MCM-41分子筛负载铁铈催化降解甲基橙

采用等体积浸渍法制备了负载型有序介孔Fe-Ce/MCM-41催化剂。研究了该催化剂降解甲基橙的适宜工艺条件,并采用XPS,XRD,TEM技术对该催化剂进行了表征。实验结果表明,该催化剂Fenton氧化降解甲基橙的较适宜工艺条件为:溶液pH 5.0、甲基橙溶液初始质量浓度100 mg/L、催化剂加入量2.0 g/L、H_2O_2浓度20 mmol/L,在此适宜条件下反应120 min时,甲基橙去除率接近100%。表征结果显示:Fe-Ce/MCM-41催化剂主要由铁、铈、氧、碳4种元素组成;铁与铈的摩尔比接近3∶1;铁和铈主要以Fe_3O_4和CeO_2的形态存在于催化剂表面。     

γ-Al2O3负载多金属复合催化剂选择性催化还原烟气脱硝

以γ-Al₂O₃作为载体,先后负载CeO₂,MnC₂O₄,Fe（NO₃）₃,CrO₃,Ni（NO₃）₂,NH₄VO₃等多种金属组分制备γ-Al₂O₃负载多金属复合催化剂,并用于模拟烟气的选择性催化还原脱硝。通过SEM和XRD技术对催化剂进行了表征。表征结果显示：Fe,Mn,Cr的添加能增加催化剂的低温催化活性、提高催化剂的N₂选择性;γ-Al₂O₃对活性金属氧化物的负载效果良好。实验结果表明：各金属化合物的最佳加入量为 w（MnC₂O₄·2H₂O）=20%,w（Fe（NO₃）₃·9H₂O）=15%,w（CrO₃）=10%,w（Ni（NO₃）₂·6H₂O）=5%,w（NH₄VO₃）=10%,w（CeO₂）=5%,w（γ-Al₂O₃）=35%;以在最佳正交实验条件下制得的γ-Al₂O₃负载多金属复合物为催化剂,在脱硝反应温度为205 ℃的条件下,NO转化率为96.7%;γ-Al₂O₃负载多金属复合催化剂经5次重复使用,NO转化率仍可稳定在94%左右。     

大肠杆菌吸附-化学还原法用废含金催化剂制备金纳米线

采用大肠杆菌吸附-化学还原法,以大肠杆菌(ECCs)为模板、十六烷基三甲基溴化铵为保护剂、抗坏血酸为还原剂,由废含金催化剂制备金纳米线(AuNWs)。采用XRD,SEM,TEM等技术对AuNWs进行表征。研究了AuNWs对罗丹明6G(R6G)和4-巯基苯甲酸(4-MBA)的拉曼散射信号的增强效果。实验结果表明:在制备过程中加入微生物ECCs,可使金回收率提高约20百分点;当溶液pH小于4时,反应2 h后,有大量呈线状的AuNWs聚集沉降,金回收率可达99%1以上。表征结果显示,AuNWs呈多晶结构,晶格间距为0.23 nm。表面增强拉曼散射分析表明,AuNWs对R6G和4-MBA具有良好的拉曼光谱增强性能。     

含镍废催化剂的回收利用

介绍了从含镍废催化剂中以硝酸镍形式加收镍的方法，镍回收率为70％，硝酸镍纯度为96．6％。该工艺简单，具有较好的经济效益和环境效益。     

溶胶凝胶法制备铜催化剂及其稳定性的研究

介绍了利用溶胶凝胶方法制备铜系催化剂，并考察了制备过程中各个工艺参数对铜系催化剂稳定性的影响。通过优化催化剂的设计和制备方法，可有效地改善Cu^2＋的溶出问题，使该类催化剂具有广阔的应用前景。     

催化还原SO2为单质硫技术的研究进展

催化还原法脱硫是一种能够直接回收单质硫的烟气脱硫(FGD)技术,近年来倍受关注.尽管催化还原法脱硫技术所采用的催化剂的种类繁多,但是该技术所采用的还原剂的种类却相对较少.以H2、C、CH4、NH3和CO 5种还原剂为分类标准,综述了催化还原SO2为单质硫技术的主要研究成果;讨论了相关催化剂的性质和催化反应机理;分析了不同还原脱硫技术的优缺点.最后,论述了催化还原法脱硫有待解决的关键问题与发展趋势.     

活化改性半焦用于烟气脱硫催化剂制备工艺优化

为研究不同制备工艺条件下的烟气脱硫催化剂吸附去除烟气中硫化物的性能,采用硝酸活化的半焦脱硫剂,通过穿透时间和硫容评价所制备催化剂的脱硫性能.采用固定床反应器考察了催化剂表面基团酸碱性、催化剂成型的制备顺序、黏结剂和催化剂尺寸及负载金属氧化物等制备工艺条件对催化剂脱硫性能的影响.结果表明:原料半焦表面呈碱性,半焦经硝酸氧化改性后,表面呈酸性,高温煅烧可以使半焦表面酸性官能团分解成碱性官能团,催化剂表面净碱量越大,脱硫性能越好;采取先将半焦成型再进行高温煅烧、水气活化的工艺,脱硫活性更高;最适合的黏结剂为煤焦油;最佳的催化剂粒径为3mm;烟气中通入O2能显著提高半焦吸附催化剂的脱硫性能,O2体积分数以5％为宜,烟气中适量H2O是脱硫必不可少的条件,水汽体积分数以8％最佳;在催化剂制备过程中添加质量分数为1％的V2O5,可以明显改善催化剂的脱硫性能.     

Heterogeneous oxidation of SO2 by O3-aged black carbon and its dithiothreitol oxidative potential

Ozone (O₃) is an important atmospheric oxidant. Black carbon (BC) particles released into the atmosphere undergo an aging process via O₃ oxidation. O₃-aged BC particles may change their uptake ability toward trace reducing gases such as SO₂ in the atmosphere, leading to different environmental and health effects. In this paper, the heterogeneous reaction process between O₃-aged BC and SO₂ was explored via in-situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS). Combined with ion chromatography (IC), DRIFTS was used to qualitatively and quantitatively analyze the sulfate product. The results showed that O₃-aged BC had stronger SO₂ oxidation ability than fresh BC, and the reactive species/sites generated on the surface had an important role in the oxidation of SO₂. Relative humidity or 254 nm UV (ultraviolet) light illumination enhanced the oxidation uptake of SO₂ on O₃-aged BC. The oxidation potentials of the BC particles were detected via dithiothreitol (DTT) assay. The DTT activity over BC was decreased in the process of SO₂ reduction, with the consumption of oxidative active sites.     

CuSnZr三元催化剂应用于NTP强化催化脱硫过程的特性

为高效地在低温下处理大量低浓度电解铝烟气, 采用浸渍法制备了Sn Zr型金属氧化物并添加Cu作为助剂的催化剂, 并首次测试了它在低温等离子体(NTP)技术上的脱硫效果, 结果表明负载了20wt% Cu老化温度为40℃的催化剂表现出最佳的脱硫性能.并对强化之后的催化剂进行了表征, 与新鲜的催化剂对比, X射线衍射分析(XRD)结果表明放电对催化剂晶型基本不产生影响; 扫描电子显微镜(SEM), 氮吸附和脱吸(BET)表明放电会使催化剂的吸附脱附能力与孔道结构有较大提升; X射线光电子光谱(XPS)也表明放电会使催化剂表面元素价态变化, 从而使其氧化还原性能改变, 反应路径发生偏向; 催化剂性能理论计算表明铜含量的上升会导致催化剂能带结构改变, 更好利用于激发气体.     

锰铈脱硝催化剂的制备及其再生性能研究

采用等体积浸渍法制备了一系列Mn-Ce-Ox复合氧化物脱硝催化剂用于NH3选择性催化还原(NH3-SCR)NO。考察了Mn/Ce摩尔比、焙烧温度、H2O和SO2对Mn-Ce-Ox复合氧化物脱硝催化剂活性的影响及催化剂中毒再生性能。结果表明:当NH3:NO=1:1,空速为5 000 h-1,550℃焙烧制得的Mn/Ce摩尔比为5∶1的Mn-Ce-Ox复合脱硝催化剂活性最佳,活性温度窗口为100~260℃,在此温度区间内催化剂活性大于90%。200℃时,Mn-Ce-Ox复合催化剂活性最高为97.84%;在10%(V/V)H2O蒸汽和300×10-6SO2共存条件下,200℃时,催化剂活性在开始反应2.5 h内迅速下降至53%左右,并在之后的6 h内没有明显变化;中毒催化剂经常温水洗再生处理、质量分数为3%的硝酸溶液再生处理和550℃焙烧2 h再生处理后200℃活性均能恢复到90%以上,其中中毒催化剂经质量分数为3%硝酸处理后活性恢复率最高。