沸石等材料制备了羟基磷灰石-四氧化三铁-沸石(HAPFe3O4-沸石)复合材料,对该复合材料进行了表征,并考察了该复合材料对水中刚果红的吸附作用.结果表明,HAP-Fe3O4-沸石复合材料对水中的刚果红具备良好的吸附能力.当pH由3增加到4或由7增加到11时,HAP-Fe3O4-沸石复合材料对水中刚果红的去除能力下降;当pH由4增加到7时,对刚果红的吸附能力基本保持不变.HAP-Fe3O4-沸石复合材料对水中刚果红的去除率随吸附剂投加量的增加而增加,而对水中刚果红的单位吸附量则随吸附剂投加量的增加而降低.HAP-Fe3O4-沸石复合材料对水中刚果红的吸附动力学过程可以较好地采用准二级动力学模型加以描述,对刚果红的吸附平衡数据可以采用Langmuir和Freundlich等温吸附模型加以描述.根据Langmuir模型确定的最大吸附容量为117 mg·g-1.(pH 7和303 K).HAP-Fe3O4-沸石复合材料对水中刚果红的吸附是自发吸热并伴随熵增加的过程.当pH为7时,HAP-Fe3O4-沸石复合材料吸附水中刚果红的主要机制包括表面配位作用、氢键作用以及路易斯酸碱反应.采用热再生的方法可以使吸附刚果红后的HAP-Fe3O4-沸石复合材料得到再生,热再生后的复合材料可以循环使用并且对水中刚果红的吸附性能良好.X射线衍射分析结果表明HAP-Fe3O4-沸石复合材料含Fe3O4,磁滞回线结果表明HAP-Fe3O4-沸石复合材料具备较高的磁饱和强度,复合材料吸附刚果红后可以很容易地通过外加磁场的作用快速地与水溶液分离.结果表明,HAP-Fe3O4-沸石复合材料适合作为一种吸附剂去除废水中的刚果红.     

东莞市城区地下空间空气质量状况探析研究

文章抽样调查了东莞市城区16处地下空间的空气质量状况,结果表明,地下通道、地下商业设施、公建类和住宅类地下停车场这四类地下空间的气态污染物CO、甲醛、O3、SO2的浓度日均值分别为0.385 mg/mN3、0.055 mg/mN3、0.046 mg/mN3和0.035 mg/mN3;其中,甲醛、O3平均污染指数明显高于CO、SO2,地下通道及地下商业设施的甲醛浓度接近标准值,地下通道部分时段点位出现了超标现象。     

NO参与铝诱导蚕豆保卫细胞死亡的调控

铝(Al)是地壳中含量最丰富的金属元素,是酸性土壤中导致植物生长抑制和作物产量下降的一个主要因素,但铝毒性作用机制尚不清楚.本文以蚕豆叶表皮为材料,研究铝胁迫对气孔保卫细胞活性的影响,探讨NO在铝诱导细胞死亡中的作用.结果表明,一定浓度的A1Cl3可诱导气孔保卫细胞活性降低,部分细胞死亡,且随着铝浓度的增高细胞死亡率增高.死细胞呈现核固缩、核崩解、凋亡小体等典型凋亡特征,且凋亡抑制剂Z-Asp-CH2-DCB能阻止AlCl3诱发的细胞死亡.用NO清除剂c-PTIO、NO合酶抑制剂L-NAME或硝酸还原酶抑制剂NaN3降低铝处理组胞内NO后,细胞死亡率显著降低,胞内ROS、Ca2+水平同期降低;NaN3还能降低铝处理组中具有程序性死亡特征的细胞比率.用ROS清除剂AsA清除铝处理组胞内ROS后,细胞死亡率显著降低,胞内Ca2+和NO水平亦显著降低;铝处理液中加入Ca2+通道抑制剂LaCl3后,细胞死亡率低于铝单独处理组,胞内ROS和NO水平无明显改变.研究结果表明,铝胁迫引起的胞内NO合成增加通过Ca2+信号途径介导了保卫细胞的程序性死亡.     

湘江流域湘潭段水体中氨氮变化趋势的研究

对湘江流域湘潭段2001-2010年近10年来氨氮的污染状况、变化趋势、污染原因等进行分析.结果表明：2001-2010年,湘江湘潭段的氨氮污染虽有起伏变化,但仍呈显著上升趋势,2007年发展至顶峰,随后逐年下降;涟水湘潭段的氨氮污染值自2006年起呈不显著下降趋势;从2008年开始湘江流域湘潭段氨氮年均值未再超标.     

Application of red mud as a basic catalyst for biodiesel production

Red mud was investigated in triglyceride transesterification with a view to determine its viability as a basic catalyst for use in biodiesel synthesis.The effect of calcination temperature on the structure and activity of red mud catalysts was investigated.It was found that highly active catalyst was obtained by simply drying red mud at 200°C.Utilization of red mud as a catalyst for biodiesel production not only provides a cost-effective and environmentally friendly way of recycling this solid red mud waste,significantly reducing its environmental effects,but also reduces the price of biodiesel to make biodiesel competitive with petroleum diesel.