铜铈掺杂六铝酸盐的脱硝性能

用共沉淀法制备用于脱除NO的六铝酸盐催化剂LaMxAl12-xO19(M =Cu,Ce,CuCe).用XRD、H2-TPR和BET对催化剂进行了结构和物性表征.用微型催化反应装置考察了催化剂在CO选择性催化还原NO中的活性.结果表明,Cu离子易于进入六铝酸盐晶格内,形成完整的六铝酸盐结构.Ce离子不易于进入六铝酸盐晶格内,主要以CeO2的形式存在.在CO+ NO条件下,3种催化剂都表现出较好的脱硝活性,LaCuCeAl10O19中由于Cu离子与Ce离子间产生协同作用,该催化剂的脱硝活性有所增加.加入SO2后,3种催化剂都有不同程度的失活现象发生,其中LaCuAl11O19催化剂受SO2中毒影响最严重,LaCuCeAl10O19催化剂的脱硝活性在三者中最好.     

The use of electrolyte redox potential to monitor the Ce(IV)/Ce(III) couple

Mathematical modelling of the oxidation reduction redox potential (ORP) of an electrolyte has been carried out for a batch system comprising an electrochemical reactor and an electrolyte circuit containing a redox couple. The ORP can be useful to monitor the environmental impact of chemical species in solution that represent a risk to the environment. Considerations of four fundamental equations, namely, the Nernst equation, a mass balance, Faraday's laws of electrolysis and a first order kinetic equation, leads to an expression for the electrolyte redox potential as a function of the batch time, the electrical charge and the redox concentration. Such an expression facilitates graphical plots which can be used to estimate kinetic parameters, current efficiency and the relative redox concentration. The Ce(IV)/Ce(III) system has been chosen as a model reaction for electrolyte redox potential measurement in a batch recycle system consisting of a pumped flow through a divided FM01-LC parallel-plate electrochemical reactor (64cm(2) projected electrode area) and a well mixed tank (3600cm(3)). The differences between experimental and model predictions are discussed.     

Fe~(3+)及Ce~(3+)掺杂对TiO_2纳米粒子性能的影响

以溶胶-凝胶法制备纯的和分别掺杂Fe3+、Ce3+的TiO2纳米粒子,以橙黄IV的光催化氧化评价纳米粒子的紫外光与可见光活性,利用TG-DSC、XRD、BET及UV-Vis吸收光谱考察掺杂对TiO2的相变、粒径、比表面积及光吸收性能的影响,在归一化条件下探讨Fe3+及Ce3+掺杂对TiO2活性和表面性质产生影响的机制。结果表明:Fe3+及Ce3+的最佳掺杂量分别为0.2%和0.04%;Ce3+抑制TiO2由锐钛矿向金红石转变以及改善TiO2高温组织稳定性的能力均明显大于Fe3+;Fe3+和Ce3+掺杂均能提高TiO2的紫外光活性并扩展TiO2的光响应范围,但光生电子与空穴复合以及光腐蚀使它们对TiO2可见光活性的提高并不显著。Fe3+和Ce3+的半径及其相应氧化物的性质决定了两者对TiO2性能的不同影响。     

Pd／Ce02-A1203对烟气中多环芳烃的催化氧化性能研究

采用浸渍法制备了不同负载量及不同钯铈比（Pd：Ce）的Pd/CeO2-Al2O3催化剂,并结合XRD、BET、SEM、O2-TPD和H2-TPR等方法对催化剂的性质进行了表征,研究了所制备的催化剂对燃煤烟气中多环芳烃（PAHs）的催化转化效率.XRD和SEM结果表明,Ce和Pd在Al2O3表面呈高度分散状态,有利于PAHs的催化氧化.BET测试表明,Ce的引入改变了催化剂表面孔径结构,提高其比表面积.O2-TPD和H2-TPR测试表明,适当钯铈比条件下制备的催化剂有较强的储氧能力和活性.催化氧化实验结果表明,所制备的Pd/CeO2-Al2O3催化剂对PAHs具有较高的转化效率,其平均转化率均在80%以上,且PAHs的毒性当量显著降低,钯铈比对PAHs的催化氧化性能影响较大,当催化剂的钯铈比为1：1时,PAHs的转化率最高,可达90%以上.     

不同水汽来源对湖南长沙地区降水中 δD、δ18O的影响

根据2010年在长沙地区进行降水收集和气象要素观测的资料,分析了该地区降水中δ¹⁸O与温度、降水量之间的关系,揭示了降水中δD、δ¹⁸O的变化特征,讨论了水汽输送对降水中δ¹⁸O变化的影响。结果表明,在天气尺度下,长沙地区大气降水中δ¹⁸O与降水量、温度之间存在显著的负相关关系,即该地区降水中δ¹⁸O的变化具有显著的降水量效应及反温度效应。对长沙地区的降雪样和降雨样进行线性回归,得出大降水事件和降雪的大气降水线具有较大斜率和截距。随着降水量的减小,大气降水线方程的斜率和截距也逐渐减小,这主要由于小降水事件的雨滴在降落过程中受到二次蒸发强烈,同位素分馏强烈。利用HYSPLIT模式追踪该地区气流的轨迹发现,在季风降水期间(5—9月),δ¹⁸O值偏低的水汽主要来自孟加拉湾、南海洋面与西太平洋海区;在非季风降水期间(10—4月),δ¹⁸O值偏高的水汽主要来自西风带携带的水汽和局地水汽环流。     

典型排放源黑碳的稳定碳同位素组成研究

采集了我国主要的黑碳排放源(生物质燃烧、民用燃煤和机动车尾气)的烟尘样品,分析烟尘中黑碳(BC)和总碳(TC)与原始燃料的稳定碳同位素组成(δ13C),对比各种δ13C值之间的关联性,评估运用δ13C技术进行BC源解析的潜力.结果表明:①3种典型排放源烟尘样品的δ13CBC与燃料有较好的一致性,且不同排放源的δ13CBC变化范围之间有比较明显的差别:生物质燃料除玉米秸(C4植物,δ13CBC为-13.62‰)显著不同外,C3植物的δ13CBC平均值为-26.49‰±1.17‰;烟煤的平均值为-23.46‰±0.37‰;机动车尾气(包括柴油车和汽油车)的平均值为-25.17‰±0.40‰.②各种排放源的BC形成过程存在程度各异的碳同位素分馏,C4植物(玉米秸)燃烧过程分馏作用较明显(BC的δ13C相对燃料负偏1.62‰),而C3植物和民用煤燃烧过程的分馏较小(分别正偏0.63‰和0.52‰).③BC的纯化手段(CTO-375方法)对生物质烟尘的δ13C有一定的影响(BC和TC的δ13C相差约为0.50‰),对化石燃料烟尘没有影响.上述典型排放源的δ13C数据库可为BC源解析提供依据.     

A comparative study on the effect of GTAW processes on the microstructure and mechanical properties of P91 steel weld joints

Modified 9Cr-1Mo (P91) steel is widely used in the construction of power plant components. In the present study, a comparative study on influence of activated flux tungsten inert gas (A-TIG), and gas tungsten arc (GTA) welding processes on the microstructure and the impact toughness of P91 steel welds was carried out. P91 steel welds require a minimum of 47 J during the hydrotesting of vessels as per the EN1557: 1997 specification. Toughness of P91 steel welds was found to be low in the as-weld condition. Hence post-weld heat treatment (PWHT) was carried out on weld with the objective of improving the toughness of weldments. Initially as per industrial practice, PWHT at 760 °C – 2 h was carried out in order to improve the toughness of welds. It has been found that after PWHT at 760 °C – 2 h, GTA weld (132 J) has higher toughness than the required toughness (47 J) as compared with A-TIG weld (20 J). The GTA weld has higher toughness due to enhanced tempering effects due to multipass welding, few microinclusion content and absence of δ-ferrite. The A-TIG weld requires prolonged PWHT (i.e. more than 2 h at 760 °C) than GTA weld to meet the required toughness of 47 J. This is due to harder martensite, few welding passes that introduces less tempering effects, presence of δ-ferrite (0.5%), and more alloy content. After PWHT at 760 °C – 3 h, the toughness of A-TIG weld was improved and higher than the required toughness of 47 J.     

Pseudomonas putida MnB1氧化Mn2+实验研究

Pseudomonas putida MnB1是存在于淡水和土壤中的锰氧化细菌。本文在中性条件下对MnB1锰氧化特性及锰氧化产物进行了研究。XANES结果显示,MnB1可将溶液中Mn(Ⅱ)氧化并形成Mn(Ⅳ)的锰氧化物;XRD结果进一步证实锰氧化物为δ-MnO2。MnB1的锰氧化性能受重金属离子的影响,其中Cd2+影响最大、Cu2+影响最小。在4μM Cd2+、6μM Pb2+、200μM Cu2+和20μmol/L Ni 2+的体系中,锰氧化速率和氧化量均有所降低,锰氧化量由208.5μM分别降至20.3μM、192.5μM、129.5μM和52.7μM。     

西南喀斯特流域风化作用季节性变化研究

以西南地区典型喀斯特流域,长江上游一级支流嘉陵江温塘峡段为例,连续2 a按月取样,并通过水化学分析、同位素分析等方法,研究得出嘉陵江温塘峡段水化学类型受地层控制,为HCO3--Ca型.在稀释作用的影响下,除HNO3-的浓度因受人类活动的影响雨季偏大外,其余大部分离子浓度雨季较旱季偏小.所有样品的(Ca2++Mg2+)/HCO3-(浓度比)在0.5～1之间,(Ca2++Mg2+)/(HCO3-+SO24-)(浓度比)大部分处于0.5～1之间,由此表明嘉陵江风化作用主要以碳酸的风化和硫酸风化碳酸岩盐为主,硫酸岩盐的风化为辅.根据同位素分析结果表明嘉陵江水中δ13CHCO-3值为-8.74‰～-7.36‰,δ34SSO2-4值旱季为14.43‰,雨季为12.21‰,表明硫酸对碳酸盐岩的风化作用和硫酸盐岩自身的风化作用在雨季均表现更强,其中,硫酸岩盐自身的风化作用在雨季强度更大,而旱季碳酸对碳酸盐岩的风化作用比较强.     

Mn-Ce/分子筛的脱汞特性研究

采用浸渍法在分子筛载体上负载活性锰、铈组分得到一种复合催化剂,在小型实验台架上考察了催化剂的脱汞性能,并对改性前后的样品进行XPS表征以研究制备的催化剂的活性组分的变化.结果表明负载锰、铈组分的催化剂在300~450℃内有较高的氧化单质汞的能力,特别是在450℃时单质汞的氧化效率仍保持在80%以上.催化剂具有较多的利于单质汞氧化的官能团,其主要靠化学吸附脱汞.烟气中的SO2与NO对单质汞的氧化有一定的抑制作用.