无机高分子铝盐絮凝剂的应用

介绍了国内外无机高分子铝盐絮凝剂的制造方法、无机高分子铝盐絮凝剂对各种废水的处理效果以及无机高分子铝盐絮凝剂的研究方向 .     

铝盐改性活性炭对水中Cr(Ⅵ)的吸附

采用铝盐浸渍法制备改性活性炭。研究了铝盐种类、浸渍液浓度和不同吸附条件对Cr(Ⅵ)吸附性能的影响。结果表明:采用0. 1 mol/L Al_2(SO_4)_3浸渍法制得的改性PAC吸附效果最好,Cr(Ⅵ)的吸附量由0. 75 mg/g提高到4. 86 mg/g。当温度为30℃时,Al-PAC的最佳吸附条件为:投加量0. 2 g(每100m L),p H为4,吸附时间30 min,溶液中Cr(Ⅵ)浓度由10 mg/L降至0. 45 mg/L以下,低于排放限值。吸附动力学符合拟二级动力学方程,吸附等温线符合Freundlich方程,吸附过程为以离子交换为主要机制的化学吸附。     

酸-碱改性粉煤灰基铝铁复合混凝剂的除磷机理

为解决城市污水排放磷超标的问题,本研究制备出一种新型铝铁复合混凝剂。混凝剂以粉煤灰和铝土矿为原料,采用常压高温酸碱两段改性法制备,并研究了其除磷性能及机理。结果表明:(1)最佳制备条件为:碱改性过程使用4 mol/L Na OH溶液,温度100℃,时间2 h;酸改性过程使用2 mol/L盐酸,温度100℃,时间4 h;酸性上清液与碱性上清液比例为1∶16。(2)混凝剂对污水中TP去除率达97.73%,出水TP含量为0.132 0 mg/L,优于《城镇污水处理厂污染物排放标准》(GB 18918-2002)一级A标准。(3)对新型混凝剂进行表征测试发现,混凝剂主要由Al Cl_3·6H_2O、Na Cl、KMg F_3、Na_3Al H_x、Sr Fe O_(2.5)构成,主要有效成分为Al_2O_3(13.343%)、Fe_2O_3(5.497%)及Si O_2(17.920%)等。混凝剂投入水中后,其中的铁离子和铝离子及其水解产物形成Fe_3(OH)_2~(7+)、Al_n(OH)_m~((3n-m)+)等不饱和多羟基络合离子,并从溶液中吸取羟基来补充其未饱和位,从而对水中聚磷酸盐等胶体颗粒产生强烈吸附作用。同时,由于混凝剂表面粗糙,孔隙发达,比表面积大,可进一步提高其除磷效果。     

钢和硬铝的加速腐蚀试验研究

目的研究45号钢和12号硬铝的温、湿度加速腐蚀情况。方法在不同的温、湿度环境下开展45号钢和12号硬铝的加速腐蚀试验,并将不同条件下的试验结果进行对比。结果得到了45号钢和12号硬铝的腐蚀速度与温、湿度条件的关系,获得了45号钢和12号硬铝分别在“40℃,RH为85％”和“70℃,RH为85％”2种温、湿度环境下的“腐蚀速度-时间”函数关系。结论45号钢和12号硬铝在温、湿度环境下的加速因子与贮存时间呈逆幂率关系。     

氟化物排放分析及防治对策探讨——以包头铝业股份有限责任公司为例

本论文通过对包头铝业股份有限责任公司排氟源的测试,分析研究有组织和天窗无组织排放氟化物贡献率,并提出科学合理的污染防治措施。研究表明,电解车间天窗无组织排放所占的污染贡献率较大,对周边环境的污染影响严重,是造成周边环境质量超标的主要原因;提高烟气的捕集效率,减少从天窗排放的无组织烟气以达到控制环境污染的目的是一条比较实际、可行的措施。具体控制措施如下:第一,加强对电解铝厂技术工人的技术教育和培训,提高工人的操作技能,严格生产管理,制定相应的规章制度;第二,科学控制排烟量;第三,尝试使用新的技术手段。     

刘铁男：要加快推进铝工业的优化升级

8月25日,由国务院参事室和中国有色金属工业协会共同举办的＂促进铝应用高层论坛＂在北京钓鱼台国宾馆召开。国家发改委刘铁男副主任出席论坛并致辞。     

聚合铝铁对A2/O系统 EPS及生物絮凝性能的影响

通过向实验室构建的A2/O模型好氧池末端投加聚合铝铁(PAFC)来强化系统的生物除磷,使得出水总磷达到《城市污水处理厂污染物排放标准GB 18918-2002》中的一级A标准,并重点分析投加的PAFC对A2/O系统中活性污泥胞外聚合物(EPS)和活性污泥生物絮凝性能的影响.结果表明,随着PAFC投药量的增加,A2/O系统活性污泥EPS总量变化不大,但EPS组分中蛋白/多糖含量的比值逐渐降低,由投药前的3.30降低至投药后的2.30;EPS中金属离子含量逐渐增加,在厌氧-缺氧-好氧的运行周期内,各处理单元污泥的EPS中金属铝离子含量增加.投加PAFC后,活性污泥颗粒变大,二沉池出水的Zeta电位明显降低,由投药前-15.83 mV降低至-21.20 mV,污泥产量增加.因此,适量投加PAFC后,生物絮凝性能得到改善,出水中悬浊颗粒减少,出水水质变好.     

Preparation and coagulation efficiency of polyaluminium ferric silicate chloride composite coagulant from wastewater of high-purity graphite production

The aim of the present work was to produce a polyaluminium ferric silicate chloride (PAFSiC) coagulant from acidic and alkaline wastewater of purifying graphite by roasting, and subsequently to evaluate coagulation efficiency of the reagent by treating surface water from the Yellow River as well as municipal wastewater in comparison with the conventional coagulant polyaluminium chloride (PAC). The PAFSiC coagulant was prepared by co-polymerization. The effects of (Al+Fe)/Si molar ratio, OH/(Al+Fe) molar ratio (i.e., value), coagulant dosage and pH value of test suspension on the coagulation behavior of FAFSiC and the stability of the PAFSiC were also examined. Results showed that PAFSiC performed more efficiently than PAC in removing turbidity, chemical oxygen demand (COD), and total phosphate (TP). The PAFSiC with a value of 2.0 and (Al+Fe)/Si ratio of 5 (PAFSiC 2.0/5) showed excellent coagulation effect for both turbidity and COD, while PAFSiC 1.0/5 was the best for TP. The optimum coagulation pH range of PAFSiC 2.0/5 was 5.0–9.0, slightly wider than that of PAC (6.0–8.0). The process can be easily incorporated into high-purity graphite production plants, thereby reducing wastewater pollution and producing a valuable coagulant.     

再生铝项目环境影响评价重点

再生铝生产在国内铝工业中占有重要位置,也是国内鼓励发展循环经济的重点项目之一。在环境保护越来越受到重视的形势下,正确把握环境污染问题对促进再生铝经济稳定有序发展,保护生态环境十分重要。文章结合再生铝生产特征,对其环境影响评价重点予以概要性的阐述。     

聚硅酸对不同形态铝沉积行为的影响

针对给水管网中残余铝沉积和再溶解现象可能引起的水质问题,研究了聚硅酸对不同水解聚合形态铝沉积、再溶解的影响,并以石英微晶天平为表征手段,初步探讨了聚硅酸对不同形态铝沉积、再溶解过程影响的机理.结果表明,聚硅酸能显著改变不同水解聚合形态铝的沉积、再溶解行为.聚硅酸可与3种水解聚合形态的铝迅速结合而生成可沉积产物,但产物性质不同.以单体形态为主的Al_0与聚硅酸的反应产物性质较稳定,部分以溶解态存在,部分以非溶解态(可沉积态)存在;尽管铝的两种聚合形态Al_(13)和Al_(30)与聚硅酸反应也生成了部分可沉积产物,但随着时间的推移,这些产物又逐渐向溶解态转化.铝硅比对Al_0体系中铝的沉积溶解行为影响较小,而对Al_(13)和Al_(30)影响较大,且在0.2∶20(以Al和SiO_2计的质量比)时,沉积态铝的溶解速率最快.