六铝酸盐催化剂的催化还原脱硫脱硝性能

采用共沉淀法制备Cu和Fe掺杂的六铝酸盐催化剂(SrCuxFe1-xAl11O19-δ,x为0,0.2,0.4,0.5,0.6,0.8,1),通过XRD、TPR、BET等技术方法对催化剂的结构及性质进行了研究,并考察了以CO为还原剂的催化脱硝活性。结果表明,用碳酸铵作为沉淀剂在1 200℃焙烧4 h可以形成完整的六铝酸盐晶型,Cu和Fe能够取代Al3+,很好地促进六铝酸盐晶体结构的形成;SrCuxFe1-xAl11O19-δ催化剂有很好的脱硫脱硝催化活性,此类型的催化剂均使SO2、NO的转化率在空速为6 000 h-1下达到了80%和90%以上。向体系中加入氧气会对催化活性有较大影响。     

商业SCR烟气脱硝催化剂钙中毒研究

使用2种不同浓度的前驱体溶液(Ca(NO3)2和Ca(CH3COO)2溶液)浸渍新鲜商业SCR(selective catalytic reduction)烟气脱硝催化剂,并对浸渍中毒后催化剂的性能进行了研究。实验结果表明,物理中毒在本研究中占主导位置,化学中毒并不明显。采用离子色谱、氮气吸附-脱附分析、红外光谱分析、X射线衍射分析、扫面电镜分析等多种表征技术对中毒后催化剂进行了表征。结果表明,中毒后催化剂孔结构性质发生了变化,特别是Ca(CH3COO)2溶液浸渍催化剂,内部孔道堵塞较为严重。X射线衍射分析和扫描电镜分析也从另一方面说明了CaCO3的出现及积累导致催化剂脱硝效率降低。此外,催化剂红外光谱分析从表面活性位的角度说明了本研究催化剂化学中毒现象并不明显。     

焙烧条件对CuO/ZSM-5催化剂脱硫脱硝性能的影响

以ZSM-5分子筛为载体,通过浸渍法制备10％ CuO/ZSM-5(金属氧化物质量占载体质量)催化剂,以CH4为还原气,考察不同焙烧温度和焙烧时间对催化剂脱硫脱硝性能的影响.XRD和TPR的表征结果显示,最佳焙烧条件为550℃下焙烧4h,在此焙烧条件下,10％ CuO/ZSM-5催化剂达到的最高脱硝脱硫率分别为90.6％和98.8％.     

改进钒基SCR脱硝催化剂的抗碱金属中毒性能

以锐钛矿型二氧化钛和钛钨粉(5%WO3-TiO2)为载体,制备了系列钒和钨负载量不同的钒钛催化剂,考察碱金属和碱土金属(钾、钠和钙)对催化剂在氨选择性催化还原(NH3-SCR)氮氧化物反应中催化活性的影响。钾、钠和钙对钒钛催化剂的中毒影响大小顺序为钾钠钙。提高钒钛催化剂中钒的含量可显著提高催化剂的SCR活性和抗碱金属中毒性能,但高钒负载量(4.5%V2O5)造成催化剂氮气选择性明显下降,氧化亚氮生成显著增加。钨的添加有利于提高钒钛催化剂的低温活性和抗碱金属中毒性能,对氮气选择性无明显影响。     

金属催化剂对油漆板材催化热解产物的影响

研究使用CaCO3、CaO、Fe2O3、还原铁粉、Na2CO35种金属催化剂对油漆板材进行热解,收集固、液两相产物进行产率计算和检测分析.结果表明,5种催化剂都有效提高了热解固相产物的产率,CaCO3、Na2CO3以及还原铁粉可以增加液相产品产率.钛元素在所有催化热解固相产物含量均较高,可能造成潜在的环境污染.热解液相...     

Mn1-yNiyOx的制备及其催化燃烧甲苯性能的研究

通过水热共沉淀法制备了Mn_1-yNi_yO_x复合氧化物催化剂(y=0.1~0.5),考察掺杂Ni对Mn基氧化物在甲苯燃烧中的影响,在获得最优锰镍比例后,对其热稳定性与耐久性进行测试,然后通过XRD、N₂吸脱附、SEM、H₂-TPR以及XPS对其物理结构和氧化还原性能进行表征.结果表明,Mn和Ni在甲苯吸附和活化中产生相互作用,生成更多的Mn⁴⁺以及表面吸附氧,提供大量的反应活性位点,增强了催化氧化性能.Mn_0.8Ni_0.2O_x在甲苯催化燃烧中表现出的催化性能最好,其热稳定性与耐久性也表现优异,与MnO_x在甲苯催化燃烧中相比,其T₅₀、T₉₀分别下降12和11 ℃,在238℃即可将甲苯完全氧化,并且碳平衡值约为99%,无二次污染产生,该研究成果可为挥发性有机化合物(VOCs)催化燃烧提供更好的方式和材料.     

钒和钨负载量对V2O5-WO3/TiO2表面形态及催化性能的影响

采用浸渍法制备了一系列不同钒和钨负载量的V₂O₅-WO₃/TiO₂催化剂样品,对样品NH₃选择性催化还原NO性能进行了评价,并用BET、XRD、XPS等手段对催化剂样品的表面形态进行了表征.研究发现,钒的负载量对催化剂的比表面积和催化活性有显著影响,当钒负载量从1％升高到8％时,催化剂比表面积下降了16 m²/g,最高活性温度降低了约100℃.钨起到稳定剂和助剂的双重作用,当钒负载量为1％时,钨负载量从0升高到6％,催化剂比表面积仅下降了3 m²/g,而活性温度窗口向高温和低温各拓宽了约50℃.研究表明钒和钨负载量都能影响催化剂表面的VO_x物种,但对催化剂的表面晶型没有明显影响.     

A comparative investigation of NdSrCu_(1-x)Co_xO_(4-δ) and Sm_(1.8)Ce_(0.2)CU_(1-x)Co_xO_(4-δ) (x: 0-0.4) for NO decomposition

A series of single-phase T-structured NdSrCu_(1-x)Co_xO_(4-δ) with oxygen vacancies and T'-structured Sm_(1.8)Ce_(0.2)Cu_(1-x)Co_xO_(4-δ) (x:0-0.4) with oxygen excess were prepared using ultrasound-assisted citric acid complexing method, and characterized by means of techniques such as thermogravimetric analysis and NO temperature-progranuned desorption (NO-TPD). The catalytic activities of these materials were evaluated for the decomposition of NO. It was found that the NdSrCut_xCoxO4_b catalysts were of oxygen vacancies whereas the Sm_(1.8)Ce_(0.2)CU_(1-x)Co_xO_(4-δ) ones possessed excessive oxygen (i.e., over-stoichiometric oxygen); with a rise in Co doping level,the oxygen vacancy density of NdSrCu_(1-x)Co_xO_(4-δ) decreased while the over-stoichiometric oxygen amount of Sm_(1.8)Ce_(0.2)CU_(1-x)Co_xO_(4-δ)increased. The NO-TPD results revealed that NO could be activated much easier over the oxygen-deficient perovskite-like oxides than over the oxygen-excessive perovskite-like oxides, with the NdSrCuO_(3.702) catalyst showing the best efficiency in activating NO molecules. Under the conditions of 1.0% NO/helium, 2800 hr~(-1), and 600-900℃, the catalytic activity of NO decomposition followed the order of NdSrCuO_(3.702)> NdSrCu_(0.8)Co_(0.2)O_(3.736) > NdSrCu_(0.6)Co_(0.4)O_(3.789) > Sm_(1.8)Ce_(0.2)Cu_(0.6)Co_(0.4)O_(4.187)> Sm_(1.8)Ce_(0.2)Cu_(0.8)Co_(0.2)O_(4.104)> Sm_(1.8)Ce_(0.2)CuO_(4.045), in concord with the sequence of decreasing oxygen vacancy or oxygen excess density. Based on the results, we concluded that the higher oxygen vacancy density and the stronger Cu~(3+)/Cu~(2+) redox ability of NdSrCu_(1-x)Co_xO_(4-δ) account for the easier activation of NO and consequently improve the catalytic activity of NO decomposition over the catalysts.     

不同空速下Pd/CeZrO_4/γ-Al_2O_3的起燃特性

以渍法制备了Pd/Ce0 ZrO4 /γ Al2 O3三效催化剂。在不同空速下 ,分别考察了空速对催化剂T30 % 、T50 % 、T90 % 的影响规律。详细分析了不同空速对催化剂起燃特性产生不同影响的原因所在。Pd/CeZrO4 /γ Al2 O3催化剂具有很好的起燃能力及空速特性。     

净化汽车尾气的三效催化剂

在我国，汽车尾气对大气的污染日趋严重，使用三效催化剂净化汽车尾气势在必行。介绍了几种主要的三效催化剂及其应用情况。