Metal distribution characteristic of MSWI bottom ash in view of metal recovery

Bottom ash is the major by-product of municipal solid waste incineration(MSWI), and is often reused as an engineering material, such as road-base aggregate. However, some metals(especially aluminum) in bottom ash can react with water and generate gas that could cause expansion and failure of products containing the ash; these metals must be removed before the ash is utilized. The size distribution and the chemical speciation of metals in the bottom ash from two Chinese MSWI plants were examined in this study, and the recovery potential of metals from the ash was evaluated. The metal concentrations in these bottom ashes were lower than that generated in other developed countries. Specifically, the contents of Al,Fe, Cu and Zn were 18.9–29.2, 25.5–32.3, 0.7–1.0 and 1.6–2.5 g/kg, respectively. Moreover,44.9–57.0 wt.% of Al and 55.6–75.4 wt.% of Fe were distributed in bottom ash particles smaller than 5 mm. Similarly, 46.6–79.7 wt.% of Cu and 42.9–74.2 wt.% of Zn were concentrated in particles smaller than 3 mm. The Fe in the bottom ash mainly existed as hematite, and its chemical speciation was considered to limit the recovery efficiency of magnetic separation.     

粉煤灰综合利用过程中汞的二次释放规律研究

我国粉煤灰年产生量4亿t左右,近年来利用率稳定在65%～68%,主要利用方式包括建材生产、道路施工、建筑工程和农业利用.建材生产包括高温工序,可能存在粉煤灰中汞的二次释放.本研究设计实验模拟了水泥生产、蒸养砖生产的主要环境因素,利用程序升温脱附的方法研究粉煤灰利用过程中的汞迁移转化规律,并对全国范围内粉煤灰利用过程汞的二次释放量做出估算.研究发现,粉煤灰中的汞以HgCl2(Hg2Cl2)、HgS和HgO的形式存在;水泥生产过程中,粉煤灰中98%以上的汞会释放;蒸养砖生产过程中,粉煤灰中汞的平均释放率为28%,释放率主要受到粉煤灰中的HgCl2(Hg2Cl2)比例的影响.我国粉煤灰利用过程中的汞二次排放量由2002年的4.07 t.a-1增至2008年的9.18 t.a-1,其中水泥行业的贡献率占到96.6%.     

关于医疗垃圾飞灰中二噁英在惰性气氛下的低温热脱附研究

以医疗垃圾焚烧炉布袋除尘器前管道内飞灰(BG)及布袋除尘器后飞灰(AG)为对象,研究不同温度及时间段下其在管式炉中的热脱附特性.结果表明,在低温氮气气氛下,热脱附作用较为明显,2种飞灰中的二噁英都有了不同程度的脱除,其中布袋前飞灰中二噁英的脱除率为82.9%～99.9%之间,毒性当量脱除率为77.3%～99.8%,布袋后飞灰中二噁英的脱除率为66.8%～99.8%之间,毒性当量脱除率为43.5%～99.6%.检测收集到的实验尾气,发现了二噁英的存在,且在300～350℃这个温度段生成量最多,且生成的有毒二噁英同系物中以OCDD为主.通过比较发现,当温度为400℃,加热时间为45 min时2种飞灰中的二噁英脱除效率最高.鉴于惰性气氛下的热脱附对处理飞灰中的二噁英具有较好的作用,可将其大规模应用于实际工程中.     

氨对垃圾焚烧飞灰浸出特性的影响及地球化学模拟

垃圾焚烧飞灰可能因为选择性非催化还原法(SNCR)脱硝过程中氨泄漏、垃圾携带的渗滤液受热挥发等原因而吸附氨.本研究中采用人为添加氨水,在pH为3.66～12.44范围内,研究氨对飞灰中溶解性有机碳(DOC)和重金属浸出的影响,并利用地球化学模拟软件Visual MINTEQ从金属化学形态分布上分析氨对飞灰浸出的影响机制.结果表明,DOC在pH>9和有高浓度氨(≥1 357 mg·L-1)存在时,其浸出量大幅增加,而在浸出液中氨的水平不高于537 mg·L-1时则受氨的影响很小;在pH<6时,飞灰中各金属主要以自由态的金属离子和金属-氯络离子形态大量溶出,且受氨的影响较小;而在pH为8～12的碱性环境中和氨浓度较高时(≥3 253 mg·L-1),氨与金属生成了可溶性的金属-氨配合物,能显著增加Cd、Cu、Ni、Zn的浸出,且在pH=9附近时浸出量达到最大值,但氨对Al和Pb的浸出影响甚微;在pH>12时,Cd、Cu、Ni、Zn主要以羟基金属离子形式存在.在氨浓度为3 253 mg·L-1时,通过利用Visual MINTEQ模拟浸出值与试验数据的对比,发现Al、Pb、Zn的浸出主要由溶解/沉淀模型控制,而Cd、Cu、Ni由溶解/沉淀模型和表面吸附反应模型同时控制,且Visual MINTEQ模型能较好地预测飞灰中Al、Cu、Pb、Zn的浸出特性.     

半干法烟气脱硫灰改性及应用

文章主要对半干法脱硫灰中亚硫酸钙的氧化转化进行研究。半干法脱硫灰中亚硫酸钙对建材质量具有一定影响,通过筛选合适的催化-氧化剂体系对其进行了氧化改性。试验得到了一种复合催化剂,成功用于半干法脱硫灰改性。结合蒸压砖的生产工艺,使亚硫酸钙在生产过程中实现了部分转化,生产的蒸压砖能达到JC239-2001《粉煤灰砖》MU10强度等级。     

高碱性烟气脱硫灰中亚硫酸钙含量分析方法

针对烟气脱硫灰中的亚硫酸钙含量测定方法没有国家标准和行业标准,在参考不同标准中亚硫酸盐的测定方法基础上,对碘量法测定烟气脱硫灰中亚硫酸钙含量的方法进行实验研究。通过自制烟气脱硫灰模拟样的滴定,结果表明高碱性脱硫灰在滴定前应采用先加碘后加酸的顺序进行处理,并使用盐酸或磷酸作为酸化剂,而不宜使用硫酸酸化;采用磷酸(1+1)作酸化剂,控制溶液pH值在2.49¹.40之间,可以准确测定高碱性烟气脱硫灰中亚硫酸钙含量,重复性好,同时可有效避免Fe3+干扰。     

采用巯基捕收剂稳定化处理垃圾焚烧飞灰中的重金属

研究了3种巯基捕收剂,二乙基二硫代氨基甲酸钠（乙硫氮）、乙基黄原酸钾（乙基黄药）和二丁基二硫代磷酰铵（丁铵黑药）,对垃圾焚烧飞灰中重金属的稳定化效果。3种巯基捕收剂的用量均为62.5μmol?g-1飞灰。扫描电镜观察发现,飞灰经稳定化处理后,巯基捕收剂均匀地覆盖于飞灰晶体表面,使矿物晶体棱角变得模糊。利用酸浸提程序（TCLP法）和水浸提程序（水平振荡法）评价飞灰中重金属Cu、Pb、Cd、Cr和Zn的浸出毒性。在0.1mol?L-1醋酸浸提条件下,与Na2S相比,巯基捕收剂对Cu和Pb的稳定化效果较好,其中乙硫氮对Cu的稳定化比率接近100%,丁铵黑药对Pb的稳定化比率达到69.2%;在水浸提条件下,乙硫氮、乙基黄药和丁铵黑药对5种重金属的稳定化比率分别为72.6%、73.5%和76.8%,显著高于Na2S处理（52.4%）。三种巯基捕收剂对5种重金属亲和力的强弱顺序大致为Cu＞Pb＞Cr＞Cd＞Zn,并且超过60%的巯基捕收剂与酸可浸提重金属离子发生了螯合沉淀反应。重金属-巯基捕收剂絮凝物在中性和碱性条件下（pH>6）比较稳定,在酸性条件下（pH<6）可发生部分溶解。为获得较好的重金属稳定化效果,维持稳定化飞灰的高酸缓冲容量十分重要。     

微波酸活化粉煤灰吸附酸性大红染料废水实验研究

以微波酸活化改性后的粉煤灰为吸附剂,对酸性大红染料废水进行吸附脱色处理,考察了吸附时间、pH值、吸附剂投加量等对吸附脱色效果的影响。在酸性大红染料溶液初始浓度为100 mg/L、pH=5、活化粉煤灰投加量为10 g/L吸附1 h时,活化粉煤灰对酸性大红的脱色效果较好,去除率可达96%。对实验数据进行相关数学模型拟合,结果表明微波酸活化改性后的粉煤灰吸附去除酸性大红的等温吸附平衡符合Langmuir吸附等温式,改性前后的吸附过程动力学符合准二级吸附动力学模型,线性相关系数良好。     

生活垃圾焚烧飞灰制陶瓷砖表征

为了探索生活垃圾焚烧飞灰资源化利用途径,在对飞灰化学组成及矿物成分分析的基础上,利用飞灰、黄陶土、耐火砂及长石研制陶瓷砖,最佳配比方案为:飞灰20%,黄陶土60%,长石10%,耐火砂10%,分析了最佳配比制品的吸水率、抗压强度、微观结构及水平振荡浸出毒性。结果表明:飞灰属SiO2-Al2O3-金属氧化物体系,主要矿物成分是钙硅酸盐及铝硅酸盐等,可用于制陶瓷砖;最佳配比制品达MU15强度等级,满足抗风化的要求;随煅烧温度的升高,制品结构不断密实化,960℃烧成的制品显示出完全烧结的特点,960~1 000℃烧成的制品中出现明显的晶化、玻璃化过程。最佳配比制品重金属浸出毒性完全达标,重金属的浸出率与坯体相比大大降低。     

免烧粉煤灰陶粒作为BAF填料处理城市污水

以电厂粉煤灰为主要试验原料,辅以外加药剂(水泥、石灰、石膏、水玻璃),经混合、成球、陈化和养护等工序,制得免烧粉煤灰陶粒,并将其作为曝气生物滤池(BAF)工艺的载体填料处理城市污水.待挂膜启动成功后,考察了水力停留时间( HRT)、COD负荷、氨氮负荷对COD和氨氮去除效果的影响.实验结果表明:在温度为18～21℃、气...