核级高效空气过滤器的结构与阻力关系探讨

探讨了核级高效空气过滤器的结构形式与过滤阻力之间的关系.分别采用进口的和国产的过滤材料,制作了一批不同褶间距(2.5～8.2mm)、褶深(33～275 mm)和褶形状的高效空气过滤器,并对其过滤阻力进行了测试,研究了高效空气过滤器的结构与阻力之间的关系.实验结果表明,对于进口过滤材料.当褶深为33 mm、52 mm和73 mm时,过滤阻力最低时相应的褶间距分别为2.7 mm、3.4 mm和4.0 mm;对于国产过滤材料,当褶深为33 mm、52 mm、73 mm、105 mm和245 mm时,过滤阻力最低时,相应的褶间距分别为2.5 mm,3.1 mm、3.7 mm、4.8 mm和5.4 mm.因此,不同的过滤材料.应该有不同的过滤器最佳结构参数.此外,V形过滤材料褶过滤器比矩形过滤材料褶过滤器的阻力低.     

MnO2/Al2O3催化剂-微气泡臭氧体系催化降解喹啉及其机理

制备了纳米MnO₂,并以Al₂O₃为载体制备了掺杂型MnO₂/Al₂O₃颗粒催化剂.催化剂焙烧温度和时间分别为500℃和4 h、MnO₂质量分数为8%时,催化剂具有最高的臭氧催化氧化活性.SEM分析表明,纳米MnO₂均匀分布于Al₂O₃载体表面.MnO₂/Al₂O₃催化剂的比表面积（BET）为183.22 m²·g^-1,平均孔容为0.27 cm³·g^-1,平均孔径为4.87 nm.建立了MnO₂/Al₂O₃催化剂-微气泡臭氧催化反应体系,研究了该体系对喹啉的降解去除效果及其机理.臭氧微气泡的平均粒径为61.7 μm.微气泡臭氧投量为30 mg·L^-1时,反应60 min后喹啉去除率能达到95%以上;反应20 min后,MnO₂/Al₂O₃催化剂-微气泡臭氧体系对实际煤化工废水二级出水的TOC去除率可达到55%以上.以叔丁醇作为分子探针,证明了羟基自由基（·OH）氧化作用在臭氧微气泡催化氧化体系中对喹啉的降解起到主导作用.     

MgO催化臭氧氧化降解苯酚机理研究

对氧化镁(MgO)催化臭氧氧化降解苯酚的机理进行了探讨,并验证其与现有的3种催化臭氧氧化机理的吻合性.同时,研究了羟基自由基(·OH)抑制剂对苯酚去除效果的影响,·OH的产生量,以及臭氧在该体系中的存在位置及苯酚在该体系中的作用.结果表明,O_3和MgO/O_3两种反应体系中都存在·OH,MgO/O_3体系中的·OH是O_3体系中的2.14倍.O_3和MgO/O_3体系中的·OH与臭氧浓度的比值分别为1.47×10~(-9)和3.15×10~(-9).苯酚在MgO催化臭氧氧化体系中起到了促进臭氧吸附在MgO表面的作用,臭氧吸附到MgO表面后,分解产生·OH,一部分释放在溶液中降解苯酚,一部分则留在其表面增加表面羟基密度.     

钴氨溶液脱除NO研究

利用Co(NH₃)₆²⁺离子作主催化剂(由可溶性钴盐溶于氨水中形成),烟道气中的O₂作氧化剂,碘阴离子作助催化剂,在液相中实现NO的催化氧化和回收、SO₂的吸收和氧化.与过氧化氢和Fe-EDTA法相比该法具有持续时间长、效率高等优点,NO的脱除率可达80%以上;SO₂的脱除率可达100%,能实现高效率地同时脱硫脱硝.     

Fe2O3 particles as superior catalysts for low temperature selective catalytic reduction of NO with NH3

Fe203 particle catalysts were experimentally studied in the low temperature selective catalytic reduction （SCR） of NO with NH3. The effects of reaction temperature, oxygen concentration, [NH3]/[NO] molar ratio and residence time on SCR activity were studied. It was found that Fe203 catalysts had high activity for the SCR of NO with NH3 in a broad temperature range of 150-270℃, and more than 95% NO conversion was obtained at 180℃ when the molar ratio [NH3]/[NO] = 1, the residence time was 0.48 seconds and 02 volume fraction was 3%. In addition, the effect of SO2 on SCR catalytic activity was also investigated at the temperature of 180℃. The results showed that deactivation of the Fe2O3 particles occurred due to the presence of SO2 and the NO conversion decreased from 99.2% to 58% in 240 min, since SO2 gradually decreased the catalytic activity of the catalysts. In addition, X-ray diffraction, Thermogravimetric analysis and Fourier transform infrared spectroscopy were used to characterize the fresh and deactivated Fe2O3 catalysts. The results showed that the deactivation caused by SO2 was due to the formation of metal sulfates and ammonium sulfates on the catalyst surface during the de-NO reaction, which could cause pore plugging and result in suppression of the catalytic activity.     

锰铜复合氧化物催化氧化甲苯的性能研究

利用水热法制备了一系列锰铜摩尔比例不同的锰铜复合氧化物催化材料,借助场发射扫描电镜(FE-SEM)和X-射线粉末衍射(XRD)对催化剂进行表征,研究了复合物催化剂在催化降解甲苯反应中的催化活性,筛选出最佳锰铜比例的复合氧化物,并考察了其重复使用性能。结果表明:Mn∶Cu(摩尔比)=1∶4时催化剂的活性最高,甲苯转化率达90%时的温度为190℃,其选择性最好,连续使用5次催化活性变化不大,重复使用性能好。     

包装印刷VOCs废气治理

介绍了应用吸附 催化燃烧法原理 ,采用FCJ型有机废气净化装置进行包装印刷厂挥发性有机化合物 (VOCs)废气治理 ,详细描述了包装印刷车间VOCs废气治理的工艺过程及其治理效果。测试结果表明 ,应用这类工艺和设备可以有效地进行大风量的VOCs废气治理 ,净化治理效果达到了国家二级排放标准。     

脱硫石膏综合利用现状及其抹面材料的研制

概述了目前有关脱硫石膏性能及其利用的研究现状，研究开发了建筑用脱硫石膏抹面材料，此种材料经性能检测，其抗压强度、抗折强度分别达到4．5MPa、17．5MPa，且粘结性能优良，为脱硫石膏的再生利用提供了另外一条有效的途径。     

催化湿式氧化处理H—酸溶液的反应动力学

两阶段一级反应动力学模型和广义动力学模型被用来描述湿式氧化（ＷＡＯ）及催化湿式氧化（ＣＷＡＯ）反应过程，并确定了动力学参数。２个模型的计算值均与实验值相符，而广义动力学模型相对现准确些。２个确定均表明反尖分２个步骤：首先是Ｈ－酸被迅速氧化成小分子有机酸，后者再缓慢氧化，这２个步骤由模型参数加以表征，因而模型可被用来对ＣＷＡＯ催化剂进行评价。     

生物质材料在重金属废水处理中的应用

可再生、低成本、有效且易从环境获取的生物质材料越来越多地用于去除废水中的重金属离子。本文着重介绍三大类生物质材料：Ⅰ、动物类（主要是甲壳素和壳聚糖衍生物）;Ⅱ、植物类（包括木质素、活性炭、竹炭、富含单宁的物质、农林废弃物等）;Ⅲ、微生物类（各种茵类等）,及其改性产物在处理有毒重金属废水方面的应用研究进展。