负载型TiO2膜太阳光光催化降解活性深蓝K-R的研究

采用抛物线槽型反应装置,研究了玻璃弹簧和微珠负载型TiO2膜太阳光催化降解活性深蓝K-R,结果表明,由于玻璃弹簧具有良好的光透距离,脱色性能显著优于玻璃微珠,玻璃弹簧为载体,水溶液浓度为15 mg/L,pH为3,流速为20 mL/s,太阳光强度在1200 μW/cm2以上,光降解6 h时,脱色率达到96%;该降解反应可用一级反应动力学方程进行描述,反应速率常数(K)与光强I的关系为:K∝I1.92.     

活性红M-3BE脱色真菌的筛选及脱色性能研究

从自然环境中分离到2株对染料活性红M-3BE具有明显脱色效果的真菌,经形态学和26S rDNA序列分析,将其鉴定为Fusarium oxysporum和Geosmithia viridis.采用初始浓度50 mg/L M-3BE的液体培养基同步脱色培养,F.oxysporum在24 h内对M-3BE的脱色率为96%,G.viridis在36 h内的脱色率为82%.对脱色酶系的检测结果表明,脱色过程中F.oxysporum能产生LiP和MnP,G.viridis则仅产生LiP.此外,F.oxysporu和G.viridis对另外7种染料的脱色率也可分别达到16%～100%和83.3%～100%.     

玻璃弹簧负载镶嵌纳米粒子TiO2膜光催化降解活性深蓝K-R

以玻璃弹簧负载镶嵌纳米粒子的TiO2膜降解活性深蓝K-R模拟废水,考察了pH值和温度对脱色率的影响以及CODCr去除率与脱色率之间的关系,并用XRD和SEM对催化剂进行了表征.结果表明,pH值和温度对脱色率均有显著影响,CODCr去除率与脱色率的比值约为70%左右;XRD表明,TiO2矿相主要为锐钛型,SEM表明,镶嵌TiO2粒子均匀,粒径约50nm.     

微米气泡强化臭氧氧化的作用机理研究

采用微米气泡系统(平均粒径约为58 μm)和普通的鼓泡系统进行对比研究微米气泡对臭氧氧化的强化作用机理.在相同的进气流率下,采用微米气泡体系臭氧在水中的传质系数和利用率是鼓泡系统的1.6-2.7倍和2.3-3.2倍.利用臭氧氧化模拟活性艳蓝KN-R废水(100 mg·l-1)的实验结果表明,染料在微米气泡体系中的脱色速率高于鼓泡系统,二者达到99%脱色效率所需的时间分别为30 min和60 min.在同样的脱色速率下,染料在微米气泡系统中的TOC去除率较大,说明微米气泡不仅能够提高臭氧的传质速度,而且可以强化臭氧的氧化能力.     

水溶液中活性成分对壬基酚聚氧乙烯醚光降解的影响

采用长波紫外灯(UV365)和模拟日光灯研究光化学活性成分对水溶液中壬基酚聚氧乙烯醚(NPEOs)光降解效率的影响,并讨论了光降解导致NPEOs成分分布的变化.研究表明,在UV365辐射下,亚硝酸根,Fe(Ⅲ),H2O2和腐殖酸(HA)等的存在对NPEOs96h的降解效率有较明显的促进作用;在模拟日光下,Mn(Ⅱ),Fe(Ⅲ),H2O2等对NPEOs的光降解也有一定的促进,而此条件下HA的存在则表现为对光降解的抑制作用.此外,还考察了NPEOs在不同比例的Fe(Ⅲ)-HA和Fe(Ⅲ)-H2O2复合体系中的光降解效率.除了导致光降解效率的提高外,活性成分的存在也会导致降解后NPEOs成分分布的变化.以在UV365辐射下为例,H2O2(1000 μmol·l-1)或Fe(Ⅲ)(10和100 μmol·l-1)的加入使反应后短链NPEOs所占比例从初始的22.52%明显提高至29.75%,29.89%和51.89%.这种成分分布的变化可能是由于长链NPEOs在降解过程中发生EO链衰减,从而使短链NPEOs成为其降解中间产物;或是由于长链NPEOs比其短链同系物具有更高的敏化降解速率所导致的.     

铂载钴钼二元硫化物对H_2S电催化活性研究

为考察溶胶凝胶法制备的Co-Mo二元硫化物对H_2S气体的电催化活性,通过循环伏安法和Tafel曲线分析对铂载不同Co、Mo掺杂比的电催化剂进行表征.结果表明,不同阳极电催化剂交换电流密度J_0由大到小依次为,铂载n(Co):n(Mo)=2:3、铂载n(Co):n(Mo)=2:1、铂载n(Co):n(Mo)=1:1和铂,即铂载n(Co):n(Mo)=2:3阳极电催化剂具有较好的活性,这与循环伏安曲线测试结果一致.电解质溶液pH值为6～7时,随着温度的升高铂载n(co):n(Mo)=2:3阳极电催化剂活性呈现上升的趋势.优化后的Co、Mo掺杂原子比约为0.66,此类电催化剂在操作温度80℃下,交换电流密度为1.318mA/cm~2,表观活化焙值为616.6 kJ/mol .研究表明,铂载钴钼二元硫化物适合作为低温H_2S燃料电池阳极电催化剂,其中Co、Mo掺杂比对电催化活性影响较大.     

Non-UV based germicidal activity of metal-doped TiO2 coating on solid surfaces

A stain-based screening method was developed to screen different catalyst coatings for their germicidal activity. A Baclight dead/live bacteria viability kit （invitrogen, molecular probes） was used for staining the cell. The screening was carried out following a standard procedure. This included loading cell suspension to solid surface and maintaining contact for 30 min, then staining with a mixture containing dyes. The stained cells were observed using an epifluorescent microscope and photographed with a CCD camera under UV. Metal-doped TiO2 coatings on AI plates were prepared and tested for non-UV germicidal activity without using UV. It was tested using model microorganisms such as Bakers Yeast （Saccharomyces cerevisiae）, Bacillus subtilis, Pseudomonas putida, and Escherichia coli. On the basis of the germicidal activity of catalyst and the degree of damage caused to the cells, the stained cells may appear green （viable）, green with red or yellow nuclei and yellow （compromised） or red （nonviable）. According to their stained color, cells were counted to calculate the percentage of dead, live, and compromised cells. Compromised cells are cells that grow very slowly after reculturing indicating a degree of reversible cell damage. Screening the germicidal activity using this staining method is accurate and efficient, and requires less time than the culture-based method. A modification to the procedure for measuring germicidal activity of rough surfaces or fibrous coatings was developed. Both TiO2 and metal-doped TiO2 （Ag, Pt, Au, Cu） possess non-UV based germicidal activity. The germicidal activity of TiO2 was found to be related with its wetting property and can be improved by UV irradiation before testing. It is not greatly affected by contact time, indicating a fast acting germicidal activity.     

长江口潮滩沉积物中活性重金属的空间分异及控制机制

利用盐酸羟氨-25%醋酸溶液,提取了长江口潮滩沉积物中活性重金属含量。研究发现,长江口潮滩沉积物中活性重金属占总量的百分含量依次为Cu 26%,Pb 36%,Fe 7%,Mn 49%,Zn 32%,Cr 14%和Al 16%,沉积物基本未受到Cr污染,其余重金属污染程度处于中等偏下水平。除Zn、Cr外,其余活性重金属在夏季沉积物中的含量明显低于春季,其主要原因是夏季风暴潮将大量细颗粒泥沙及其富集的重金属带离潮滩进入了河口水体中。受点源污染排放及沉积物粒度影响,活性重金属在长江口南岸的浒浦、顾路和浦东机场出现峰值含量,且高潮滩含量明显高于中、低潮滩。在垂向上,重金属一般在沉积物表层或亚表层形成富集。在口门附近的滨岸潮滩沉积物中,Cu、Pb的空间分异主要受早期成岩作用的控制,在污染较为严重、水动力作用相对较弱的潮滩沉积物中,Cu、Pb的空间分异主要受沉积物中有机质含量变化的控制.     

负载型TiO2薄膜光催化剂降解亚甲基蓝

采用溶胶-凝胶法制备了玻璃负载的TiO2薄膜光催化剂,研究了该催化剂对亚甲基蓝溶液的光催化降解,考察了反应时间、水样的初始浓度、溶液的pH等对光催化降解效果的影响。     

超细粉煤灰基成型吸附剂的动态吸附实验

以粉煤灰为原料制备成型吸附剂,对水溶液中亚甲基蓝和Cr⁶⁺进行动态吸附研究,绘制穿透曲线,利用Origin软件对实验数据分析处理,得出穿透曲线的通式C_t=A₁－A₂〖〗1+(t/t₀)^p+A₁。结果表明,初始浓度C₀=25 mg/L,填料高度不同时,达到穿透点的时间随填料高度的增加而增加;填料高度h=200 mm,初始浓度不同时,达到穿透点的时间随初始浓度的增加而减小;该吸附剂对有机染料和重金属离子均有较好的吸附性能;穿透曲线通式的回归线性相关系数表明,该通式可很好地反映超细粉煤灰成型吸附剂的动态吸附过程。