炼铁高炉净环水高pH碱性运行的阻垢缓蚀研究

以某炼铁高炉妆环水为对象，对循环冷却水高ＰＨ碱性运行阻垢缓蚀进行了研究，筛选出了一复合配方。工业应用试验结果表明，此配方对Ａ３钢的污垢附着速率，腐蚀速率和污垢热阻均低于国家规定的指标要求，说明该配方具有良好的阻垢缓蚀性能。     

热镀锌板表面钝化时的磷化工艺

热镀锌板表面钝化（铬酸盐钝化），主要是为了防止在使用过程中其表面被氧化。由于表面的钝化膜的存在。使得磷化工艺无法进行，从而影响涂装后涂层的附着力（铬酸盐钝化膜不如磷化膜附着性好）和耐蚀性能（铬离子不耐氯离子的腐蚀）。为了提高热镀锌板表面钝化后其表面的涂装性能，开发出一种适合上述条件的磷化工艺。     

多孔氧化铝层制备的研究

采用预腐蚀与交流腐蚀相结合的方法．研究了多孔氧化铝层的制备工艺．探讨了制备工艺中各步骤的作用以及影响因素。利用扫描电镜，研究了多孔氧化铝层制备工艺对铝箔微观形貌的影响。研究表明．交流腐蚀工艺对铝箔表面微观形貌的改变作用最明显。一次后处理后铝箔表面蚀孔变密．氧化膜的结构更加疏松细腻。二次后处理，调整和热处理等步骤对铝箔表面的微观形貌影响不大。     

硝酸盐对铝合金点蚀行为的影响

采用动电位极化测量技术研究在一定氯离子存在下硝酸盐对 LY12CZ硬铝合金点蚀发生、发展行为的影响。试验认为,硝酸盐在 浓度较低时没有钝化作用,使铝合金电位从钝化区向活化区过渡,但 它使再钝化电位提高,在一定的钝化条件下,可促进氧化膜的修复; 当硝酸盐浓度大于某一数值时,铝的点蚀电位明显增加,能有效抑制 点蚀发生。这一值的大小与介质中存在的氯离子含量有关。     

Experimental study on the synergistic inhibition effect of nitrogen and ultrafine water mist on gas explosion in a vented duct

In this study, in order to research the synergistic inhibition effect of nitrogen and ultrafine water mist on gas explosion in a vented duct, a semi-confined transparent chamber was designed with the size of 120 × 120 × 840 mm, and the experiments were carried out with stoichiometric methane/air premixed mixture (fraction of methane: 9.5%), adding different fractions of nitrogen and ultrafine water mist. The experimental results showed the following: The combination of nitrogen and ultrafine water mist had a synergistic inhibiting effect on methane/air explosion, which was preferable to the single use of any kind. With the increase of spraying time of water mist and fraction of nitrogen, the initial shape of the explosion flame became snakelike, and at the same time the peak flame propagation speed and peak overpressure decreased significantly. When the nitrogen fraction was increased to 10% and the mist spraying time was increased to 2min, synergistic inhibiting effect on overpressure was high efficient. However, with the increase of spraying time of water mist and fraction of nitrogen going on, the amount of increase of explosion inhibition efficiency was gradually reduced.     

Experimental study on explosion inhibition by heptafluoropropane and its synergy with inert gas

The inhibition effect of heptafluoropropane (CF₃CHFCF₃) on methane explosions under different inhibitor concentrations in a closed vessel was studied. A high-speed camera and a pressure sensor were adopted respectively to record flame propagation characteristics and pressure data. Results indicate that the relationship between flame propagation and pressure rising was correlated. As the equivalent ratio (ϕ)≤1, the pressure presented a trend of rising firstly and then decreasing with increasing CF₃CHFCF₃ concentration, and it was found that there existed a critical concentration for pressure decrease. As ϕ > 1, the pressure exhibited a decreasing trend. Although the pressure appeared to seemingly increase, the moment that the pressure began to rise (t_rise) and the moment that the maximum explosion overpressure appeared (t_Pmax) were obviously delayed. The average rate of pressure rise ((dP/dt)_ave) was decreased as the concentration of CF3CHFCF3 increased. It indicates that CF₃CHFCF₃ can effectively reduce the explosion reaction rate. The critical concentration of CF₃CHFCF₃ for complete inhibition was determined. Meanwhile, the synergy of CF₃CHFCF₃-inert gas can improve the inhibition effect. Compared with CF₃CHFCF₃–N₂, the synergy of CF₃CHFCF₃–CO₂ presented a better inhibition effect, and the inhibition effect was increased with increasing inert gas concentration. And the mechanisms of physical and chemical effects on explosion inhibition were analyzed.     

A mathematical model of crevice corrosion for buried pipeline with disbonded coatings under cathodic protection

Crevice corrosion occurs in a holiday and disbonded region between coating and pipeline steel. Cathodic protection (CP) is generally recognized as the most effective method for corrosion prevention of pipeline, but its effectiveness may be reduced at defects in a disbonded coating. It is difficult to measure and probe corrosion parameters accurately based on experimental work. Therefore, a mathematical model is necessary to identify the phenomena and mechanisms that contribute to the crevice corrosion process. In this work, a mathematical model was developed to determine the evolution of chemical and electrochemical transient processes of crevice corrosion in NaCl dilute solution, and the effect of cathodic protection and crevice width on corrosion of 20# steel pipeline with disbonded coatings. Results have demonstrated that the extent of crevice corrosion depends on the crevice geometry and could be influenced by the increase of crevice depth and decrease of its width. The oxygen concentrations drop significantly inside a crevice whether CP is applied or not and whether crevice width decreased or not. The pH values and conductivity of crevice solution increase with the time. The research provides a theoretical foundation for cathodic protection of pipelines and establishes an effective corrosion model which can identify the phenomena and mechanisms of the crevice corrosion process. This work could be used to help mitigate the corrosion failure of pipelines to prevent catastrophic accidents in oil, gas and chemical process industries.     

磷酸盐对亚硝化系统的抑制及恢复

通过接种城镇污水处理厂的污泥,采用连续流反应器启动亚硝化系统并改变进水磷酸盐的浓度,研究了不同磷酸盐浓度对亚硝化系统的影响.结果表明经过14 d的运行,亚硝化系统启动成功,氨氮转化率达到92.2%,亚硝酸盐累积率为73.66%,亚硝酸盐产生速率达到14.42 g·(m~3·d)~(-1).磷酸盐浓度在10~30 mg·L~(-1)时对亚硝化系统的影响并不大;随着磷酸盐浓度持续提高,氨氮转化率在不断降低.当磷酸盐的浓度为80 mg·L~(-1)时,系统的氨氮转化率为13.6%,亚硝酸盐累积率仅18.19%,亚硝酸盐产生速率仅0.54 g·(m~3·d)~(-1),亚硝化反应受到严重抑制.将进水磷酸盐浓度降低到0,经过14 d运行,亚硝化系统获得恢复,且氨氮转化率可以达到80%以上,亚硝酸盐累积率达到86.96%,亚硝酸盐产生速率为15.63g·(m~3·d)~(-1).     

我国工业危险废物的来源、处理及监管对策与建议

通过大量环境统计数据的分析,对我国工业危险废物的产生、综合利用、处置和贮存,从行业来源、区域分布进行了分析和总结。结合我国工业危险废物企业自建设施和政府集中处理设施处理情况,对我国工业危险废物的处理和环保监管对策提出了若干建议。     

Effects of free ammonia on volatile fatty acid accumulation and process performance in the anaerobic digestion of two typical bio-wastes

The effect of free ammonia on volatile fatty acid(VFA)accumulation and process instability was studied using a lab-scale anaerobic digester fed by two typical bio-wastes:fruit and vegetable waste(FVW)and food waste(FW)at 35°C with an organic loading rate(OLR)of 3.0 kg VS/(m~3·day). The inhibitory effects of free ammonia on methanogenesis were observed due to the low C/N ratio of each substrate(15.6 and 17.2,respectively). A high concentration of free ammonia inhibited methanogenesis resulting in the accumulation of VFAs and a low methane yield. In the inhibited state,acetate accumulated more quickly than propionate and was the main type of accumulated VFA. The co-accumulation of ammonia and VFAs led to an "inhibited steady state" and the ammonia was the main inhibitory substance that triggered the process perturbation. By statistical significance test and VFA fluctuation ratio analysis,the free ammonia inhibition threshold was identified as 45 mg/L. Moreover,propionate,iso-butyrate and valerate were determined to be the three most sensitive VFA parameters that were subject to ammonia inhibition.