催化湿式氧化法处理糖蜜酒精废液的研究

以非贵金属Cu、Fe、Mn和Ce为主要活性成分和TiO2、-γA l2O3为载体,制备了10种用于催化湿式氧化法处理糖蜜酒精废液的催化剂。考察了载体、焙烧温度、成分配比对催化剂催化活性与稳定性的影响,研究了氧气分压、催化剂投加量、反应温度和反应时间对催化湿式氧化过程的影响规律。结果表明:(1)Fe-Mn/-γA l2O3(3∶1∶1)催化剂是催化湿式氧化法处理糖蜜酒精废液的可选催化剂;(2)适宜的氧气供应量为理论需氧量的3.4~4.6倍,催化剂的投加量以10 g/L为佳;在300℃下反应30 m in或在280℃下反应60 m in,处理水可达到污水综合排放标准GB9878-1996的三级标准。     

催化铁内电解法处理硝基苯废水的机理与动力学研究

对催化铁内电解法处理硝基苯废水降解动力学特性进行了研究。结果表明,降解过程符合准一级动力学规律。进水浓度、pH值和反应温度强烈影响硝基苯的降解速率。在实验pH值范围内,反应速率常数依次为:强酸性>弱碱性>弱酸性>中性;循环伏安扫描图显示了硝基苯可以在铜电极上直接得电子还原,该反应在强酸和弱碱性条件下效果较好。反应速率常数随进水浓度的增大而减小。提高反应温度可改善处理效果,在30~45℃范围内,提高温度对处理效果的改善并不显著;当温度升高到45℃以上时,升温可以显著改善处理效果。     

Pd/CZ/Al2O3催化剂的制备、表征与三效催化性能

以共浸渍法制得的氧化铝负载铈锆固溶体为载体,并浸渍贵金属Pd得到了Pd/CZ/Al2O3催化剂.实验结果表明,该催化剂在老化前后都表现出良好的三效催化活性,新鲜样品Pd/CZ/Al2O3活性与Pd/CZ相当,老化后样品前者优于后者.结合XRD,BET,TPR等表征手段,讨论了Pd/CZ/Al2O3的催化活性特别是高温老化后活性与其组成结构之间的内在关系,揭示了其老化后仍具有较高活性的主要原因在于保持了Pd与CZ/Al2O3复合载体之间的强相互作用(SMSI).     

Toluene removal characteristics by a superimposed wire-plate dielectric barrier discharge plasma reactor

A superimposed wire-plate dielectric barrier discharge reactor was used to remove toluene in this study. The effects of oxygen content, gas flow rate, gas initial concentration and with/without catalyst on toluene decomposition were investigated. It was found that an optimal toluene removal was achieved when the oxygen content was about 5%. Under this condition, the highest toluene removal efficiency of 80.8% was achieved when the gas concentration was 80 mg/m^3. The toluene removal efficiency decreased with the increase of the gas flow rate and the initial concentration of toluene. In addition, the ozone concentration decreased with the increase of the initial concentration of toluene. It suggested that combining DBD （dielectric barrier discharge） with Co3O4/Al2O3/foam nickel catalyst in-situ could improve the toluene removal efficiency and suppress ozone formation. Products analysis showed that the main products were CO and CO2 when oxygen was more than 5%.     

石油化工催化剂生产过程中的职业病防治及应急处理

石化企业使用了大量的催化剂,催化剂开发、生产过程复杂,有许多原料和生产工艺,存在许多潜在的安全隐患和职业病危害因素。为预防催化剂生产过程中的事故,通过分析催化剂生产过程中的职业病危害分析,提出了相应的职业病防范及应急处置措施,加强催化剂生产过程中的职业病防治和应急处置能力,创造良好的经济、生态和社会效益,有效防止催化剂生产过程中发生安全事故和职业病。     

石油化工企业含苯胺消防污水处理技术研究

针对石油化工企业含苯胺的消防污水,利用基于过氧化氢和氯化铁为氧化剂的深度氧化技术,通过氧化、絮凝、过滤和吸附对消防污水进行处理。实验确定氧化剂的投加量为理论投加量,氧化时间1.0h,消防污水pH值为6.86时,絮凝剂最佳使用浓度约为2%,消防污水中苯胺和COD去除率达到99.5%以上,达到了消防污水处理效果。     

The inhibitory combustion reaction performance and tail gas analysis of composite ultra-fine dry powder extinguishing agent containing different additives

For lack of an extinguishing agent with high-efficiency, non-toxic and environmentally friendly, a new type of extinguishing agent was fabricated to solve such an urgent problem. In this study, the zinc borate (ZB) and ferrocene (Fe(Cp)₂) were utilized as two additives for extinguishants to suppress combustion reaction and the toxicity of the tail gas was detected. The mass fraction of ZB corresponding to the optimal inhibitory effect was determined to be 0.5–1.5%, by contrast, the optimum interval of Fe(Cp)₂ was detected as 0.5–1.0%. Similarly, with the increasing proportion of the two additives, the homologous inhibitory action was gradually weakened. From the perspective of thermogravimetric analysis (TGA), it was indicated that the ZB accelerated the pyrolysis process of the extinguishant, making its thermal decomposition process more thoroughly. Meanwhile, the differential scanning calorimetry (DSC) demonstrated that the decomposition efficiency was markedly improved when the amount of ZB was maintained at 0.5–1.5%. Besides, the tail gas tests were implemented to assess the extent of toxic and harmful properties. In terms of the carbon monoxide (CO) and carbon dioxide (CO₂) generated, once the mass fraction of ZB and Fe(Cp)₂ was less than 1.5% and 1.0% respectively, the concentration of CO and CO₂ was distinctly lower than that without additives. Moreover, the inhibitory ability on nitrogen oxides (NOx) was enhanced when the mass fraction of the two additives was kept below 1.0%. The results confirmed that a more practical extinguishant was proposed and it can provide guidance for the application and development of extinguishants.     

Kinetics and thermodynamic studies of Methyl Orange removal by polyvinylidene fluoride-PEDOT mats

We report the preparation of poly(3,4-ethylene dioxythiophene) (PEDOT)-modified polyvinylidene fluoride electrospun fibers and their use as a novel adsorbent material for the removal of the anionic dye Methyl Orange (MO) from aqueous media. This novel adsorbent material can be used to selectively remove MO on a wide pH range (3.0–10.0), with a maximum capacity of 143.8 mg/g at pH 3.0. When used in a recirculating filtration system, the maximum absorption capacity was reached in a shorter time (20 min) than that observed for batch mode experiments (360 min). Based on the analyses of the kinetics and adsorption isotherm data, one can conclude that the predominant mechanism of interaction between the membrane and the dissolved dye molecules is electrostatic. Besides, considering the estimated values for the Gibbs energy, and entropy and enthalpy changes, it was established that the adsorption process is spontaneous and occurs in an endothermic manner. The good mechanical and environmental stability of these membranes allowed their use in at least 20 consecutive adsorption/desorption cycles, without significant loss of their characteristics. We suggest that the physical-chemical characteristics of PEDOT make these hybrid mats a promising adsorbent material for use in water remediation protocols and effluent treatment systems.     

催化超临界水氧化处理1,5-萘二磺酸

采用Mn2O3/γ-AL2O3和V2O5/γ-Al2O/为催化剂,在一连续流固定床反应器中进行了超临界水氧化1,5-萘二磺酸实验.实验结果表明,在380～440℃,24 MPa条件下,Mn2O3/γ-Al2O3和V2O5/y-Al2O3催化剂对1,5-萘二磺酸的氧化降解具有显著的促进作用,TOC去除率达到90%以上;催化剂的催化效果随反应温度的升高而增强,随pH值的降低而增强,随停留时间的延长先增强后趋于平缓.     

全白土催化剂生产废水的处理

用4种无机絮凝剂和3种有机絮凝剂进行了脱除全白土催化剂生产废水（简称废水）中固体悬浮物（SS）的实验研究。实验结果表明：在废水pH6．8条件下,无机絮凝剂和有机絮凝剂脱除废水中SS的效果均较差,用无机絮凝剂时的SS去除率低于26％,用有机絮凝剂时的SS去除率低于18％;废水pH对SS去除率的影响较大,当调节废水pH为8．0时,无机絮凝剂中硫酸铝脱除废水中的SS效果最好,在硫酸铝加入量为0．02mg／L、沉降时间为2h的最佳操作条件下,SS的去除率可达93％。