Effect of platinum on the photocatalytic degradation of chlorinated organic compound

TiO2 nanoparticles, doped with di erent Pt contents, were prepared by a modified photodeposition method using Degussa P-25 TiO2, H2PtCl6 6H2O and methanol as the solvents. The physicochemical properties of Pt/TiO2 were investigated by the nitrogen adsorption and desorption isotherm measurement technique, X-ray di raction analysis and photoluminescence spectra, respectively. Reaction rates from photocatalytic removal of dichloromethane over Degussa P-25 TiO2 and Pt/TiO2 were evaluated. The average diameter and BET surface area of the TiO2 catalyst particles were 300 nm and 50 m2/g, respectively. The degradation e ciency was 99.0%, 82.7%, 55.2%, and 57.9% with TiO2 at inlet concentrations of 50, 100, 200, and 300 ppm, respectively. And the degradation e ciency was 99.3%, 79.7%, 76.5%, and 73.4% with a 0.005 wt.% Pt/TiO2 at inlet concentrations of 50, 100, 200, and 300 ppm, respectively. In addition, we found that the photoluminescence emission peak intensities decreased with increases in the doping amount of Pt, which indicates that the irradiative recombination was weakened. Furthermore, the results showed that the UV/0.005 wt.% Pt/TiO2 process was capable of e ciently decomposing gaseous DCM in air.     

Application of magnetic particles modified with amino groups to adsorb copper ions in aqueous solution

A magnetic adsorbent can be easily recovered from treated water by magnetic force,without requiring further downstream treatment.In this research,amine-functionalized silica magnetite has been synthesized using N-[3-(trimethoxysilyl)propyl]-ethylenediamine(TPED) as a surface modification agent.The synthesized magnetic amine adsorbents were used to adsorb copper ions in an aqueous solution in a batch system,and the maximum adsorption was found to occur at pH 5.5 ± 0.1.The adsorption equilibrium data fitted t...     

TiO2 nanotubes as solid-phase extraction adsorbent for the determination of polycyclic aromatic hydrocarbons in environmental water samples

An analytical method based on TiO2 nanotubes solid-phase extraction (SPE) combined with gas chromatography (GC) was established for the analysis of seven polycyclic aromatic hydrocarbons (PAHs): acenaphtylene, acenaphthene, anthracene, fluorene, phenanthrene, fluoranthene and pyrene. Factors a ecting the extraction e ciency including the eluent type and its volume, adsorbent amount, sample volume, sample pH and sample flow rate were optimized. The characteristic data of analytical performance were determined to investigate the sensitivity and precision of the method. Under the optimized extraction conditions, the method showed good linearity in the range of 0.01–0.8 g/mL, repeatability of the extraction (RSD were between 6.7% and 13.5%, n = 5) and satisfactory detection limits (0.017–0.059 ng/mL). The developed method was successfully applied to the analysis of surface water (tap, river and dam) samples. The recoveries of PAHs spiked in environmental water samples ranged from 90% to 100%. All the results indicated the potential application of titanate nanotubes as solid-phase extraction adsorbents to pre-treat water samples.     

Adsorptive property of Cu^2＋-loaded montmorillonite clays for Escherichia coli K_（88） in vitro

The Cu²⁺-loaded montmorillonite clays (MMT-Cu) may be a good material for the adsorbed and eliminated pathogenic bacteria from aqueous solution.     

Modification of Ce02-ZrO2 catalyst by potassium for NOx-assisted soot oxidation

Potassium-modified ceria-zirconia catalyst was synthesized by wetness impregnation method. The ageing treatment was performed in static air at 800℃ for 20 hr to evaluate the thermal stability of the catalyst. The catalysts were characterized by X-ray diffraction,BET surface area, oxygen storage capacity, NOx-temperature programmed desorption and soot-temperature programmed oxidation measurements. By introduction of potassium, the maximum soot oxidation rate temperature (Tm) of the ceria-zirconia based catalyst decreased from 525 to 428℃ in the presence of NO under a loose contact mode. The shift of Tm of the K-modified catalyst after ageing is only 15℃. The enhanced activity of the aged catalyst mainly lies in the promotional effect of potassium on the NOx/oxygen storage cacity as well as the soot-catalyst contact.     

中心组合设计优化S-Cr-TiO2催化剂光降解工艺条件

在确定的温度和光照条件下,采用中心组合设计法研究了固相反应法合成的硫与铬共掺杂二氧化钛(S-Cr-TiO2)光催化剂与水溶苯胺蓝(ANB)可见光降解过程中的三个作用因子:催化剂的浓度、水溶苯胺蓝水溶液的pH值及其初始浓度之间的相互作用关系,得到了影响因子与降解速率之间的回归方程及因素之间相互作用的响应面图.结果表明,S...     

Ti/SnO2-Sb2O5/PbO2阳极电化学氧化降解苯甲酸研究

文章研究了TI/SnO2-Sb2O5/Pbo2在两室电解池中氧化降解苯甲酸的性能,主要考察了电流密度、初始pH值、初始苯甲酸浓度和支持电解质这四个参数对TOC去除效率的影响。实验表明在电流密度为30 mA/cm2,初始苯甲酸浓度为0.5 mmol/L,支持电解质(Na2SO4)为0.1mol/L的条件下,经过6 h反应...     

H2O2胁同三维电极法处理罗丹明B废水的研究

为了了解过氧化氢与三维电极的协同作用,以罗丹明B模拟废水进行了实验研究,探索了填料配比、外加电压、过氧化氢投加量、初始废水pH值、染料初始浓度等单因子对降解罗丹明B的影响,并通过正交试验研究各因素对该法处理罗丹明B模拟废水的效应.结果表明,过氧化氢与三维电极在处理罗丹明B模拟废水时具有明显的协同作用;外加电压=20v,...     

聚丙烯中空纤维膜吸收法烟气脱硫实验研究

采用质量分数为30%的甲基二乙醇胺(MDEA)水溶液为烟气SO2吸收液,聚丙烯(PP)中空纤维微孔膜组件为吸收器,研究吸收液温度、流量变化,气体停留时间,以及气液两相流程等操作条件对聚丙烯(PP)中宅纤维膜脱硫率的影响,研究表明30%MDEA水溶液在温度35℃,流量100mL/min的最佳试验条件下,经过一个膜吸收过程...     

提高煤层气采收率的CO2埋存技术

作为常规油气重要接替补充的非常规天然气,煤层气越来越受到世人的关注.如何提高煤层气采收率是摆在煤层气开发工程师面前迫切需要解决的技术难题.通过向煤层中注入CO2,既可以提高煤层气采收率又能间接地实现CO2减排,即提高煤层气采收率的CO2埋存技术(CO2-ECBM).该项技术已在世界各地迅速发展,并取得一些实质性进展.文...