Hemoglobin (Hb) immobilized on amino-modified magnetic nanoparticles for the catalytic removal of bisphenol A

Catalytic removal of bisphenol A from aqueous solution with hemoglobin immobilized on amino-modified magnetic nanoparticles as an enzyme catalyst was reported. The amino-modified magnetite nanoparticles were firstly prepared by the coprecipitation of Fe²⁺ and Fe³⁺ with NH₃·H₂O and then modified by 3-aminopropyltriethoxysilane. The immobilization process was optimized by examining enzyme concentration, glutaraldehyde concentration, cross-link time, and immobilization time. The optimum conditions for the removal of bisphenol A with immobilized hemoglobin were also investigated. Under the optimality conditions, the removal efficiency of bisphenol A was about 80.3%. The immobilization had a beneficial effect on the stability of hemoglobin and conversions of bisphenol A. According to the proposed breakdown pathway and the intermediates, the enzyme-catalytic removal of bisphenol A by the immobilized hemoglobin is considered to be an effective method.     

制药工业发酵副产品磁性吸附剂吸附六价铬的研究

利用包埋法,以海藻酸钠和聚乙烯醇作为基质,制药工业发酵副产品主要为红色链霉菌菌体为吸附剂,与磁性纳米颗粒制备磁性吸附剂,对含Cr(Ⅵ)废水进行吸附研究。磁性吸附剂吸附饱和后,在外加磁场作用下迅速与液相分离。研究结果表明,在溶液pH为0~12,搅拌转速为0~200 r/min,温度变化范围在0~50℃的条件下,经过5个循环,吸附剂的形状,机械强度等性能均保持完好;优化的pH为2;最佳温度为25℃;吸附过程符合Langmuir吸附等温线模型;吸附动力学过程符合Lagergren模型;经5次吸附-解吸附循环实验,磁性吸附剂对六价铬的吸附和解吸附能力均保持良好。     

磁场对厌氧活性污泥的生物活性影响研究

研究了磁场对厌氧活性污泥的生物活性影响.使用场强为0、100、200、300、400 GS的磁场对样品分别作用10 min, 同时加以搅拌,通过测量各样品的pH值、ORP、电导率等考察其活性.结果表明, 磁场对厌氧活性污泥的活性存在着影响,并存在最佳值范围.本实验中,磁场场强为200 GS左右时,厌氧活性污泥的活性被明显强化.     

基于磁性分离测定水样中的吲哚美辛

免疫磁性微球(SMPPA)应用于水样中吲哚美辛的分离富集,并应用高效液相色谱法对吲哚美辛进行测定。在优化的淋洗和洗脱条件下,70%甲醇和10%甲醇分别作为洗脱液和淋洗液,其回收率能达到90%。选择了湖水、河水、自来水、污水厂进口水以及医院排水为真实样品进行测定,其中湖水、河水、自来水3种真实水样中未能检测出吲哚美辛,污水厂进口水以及医院排水中吲哚美辛的含量分别为0.762、35.4 ng/m L。对这5种水进行加标回收吲哚美辛,加标回收率为92.7%~113%,RSD为1.09%~7.73%。该方法具有简便、快速、特异性等特点,能有效地分离富集水样中的目标物,对其他目标物具有广泛的实际应用价值。     

充电式交流磁粉探伤仪的应用研究

本研究把锂电池的直流电转换为交流方波电来驱动磁探仪工作,这样得到一种全新的充电式磁粉探伤仪,它不需要外部接电、电磁转换效率高、可以连续工作、输出为交流磁场或交叉磁场、灵敏度高、安全可靠.它解决了现有磁粉探伤仪需要搭接长长的电缆、存在漏电危险、发热严重、不能连续工作等缺点.本研究将给磁粉探伤领域带来革命性的发展,并促进新...     

磁性膨润土的制备及类Fenton氧化法处理焦化废水

以Al-Fe柱撑膨润土为原料,通过原位氧化沉淀法负载纳米Fe₃O₄颗粒,制备磁性膨润土。采用XRD,SEM,EDS技术对磁性膨润土进行了表征,并将其作为类Fenton反应催化剂对焦化厂二沉池出水（COD为267.6 mg/L、色度为428度）进行了深度处理,探讨了各反应条件对处理效果的影响。实验结果表明：Fe₃O₄颗粒较为均匀地分布在膨润土表面,负载牢固;在H₂O₂加入量70 mmol/L、磁性膨润土加入量0.8 g/L、反应温度30 ℃、初始废水pH 5.0的条件下反应30 h,废水COD和色度的去除率分别达到78.5%和93.4%,COD和色度分别降至57.5 mg/L和28度,满足GB/T 19923—2005《城市污水再生利用 工业用水水质》的要求;磁性膨润土使用4次后,对废水的处理效果仍很稳定。     

赋磁硅气凝胶的制备、表征和吸附异狄氏剂特性

以工业水玻璃为硅源,采用六甲基二硅胺烷(HMDZ)作为改性剂,掺杂纳米级Fe3O4,通过溶胶-凝胶、常压干燥技术,制备得到赋磁硅气凝胶吸附材料(MSA)。采用红外光谱(FTIR)、扫描电镜(SEM)、比表面分析(BET)及振动样品磁强计(VSM)等方法对其结构进行了表征,并对其吸附性能进行研究。结果表明,制得的赋磁硅气凝胶接触角在113°～116°之间,比表面积可达589.79 m2/g,密度约为0.192 g/cm3,饱和磁化强度约为0.44 emu/g,具有超顺磁性。赋磁硅气凝胶对疏水性有机物异狄氏剂表现出良好的吸附性能,符合Freundlich等温吸附模型,KF为42.91;吸附动力学符合准二级动力学模型,吸附速率常数为0.0341 g/(mg.min)。     

稳恒磁场作用下微生物燃料电池的产电特性和电化学阻抗谱分析

对混合菌接种的双室微生物燃料电池加载磁场强度为175 mT的稳恒磁场,利用电化学交流阻抗等电化学分析方法,考察了在磁场作用下微生物燃料电池（MFC）产电性能的变化,分析了磁场对MFC各部分内阻的影响。加载磁场使已启动完成的MFC的产电明显增强,开路电压提高了10%。加载磁场后最大功率密度为2.08 W/m2,大于加载前的1.58 W/m2,表观内阻由170Ω降至80Ω。电化学阻抗谱分析确定了阳极、阴极和全电池的等效电路模型,拟合结果发现阳极极化内阻约为5Ω。加载磁场使MFC的阴极极化内阻由74.98Ω降至56.73Ω。     

锰磁活性炭的制备及其性能表征

以酶解提制烟碱后的烟渣和电解锰渣回收锰为原料,制备具备磁性和发达孔隙的活性炭。利用氮气吸附技术、红外光谱（FTIR）表征与分析了活性炭表面的孔隙结构和物化性质,考察了活性炭对亚甲基蓝的吸附性能和磁学性能。结果表明：以Mn／C基质废弃物为原料制得活性炭具有磁学性能;适量锰的添加有利于活性炭微孔的形成和发育;采用一步焙烧法有助于磁化物和活性炭基体相互作用形成化学键合,提高饱和磁化强度,实现废弃资源的充分利用。     

磁场强化臭氧液相传质

对不同种气液接触方式的臭氧气液传质性能进行了研究,考察了磁场作用下的臭氧进气量,液面高度以及液相p H值对微气泡臭氧传质效果的影响规律。实验研究表明,相同实验条件下,采用微气泡附加磁场(磁铁相吸)比底部曝气盘和微气泡发生器接触方式,液相中溶解的臭氧浓度分别提高了72.6%和11.4%,经过30 min后,水中溶解的臭氧浓度为8.91 mg/L,传质系数为0.2272 min-1,传质系数显著提高;在磁场的作用下的微气泡臭氧接触方式,臭氧气体流量较小的情况下,臭氧在液相溶解效率较高,液面高度h越高溶解的臭氧浓度越低,传质系数kLa值随着气液流量的增加而增加,但是随着液面高度h的增加而降低,液相的p H值也影响着传质效果,p H越低,水中溶解的臭氧浓度越高,传质系数越高。