木材胶粘剂生产中的污染及防治

阐述了木材胶粘剂－脲醛树脂胶粘剂（ＵＦ）,密胺甲醛树脂胶粘剂（ＭＦ）,酚醛树脂胶粘剂（ＰＦ）生产过程中产生的废气,釜垢及碱洗废液的污染,提出了从工艺上改善排放条件及治理的方法,同时提出了控制产品中游离甲醛的方法。     

超高交联树脂对酚类化合物吸附动力学研究

文章重点研究超高交联树脂NDA-100对苯酚的静态吸附动力学,通过动力学实验探讨了不同温度和初始浓度对吸附苯酚的影响,实验结果表明:苯酚在NDA-100树脂上的静态吸附动力学过程符合准二级动力学方程,其吸附速率受膜扩散和颗粒内扩散共同控制,对于高浓度的苯酚溶液微孔填充占主导作用,而低浓度的苯酚溶液表现为先经过大孔吸附后经由微孔填充两个阶段,低浓度吸附时出现双平台动力学现象。进一步阐述了超高交联树脂对于酚类化合物的吸附机理,为树脂固定床吸附酚类化合物的研究和实际工业应用提供理论基础。     

三层混床技术在水处理装置中的应用

某化肥厂水处理装置采用混合离子交换器生产精制水,针对现存的阴阳双层离子交换树脂交叉污染问题,在不改变设备结构及工艺的前提下,采用三层混床技术将阴阳离子树脂彻底分离,有效消除了交叉污染问题,再生次数减少,混床运行周期平均延长到10d,周期制水量由原来的3.02×104 m3提高到4.32×104 m3;再生酸碱消耗量、用水量和污水排放量都得到了降低。     

Simultaneous adsorption of lead and cadmium on MnO2-loaded resin

MnO2-loaded D301 weak basic anion exchange resin has been used as adsorbent to simultaneously remove lead and cadmium ions from aqueous solution. The e ects of adsorbent dosage, solution pH and the coexistent ions on the adsorption were investigated. Experimental results showed that with the adsorbent dosage more than 0.6 g/L, both Pb2+ and Cd2+ were simultaneously removed at pH range 5–6. Except for HPO4 2??, the high concentration coexistent ions such as Na+, K+, Cl??, NO3??, SO4 2?? and HCO3??, showed no significant e ect on the removal e ciency of both Pb2+ and Cd2+ under the experimental conditions. The coexistence of Mg2+, Ca2+ caused the reduction of Cd2+ removal, but not for Pb2+. The adsorption equilibrium for Pb2+ and Cd2+ could be excellently described by the Langmuir isotherm model with R2 > 0.99. The maximum adsorption capacity was calculated as 80.64 mg/g for Pb2+ and 21.45 mg/g for Cd2+. The adsorption processes followed the pseudo first-order kinetics model. MnO2-loaded D301 resin has been shown to have a potential to be used as an e ective adsorbent for simultaneous removal of lead and cadmium ions from aqueous solution.     

环氧固化剂及其应用与发展

介绍了环氧固化剂的分类,包括显在型与潜伏型两大类,显在型主要有胺类、酸酐类、合成树脂类以及硫醇类,潜伏型以双氰胺和咪唑类为主。详细论述了各种环氧固化剂的优缺点,胺类可室温固化,酸酐类综合性能优异,合成树脂类与硫醇类分别具有耐化学性能与防腐性能。简述了多元胺类、叔胺类与咪唑类固化剂及固化机理,即通过固化剂中的活性原子进攻环氧基,开环加成形成交联结构并赋予环氧树脂性能。最后叙述了各类固化剂在胶黏剂与涂料中的应用,并展望了其在耐热性能、力学性能、绿色环保方面的发展趋势。     

Removal of cadmium using MnO2 loaded D301 resin

MnO2 loaded weak basic anion exchange resin D301 （Anion exchange resin, macroreticular weak basic styrene） as adsorbent has been prepared and applied to the removal of cadmium. The adsorption characteristics have been investigated with respect to effect of pH, equilibrium isotherms, removal kinetic data, and interference of the coexisting ions. The results indicated that the Cd^2＋ could be efficiently removed using MnO2 loaded D301 resin in the pH range of 3-8 from aqueous solutions with the co-existence of high concentration of alkali and alkaline-earth metals ions. The saturate adsorption capacity of the Cd^2＋ was 77.88 mg/g. The adsorption process followed the pseudo first-order kinetics. The equilibrium data obtained in this study accorded excellently with the Langmuir adsorption isotherm.     

大孔树脂吸附去除水中的2,4,6-三硝基甲苯

研究了2种大孔树脂XAD-4和NDA-804对水中的TNT的吸附行为。2种树脂对TNT的吸附等温线表明,温度的升高有利于吸附,在35℃条件下XAD-4树脂与NDA-804树脂对TNT的最高平衡吸附量分别达82.86 mg/g和94.26mg/g。采用Langmuir方程和Freundlich方程用于吸附等温线的解释,结果表明,吸附等温线更加符合Langmuir模型,相关系数均大于0.99。TNT在2种树脂上的吸附符合准二级动力学方程,TNT初始浓度越低,达到吸附平衡所需时间越短,在1 h内可达到吸附平衡。采用NDA-804处理对TNT废水,废水中TNT浓度由103.58 mg/L降至0.4 mg/L,去除率达99.6%,吸附后的树脂采用pH=2的乙醇和盐酸的混合液脱附可再生,高浓度再生溶液经蒸馏可回收TNT,实现了废水治理与资源化。     

阳离子树脂法提取活性污泥胞外聚合物的研究

考察了树脂法提取活性污泥中胞外聚合物（extracellular polymeric substance,EPS）的影响因素,确定了最佳的提取条件.试验结果表明,树脂量60g/g VSS,振摇频率200r/min下处理4 h,EPS的提取量达到111.20 mg/L,DNA占提取量的12.13%.该方法的重现性试验结果还表明,EPS及其各成分的相对标准偏差在2.21%～6.07%之间,能较好地满足试验要求,是一种可靠的EPS提取方法.     

废旧线路板真空热解油合成热固性酚醛树脂

以废旧线路板真空热解油为原料,NaOH为催化剂,与甲醛的缩聚反应合成热固性酚醛树脂(TPR),重点考察了合成条件对产物固含量的影响。结果表明,合成热固性酚醛树脂的最佳条件为:每38.5 g热解油加入甲醛、催化剂分别为40 g、10 g,第1阶段温度为60℃、反应时间为3 h,第2阶段温度为95℃、反应时间按为3 h,其中催化剂的加入量是最主要的影响因素。通过红外光谱分析(IR)及热重分析(TG)测定了合成产物的结构和性能,并对产物进行了力学性能的检测。结果证明,以热解油为原料合成的酚醛树脂出现了CH2、CH—OH等特征峰,且产物的耐热温度在300℃以上,拉伸强度达到了39.6 MPa,与以苯酚为原料合成的酚醛树脂相近,研究结果表明,真空热加油为原料合成酚醛树脂是可行的。     

树脂吸附法预处理增塑剂DOP生产废水

高浓度DOP生产废水生物毒性强,采用常规手段难以有效处理,对环境存在较高危害性。采用树脂吸附技术预处理增塑剂DOP生产废水,考察了树脂吸附与脱附的最佳工艺条件,结果表明,采用NDA99吸附树脂,在室温、吸附pH=2、吸附流速4 BV/h条件下,每批次处理量16 BV,COD去除率可达94%以上;对吸附饱和的树脂采用1 BV 8%NaOH+1 BV 4%NaOH+2 BV水,在60℃下以1 BV/h的流速进行脱附,COD脱附率超过97%,树脂的吸附-脱附性能良好。