Efficient dechlorination of chlorinated solvent pollutants under UV irradiation by using the synthesized TiO2 nano-sheets in aqueous phase

Titanium dioxide(TiO2), which is the widely used photo-catalyst, has been synthesized by simple hydrothermal solution containing tetrabutyl titanate and hydrofluoric acid. The synthesized product has been applied to photo-degradation in aqueous phase of chlorinated solvents, namely tetrachloroethene(PCE), trichloroethene(TCE) and 1,1,1-trichloroethane(TCA). The photo-degradation results revealed that the degradation of these harmful chemicals was better in UV/synthesized TiO2 system compared to UV/commercial P25 system and UV only system. The photo-catalytic efficiency of the synthesized TiO2 was 1.4, 1.8 and 3.0 folds higher compared to the commercial P25 for TCA, TCE and PCE degradation, respectively. Moreover, using nitrobenzene(NB) as a probe of hydroxyl radical(.OH), the degradation rate was better over UV/synthesized TiO2, suggesting the high concentration of.OH generated in UV/synthesized TiO2system. In addition,.OH concentration was confirmed by the strong peak displayed in EPR analysis over UV/synthesized TiO2system. The characterization result using XRD and TEM showed that the synthesized TiO2 was in anatase form and consisted of well-defined sheet-shaped structures having a rectangular outline with a thickness of 4 nm, side length of 50 nm and width of 33 nm and a surface 90.3 m2/g. XPS analysis revealed that ≡Ti-F bond was formed on the surface of the synthesized TiO2. The above results on both photocatalytic activity and the surface analysis demonstrated the good applicability of the synthesized TiO2 nano-sheets for the remediation of chlorinated solvent contaminated groundwater.     

太湖梅梁湾水体中可见光的衰减、吸收及散射

对太湖梅梁湾沿岸带和敞水区的水体进行了光学特性研究。结果发现，沿岸带的水下光辐射衰减系数(Kd)值较敞水区小；400nm与500nm向上辐照度比值(Eu440／Eu550),沿岸带在1m左右最小,敞水区在0．5m左右最小;沿岸带的水面下向上辐照度与向下辐照度的比值(R)低于敞水区：440、550、670nm的后向散射与吸收的比值(b／a),在沿岸带的1m处最大,敞水区在0．5m处最大。这些结果说明,相对于敞水区而言,沿岸带的光衰减较弱,无机悬浮颗粒的含量较少,最大叶绿素a分布较深。     

不同煅烧温度制备的Mn、N掺杂TiO2光催化性能研究

以MnSO4·H2O为锰源,尿素为氮源,采用溶胶-凝胶法制备不同锻烧温度的纯TiO2、Mn-TiO2及Mn-N-TiO2光催化剂,利用X射线衍射、紫外-可见光漫反射光谱及电子自旋共振等技术对样品形貌和结构进行表征,并以罗丹明B的光催化降解为模型反应,考察不同锻烧温度对其光催化活性的影响.结果表明,Mn、N成功掺入TiO2后,有利于提高光催化剂的热稳定性,抑制锐钛矿相向金红石相转化,且光吸收拓展到可见光区域.Mn、N共掺杂样品比单Mn掺杂样品具有更高的光催化活性,400℃下锻烧的Mn-N-TiO2在可见光下对罗丹明B的降解具有最高的光催化活性,光照2h降解率达到100%.高温锻烧Mn-N-TiO2和Mn-TiO2样品在紫外光照射30min后对罗丹明B的降解率在90%以上.     

多壁碳纳米管的制备与可见光催化性能

采用溶胶-凝胶法,制备了多壁碳纳米管(MWCNTs)/CdS/TiO2复合半导体光催化剂。通过扫描电镜(SEM)、X射线衍射(XRD)和紫外-可见吸收光谱(UV-vis)等分析方法对光催化剂进行了结构表征,并考察了在可见光照射条件下MWCNTs/CdS/TiO2对甲基橙(MO)降解的光催化性能。结果表明,MWCNTs/CdS/TiO2能有效降解甲基橙。低浓度MO降解效果比高浓度好,光催化剂投加量为1.2 g/L即可达到较好的催化效果,酸性条件有利于光催化,投加适宜浓度的H2O(2低于10 mmol/L)时会和催化剂产生协同效果,浓度过大,催化效果下降。阴离子对催化效果有抑制作用,其中PO43-的抑制作用最强。所制备的复合催化剂具有较好的实际应用价值。     

MIL-101(Cr~(3+))可见光催化氧化降解甲基橙的研究

以金属有机多孔材料MIL-101(Cr3+)为非均相催化剂,过硫酸钠(Na2S2O8)为类Fenton体系的氧化剂,在可见光(300 W)下对甲基橙进行催化氧化降解研究。结果表明,MIL-101(Cr3+)在反应时间为120 min时对甲基橙降解率高达91.0%,且回收利用3次后仍表现出优异的降解性能(降解率达到81.0%)。同样条件下,把MIL-101(Cr3+)替换为TiO2或者不添加任何催化剂,甲基橙的降解率分别为25.6%和8.8%。采用紫外-可见漫反射光谱考察了常温下MIL-101(Cr3+)的禁带宽度大小,进一步证明其优异的光催化降解性能;同时还探讨了MIL-101(Cr3+)催化降解甲基橙的可能机理。     

沉积贵金属Pt的Pt/TiO2膜利用可见光催化降解苯酚

采用溶胶-凝胶法制备锐钛矿纳米TiO2光催化材料,并用化学还原法还原氯铂酸溶液(H2PtCl6·4H2O)制备Pt胶体,然后滴涂在制备好的锐钛矿纳米TiO2基片上即对其进行贵金属修饰,从而得到纳米光催化材料Pt/TiO2膜.采用XRD、XPS、UV-Vis和SEM等手段对其表面理化特性进行了表征.以苯酚溶液为光催化降解...     

柳州新一代天气雷达电磁辐射影响的分析

通过模拟类比计算,对柳州新一代天气雷达(CINRAD/SB)的电磁辐射影响进行分析,得出该项目的建设不会对周围居民及值班工作人员构成电磁辐射的危害.     

溶剂热法合成SnWO_4及其可见光催化活性

采用溶剂热法合成了新型的可见光催化剂SnWO4,以甲基橙为目标污染物,考察了合成温度、合成时间和煅烧工艺对催化剂可见光催化活性的影响。实验结果表明:煅烧工艺会明显降低催化剂的光催化活性;在合成温度为180℃、合成时间为8h、未煅烧的条件下,合成的催化剂的光催化效果最好,光照90min后,对甲基橙的降解率可达99.93%。     

不同煅烧温度的N-TiO2制备、表征及可见光催化性能

以钛酸丁酯为钛源,氯化铵为氮源,采用溶胶-凝胶法,不同煅烧温度条件制备N掺杂TiO2纳米材料,采用X射线粉末衍射(XRD)、傅里叶变换红外(FT-IR)、扫描电镜(SEM)、紫外-可见漫反射(UV-Vis DRS)手段对其进行表征,并通过降解腐殖酸(HA)实验,探讨N-TiO2可见光催化性能。结果表明,制备的光催化纳米材料为锐钛矿相,TiO2光响应范围可拓宽到可见光区;煅烧温度是影响可见光催化活性的重要因素,350℃煅烧的N-TiO2可见光催化活性最佳,光反应140 min后,对初始浓度为5 mg/L的HA溶液降解率达80.32%,光催化反应过程符合准一级动力学,煅烧温度过高或过低,动力学反应速率常数呈现不同程度的减小,降解反应速率明显下降。