Preparation and application of efficient TiO2/ACFs photocatalyst

Activated carbon fibers （ACFs） supported titanium dioxide （TiO2） photocatalyst was developed by sol-gel method. The surface morphology and microstructure of the photocatalyst were characterized with scan electron microscope（SEM）, X-ray diffraction patterns and specific surface area analysis. The prepared photocatalyst is specially helpful for the removal of low molecular weight organic pollutants in wastewater. Decomposition efficiency of methylene blue solution by TiO2/ACFs catalyst reached almost 100% under 60 min reaction, while the decomposition efficiency by pure TiO2 was only 25% under 3 h reaction. The mineralization of toluene aqueous solution was measured by total organic carbon instrument, and the evolution of intermediate species was detected by gas chromatograph instrument. The results indicated that the prepared photocatalyst not only enhanced the photoactivity of TiO2, but also suppressed the emergence of intermediate species, which may be more deleterious to human. The enhancement of photocatalysis was due to increased efficiency of adsorption and desorption, which were control steps in heterogeneous photocatalysis.     

抚仙湖生态脆弱性特征分析与改善对策研究

从水生态系统、湖滨带、陆域生态系统、水质状况、水资源状况等方面对抚仙湖的生态脆弱性进行了分析研究,并根据抚仙湖的实际状况,提出了改善对策措施。     

纳米酸性水钠锰矿去除亚甲基蓝的研究

酸性水钠锰矿是普遍存在于土壤与海洋、湖泊及河流沉积物中的一种氧化锰矿物,因其颗粒细小、比表面积大、负电荷量高、表面活性强,影响和决定着污染物的行为和归趋。采用回流法制备纳米酸性水钠锰矿,运用X射线衍射(XRD)与Rietveld粉末衍射峰形全谱拟合技术表征其晶体结构,并通过扫描电镜(SEM)和透射电镜表征(TEM)观察其晶体形貌。研究纳米酸性水钠锰矿对亚甲基蓝(Methylene Blue,MB)的去除作用,并讨论影响因素(p H值、矿物浓度、染料浓度和温度)对MB去除的影响。研究结果表明,降低反应p H值、升高锰氧化物浓度、降低染料浓度及升高反应温度都可以促进MB的去除。     

洪湖流域半封闭池塘河蟹养殖氮磷污染负荷研究

选取洪湖流域半封闭池塘河蟹养殖区域为调查样本,针对一个养殖周期内6个监测点位(1个背景点,3个养殖水体点,2个纳污水体点)TN、TP值进行监测分析。监测结果表明,养殖准备期(12月～1月),养殖水体TN、TP值与同期背景值没有明显差异;养殖中后期(3月～10月),养殖水体和纳污水体TN、TP均明显高于同期背景值,大部分为劣Ⅴ类水质。按5～10月份养殖水体TN、TP实测值进行化学分析法估算,一个养殖周期内养殖水体TN、TP污染负荷为27.61kg/hm2、7.33kg/hm2,则洪湖流域半封闭池塘河蟹养殖排放的TN、TP污染负荷约为269.11t/a、71.46t/a。另据对样本区域养殖生产过程的调查,按物料平衡法估算的TN、TP污染负荷为57.61kg/hm2、11.60kg/hm2,而洪湖流域半封闭池塘河蟹养殖TN、TP污染负荷约为561.51t/a、113.06t/a。     

六价铬抑制淡水蓝绿藻生长的毒性效应

采用化学品毒性藻类测试的标准方法得到Cr(Ⅵ)抑制蛋白核小球藻、聚球藻、极大螺旋藻、钝顶螺旋藻、羊角月牙藻和四尾栅藻生长的96h-EC₅₀分别为4.96、6.50、11.16、11.74、12.43、20.89mg/L;6种蓝绿藻对Cr(Ⅵ)耐受性大小顺序为:四尾栅藻＞羊角月牙藻＞钝顶螺旋藻＞极大螺旋藻＞聚球藻＞蛋白核小球藻.不同藻类对Cr(Ⅵ)的敏感程度可能与细胞大小和形状、细胞壁结构、藻类分泌物以及酶的作用有关.本文运用X射线吸收近边结构(XANES)初步研究了蛋白核小球藻对Cr(Ⅵ)的吸收和转化.     

低温燃烧合成纳米Ni掺杂TiO2光催化剂的表征及活性研究

采用低温燃烧合成法制备了Ni掺杂TiO₂光催化剂,通过紫外-可见漫反射光谱(UV-Vis DRS)、X射线粉末衍射(XRD)、激光散射、热重-差示扫描量热分析(TG-DSC)等方法对催化剂的光吸收特性、晶相组成、粒度分布、升温过程中化学变化等进行了表征,以亚甲基蓝为模型污染物考察了催化剂在可见光下的光催化活性.结果表明,相对P25而言,Ni掺杂TiO₂的光吸收带边红移,当Ni/Ti原子比为0.4时,催化剂的带隙宽度为2.3eV,对应的吸收带边为564nm;催化剂晶型以锐钛矿TiO₂为主,随Ni掺杂量增大,NiTiO₃比例升高;催化剂粒径主要分布在50～150nm之间,占总量的96.9%;升温过程中催化剂在445.2℃发生晶型转化,出现锐钛矿和NiTiO₃晶体.催化剂显示出较高的催化活性,在可见光作用150min后最高可使93.9%的亚甲基蓝分解,活性高于P25.     

TiO_2/ACFs催化剂光催化降解染料废水活性研究

以活性炭纤维为载体,采用溶胶-凝胶法制备得到了活性炭纤维负载二氧化钛光催化剂(TiO2/ACFs),并且以亚甲基蓝为模型化合物模拟研究了活性炭纤维负载二氧化钛光催化剂(TiO2/ACFs)对染料废水的光催化活性。通过扫描电镜(SEM)、XRD等表征方法对活性炭纤维负载二氧化钛光催化剂(TiO2/ACFs)的结构进行了研究。SEM表征显示,大部分二氧化钛以膜的形式均匀地包裹在活性炭纤维丝上,二氧化钛膜层的厚度大约为330 nm,还有一部分TiO2是以颗粒的形式负载在活性炭纤维上。FT-IR分析可知,ACF与TiO2之间有Ti—O—C键生成,说明TiO2与ACF结合牢固,TiO2不易脱落。通过对亚甲基蓝降解可知当煅烧温度为500℃时,TiO2/ACF的光催化性能最好,通过对比发现500℃煅烧制备的催化剂也具有最好的循环使用性能,经过4次循环后该催化剂对亚甲基蓝的去除率仍达到90.2%。     

H4SiW12O40/TiO2/beads光催化降解亚甲基蓝的研究

以钛酸四丁酯为原料,空心微珠为载体,采用溶胶凝胶法制备TiO₂/beads光催化剂载体,然后浸渍法制备出H₄SiW₁₂O₄₀/TiO₂/beads表面负载修饰型复合光催化剂,并运用SEM、XRD、FT-IR和DRS对催化剂进行表征和分析。研究了H₄SiW₁₂O₄₀/TiO₂/beads对亚甲基蓝降解的光催化活性,考察了光强度、pH值、曝气量、底物浓度和催化剂用量等对催化效率的影响。实验结果表明,在中性条件下,H₄SiW₁₂O₄₀/TiO₂/beads催化剂的投加量为0.25 g/L,浓度为7.5 mg/L的亚甲基蓝溶液在250 W的紫外灯和600 W的可见光灯下光照60 min降解率分别可达到94.5%和55%。     

杂多酸/TiO2复合光催化材料的制备及光催化性能

采用浸渍法制备了复合杂多酸(H3PW12O40/TiO2,H4SiW12O40/TiO2)催化材料,通过UV-Vis、IR和XRD对其结构进行了表征,研究了合成的催化剂对有机染料亚甲基蓝降解的催化活性.讨论了催化剂投加量、亚甲基蓝溶液的初始浓度、酸度等对催化脱色效果的影响.结果表明,当溶液酸度为pH=3,催化剂用量为4...     

两种染料与阿特拉津在沉积物上的竞争吸附

通过批量吸附实验研究了两种染料对阿特拉津(AT)在天然水体沉积物上吸附的影响.结果表明,与对照相比,刚果红(CR)和亚甲基蓝(MB)在实验浓度范围内均与AT发生竞争吸附,分别使AT的吸附率降低了14.29%和30.16%.共存体系的溶液化学条件发生变化时,AT的吸附有所不同.当体系pH值和温度升高时,AT的吸附量减小;而离子强度的升高,促使AT在沉积物上的吸附量增大.