BiOCl/TiO_2复合材料的可见光活性及机理研究

采用水热法和溶胶凝胶法制备新型BiOCl/TiO2复合材料并明确了最优的掺杂比例(2%).随后利用X射线衍射(XRD)、紫外可见漫反射(DRS)、透射电镜(TEM)和X射线光电子能谱(XPS)对该材料进行表征.由于禁带宽度较大,纯BiOCl和TiO2的可见光催化性能极差,然而二者复合后,同条件下的苯降解率却大幅提升,可以达到40%以上.经证实,催化剂制备过程中,Bi的状态发生变化,在TiO2导、价带之间插入新的能级,使其禁带宽度变窄,电子可以实现可见光跃迁.     

基于BP神经网络优化制备Cu-Ce/TiO_2及其光催化活性研究

采用Cu和Ce对TiO2进行改性,基于正交实验设计和BP神经网络研究了Cu-Ce/TiO2中Cu-Ce对TiO2的摩尔百分数、Cu-Ce/TiO2中CuCe摩尔比及Cu-Ce/TiO2烧结温度对Cu-Ce/TiO2光催化降解甲醛溶液性能的影响.同时,对Cu-Ce/TiO2制备方案进行了优化,并运用X射线衍射仪、扫描电子显微镜和紫外-可见分光光度计对最佳条件下制备的Cu-Ce/TiO2进行表征.结果表明,优化的制备条件为Cu-Ce/TiO2中Cu-Ce对TiO2的摩尔百分数为2.88%,Cu-Ce/TiO2中Cu-Ce的摩尔比为1∶1,Cu-Ce/TiO2的烧结温度为570℃.共掺杂Cu离子和Ce离子能有效避免掺杂TiO2晶格内部表层和近表层产生较多的位错,从而抑制晶格畸变增大;诱导TiO2中锐钛矿型晶体向金红石型晶体转变的能力增强,有效抑制电子-空穴对的复合,产生介电局域效应.     

秸秆添加对厨余垃圾堆肥时H_2S和NH_3排放的影响

厨余垃圾堆肥过程中NH3和H2S的排放不但降低了堆肥的养分含量,而且会引发严重的恶臭。以厨余垃圾为研究对象,以玉米秸秆为膨松剂,设置5%、10%、15%、20%(质量分数)4个添加比例(湿基)的堆肥处理,研究秸秆添加量对厨余垃圾堆肥过程中H2S和NH3排放的影响。结果表明:从温度来看,仅T4处理未达到无害化和腐熟的要求。氧气不足是造成H2S排放的主要原因,4个堆肥处理的H2S主要集中在前2周排放,随着秸秆添加量的增加,H2S的排放量逐渐降低。与T1处理相比,T2、T3、T4的H2S累积排放量分别降低了35.5%、44.7%、64.2%。各处理NH3的排放趋势与H2S类似,高温期为NH3释放的关键时期,NH3累积释放量占总释放量的62.2%~72.2%,与T1处理相比,T2、T3和T4的NH3累积排放量分别降低了36.9%、45.2%、76.3%。由此可见,添加适量的玉米秸秆不但能促进厨余垃圾堆肥的进行,明显降低堆肥过程中H2S和NH3的排放,而且可以实现玉米秸秆的资源化利用。     

内蒙古未利用地工业开发对大气环境的影响研究

预测了内蒙古各盟市未利用地工业开发利用过程中以SO2排放为代表的有害气体对大气环境的影响,研究显示,2014—2018年间SO2排放量随着开发面积的增加而增长,单位面积SO2排放量呈逐年线性递减,新增加开发排入大气中SO2的总量呈增加趋势。同时规划期内SO2对区域空气质量的影响与SO2的排放总量呈正相关。新增工业产生的SO2排放导致5个盟市大气SO2浓度超标。     

臭氧/TiO_2纳米管工艺处理水中2,4-二氯酚的效能研究

采用水热合成法制备TiO2纳米材料,用BET、XRD、TEM技术对样品进行表征,结果表明,制备出来的样品均为纳米管,随着煅烧温度的增加,晶型从锐钛矿变成金红石相。实验考察了体系参数对臭氧/TiO2纳米管工艺降解2,4-二氯酚废水影响,结果表明:随着臭氧投加量的增加,废水COD的去除效率随之增加,初始浓度的增加会抑制降解效率,中性或弱碱性水环境有利于反应的进行。另外,通过研究叔丁醇对反应体系的影响,表明实验反应遵循羟基自由基的反应机理。     

Enhanced bio-decolorization of 1-amino-4-bromoanthraquinone-2-sulfonic acid by Sphingomonas xenophaga with nutrient amendment

Bacterial decolorization of anthraquinone dye intermediates is a slow process under aerobic conditions. To speed up the process, in the present study, effects of various nutrients on 1-amino-4-bromoanthraquinone-2-sulfonic acid (ABAS) decolorization by Sphingomonas xenophaga QYY were investigated. The results showed that peptone, yeast extract and casamino acid amendments promoted ABAS bio-decolorization. In particular, the addition of peptone and casamino acids could improve the decolorization activity of strain QYY. Further experiments showed that L-proline had a more significant accelerating effect on ABAS decolorization compared with other amino acids. L-Proline not only supported cell growth, but also significantly increased the decolorization activity of strain QYY. Membrane proteins of strain QYY exhibited ABAS decolorization activities in the presence of L-proline or reduced nicotinamide adenine dinucleotide, while this behavior was not observed in the presence of other amino acids. Moreover, the positive correlation between L-proline concentration and the decolorization activity of membrane proteins was observed, indicating that L-proline plays an important role in ABAS decolorization. The above findings provide us not only a novel insight into bacterial ABAS decolorization, but also an L-proline-supplemented bioaugmentation strategy for enhancing ABAS bio-decolorization.     

Mg2+ improves biomass production from soybean wastewater using purple non-sulfur bacteria

Soybean wastewater was used to generate biomass resource by use of purple non-sulfur bacteria (PNSB). This study investigated the enhancement of PNSB cell accumulation in wastewater by Mg²⁺ under the light-anaerobic condition. Results showed that with the optimal Mg²⁺ dosage of 10 mg/L, biomass production was improved by 70% to 3630 mg/L, and biomass yield also was improved by 60%. Chemical Oxygen Demand (COD) removal reached above 86% and hydraulic retention time was shortened from 96 to 72 hr. The mechanism analysis indicated that Mg²⁺ could promote the content of bacteriochlorophyll in photosynthesis because Mg²⁺ is the bacteriochlorophyll active center, and thus improved adenosine triphosphate (ATP) production. An increase of ATP production enhanced the conversion of organic matter in wastewater into PNSB cell materials (biomass yield) and COD removal, leading to more biomass production. With 10 mg/L Mg²⁺, bacteriochlorophyll content and ATP production were improved by 60% and 33% respectively.     

Applying a new method for direct collection, volume quantification and determination of N2 emission from water

The emission of N₂ is important to remove excess N from lakes, ponds, and wetlands. To investigate the gas emission from water, Gao et al. (2013) developed a new method using a bubble trap device to collect gas samples from waters. However, the determination accuracy of sampling volume and gas component concentration was still debatable. In this study, the method was optimized for in situ sampling, accurate volume measurement and direct injection to a gas chromatograph for the analysis of N₂ and other gases. By the optimized new method, the recovery rate for N₂ was 100.28% on average; the mean coefficient of determination (R²) was 0.9997; the limit of detection was 0.02%. We further assessed the effects of the new method, bottle full of water, vs. vacuum bag and vacuum vial methods, on variations of N₂ concentration as influenced by sample storage times of 1, 2, 3, 5, and 7 days at constant temperature of 15°C, using indices of averaged relative peak area (%) in comparison with the averaged relative peak area of each method at 0 day. The indices of the bottle full of water method were the lowest (99.5%-108.5%) compared to the indices of vacuum bag and vacuum vial methods (119%-217%). Meanwhile, the gas chromatograph determination of other gas components (O₂, CH₄, and N₂O) was also accurate. The new method was an alternative way to investigate N₂ released from various kinds of aquatic ecosystems.     

Acid-assisted hydrothermal synthesis of nanocrystalline TiO2 from titanate nanotubes: Influence of acids on the photodegradation of gaseous toluene

In order to efficiently remove volatile organic compounds (VOCs) from indoor air, onedimensional titanate nanotubes (TiNTs) were hydrothermally treated to prepare TiO₂ nanocrystals with different crystalline phases, shapes and sizes. The influences of various acids such as CH₃COOH, HNO₃, HCl, HF and H₂SO₄ used in the treatment were separately compared to optimize the performance of the TiO₂ nanocrystals. Comparedwith the strong and corrosive inorganic acids, CH₃COOH was not only safer andmore environmentally friendly, but also more efficient in promoting the photocatalytic activity of the obtained TiO₂. Itwasobserved that the anatase TiO₂ synthesized in 15 mol/L CH₃COOH solution exhibited the highest photodegradation rate of gaseous toluene (94%), exceeding that of P25 (44%) by a factor ofmore than two. The improved photocatalytic activity was attributed to the small crystallite size and surface modification by CH₃COOH. The influence of relative humidity (20%-80%) on the performance of TiO₂ nanocrystals was also studied. The anatase TiO₂ synthesized in 15 mol/L CH₃COOH solution was more tolerant tomoisture than the other TiO₂ nanocrystals and P25.     

Synthesis, crystal structure, photodegradation kinetics and photocatalytic activity of novel photocatalyst ZnBiYO4

ZnBiYO₄ was synthesized by a solid-state reaction method for the first time. The structural and photocatalytic properties of ZnBiYO₄ were characterized by X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy and UV-Vis diffuse reflectance. ZnBiYO₄ crystallized with a tetragonal spinel structure with space group I41/A. The lattice parameters for ZnBiYO₄ were a = b = 11.176479 Å and c= 10.014323 Å. The band gap of ZnBiYO₄ was estimated to be 1.58 eV. The photocatalytic activity of ZnBiYO₄ was assessed by photodegradation of methyl orange under visible light irradiation. The results showed that ZnBiYO₄ had higher catalytic activity compared with N-doped TiO₂ under the same experimental conditions using visible light irradiation. The photocatalytic degradation of methyl orange with ZnBiYO₄ or N-doped TiO₂ as catalyst followed first-order reaction kinetics, and the first-order rate constant was 0.01575 and 0.00416 min^-1 for ZnBiYO₄ and N-doped TiO₂, respectively. After visible light irradiation for 220 min with ZnBiYO₄ as catalyst, complete removal and mineralization of methyl orange were observed. The reduction of total organic carbon, formation of inorganic products, SO₄^2- and NO₃^-, and evolution of CO₂ revealed the continuous mineralization of methyl orange during the photocatalytic process. The intermediate products were identified using liquid chromatography- mass spectrometry. The ZnBiYO₄/(visible light) photocatalysis system was found to be suitable for textile industry wastewater treatment and could be used to solve other environmental chemical pollution problems.