过渡金属催化剂上CO还原NO反应性能的研究

在一系列负载型过渡金属催化剂上考察了ＣＯ－ＮＯ和ＣＯ－Ｏ２的反应性能。结果表明，催化剂的ＣＯ－Ｏ２反应活性高于ＣＯ－ＮＯ反应，催化剂表面ＮＯ解离是ＣＯ－ＮＯ反应的速率控制步骤。低温反庆有利于Ｎ２Ｏ的生成，高温有利于Ｎ２的生成。     

Effects of synthesis methods on catalytic activities of CoOx–TiO2 for low-temperature NH3-SCR of NO

A series of cobalt doped TiO_2(Co-TiO_2) and Co Oxloaded TiO_2(Co/TiO_2) catalysts prepared by sol–gel and impregnation methods respectively were investigated on selective catalytic reduction with NH_3(NH_3-SCR) of NO. It was found that Co-TiO_2 catalyst showed more preferable catalytic activity at low temperature range. From characterization results of XRD,TEM, Raman and FT-IR, Co species were proved to be doped into TiO_2 lattice by replaced Ti atoms. After being characterized and analyzed by NH_3-TPD, PL, XPS, EPR and DRIFTS, it was found that the better NH_3-SCR activities of Co-TiO_2 catalysts, compared with Co/TiO_2 catalyst, were ascribed to the formation of more oxygen vacancies which further promoted the production of more superoxide ions(O-2). The superoxide ions were crucial for the formation of low temperature SCR reaction intermediates(NO-3) by reacting with adsorbed NO molecule. Therefore, these aspects were responsible for the higher low temperature NH_3-SCR activity of Co-TiO_2 catalysts.     

甲基橙废水的常温常压催化湿式氧化实验研究

以Fe、Mn、Cu和Zn的金属氧化物为活性组分,以γ-Al2O3为载体,制备了负载型催化剂,并分别以H2O2和NaClO为氧化剂,对比了在常温常压条件下催化湿式氧化工艺中处理甲基橙模拟废水的效果.结果表明,Fe/y-Al2O3催化剂较其他催化剂表现出较好的催化活性和稳定性,H2O2为适宜的氧化剂.在Fe/γ-Al2O3加入量为10g/L,氧化剂H2O2加入量为5 mL/L的条件下,处理甲基橙质量浓度为500 mg/L的模拟废水,其脱色率和COD去除率在3 h内均能达到70%以上.与传统的Fenton试剂法相比,以Fe/γ-Al2O3为催化剂的催化湿式过氧化氢氧化工艺具有矿化程度高,催化剂易回收再用的优点.     

ZrxMg1-xO supported cobalt catalysts for methane decomposition into COx-free hydrogen and carbon nanotubes

Zirconia-magnesia supported cobalt catalysts with various Zr/Mg atomic ratios were prepared and evaluated for non-oxidative catalytic decomposition of methane to produce CO_x-free hydrogen and carbon nanotube. The catalytic performance of the catalysts was performed in a continuous fixed bed flow reactor at 700°C under atmospheric pressure. The fresh and spent catalysts were characterized by XRD, TPR, BET, TEM, and Raman spectroscopy. The results showed that the change in Zr/Mg ratio of the mixed oxide support has a significant effect on the catalytic performance of the active Co metal. The catalyst 30%Co/Zr_0.8Mg_0.2 showed the highest activity and stability within the used series of catalysts with hydrogen yield reached up to 79%. Both Co/Mg_1.0 and Co/Zr_1.0 showed poor stability due to strong Co-Mg interaction and aggregation of Co species on Zr support, respectively. All catalysts produced mainly MWCNTs with different diameters depending on the Zr/Mg ratio. The outer diameter increased with increasing Zr content in the catalyst due to the enlargement of the particle size of cobalt as a result of aggregation.     

载体特性对Pd-Cu/TiO2催化剂催化脱氮性能的影响

以Pd-Cu／TiO2为催化剂，采用催化加氢技术进行脱氮研究．结果表明：TiO2载体的特性对催化活性及N2选择性有显著影响，与773K和973K温度下焙烧得到的载体相比，以573K温度下焙烧得到的TiO2为载体制备的Pd（5wt％）-Cu（1．25wt％）／TiO2催化剂可显著提高催化效率及N2选择性．     

稀土-过渡金属复合氧化物催化剂用于汽车尾气净化研究

以不含贵金属的稀土 过渡族金属四元复合氧化物为催化剂 ,模拟汽车尾气的组成含量 ,运用连续流动式反应器 ,研究了四元复合氧化物La0 5Sr0 5Ni1 -xCuxO3系列 (x =0—1 0 )对CO和NOx 的催化氧化还原消除活性及其在消除反应条件的抗硫中毒能力 .实验结果表明 ,钙钛矿型四元复合氧化物催化剂La0 5Sr0 5Ni0 5Cu0 5O3对CO和NOx 的氧化还原消除都具有较高的活性 ;脉冲中毒实验指出 ,当反应温度≥ 3 0 0℃ ,SO2 在催化剂中的脉冲积累含量为 1 2 2× 1 0 - 2 mmol时 ,该复合氧化物仍表现出良好的抗硫毒性能 ,它对CO的氧化消除活性并未因体系中SO2 的存在而受到影响     

Formation of aromatic chlorinated compounds catalyzed by copper and iron

This study shows the catalyzing effects of iron and copper on the formation of chlorinated compounds such as chlorobenzenes (ClBzs), chlorophenols (CIPhs), polychlorinated dibenzo-p-dioxins (PCDDs) and dibenzofurans (PCDFs). Both total concentrations and congener distributions have been studied. The parameters and conditions varied during the combustion tests were the complete and incomplete combustion and the metal and chlorine addition. The incomplete combustion promoted the formation of organic chlorinated compounds in flue gas particles. Highly chlorinated congeners of PCDD/F were dominant in the flue gas particles, whereas the importance of lower chlorinated congener were increased in the gas phase. In the complete combustion conditions the concentrations of PCDD/Fs increased when the degree of chlorination were high, nevertheless the concentrations of tetra and penta PCDD/Fs were higher in the gas phase than the concentrations in the fly ash particles. Organic chlorine promoted the formation of chlorinated compounds more effectively than inorganic chlorine, which instead promoted the formation of PCDD/Fs in the gas phase, especially with copper catalyst. Different concentration levels of chlorinated compounds were observed in the gas phase and in particles when the chlorine source and combustion conditions were varied from incomplete to optimum conditions. Both copper and iron seem to have a catalytic effect on PCDD/F formation.     

催化湿式氧化法处理对硝基酚钠废水的试验

以Mn-Ce-Zr-Cu复合型氧化物作为多相催化剂，采用催化湿式氧化法处理高浓度对硝基酚钠废水，考察了各种反应条件对废水处理效果的影响。结果表明：在温度220℃、压力2．5MPa、反应时间60min、催化剂加入量3g／L的条件下，COD去除率可达63．7％。经处理后的废水，BOD5／COD的比值由原来的0．016提高到0．33，从而为后续的生物降解创造了良好条件。     

Study on catalysts for combustion of lean CH4

In this study, cerarnics honeycomb-supported ABO₃ perovskite type oxides were preparedby changing the composition of A and B site cations, and observed their activities for lean CH₄ oxidation. In the case of change in A site composition La_0.3Sr_0.2MnO₃ and La_0.6Sr_0.4MnO₃ is the mostactive catalysts for 1 v% CH₄ and 2 v% CH₄ respectively. But LaMn_0.5Co_0.5O₃ oxide is the best ac-tive catalyst for 1-2v% CH₄ among the oxides by changing B site compositions of LaBO₃ and su-perior to La_0.3Sr_0.2MnO₃ and La_0.6S_0.4MnO₃catalysts.Adding trace Pd improved the activity and characteristics of space velocity for LaMn_0.5CO_0.5O₃and La_0.3Sr_0.2MnO₃ Although LaMn_0.5Co_0.5O₃ +Pd (0.03 wt%) was less active than the Pd catalyst,the activity was more than Pt catalyst at a conversion level below 90%.     

CuO对贵金属/CeO_2/Al_2O_3催化剂的作用

制备含少量贵金属Ｐｔ、Ｐｄ 的不同Ｃｕ 和Ｃｅ摩尔含量比（０∶１０，１∶９，２∶８）的催化剂，实验条件下加入ＣｕＯ可以提高Ｐｔ催化剂的二效活性；加入Ｃｕ∶Ｃｅ＝ ２∶８ 的ＣｕＯ降低了Ｐｄ 催化剂的三效性能，然而Ｃｕ∶Ｃｅ＝ １∶９时可以改善Ｐｄ 催化剂的三效催化性能⒚通过结构分析，认为ＣｕＯ的存在可以提高Ｐｄ 催化剂的比表面积，改善ＰｄＯ的分散度