X射线光电子能谱在HTPB推进剂老化机理研究中的应用

采用X射线光电子能谱（XPS）法研究了HTPB推进剂在80℃热空气烘箱内分别老化0周、13周和24周的元素组成、化学价态及含量变化。通过拟合C,O,N,Cl等元素的XPS谱图,推测该推进剂在常温（25℃）贮存老化初期应是氧化交联,后期则出现降解断链,并认为NH4ClO4缓慢分解,攻击C C不饱和双键,使得C C双键含量降低是HTPB推进剂老化失效的主要原因。Al粉被包裹在推进剂粘合剂内部,XPS法未能检出Al粉。由于Al粉比较稳定,不参与推进剂老化过程,故XPS仍可用于HTPB推进剂老化机理研究。     

鼓风机叶轮快速断裂的检测及失效分析

针对焦化厂鼓风机叶轮运行近15 d后产生穿透性裂纹、并延伸至叶轮半径2/3处的严重断裂事故,采用具有早期缺陷诊断功能的金属磁记忆新技术及其他多种手段,从宏观力学及微观机理角度对其进行综合性能评定及失效分析.研究结果表明,叶轮材料强度、韧性均过低,且韧性指标分散性大、同类型试样的韧性指标最大值与最小值之间相差3倍多;金相组织晶粒粗大,断口表现为脆性开裂.沿叶轮的断裂与非断裂面分别进行磁记忆扫描,磁场强度分析表明,断裂面内存在两处具有明显应力集中的危险源.分析表明,锻造及锻后热处理不良造成了快速疲劳断裂.最后,结合5年中3次叶轮断裂事故,对失效原因进行了相关性分析.     

Origin of major ions in monthly rainfall events at the Bamenda Highlands, North West Cameroon

Rainwater characteristics can reveal emissions from various anthropogenic and natural sources into the atmosphere. The physico-chemical characteristics of 44 monthly rainfall events （collected between January and December 2012） from 4 weather stations （Bamenda, Ndop plain, Ndawara and Kumbo） in the Bamenda Highlands （BH） were investigated. The purpose was to determine the sources of chemical species, their seasonal inputs and suitability of the rainwater for drinking. The mean pH of 5 indicated the slightly acidic nature of the rainwater. Average total dissolved solids （TDS） were low （6.7 mg/L）, characteristic of unpolluted atmospheric moisture/air. Major ion concentrations （mg/L） were low and in the order K＋ 〉 Ca2＋ 〉 Mg2~ 〉 Na＋ for cations and NO3 〉〉 HCO3 〉 SO] 〉 CI- 〉 PO3- 〉 F- for anions. The average rainwater in the area was mixed Ca-Mg-SO4-CI water type. The CI-/Na＋ ratio （1.04） was comparable to that of seawater （1.16）, an indication that N a＋ and CI originated mainly from marine （Atlantic Ocean） aerosols. High enrichments of Ca2＋, Mg2＋ and SO2- to Na＋ ratios relative to seawater ratios （constituting 44% of the total ions） demonstrated their terrigenous origin, mainly from Saharan and Sahelian arid dusts. The K＋/Na＋ ratio （2.24）, which was similar to tropical vegetation ash （2.38）, and NO3 was essentially from biomass burning. Light （〈 100 mm） pre-monsoon and post-monsoon convective rains were enriched in major ions than the heavy （〉 100 mm） monsoon rains, indicating a high contribution of major ions during the low convective showers. Despite the acidic nature, the TDS and major ion concentrations classified the rainwater as potable based on the WHO guidelines.     

利用淀粉/PCL共混物作为反硝化固体碳源和生物膜载体的研究

以双螺杆挤出机制备了淀粉聚己内酯(PCL,polycaprolactone)共混物(SPCL5),研究了其浸出性能及吸水性能,并在序批试验中研究了其作为反硝化固体碳源和生物膜载体的特性。结果表明,SPCL5颗粒前3 d浸出的有机物浓度较高,随后逐渐降至1.31 mgL。SPCL5颗粒吸水率在1 d左右达到饱和,约为30.97%。SPCL5可作为固体碳源用于去除低碳氮比(CN)水中的硝酸盐。以活性污泥接种时,SPCL5颗粒在1 d后就有显著的脱氮效果。驯化结束后,SPCL5颗粒的平均反硝化速率(以N计)为0.020 8 mg(g·h)。剪切力是影响反硝化速率的重要因素,转速从70 rmin提高至140 rmin时,平均反硝化速率提升近1倍,达到0.040 3 mg(g·h)。进水NO3-N浓度为15~50 mgL时对反硝化速率无显著影响,反硝化为零级反应。红外光谱结果表明利用后的共混物中淀粉和PCL均发生了降解。     

基于蒙德法的固体火箭发动机水射流清理系统安全评价

安全性是固体火箭发动机水射流清理系统的第一要求。本文针对这一要求,采用蒙德火灾、爆炸、毒性指数评价法对固体火箭发动机水射流清理系统的4个单元进行了定量安全评价,得出了各单元的危险等级,并分析了水射流清理安全中的薄弱环节,进而提出了相应的安全措施,以为固体火箭发动机水射流清理系统的安全运行提供科学指导。     

气泡尺寸对清洗固体表面油脂及颗粒污染物的影响

为明确气泡清洗技术在罐底油泥清洗中的应用情况,考察了气泡尺寸差异对固体表面清洗效果的影响.搭建了玻璃表面油污气泡清洗可视化实验装置,并设计了气泡发生器.该发生器可通过调节气液比产生多种尺寸分布的气泡.实验中产生的气泡直径分布于80～1 200μm.研究了气泡尺寸、清洗时间、距离和角度等参数对清洗效果的影响,结果表明,在...     

Pyrolysis of rice husk and sawdust for liquid fuel

The paper is focused on studying how to convert rice husk and sawdust into liquid fuel. Rice husk, sawdust and their mixture were pyrolyzed at the temperature between 420℃ and 540℃, and the main product of liquid fuel was obtained. The experimental result showed that the yield of liquid fuel heavily depended on the kind of feedstock and pyrolysis temperature. In the experiments, the maximum liquid yields for rice husk, sawdust and their mixture were 56% at 465 ℃, 61% at 490℃ and 60% at 475℃ respectively. Analysis with GC-MS and other apparatus indicated that the liquid fuel is a complicated organic compound with low caloric value and can be directly used as fuel oil without any up-grading. As a crude oil, the liquid fuel can be refined to be vehicle oil.     

沥青中毒的防治

沥青是一种棕黑色有机胶凝状物质,有液体、半固体和固体3种形态,能完全溶于二硫化碳,其主要成分为烃类混合物,主要用于涂料、塑料、橡胶等工业以及铺筑路面等。其一般分为天然沥青、石油沥青、页岩沥青和煤焦沥青4种,而日常生活中我们所接触的主要是煤焦沥青、石油沥青和天然沥青3种。     

Non-UV based germicidal activity of metal-doped TiO2 coating on solid surfaces

A stain-based screening method was developed to screen different catalyst coatings for their germicidal activity. A Baclight dead/live bacteria viability kit （invitrogen, molecular probes） was used for staining the cell. The screening was carried out following a standard procedure. This included loading cell suspension to solid surface and maintaining contact for 30 min, then staining with a mixture containing dyes. The stained cells were observed using an epifluorescent microscope and photographed with a CCD camera under UV. Metal-doped TiO2 coatings on AI plates were prepared and tested for non-UV germicidal activity without using UV. It was tested using model microorganisms such as Bakers Yeast （Saccharomyces cerevisiae）, Bacillus subtilis, Pseudomonas putida, and Escherichia coli. On the basis of the germicidal activity of catalyst and the degree of damage caused to the cells, the stained cells may appear green （viable）, green with red or yellow nuclei and yellow （compromised） or red （nonviable）. According to their stained color, cells were counted to calculate the percentage of dead, live, and compromised cells. Compromised cells are cells that grow very slowly after reculturing indicating a degree of reversible cell damage. Screening the germicidal activity using this staining method is accurate and efficient, and requires less time than the culture-based method. A modification to the procedure for measuring germicidal activity of rough surfaces or fibrous coatings was developed. Both TiO2 and metal-doped TiO2 （Ag, Pt, Au, Cu） possess non-UV based germicidal activity. The germicidal activity of TiO2 was found to be related with its wetting property and can be improved by UV irradiation before testing. It is not greatly affected by contact time, indicating a fast acting germicidal activity.