Laboratory-scale study of the suppression of PCDD/F emission during coal and MSW co-incineration

The experimental test of co-incinerating Chinese raw municipal solid waste （MSW） and coal in a laboratory-scale tubular reactor was first reported in present study, and the emission of normal gas components and the effects of the S/Cl molar ratio or coal mixing percentages on polychlorinated dibenzo-p-dioxins and dibenzofurans （PCDDs/Fs） emission were investigated and discussed. The results indicated that OCDD was the only PCDD homologues since others like TCDD-HpCDD was hardly detected, while as the categories of PCDF homologues were comparatively much more general. The amount of PCDD was much larger than that of PCDF in all operating conditions. Since ZPCDF/∑PCDD〈〈1, the dominant role of the precursor formation was proven in our experimental conductions. With increasing the coal addition to MSW （from 0 to 16%）, PCDD and PCDF were reduced considerably. Coal and MSW may suppress the PCDD/F emissions efficiently （over 95%） during the MSW incineration process. The PCDD/F suppression results of the present study could be helpful guidance to the industrial application of Chinese MSW and auxiliary coal co-incineration processes. The PCDD/F stack emission data of two industrial incinerators using co-incineration technology in China seem to have a great positive reduction of PCDDs/Fs.     

生活垃圾焚烧飞灰稳定化处理新工艺的研究

在生活垃圾焚烧处置过程中，会产生一定量的飞灰（Fly Ash）．飞灰中含有危害环境的有害元素，根据国家有关规定，必须按危险废物处置。文章介绍了传统的水泥稳定化处理飞灰的工艺及应用射流技术稳定化处理飞灰的新工艺；对磷酸盐固化剂的固化机理及配比进行了分析；并对新老工艺的成本进行了比较。     

电镀污泥焚烧残渣中的Cu、Ni形态分析

电镀污泥的安全处置治理和资源化利用已成为研究热点,采用改进的BCR和Sposito顺序浸提法考察了不同温度(200,400,600,800℃)焚烧电镀污泥残渣中重金属Cu、Ni的赋存形态分布特征。结果表明:焚烧处理具有显著的减量化效应,重金属铜的残留率为98.6%～90.3%,高于镍(88.6%～76.3%),残渣中的Cu、Ni重金属呈现出富集效应。形态分析表明,随着焚烧温度的提高,生物可利用性形态含量呈现下降趋势,实现了不稳定态向稳定态的转化。     

城市生活垃圾露天焚烧排放PM2.5中重金属污染特征及其暴露健康风险

利用烟气稀释采样系统,针对不同功能区城市生活垃圾(MSW)样品,分别考虑桶内焚烧和自然堆积焚烧两种常见露天焚烧方式,对城市生活垃圾露天焚烧排放PM2. 5中重金属的污染特征及其居民暴露健康风险进行分析和评估.结果表明,5种不同组分垃圾焚烧排放的重金属中,锌(Zn)含量均为最高,可达1 324. 03～3 703. 12 mg·kg~(-1),镉(Cd)含量最低,为20. 25～63. 68 mg·kg~(-1);地累积指数结果显示,铅(Pb)、Zn、砷(As)和Cd的污染程度较高,自然堆积焚烧下均已达中度及以上污染水平,Cd的地累积污染指数远大于5;人体健康风险评估结果表明,8种重金属(Pb、Zn、Cu、Mn、As、Cd、Cr和Ni)经呼吸暴露的非致癌风险值均小于1,属于安全范围内;自然堆积焚烧下,As和Pb对儿童经皮肤接触的非致癌总风险值大于1,存在非致癌风险; 4种致癌元素(As、Cd、Cr和Ni)的致癌风险值均小于1. 0×10~(-4),但若长期处于这种环境下,会存在较低的潜在致癌风险.     

论集中焚烧处置深圳市医疗废物

该文分析了深圳市医疗废的的现状和现行处置方式中存在的问题，根据国内外大中城市医疗废物处置的先进模式与经验和深圳市各方面的条件，论述了集中焚烧处置深圳市医疗废物的可行性和重要性。     

污泥处置国内外进展

随着污水处理率的迅速提高,污泥产量也将大大增加.如不进行妥善处理,污泥中的重金属等有毒有害物质必将造成二次污染.目前国内外污泥处置方法有卫生填埋、堆肥处理、海洋倾倒、农用绿化、焚烧和热处理等.焚烧和热处理被认为是最有前景的处理方法.     

不同粒径铁铝泥对砷(Ⅲ)的吸附效果

以给水处理厂废弃铁铝泥(ferric and alum water treatment residuals,FARs)为载体,考察了不同粒径FARs对砷(Ⅲ)的吸附效果.不同粒径FARs的有效铁铝含量、比表面积和孔体积分别为523.72～1 861.72 mmol.kg-1、28.15～265.59 m2.g-1和0.03～0.09 cm3.g-1,总有机质、富里酸、胡敏酸和胡敏素分别为46.97～91.58、0.02～32.27、22.27～34.09和10.76～34.22 mg.kg-1.SEM和XRD检测表明,不同粒径FARs均以无定形结构存在.批量实验结果表明,准一级和准二级动力学方程均能较好地反映FARs吸附砷(Ⅲ)的动力学过程.不同粒径FARs对砷(Ⅲ)的吸附量随着浓度的增加而增高,用Langmuir等温线方程拟合获得理论饱和吸附量在6.72～21.79 mg.g-1之间.pH值对FARs吸附砷(Ⅲ)的作用影响不大.砷(Ⅲ)吸附量大小与不同粒径FARs的理化性质的变化趋势基本一致,由相关性分析可得,有效铁铝含量和孔体积大小是影响FARs对砷(Ⅲ)吸附的主要因素.     

南京地区冬夏季大气重污染个例对比分析

本文研究了南京仙林地区在秸秆焚烧、逆温造成的大气污染的特征,分析了不同时期大气各成分的浓度变化.秸秆焚烧产生的大气污染事件中,颗粒物浓度上升最为显著,其中PM10的浓度最高可达0.65mg/m3,污染持续时间约36h.冬季污染期持续更长,但颗粒物峰值小于夏季,PM10浓度约在0.4mg/m3.根据Fernald方法反演得到的激光雷达消光系数计算不同高度AOD表明,秸秆焚烧造成的污染在空间上的分布较为均匀而冬季污染期近地表AOD的贡献超过40%.后向轨迹分析表明了污染期的气团在1500m高度的来源和1000m之下有差异,48h内的来源距离较短,近地表的大气质量受到周边地区的影响大,非污染期的气团垂直高度上性质较为均一,来源较为一致,来源距离较长.     

疏浚泥固化处理的优化设计研究

将疏浚泥固化处理后的力学性质指标作为优化设计的约束条件,二次污染问题以及造价作为优化的目标函数,建立了固化处理的多目标优化设计模型。通过对固化处理进行优化设计可以解决力学性质、二次污染以及造价三者之间存在的矛盾,为建立系统的固化理论奠定了基础。并采用所建立的优化模型对大亚湾疏浚泥的固化处理进行了优化设计。     

电镀污泥焚烧渣资源化及无害化处理研究

研究了用化学浸出方法从焚烧法预处理后的电镀污泥中回收有价金属－铜和镍及制取高质量的海绵铜和硫酸镍产品的工艺流程和技术条件，结果表明，选用H2SO4加入量为7mL加入量为7mL、液固比为3，浸出时间为1h，浸出温度为20℃，给料细度为－74μm占77％时，铜、镍的浸出效果较好，扩大试验也验证了其准确性，同时，探讨了浸出渣和除铁渣无害化处置的可能性。