聚叠氮缩水甘油醚嵌段聚叠氮乙酸乙烯酯的合成及热稳定性研究

以聚叠氮缩水甘油醚(GAP)和4,4'-偶氮(4-氰基戊酸)(ACVA)为原料合成大分子引发剂(MI-GAP),用其引发氯乙酸乙烯酯自由基聚合,得到聚叠氮缩水甘油醚嵌段聚氯乙酸乙烯酯(GAP-bPVCA),最后将其叠氮化得到含能聚合物——聚叠氮缩水甘油醚嵌段聚叠氮乙酸乙烯酯(GAP-b-PVAA)。采用傅里叶变换红外光谱(FT-IR)、紫外-可见光谱(UV-Vis)、核磁共振氢谱(1H NMR)对GAPb-PVAA的结构进行了表征。利用差热分析(DTA)、热重分析(TG)和微分热重分析(DTG)对GAP-b-PVAA的热稳定性进行了研究。结果表明,GAP-b-PVAA在空气中200℃未见分解;GAP-b-PVAA具有两个热失重过程,其中最大质量损失发生在228~243℃范围内,失重率为68.74%。GAP-b-PVAA热分解动力学参数由不同升温速率下的DTA表征数据,通过Kissinger方法和Ozawa方法计算得到,两种方法得到的表观活化能Ea数值相近,表明GAP-b-PVAA热稳定性良好,有望用于熔铸炸药中作为一种含能黏结剂。     

Ti-MCM-41的微波水热法合成、表征及其催化氧化性质研究

本研究利用微波水热法合成Ti-MCM-41,并采用XRD、FTIR、BET、XPS及TEM等技术对材料进行表征.同时,使用甲基橙溶液作为光催化氧化的对象,对光催化剂的氧化性能进行考察.实验结果表明:利用微波水热法合成Ti-MCM-41,可将合成时间缩短至3 h,能够大大缩减反应时间并节省能源.通过在MCM-41多孔结构中掺杂钛,可明显提高其光催化活性.在酸性溶液中,Ti-MCM-41的催化氧化效率较高.XRD、FTIR、BET、XPS及TEM等表征结果表明,钛成功地掺入到了MCM-41中,并未破坏其多孔有序的结构,Ti-MCM-41同时兼具介孔材料的高比表面积和二氧化钛的光催化性能,有利于在环境污染修复上的应用.     

淀粉基超强吸水剂的研究

本文研究了淀粉基超强吸水剂的合成方法，探讨了反应条件对吸水性的影响.     

REGIONALIZATION OF STORM HYETOGRAPHS1

ABSTRACT: Regionalization of design storms can enhance their utility. Otherwise they have to be separately developed for different regions. Huff curves developed from point rainfall data collected at Coshocton, Ohio, and Chicago, Illinois, and from area-averaged Illinois and Texas precipitation data, are compared. The curves are similar in shape and position, with some visual differences depending on quartile. Kolmogorov-Smirnov tests showed no significant differences in moat of the comparisons. Where significant differences existed, they may not represent real differences due to the small number of storms sampled. Consequently, regionalization of Huff curves from Ohio to Illinois to Texas may be appropriate. The comparison of Huff curves is affected to an unknown degree both by the effects of area averaging of data and by basis. of-development differences. The effects of observed differences in Huff curves on watershed response variables (e.g., peak flow) requires further study.     

The mild hydrothermal synthesis of hydrogrossular from coal ash

In this study, an attempt was made to synthesize hydrogrossular, a group of garnet minerals, under hydrothermal conditions at temperatures below 180°C, using coal ash, which is the solid waste from thermal power plants, as a starting material. A single phase corresponding to hydrogrossular was found at around 120°C, and the hydrogrossular coexisted with 11-Å tobermorite above 140°C. The hydrogrossular phase decreased with increasing reaction temperature, while that of 11-Å tobermorite increased concurrently. The physicochemical properties of the hydrogrossular obtained from the hydrothermal synthesis was characterized by X-ray diffraction thermogravimetry/differential thermal, analysis, scanning electron microscopy, Fourier transform infrared spectroscopy, and X-ray fluorescence spectroscopy. Received: September 4, 2000 / Accepted: March 7, 2001     

聚天冬氨酸的阻垢分散性能

以马来酸酐和铵盐为原料合成聚天冬氨酸,对聚天冬氨酸进行了红外光谱和差热-热重分析表征,并对其阻碳酸钙垢及分散氧化铁的性能做了较系统的研究。结果表明：所得产品的产率均在98．11％以上,并基本具备目标产物聚天冬氨酸的各种官能团;热分解温度为386．3℃;当加入量为4mg/L时,其阻垢率已接近100％;当加入量为30mg/L时,分散氧化铁性能最好,溶液透光率为48．7％。     

化学合成聚3-羟基丁酸酯薄膜的生物降解性

利用土壤埋藏,海水降解,活性污泥及高等真菌降解实验对化学法合成的聚３－羟基丁酯,薄膜进行了生物降解性研究。结果表明,降解ＰＨＢ薄膜的微生分布比较广泛;     

钛酸纳米管的光催化性能研究

以Ti0_2(Degussa P25)和NaOH为原料,采用水热法制备钛酸纳米管.以亚甲基蓝溶液(Methylene Blue,简称MB)为模型污染物,研究水热反应条件对所制钛酸纳米管光催化性能的影响,以及钛酸纳米管加入量、溶液pH值和MB初始浓度等光催化反应条件对钛酸纳米管光催化性能的影响.研究表明:水热反应温度为150℃,反应时间为48 h制得的钛酸纳米管对MB的光催化效率最高;钛酸纳米管的加入量、溶液pH值和MB初始浓度等光催化反应条件对钛酸纳米管的光催化性能有较大影响.     

地下城市综合管廊的抗火构造与消防设计

综合管廊作为现代化城市的基础设施,能够从根本上解决管线埋设或架立引起的挖掘道路、影响交通、破坏景观等问题。提高道路和公用管线的管理水平,有效利用地下空间,提高防灾能力,是现代化都市的必然要求。本文从管廊的构造、抗火设计要求、管线布置、消防系统等方面出发,对地下城市综合管廊的设计提出了一些具体的建议。     

优选粉煤灰制备人工合成沸石及去除氨氮研究

7种粉煤灰样品的物理化学性质,如元素组成、结晶相组成、比表面积、灼失量、阳离子交换容量和pH得到表征。采用熔融法提取硅铝效率作为粉煤灰原料优选的依据,并通过L9（34）正交实验研究氢氧化钠投加量、熔融温度、氢氧化钠提取液浓度和体积对于硅铝提取效果的影响。结果表明,湿式除尘技术收集的低品位粉煤灰比电除尘技术所收集粉煤灰更...