Influence of environmental temperature and relative humidity on photocatalytic oxidation of toluene on activated carbon fibers coated TiO2

TiO₂ supported on active carbon fiber (TiO₂/ACF), an absorbable photocatalyst, is a new kind of material applied in air purification. In this paper, the influence of environmental temperature (T) and relative humidity (RH) on the gas-solid adsorption of toluene and the photocatalytic oxidation (PCO) efficiency of adsorbed toluene on TiO₂/ACF were studied, and then, the purification capability of TiO₂/ACF was estimated. PCO results showed that although the PCO efficiency increased under high RH and T levels, the amount of adsorption of toluene decreased. Moreover, quantitative analysis results of intermediates indicated that more environmental risk emerged when PCO of toluene was carried out at higher environmental T and RH levels because more toxic intermediates would be accumulated on the TiO₂/ACF. So, it is significant to control the environmental T and RH conditions in the application of the PCO technique. T = 25°C and RH530% is the optimal condition for purifying toluene in our experimental system. __________ Translated from Urban Environment & Urban Ecology, 2007, 20(5): 10–13 [译自: 城市环境与城市生态]     

Effect of manufacturing methods of AgCl/Al2O3 catalyst on selective catalytic reduction of NOx

The AgCl/Al2O3 catalyst has potential for use in the selective catalytic reduction (SCR) of NOx. A compound hydrocarbon, following oxygenation is used as a type of reducing agent. In this experiment, the AgCl/Al2O3 catalyst was produced by four different methods, and the differences among their reduction catalysis of NOx were compared. Ethanol was used as a type of reducing agent. X-ray diffraction analysis was performed to study the crystalline structure and scanning electron microscope and transmission electron microscope (TEM) were applied to determine the microindentation. The results indicated that, in the range of 350–400°C, there was no significant difference on the NOx reduction rate; however, there was dispersion at high and low temperature ranges. The size of the AgCl particles was about 20–100 nm.     

气液膜接触器分离混合气中CO2过程研究

建立了膜接触器吸收CO2 ,溶液热再生连续循环实验装置 ,评价了疏水性PP(聚丙烯 )微孔膜 ,MDEA(N 甲基二乙醇胺 )溶液及添加活化剂PZ(哌嗪 )的活化MDEA溶液吸收CO2 传质过程。结果表明 :在溶液浓度 2 5mol L ,气速0 5～ 3 0L min,液速 15～ 15 0mL min时 ,总传质系数Kov为 1 0× 10 - 5～ 3 6× 10 - 5m s(MDEA) ,1 6× 10 - 5～ 4 5×10 - 5m s(MDEA +PZ)。采用阻力层无因次关联方程模型预测Kov值 ,计算值和实验值符合较好。基于模型和实验结果 ,将PZ的吸收行为作为溶液的活化作用 ,在计算Kov值时 ,考虑活化作用因素并归结于化学增强因子E中 ,模型能更好地预测实验结果。实验证明在单一醇胺组份MDEA中添加少量PZ能提高总传质系数Kov值     

A2/O与倒置A2/O工艺低温条件下的氨氮去除能力解析

对相同进水、平行运行的A²/O与倒置A²/O工艺的冬季氨氮（NH₄⁺-N）去除能力进行了全面解析.在运行水温为14℃时,倒置A²/O工艺表现出更低的NH₄⁺-N容积去除负荷［0.13 kg·（m³·d）^-1和0.29 kg·（m³·d）^-1］和氨氧化速率（AOR）［0.07 kg·（kg·d）^-1和0.11 kg·（kg·d）^-1］,而26℃时两个工艺则相差无几.两个平行工艺中的氨氧化菌（AOB）种群定量结果几乎始终相等（倒置A²/O工艺为3.2%±0.24%,A²/O工艺为3.4%±0.31%）.克隆文库分析的结果表明,造成低温时倒置A²/O工艺中具有较低氨氮去除能力的原因是其AOB优势种属为AOR较慢的慢生型（K-生长策略）亚硝化螺菌属（Nitrosospira）,而在A²/O工艺中则为AOR较快的快生型（r-生长策略）亚硝化单胞菌属（Nitrosomonas）;而在26℃环境下两个工艺中的优势种属则均为Nitrosomonas.结合对污染物沿程去除过程的全面分析,发现尽管温度是决定AOB优势种属演替的首要原因,但由于倒置A²/O的工艺结构变化造成其好氧单元具有较高的COD负荷和高NH₄⁺-N浓度等不利于AOB生长的因素,决定了其可以在常规城市污水的条件下出现K-生长策略型的优势AOB种属.因此倒置A²/O针对异养菌（聚磷菌与反硝化菌）的工艺构造变化却通过COD负荷等间接影响到自养型氨氧化菌的种群分布与演替,并最终造成工艺在低温条件下硝化能力的减弱.     

Relation of lead adsorption on birnessites with different average oxidation states of manganese and release of Mn^2＋/H^＋/K^＋

The characteristics of Pb2+ adsorption on the surface of birnessites with different average oxidation states (AOS) of Mn, synthesized under acidic and alkali conditions, were investigated. The results indicated that the amount of adsorbed Pb2+ increased with the increase of Mn AOS in birnessites. The amount of Pb2+ adsorbed positively correlated with the amount of released Mn2+, H+, and K+ (r = 0.9962 > 0.6614, n = 14, α = 0.01). The released Mn2+, H+, and K+ were derived mostly from the corresponding catio...     

Pd/g-C3N4对水中2,4-二氯酚的催化加氢脱氯研究

分别采用光沉积法和浸渍法制备了载钯石墨相氮化碳催化剂(Pd/g-C3N4-PD和Pd/g-C3N4-IMP),并对其进行了电感耦合等离子体发射光谱(ICP-AES)、X射线衍射(XRD)、透射电镜(TEM)和Zeta电位的表征.结果表明,不同载钯量Pd/g-C3N4-PD的等电点均在pH 2.3左右;Pd/g-C3N4-PD表面Pd粒子分散均匀,且Pd粒径小于Pd/g-C3N4-IMP.分别将Pd/g-C3N4-PD和Pd/g-C3N4-IMP用于2,4-二氯酚的催化加氢脱氯研究,Pd/g-C3N4-PD的催化脱氯效果明显优于Pd/g-C3N4-IMP.低pH值利于2,4-二氯酚的催化加氢脱氯过程,但不利于保持催化剂的稳定性.     

进水C/N对A~2/O-BCO工艺反硝化除磷特性的影响

采用厌氧/缺氧/好氧与生物接触氧化工艺组成的双污泥系统(A~2/O-BCO)处理实际生活污水.通过投加乙酸钠调节进水碳氮比(C/N=2.44~8.85),考察了系统的反硝化除磷特性.试验结果表明:进水有机物主要是通过改变硝化性能(即缺氧段反硝化负荷)以及聚-β-羟基链烷酸脂(PHA)的贮存和利用,进而影响系统的脱氮除磷效果.当进水C/N为4~5时,COD、TN和PO_4~(3-)-P去除率分别达到88%,80%和96%,实现了有机物、氮和磷的同步高效去除.碳平衡分析表明,A~2/O反应器去除的COD占去除总量的71.86%~77.28%,BCO反应器去除的COD仅占2%~12%,碳源的高效利用是A~2/O-BCO工艺在低C/N条件下实现深度脱氮除磷的重要原因.此外,通过进水C/N与曝气量、硝化液回流比、厌/缺氧反应时间等相关性的分析,提出了系统的优化运行策略.     

增施CO2对C3和C4植物根际氯氰菊酯残留浓度的影响

CO2减排和土壤污染修复是我国实现经济和环境可持续发展必须解决的两大难题.基于生物固碳对根际微环境的影响,本研究提出通过增施CO2强化土壤有机污染的植物修复过程,为同时解决CO2减排和土壤污染植物修复面临的困境提供新思路.在模拟的CO2增施环境中,以C3植物菜豆和C4植物玉米为供试植物,以氯氰菊酯为目标污染物,研究增施CO2对C3和C4植物根际氯氰菊酯残留浓度的影响.结果表明,增施CO2可显著增加C3植物菜豆的地上和地下干重,在氯氰菊酯添加浓度为0、20、40 mg.kg-1时地下干重分别比自然CO2水平时增加了54.3%、31.9%和30.0%.增施CO2提高了未添加氯氰菊酯土壤的菜豆根际微生物数量,但降低了添加氯氰菊酯土壤的菜豆根际微生物数量.增施CO2对未添加氯氰菊酯土壤的菜豆根际氯氰菊酯残留浓度没有显著影响,但降低了菜豆根际氯氰菊酯的残留浓度,分别比自然CO2水平时下降24.0%（20mg.kg-1）和16.9%（40 mg.kg-1）.然而,对C4植物玉米而言,增施CO2对植物生物量、根际微生物、根际氯氰菊酯残留浓度下降没有明显促进作用,甚至有抑制作用.本实验表明,增施CO2降低了C3植物根际氯氰菊酯残留浓度,可以考虑将增施CO2作为C3植物修复土壤污染的强化措施,但对C4植物的影响还有待进一步研究.     

采用Fe2+/NaClO处理乐果废水的研究

研究了利用NaClO在酸性条件下生成的HClO代替Fenton试剂中的氧化剂H2O2,在Fe^2＋的作用下对乐果模拟废水进行处理。结果表明此方法处理乐果废水的效果比较明显。使用Fe^2＋／NaClO氧化处理乐果模拟废水,在pH值等于2,NaClO与FeSO4·7H2O的投加量分别为10mL/L,2．5g／L,振荡时间为30min,乐果初始质量浓度小于53mg／L时,乐果的处理率大于88．90％。     

不同煅烧温度制备的Mn、N掺杂TiO2光催化性能研究

以MnSO4·H2O为锰源,尿素为氮源,采用溶胶-凝胶法制备不同锻烧温度的纯TiO2、Mn-TiO2及Mn-N-TiO2光催化剂,利用X射线衍射、紫外-可见光漫反射光谱及电子自旋共振等技术对样品形貌和结构进行表征,并以罗丹明B的光催化降解为模型反应,考察不同锻烧温度对其光催化活性的影响.结果表明,Mn、N成功掺入TiO2后,有利于提高光催化剂的热稳定性,抑制锐钛矿相向金红石相转化,且光吸收拓展到可见光区域.Mn、N共掺杂样品比单Mn掺杂样品具有更高的光催化活性,400℃下锻烧的Mn-N-TiO2在可见光下对罗丹明B的降解具有最高的光催化活性,光照2h降解率达到100%.高温锻烧Mn-N-TiO2和Mn-TiO2样品在紫外光照射30min后对罗丹明B的降解率在90%以上.