水分管理对稻田土壤铁氧化物形态转化的影响及其与镉活性变化的耦合关系

稻田土壤水分管理过程中铁氧化物的形态转化对土壤镉（Cd）活性和水稻Cd累积具有重要影响.以西南地区紫色水稻土为研究对象,通过室内培养试验,探讨了淹水管理方式（持续淹水,CW;干湿交替,DW）联合铁氧化物（针铁矿,G-Fe;铁粉,Fe）施用对Cd污染土壤的pH、氧化还原性质（Eh、pe+pH）、铁氧化物形态转化和Cd有效性变化的影响,分析了水分管理驱动下铁氧化物形态转化与土壤Cd活性演变的耦合关系.结果表明CW管理可显著降低土壤Cd有效性,淹水93 d后DTPA-Cd降低了17.7%~39.2%,CW联合Fe或G-Fe施用显著提升了对土壤Cd的钝化效果,其中G-Fe短期钝化效果好,淹水14 d后DTPA-Cd的含量较对照降低24.3%,而Fe则可持续钝化土壤Cd,淹水93 d后DTPA-Cd的降幅为39.2%,干湿交替下施用铁氧化物则对土壤Cd无钝化效应.相关性分析表明,无定形铁（Fe_o）的形成（P<0.01）是驱动土壤Cd有效性变化的主要原因：CW使土壤pH逐渐降低并稳定在7.4左右,且土壤保持还原状态,促进了土壤铁氧化物由结晶态（Fe_c）向Fe_o转化,进而促使Cd由可交换态向铁锰结合态转化,并最终导致Cd有效性降低;CW联合Fe、G-Fe施用显著提升了Fe_o的含量和比例,从而强化了对土壤Cd的钝化效果.研究结果揭示了水分管理联合铁氧化物施用对稻田土壤Cd活性的调控效应和机制,为Cd污染稻田土壤安全利用中水分优化管理和含铁钝化剂施用提供了科学依据.     

天津市滨海河流N2O扩散通量及控制因子

河流是大气温室气体重要的排放源.为了探讨天津市典型景观滨海河流N₂O释放空间特征及影响因素,以天津市6条不同土地利用类型的滨海河流为研究对象,通过顶空-气相色谱法测定了N₂O浓度、饱和度和扩散通量.结果表明,天津市不同景观河流N₂O浓度都处于过饱和状态,表现为大气N₂O的源;N₂O浓度、饱和度和扩散通量均值为（23.85±15.20）nmol·L^-1、（309.71±197.38）%和（27.04±16.46）μmol·（m²·d）^-1,范围分别为12.70～115.69 nmol·L^-1、 164%～1 502%和9.17～244.79μmol·（m²·d）^-1.天津市不同土地利用类型河流N₂O浓度和扩散通量具有较大的空间异质性,表现为：排污河>城市河流>郊区河流>农业河流.天津滨海河流N₂     

氧化铜纳米颗粒(CuO NPs)对土壤环境因子与砷生物有效性的影响

氧化铜纳米颗粒（CuO NPs）可以通过农药和肥料施用、意外泄露或污水灌溉进入As污染农田土壤,从而对土壤环境因子和As生物有效性产生影响.本试验选取两种不同类型土壤（安徽宿松黄棕壤和黑龙江海伦黑土）进行人工As污染,添加不同浓度的CuO NPs,探究90 d淹水-落干过程中CuO NPs对As污染农田环境因子和As生物有效态的影响.结果表明,CuO NPs进入土壤后12 h内快速溶解产生Cu²⁺,且在黄棕壤中的溶解速度较黑土迅速.CuO NPs可在短时间内降低土壤pH,提高土壤氧化还原电位（E_h）,降低土壤电导率（EC）,但随着培养时间增加土壤EC逐渐提高.一定时间内CuO NPs在两种类型土壤中可降低51.0%~82.5%土壤浸出液中的As和15.7%~66.5%的As生物有效性,减少淹水时Fe （II）的含量.但在土壤落干时期产生一定的“纳米效应”从而促进了Fe （II）的产生.研究表明,CuO NPs进入As污染农田改变了土壤环境因子,一定时间内降低了土壤As生物有效性.     

不同SAPO分子筛负载MnOx催化剂的低温NH3-SCR性能研究

以磷酸硅铝分子筛SAPO-5、SAPO~(-1)1和SAPO-34为载体,采用乙醇分散法制备了用于低温氨选择性还原(NH_3-SCR)NO_x的分子筛负载MnO_x催化剂.活性测试结果显示,3种分子筛催化剂均展现出优良的NH_3-SCR活性,但三者在低温区间的SCR活性存在较明显差异,其SCR活性顺序如下:MnO_x/SAPO-34MnO_x/SAPO-5MnO_x/SAPO~(-1)1.借助XRD、N2吸附-脱附、XPS、H2-TPR、NH_3-TPD、NH_3FT-IR等技术对催化剂的表面活性物种及表面酸性等进行表征分析,结果表明,MnO_x主要以无定型状态分散于载体上,负载后载体的比表面积和孔体积均有所下降.XPS和H2-TPR分析证实,不同分子筛载体上MnO_x的表面浓度与氧化态明显不同.NH_3-TPD和NH_3FT-IR分析揭示了催化剂表面均存在Bronsted酸位和Lewis酸位,其中,Lewis酸性位对低温SCR反应起着关键作用.研究表明,催化剂的催化性能会因载体不同而存在差异,高Mn4+表面浓度和丰富的Lewis酸性位对催化剂在低温区间实现优良的催化活性尤为重要.     

燃煤烟气同时脱硫脱硝方法的研究进展及分析

近年来,烟气同时脱硫脱硝技术因占地面积小,可同时控制多种污染物而引起广泛的关注,但该技术多数仍停留在实验阶段。文章重点介绍了等离子体法、固相吸附法、溶液吸收法及微生物法等方法研究进展,对各方法的脱硫脱硝特点及功效进行评述,分析其问题与不足,并提出燃煤烟气同时脱硫脱硝方法的研究方向,为同时脱硫脱硝技术的改进提出建议。     

Long-term effects of silver nanoparticles on performance of phosphorus removal in a laboratory-scale vertical flow constructed wetland

Silver nanoparticles(AgNPs) have been widely used in many fields,which raised concerns about potential threats to biological sewage treatment systems.In this study,the phosphorus removal performance,enzymatic activity and microbial population dynamics in constructed wetlands(CWs) were evaluated under a long-term exposure to Ag NPs(0,50,and 200 μg/L) for 450 days.Results have shown that Ag NPs inhibited the phosphorus removal efficiency in a short-term exposure,whereas caused no obviously negative effects from a long-term perspective.Moreover,in the coexisting CW system of Ag NPs and phosphorus,competition exhibited in the initial exposure phase,however,cooperation between them was observed in later phase.Enzymatic activity of acid-phosphatase at the moderate temperature(10–20°C) was visibly higher than that at the high temperature(20–30℃) and CWs with Ag NPs addition had no appreciable differences compared with the control.High-throughput sequencing results indicated that the microbial richness,diversity and composition of CWs were distinctly affected with the extension of exposure time at different Ag NPs levels.However,the phosphorus removal performance of CWs did not decline with the decrease of polyphosphate accumulating organisms(PAOs),which also confirmed that adsorption precipitation was the main way of phosphorus removal in CWs.The study suggested that Ag NPs and phosphorus could be removed synergistically in the coexistence system.This work has some reference for evaluating the influences of Ag NPs on the phosphorus removal and the interrelation between them in CWs.     

农田土壤施用系列新型氮肥后气态氮(NH3和N2O)减排效果比较:以夏玉米季为例

为了解不同品种新型氮肥相对常规施肥其氨(NH3)和氧化亚氮(N_2O)的减排效果,本文通过田间原位试验同步研究了夏玉米生长季氮肥施用后的农田NH_3挥发和N_2O排放及其主要驱动因子.以常规施肥(复合肥+尿素,CK)为对照,设置了5个肥料处理,分别为脲铵氮肥(UA)、稳定性复合肥料(UHD)、硫包衣氮肥(SCU)、脲甲醛复合肥(UF)和有机肥(OF),施氮量(以N计)均为300 kg·hm~(-2).相关分析结果表明,氨挥发和N_2O排放受环境因子影响,均与土壤WFPS呈显著负相关(P0.05),N_2O排放还与土壤硝态氮呈极显著正相关(P0.01).进一步回归分析表明,N_2O排放(F_(N_2O))主要取决于土壤硝态氮(x)含量的变化,而氨挥发(F_(NH_3))主要取决于土壤铵态氮(x)含量的变化.与CK相比,除了UA,其它肥料处理都降低了土壤的氨挥发,尤其是UF和OF处理减少了37%~43%.但对于N_2O排放,所有处理与CK皆无显著差异.进一步计算每种处理氨挥发和N_2O的气态氮损失总量,与CK相比,UHD、SCU、UF和OF分别减排了9%、5%、30%和23%,而UA增加了3%.     

自组装纳米金修饰玻碳电极检测亚硝酸根

将N-［3-(三甲氧硅基)丙基］-乙二胺与金溶胶通过自组装制备亚硝酸根的电化学传感器.原子力显微镜图(AFM) 显示纳米金自组装在氨基硅烷修饰的玻碳电极表面.由于质子化的氨基硅烷与带负电的亚硝酸根间的相互作用以及纳米金对亚硝酸根具有较好的催化作用,亚硝酸根在该修饰电极上的氧化电位与在玻碳电极上的氧化电位相比负移了140 mV.利用微分脉冲伏安法和微分脉冲安培法研究了亚硝酸根电流响应信号与浓度间的关系.在最优实验条件下,亚硝酸根的氧化峰电流与其浓度在5.0×10^-7～1.0×10^-3 mol·L^-1的浓度范围内呈良好的线性关系, 检测限可达到2.0×10^-7 mol·L^-1(信噪比为3). 用分光光度法及本研究提出的方法对实际样品中亚硝酸根的测定进行了比较,测定结果的差异很小.本研究所提出的测定亚硝酸根的方法具有较高的灵敏度和较好的重现性.     

多孔氧化铝层制备的研究

采用预腐蚀与交流腐蚀相结合的方法．研究了多孔氧化铝层的制备工艺．探讨了制备工艺中各步骤的作用以及影响因素。利用扫描电镜，研究了多孔氧化铝层制备工艺对铝箔微观形貌的影响。研究表明．交流腐蚀工艺对铝箔表面微观形貌的改变作用最明显。一次后处理后铝箔表面蚀孔变密．氧化膜的结构更加疏松细腻。二次后处理，调整和热处理等步骤对铝箔表面的微观形貌影响不大。     

负载型金属氧化物催化剂分解臭氧的研究

用浸渍法制备了活性炭、γ-氧化铝和分子筛负载的MnO2,CuO,Fe2O3催化剂,并考察了它们对臭氧分解的催化性能。结果表明,MnO2催化剂优于CuO,Fe2O3,催化剂,活性炭为载体的催化剂优于γ-氧化铝和分子筛为载体的催化剂。温度对臭氧催化分解影响很大,在90℃时,MnO2／AC催化剂对臭氧的去除率可达80％以上。当存在一定浓度的水蒸气时,湿度越大,催化性能越差。当臭氧初始质量浓度低于50mg／L时,随着臭氧初始浓度的增加,催化性能有一定的下降。